CN107777991A - Bonding mud suitable for unlike material pug - Google Patents
Bonding mud suitable for unlike material pug Download PDFInfo
- Publication number
- CN107777991A CN107777991A CN201711076408.7A CN201711076408A CN107777991A CN 107777991 A CN107777991 A CN 107777991A CN 201711076408 A CN201711076408 A CN 201711076408A CN 107777991 A CN107777991 A CN 107777991A
- Authority
- CN
- China
- Prior art keywords
- mud
- bonding
- bonded
- bonding mud
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bonding mud suitable for unlike material pug, the chemical composition of the cohesive mud is by weight：12.18~17.96% calcium phosphate, 9.18~20.96% ripe powder, 2.18~3.96% methylcellulose, 7.65~14.73% calcium dihydrogen phosphate, 3.64~6.92% sodium metaphosphate, remaining composition be with thing identical material to be bonded, the weight of above-mentioned chemical composition is than sum for absolutely；Baume concentration when the bonding mud uses is 63~66 °.The present invention forms the siccative constituent for bonding mud with thing identical material to be bonded by being mixed from calcium phosphate, ripe powder, methylcellulose, calcium dihydrogen phosphate, sodium metaphosphate, and Baume concentration is controlled at 63~66 ° after adding water during use, so that the part bonded through the bonding mud, can be fully solved dry body bond loosely, burn till after cracked phenomenon, therefore suitably promote the use of.
Description
Technical field
The present invention relates to ceramic technical field, specifically a kind of bonding that can be adapted to unlike material pug
Mud.
Background technology
Existing cohesive mud in use, often occur dry body bond loosely, burn till after it is cracked phenomena such as so that
The defects of product, rate reached more than 30%；Particularly some comparison particular strains, if bonding piece is than relatively thin part, it is easier to
There is drawbacks described above.
The content of the invention
The purpose of the present invention is the defects of presence for prior art, there is provided one kind can solve the problem that dry body bond loosely, burn
Into it is cracked afterwards phenomena such as the bonding mud that can be adapted to unlike material pug.
The purpose of the present invention solves by the following technical programs：
A kind of bonding mud suitable for unlike material pug, it is characterised in that：The chemical composition of the cohesive mud is by weight：
12.18~17.96% calcium phosphate, 9.18~20.96% ripe powder, 2.18~3.96% methylcellulose, 7.65~14.73%
Calcium dihydrogen phosphate, 3.64~6.92% sodium metaphosphate, remaining composition be and thing identical material to be bonded, above-mentioned chemical group
Into weight than sum for absolutely；Baume concentration when the bonding mud uses is 63~66 °.
The chemical composition of the cohesive mud is by weight：14.00~15.85% calcium phosphate, 11.25~18.74%
Ripe powder, 2.67~3.45% methylcellulose, 9.08~12.59% calcium dihydrogen phosphate, 4.37~6.85% sodium metaphosphate,
Remaining composition be with thing identical material to be bonded, the weight of above-mentioned chemical composition is than sum for absolutely.
The preparation method of the cohesive mud is：Calcium phosphate, ripe powder, methylcellulose, calcium dihydrogen phosphate, sodium metaphosphate are pressed
According to corresponding ratio mix after be sent into ball mill ball milling, it is desirable to for the mesh of ball milling fineness 200 full by；Composition after ball milling with
Corresponding proportion mixes again with thing identical material to be bonded, agitated uniform rear acquisition finished product, through adding water when finished product uses
The bonding mud that Baume concentration is 63~66 ° is obtained afterwards.
Described ball mill Ball-milling Time is 12~14h.
Composition after ball milling is sent into mixer after being mixed again with thing identical material to be bonded with corresponding proportion and stirred
Mix 0.5~2h.
The present invention has the following advantages compared with prior art：
The present invention from calcium phosphate, ripe powder, methylcellulose, calcium dihydrogen phosphate, sodium metaphosphate by being mixed and thing phase to be bonded
Same material forms the siccative constituent for bonding mud, and controls Baume concentration at 63~66 ° after adding water during use so that warp
The part that the bonding mud bonds, can be fully solved dry body bond loosely, burn till after cracked phenomenon, therefore suitable promote
Use.
Embodiment
With reference to embodiment, the present invention is further illustrated.
