CN107789662A - A kind of diaper and preparation method thereof - Google Patents
A kind of diaper and preparation method thereof Download PDFInfo
- Publication number
- CN107789662A CN107789662A CN201711125874.XA CN201711125874A CN107789662A CN 107789662 A CN107789662 A CN 107789662A CN 201711125874 A CN201711125874 A CN 201711125874A CN 107789662 A CN107789662 A CN 107789662A
- Authority
- CN
- China
- Prior art keywords
- parts
- diaper
- resin material
- high hydroscopic
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of diaper and preparation method thereof, diaper includes top layer, sandwich layer and bottom, and top layer is the bamboo fiber cloth for being attached with refrigerant slow-releasing granules；Sandwich layer is made up of high hydroscopic resin material, and being coupled on high hydroscopic resin material has antimicrobial granules；Bottom is made up of PE films.The preparation method of diaper of the present invention includes preparation, the preparation of sandwich layer and the preparation of diaper on top layer.The bamboo fiber cloth top layer of diaper of the present invention has the function of refrigerant anti-inflammatory, and the sandwich layer of diaper has the ability and sterilizing function that absorb urine well, and PE film bottoms can effectively prevent the seepage of urine.
Description
Technical field
The present invention relates to a kind of articles for babies field, more particularly to a kind of diaper and preparation method thereof.
Background technology
With expanding economy and the quickening of rhythm of life, diaper turns into the deep Baby Care liked by young mother and used
One of product.What " diaper " worked is the absorbent core layer that layer structure is made up of pure wood pulp and high hydroscopic resin.
The Water-absorbing high polymer species of existing diaper is a lot, but the macromolecule that urine is different, common from the composition of water
When absorbing urine, its absorbability substantially reduces material, while the antibacterial bacteriostatic effect of existing diaper is bad, deposits for a long time
Reused after putting and be easy to cause infant's skin infection.
The content of the invention
The technical problem to be solved in the present invention is：The present invention provides a kind of diaper, has the bamboo of dry and comfortable antibacterial functions fine
Tie up cloth softness top layer, there is the high hydroscopic resin sandwich layer of bacteria resistance function and the PE film bottoms of water lock, the present invention also provides a kind of urine
Not wet preparation method.
In order to solve the above-mentioned technical problem, diaper of the invention, including top layer, sandwich layer and bottom, top layer are to be attached with
The bamboo fiber cloth of refrigerant slow-releasing granules；Sandwich layer is made up of high hydroscopic resin material, and being coupled on high hydroscopic resin material has sterilization
Grain；Bottom is made up of PE films.
The top layer of diaper and direct skin contact, and the place of breed bacteria is easiest to, top layer is using soft bamboo
Fiber cloth, due to being soaked with top layer and the skin contact of urine, easily cause skin infection bacterium, and make infant occur eczema and
Red hip, infant dress diaper after skin infection bacterium and significantly increase sense of discomfort, therefore on the top layer of diaper
The refrigerant slow-releasing granules with antibacterial, refrigerant inflammation-diminishing function are inlayed, infant infection bacterium can be effectively avoided, slow down red hip and draw
The sense of discomfort risen, a kind of refrigerant, soft comfort is provided for infant, the refrigerant slow-releasing granules, by weight, including
Following component：Purslane 10-30 parts, dandelion 15-25 parts, Chloranthus glaber 5-15 parts, balloonflower root 2-10 parts, wintergreen 1-6 parts and smoke
Clothing grass essential oil 1-5 parts.
In order that salt resistant character of the form of the high hydroscopic resin prepared in cellular and raising water-absorbing resin, and make simultaneously
High hydroscopic resin has a function of bactericidal, the high hydroscopic resin material by weight, including following component：Asian puccoon 5-
15 parts, it is ginger 5-15 parts, cactus 2-8 parts, acrylic acid 60-100 parts, sodium carbonate 15-30 parts, polyacrylamide 20-35 parts, poly-
Vinyl alcohol 10-30 parts, kaolin 20-40 parts and N,N methylene bis acrylamide 0.04-0.08 parts.