A kind of bonding mud suitable for unlike material pug, the chemical composition for bonding mud are by weight：12.18~17.96%
Calcium phosphate, 9.18~20.96% ripe powder, 2.18~3.96% methylcellulose, 7.65~14.73% calcium dihydrogen phosphate,
3.64~6.92% sodium metaphosphate, remaining composition are to compare sum with thing identical material to be bonded, the weight of above-mentioned chemical composition
For absolutely；Baume concentration when the bonding mud uses is 63~66 °.Further, the chemical composition of the bonding mud is pressed
Weight ratio is：14.00~15.85% calcium phosphate, 11.25~18.74% ripe powder, 2.67~3.45% methylcellulose,
9.08~12.59% calcium dihydrogen phosphate, 4.37~6.85% sodium metaphosphate, remaining composition are and thing identical material to be bonded
Material, the weight of above-mentioned chemical composition is than sum for absolutely.The preparation method of above-mentioned cohesive mud is：By calcium phosphate, ripe powder, first
Base cellulose, calcium dihydrogen phosphate, sodium metaphosphate are sent into 12~14h of ball mill ball milling after being mixed according to corresponding ratio, it is desirable to are
The mesh of ball milling fineness 200 full by；Composition after ball milling mixes again with corresponding proportion with thing identical material to be bonded
Be sent into mixer afterwards and stir 0.5~2h, it is agitated uniformly after obtain finished product, during finished product use through plus water after acquisition Baume concentration be
63~66 ° of bonding mud.
A group of formula is provided below to further illustrate the bonding mud provided by the invention that can be adapted to unlike material pug.
A kind of bonding mud suitable for unlike material pug, the chemical composition for bonding mud are by weight：15.25% phosphoric acid
Calcium, 15.74% ripe powder, 2.85% methylcellulose, 11.59% calcium dihydrogen phosphate, 4.85% sodium metaphosphate, remaining composition
For with thing identical material to be bonded, the weight of above-mentioned chemical composition is than sum for absolutely.The preparation side of above-mentioned cohesive mud
Method is：Ball milling is sent into after calcium phosphate, ripe powder, methylcellulose, calcium dihydrogen phosphate, sodium metaphosphate are mixed according to corresponding ratio
Machine ball milling 12h, it is desirable to for the mesh of ball milling fineness 200 full by；Composition and corresponding proportion and thing phase to be bonded after ball milling
With material mix again after be sent into mixer stirring 1h, it is agitated uniformly after obtain finished product, finished product using when through add water after obtain
Obtain the bonding mud that Baume concentration is 63~66 °.
The present invention by from calcium phosphate, ripe powder, methylcellulose, calcium dihydrogen phosphate, sodium metaphosphate mix with it is to be bonded
Thing identical material forms the siccative constituent for bonding mud, and controls Baume concentration at 63~66 ° after adding water during use, makes
The part that must be bonded through the bonding mud, can be fully solved dry body bond loosely, burn till after cracked phenomenon, therefore suitably
Promote the use of.
The technological thought of above example only to illustrate the invention, it is impossible to protection scope of the present invention is limited with this, it is every
According to technological thought proposed by the present invention, any change done on the basis of technical scheme, the scope of the present invention is each fallen within
Within；The technology that the present invention is not directed to can be realized by prior art.
Claims (5)
- A kind of 1. bonding mud suitable for unlike material pug, it is characterised in that：The chemical composition of the cohesive mud is by weight： 12.18~17.96% calcium phosphate, 9.18~20.96% ripe powder, 2.18~3.96% methylcellulose, 7.65~14.73% Calcium dihydrogen phosphate, 3.64~6.92% sodium metaphosphate, remaining composition be and thing identical material to be bonded, above-mentioned chemical group Into weight than sum for absolutely；Baume concentration when the bonding mud uses is 63~66 °.
- 2. the bonding mud according to claim 1 suitable for unlike material pug, it is characterised in that：The chemistry of the cohesive mud Form and be by weight：14.00~15.85% calcium phosphate, 11.25~18.74% ripe powder, 2.67~3.45% methyl are fine Dimension element, 9.08~12.59% calcium dihydrogen phosphate, 4.37~6.85% sodium metaphosphate, remaining composition are identical with thing to be bonded Material, the weight of above-mentioned chemical composition is than sum for absolutely.
- 3. the bonding mud according to claim 1 or 2 suitable for unlike material pug, it is characterised in that：The cohesive mud Preparation method is：Sent after calcium phosphate, ripe powder, methylcellulose, calcium dihydrogen phosphate, sodium metaphosphate are mixed according to corresponding ratio Enter ball mill ball milling, it is desirable to for the mesh of ball milling fineness 200 full by；Composition and corresponding proportion after ball milling with thing to be bonded Identical material mixes again, it is agitated uniformly after obtain finished product, when finished product uses through plus water after obtain Baume concentration for 63~ 66 ° of bonding mud.
- 4. the bonding mud according to claim 3 suitable for unlike material pug, it is characterised in that：Described ball mill ball milling Time is 12~14h.
- 5. the bonding mud according to claim 3 suitable for unlike material pug, it is characterised in that：Composition after ball milling with Mixer is sent into after being mixed again with thing identical material to be bonded of corresponding proportion and stirs 0.5~2h.