In order that the form of the super absorbent resin material porous shape of diaper is made, and make top layer and the core of diaper
Layer has the effect of joint antibacterial bacteriostatic, the preparation method of diaper, comprises the following steps：
（1）The preparation on top layer：Purslane, dandelion, Chloranthus glaber and balloonflower root are taken, mixing decocts 2-3 times, takes all filtrates to mix,
After concentrated, wintergreen and Lavender are added, coating is dried, refrigerant slow-releasing granules are prepared, by refrigerant sustained release
In bamboo fiber cloth, the bamboo fiber cloth for being attached with refrigerant slow-releasing granules, refrigerant sustained release is prepared through spraying equipment sprayed coating in particle
The emitted dose of particle is every diaper 0.1-0.5g；
（2）The preparation of sandwich layer：The frequency of radio-frequency signal generator is 526Khz, power 1Kw, discharge time 3h, obtains modified kaolin；
Asian puccoon, ginger and cactus is taken to be mixed to prepare medicinal extract, spray-dried obtained antimicrobial granules；Sodium carbonate is taken to be slowly added into propylene
In acid, after being quickly well mixed, add polyacrylamide and polyvinyl alcohol uniformly mixes, add feature kaolin, stir
15min, N is eventually adding, N- methylene-bisacrylamides, is well mixed, mixture is put into two pieces of connection radio-frequency signal generator
Between copper coin, discharge 3min, after electric discharge terminates, all melts in 80 DEG C of heating water baths to reaction solution, after uniformly mixing, places
Lucifuge reacts 2h in 30 DEG C of waters bath with thermostatic control, then soaks resin material 24h with methanol, filtering, is put into oven for drying, through crushing
High hydroscopic resin material is obtained, antimicrobial granules are ejected into high hydroscopic resin material surface, obtained coupling there are antimicrobial granules
High hydroscopic resin material；
（3）The preparation of diaper：By bamboo fiber cloth top layer, high hydroscopic resin material sandwich layer and PE film bottoms by method hot rolling and
Stamp processing is fixed together, and diaper is made.
The beneficial effects of the invention are as follows：Diaper of the present invention includes top layer, sandwich layer and bottom, and top layer is bamboo fiber cloth, bamboo
The refrigerant slow-releasing granules with refrigerant, anti-inflammatory, antibacterial functions are uniformly inlayed in fiber cloth, refrigerant slow-releasing granules are dressed in infant
During rupture release function molecule, provide refrigerant soft comfort for infant, refrigerant slow-releasing granules are only gentle
Environment in rubbed and can just be ruptured, even if so diaper storage for a long time in natural environment remain on it is refrigerant,
Anti-inflammatory, the function of antibacterial, the skin for having infected bacterium, refrigerant slow-releasing granules also have treatment bacterium infection, promote skin
The effect of recovery.
The sandwich layer of diaper has the high hydroscopic resin material of Fungicidal substance for coupling, high hydroscopic resin material for it is inorganic-have
Machine composite resin material, the inorganic plasma-treated activation of kaolin, make kaolin surface that there is abundant hydrogen bond and sun
Ion so that high hydroscopic resin material has preferable salt tolerance, has larger absorbability to urine, while to high water absorption
The antimicrobial granules sprayed on resin are evenly distributed on the duct and surface of high hydroscopic resin material, can effectively avoid bacterium
Breeding, provide health sterile environment for infant.
Diaper PE film bottoms effectively can prevent diaper from oozing out.
When in use, urine first passes around sandwich layer of the top layer subsequently into diaper of diaper, urine core to diaper
The high hydroscopic resin material of layer is absorbed, and the refrigerant slow-releasing granules in top layer are handed over the Asian puccoon in sandwich layer, ginger and cactus
Join, purslane, dandelion, Chloranthus glaber, balloonflower root and Asian puccoon, ginger, cactus synergy in refrigerant slow-releasing granules, common suppression
The growth breeding of staphylococcus aureus, Escherichia coli and Candida albicans processed etc., and kill the golden yellow grape grown
Coccus, Escherichia coli and Candida albicans etc., meanwhile, the refrigerant slow-releasing granules on top layer also have refrigerant anti-inflammatory solution prickly heat and go to dislike
Smelly effect, effectively alleviate the humid sense for absorbing urine by diaper and bringing.
Embodiment
The present invention is prepared by the following method diaper, and the raw material is parts by weight：
（1）The preparation on top layer：Purslane, dandelion, Chloranthus glaber and balloonflower root are taken, mixing decocts 2-3 times, takes all filtrates to mix,
After concentrated, wintergreen and Lavender are added, coating is dried, refrigerant slow-releasing granules are prepared, by refrigerant sustained release
In bamboo fiber cloth, the bamboo fiber cloth for being attached with refrigerant slow-releasing granules, refrigerant sustained release is prepared through spraying equipment sprayed coating in particle
The emitted dose of particle is every diaper 0.3g；
（2）The preparation of sandwich layer：The frequency of radio-frequency signal generator is 526Khz, power 1Kw, discharge time 3h, obtains modified kaolin；
Asian puccoon, ginger and cactus is taken to be mixed to prepare medicinal extract, spray-dried obtained antimicrobial granules；Sodium carbonate is taken to be slowly added into propylene
In acid, after being quickly well mixed, add polyacrylamide and polyvinyl alcohol uniformly mixes, add modified kaolin, stir
15min, N is eventually adding, N- methylene-bisacrylamides, is well mixed, mixture is put into two pieces of connection radio-frequency signal generator
Between copper coin, discharge 3min, after electric discharge terminates, all melts in 80 DEG C of heating water baths to reaction solution, after uniformly mixing, places
Lucifuge reacts 2h in 30 DEG C of waters bath with thermostatic control, then soaks resin material 24h with methanol, filtering, is put into oven for drying, through crushing
High hydroscopic resin material is obtained, antimicrobial granules are ejected on high hydroscopic resin material, it is obtained to be coupled the height for having antimicrobial granules
Absorbing resin material, it is 31g that coupling, which has the weight of the high hydroscopic resin material of antimicrobial granules, in every diaper；
（3）The preparation of diaper：By bamboo fiber cloth top layer, high hydroscopic resin material sandwich layer and PE film bottoms by method hot rolling and
Stamp processing is fixed together, and diaper is made.
It is of the invention specific to implement following groups embodiment as stated above, the group of refrigerant slow-releasing granules in every group of embodiment
Divide and content is shown in Table 1, be coupled the component for the high hydroscopic resin material for there are antimicrobial granules in every group of embodiment and content is shown in Table 2, its
The degree of polymerization of middle polyvinyl alcohol is 2800-3200.
Table 1
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | |
| Purslane | 20 parts | 30 parts | 25 parts | 24 parts |
| Dandelion | 20 parts | 15 parts | 18 parts | 24 parts |
| Chloranthus glaber | 10 parts | 10 parts | 12 parts | 10 parts |
| Balloonflower root | 6 parts | 4 parts | 4 parts | 2 parts |
| Wintergreen | 4 parts | 4 parts | 2 parts | 2 parts |
| Lavender | 2 parts | 2 parts | 2 parts | 2 parts |
Table 2
| Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | |
| Asian puccoon | 10 parts | 15 parts | 12 parts | 10 parts |
| Ginger | 10 parts | 10 parts | 12 parts | 15 parts |
| Cactus | 6 parts | 2 parts | 4 parts | 6 parts |
| Acrylic acid | 80 parts | 90 parts | 90 parts | 90 parts |
| Sodium carbonate | 22 parts | 25 parts | 28 parts | 18 parts |
| Polyacrylamide | 28 parts | 30 parts | 30 parts | 32 parts |
| Polyvinyl alcohol | 25 parts | 25 parts | 28 parts | 24 parts |
| Kaolin | 28 parts | 30 parts | 32 parts | 25 parts |
| N,N methylene bis acrylamide | 0.04 part | 0.05 part | 0.05 part | 0.05 part |
The high hydroscopic resin material obtained to above example carries out physiological saline water absorption and the performance of rate of liquid aspiration is surveyed
Bactericidal property after examination, the bactericidal property of the diaper obtained to above example and storage one month is tested, test knot
Fruit is as shown in table 3.Wherein the method for testing of uptake is according to National Standard of the People's Republic of China, paper diaper water-absorbing resin GB/
T22905-2008 and sanitary napkin high hydroscopic resin GB/T22975-2008, anti-microbial property test method are total to according to the Chinese people
With state's national standard, Disposable Sanitary Accessory sanitary standard GB/T15979-2002.
Table 3
| Physiological saline liquid absorbency rate g/g | Rate of liquid aspiration s | Bactericidal property % | Bactericidal property %（After storage one month） | |
| Embodiment 1 | 57.2 | 46 | 92 | 92 |
| Embodiment 2 | 56.8 | 47 | 86 | 86 |
| Embodiment 3 | 56.2 | 48 | 90 | 90 |
| Embodiment 4 | 54.3 | 52 | 91 | 91 |
As can be seen from the table, the high hydroscopic resin material in diaper of the present invention has preferable absorbability to urine, can
Effectively prevent the seepage of urine；Diaper of the present invention has preferable antibiotic and sterilizing effect, and diaper of the present invention through depositing for a long time
Put that bactericidal effect is also constant, can effectively reduce the incidence of disease of red hip and improve the wearing comfort of diaper.
The emitted dose of above-mentioned refrigerant slow-releasing granules and the addition of high hydroscopic resin material are only institute in the embodiment of the present invention
With data, the emitted dose of refrigerant slow-releasing granules and the specific addition of high hydroscopic resin material regard urine in diaper during actual production
Not wet size adjusts.
Claims (4)
1. a kind of diaper, including top layer, sandwich layer and bottom, it is characterised in that top layer is the bamboo for being attached with refrigerant slow-releasing granules
Fiber cloth；Sandwich layer is made up of high hydroscopic resin material, and being coupled on high hydroscopic resin material has antimicrobial granules；Bottom is by PE film structures
Into.
A kind of 2. diaper according to claim 1, it is characterised in that by weight, the refrigerant slow-releasing granules, bag
Include following component：Purslane 10-30 parts, dandelion 15-25 parts, Chloranthus glaber 5-15 parts, balloonflower root 2-10 parts, wintergreen 1-6 parts and
Lavender 1-5 parts.
A kind of 3. diaper according to claim 2, it is characterised in that by weight, the high hydroscopic resin material
Including following component：Asian puccoon 5-15 parts, ginger 5-15 parts, cactus 2-8 parts, acrylic acid 60-100 parts, sodium carbonate 15-30 parts,
Polyacrylamide 20-35 parts, polyvinyl alcohol 10-30 parts, kaolin 20-40 parts and N,N methylene bis acrylamide 0.04-
0.08 part.
4. the preparation method of a kind of diaper as described in claim 1,2 or 3, it is characterised in that comprise the following steps：
（1）The preparation on top layer：Purslane, dandelion, Chloranthus glaber and balloonflower root are taken, mixing decocts 2-3 times, takes all filtrates to mix,
After concentrated, wintergreen and Lavender are added, coating is dried, refrigerant slow-releasing granules are prepared, by refrigerant sustained release
In bamboo fiber cloth, the bamboo fiber cloth for being attached with refrigerant slow-releasing granules is prepared through spraying equipment sprayed coating in particle；
（2）The preparation of sandwich layer：Kaolin corona treatment is taken, the frequency of radio-frequency signal generator is 526Khz, power 1Kw, is put
Electric time 3h, obtains modified kaolin；Asian puccoon, ginger and cactus is taken to be mixed to prepare medicinal extract, it is spray-dried to obtain antimicrobial granules；
Take sodium carbonate to be slowly added into acrylic acid, after being quickly well mixed, add polyacrylamide and polyvinyl alcohol uniformly mixes, then
Modified kaolin is added, stirs 15min, N is eventually adding, N- methylene-bisacrylamides, is well mixed, mixture is put into company
Between connecing two pieces of copper coins of radio-frequency signal generator, discharge 3min, after electric discharge terminates, all melts to reaction solution in 80 DEG C of heating water baths
Change, after uniformly mixing, be then placed within lucifuge in 30 DEG C of waters bath with thermostatic control and react 2h, then soak resin material 24h with methanol,
Filtering, is put into oven for drying, obtains high hydroscopic resin material through crushing, antimicrobial granules are ejected into high hydroscopic resin material
On；
（3）The preparation of diaper：By bamboo fiber cloth top layer, high hydroscopic resin material sandwich layer and PE film bottoms by method hot rolling and
Stamp processing is fixed together, and diaper is made.