CN107686326A - A kind of interior wall fireproof decoration plate - Google Patents
A kind of interior wall fireproof decoration plate Download PDFInfo
- Publication number
- CN107686326A CN107686326A CN201710721941.8A CN201710721941A CN107686326A CN 107686326 A CN107686326 A CN 107686326A CN 201710721941 A CN201710721941 A CN 201710721941A CN 107686326 A CN107686326 A CN 107686326A
- Authority
- CN
- China
- Prior art keywords
- interior wall
- decoration plate
- magnesia
- wall fireproof
- fireproof decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of interior wall fireproof decoration plate, include according to the raw material of percentage by weight：Magnesium chloride solution 18~26%, thermal insulation mortar 12~18%, magnesia 21~30%, rock wool 4~8%, flyash 4~8%, magnesium cement 8~15%, titanium dioxide 3~6%, magnesia 5~9%, nano silicon 1~3%.Obtained interior wall fireproof decoration plate fireproofing and heat resistant, waterproof and dampproof, light shock strength is high, environment protection health.
Description
Technical field
The invention belongs to interior/exterior decoration technical field, is related to a kind of interior wall fireproof decoration plate.
Background technology
With the development of productivity, the continuous improvement of living environment, people are increasingly valued home improvement, and decoration is filled
Repair material more to pursue, including prevent fires, be water-fast, nontoxic, green performance.Decorating and renovating material includes external-wall heat-insulation material
With heat insulating inner wall material, heat insulating inner wall material is a kind of wall heat insulation material for collecting insulation and being combined into one with decoration.Its weight is led to
Normal only about the 1/3 of conventional ceramic brick --- 1/5, it is a kind of lightweight, insulation, heat-barrier material, and with fire prevention, waterproof, weathering resistance
Etc. performance, it compensate for well, and existing external-wall heat-insulation material field operation amount is big, and construction is complicated, cost is high, waterproof fireproofing is poor,
The deficiencies of not ageing-resistant, ultraviolet radiation resisting and freeze-thaw resistance are poor, degradable, stability is poor, easy firing, significantly improves building
The substantial effect of heat preservation energy-saving and the life-span of building, but existing interior wall fireproof decoration plate is by Effect of Materials fireproofing and heat resistant
Still have much room for improvement with strength character.
The content of the invention
It is an object of the invention to provide a kind of interior wall fireproof decoration plate, fireproofing and heat resistant is waterproof and dampproof, light shock strength
Height, environment protection health.
In order to realize the above object the present invention proposes a kind of interior wall fireproof decoration plate, according to the raw material of percentage by weight
Including：Magnesium chloride solution 18~26%, thermal insulation mortar 12~18%, magnesia 21~30%, rock wool 4~8%, flyash 4~
8%, magnesium cement 8~15%, titanium dioxide 3~6%, magnesia 5~9%, nano silicon 1~3%.
Preferably, include according to the raw material of percentage by weight：Magnesium chloride solution 23%, thermal insulation mortar 15%, magnesia
26%, rock wool 6%, flyash 6%, magnesium cement 10%, titanium dioxide 5%, magnesia 7%, nano silicon 2%.
Further, described magnesium chloride is magnesium chloride granules and water by 4:1~3:1 fused magnesium chloride solution.
Further, described magnesium cement is obtained by the light burnt powder or low temperature calcination dolomite obtained by calcined magnesite stone
Ashes.
The technical effects of the invention are that：The magnesia main component of the present invention is magnesia, using magnisite as original
Material, forms in 800~850 DEG C of temperature lower calcinations, is a kind of air-setting cementing material of fine-powdered, coordinates industrial purer oxygen
Change magnesium, using alkaline oxygenated magnesium, neutralize environmental protection, it is nontoxic.Magnesium chloride compatibility is good.Magnesium cement is to use calcined magnesite stone institute
The ashes (main component MgO) obtained by light burnt powder or low temperature calcination dolomite obtained is cementing agent, with magnesium chloride hexahydrate
(MgCL2·6H2) etc. O water-soluble magnesium salt is blender, adds water, and the light-burning magnesium powder and magnesium chloride hexahydrate formed is as master
Want raw material.The hardenite main component that magnesium cement is formed is 5Mg (OH)2·MgCL2·8H2O and 3Mg (OH)2·MgCL2·
8H2Magnesia-magnesium chloride that O crystalline phases are formed-water ternary compound crystalline phase double salt, in addition, some Mg (OH)2Glue
Solidifying body.It can be hardened quickly at normal temperatures and pressures, and the present invention utilizes its this hardening gelling, is worked into this hair
On bright interior wall fireproof decoration plate, gelatification is played.Titanium dioxide has an excellent covering power, protect light protect color and automatically cleaning,
Ageing-resistant performance is good, meanwhile, titanium dioxide also serves as pigment, has opacity.The interior wall fireproof decoration plate fire prevention of the present embodiment
Heat-resisting, 800 DEG C do not burn, and 1120 DEG C, without flare, reach the non-ignitable rank A1 levels of highest fire prevention, fire endurance reaches 3 hours, meets fire
Substantial amounts of heat energy can be absorbed during burning, postpones the rise of ambient temperature；It is waterproof and dampproof, in dry and cold and moist day
Gas, stable performance, do not influenceed by the globule and humid air is condensed, soak natural air drying after 40h takes out even if being put in water, no
It can deform, soften, can be with normal use；Light shock strength is high, and the interior wall fireproof decoration plate density of the present embodiment is smaller, light
Be advantageous to structural seismic, effectively reduce basis and main structure body cost, close structure, stability is good, indeformable, and bending strength reaches
To 310kgf/cm2(vertical) and 200kgf/cm2(level), impact strength is up to 24MPa；Environment protection health, without formaldehyde, benzene
And harmful radioactive element, fiery smokeless, nontoxic, free from extraneous odour is met, makes room and handles official business more comfortable.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one：A kind of interior wall fireproof decoration plate, includes according to the raw material of percentage by weight：Magnesium chloride solution 23%,
Thermal insulation mortar 15%, magnesia 26%, rock wool 6%, flyash 6%, magnesium cement 10%, titanium dioxide 5%, magnesia 7%, nanometer
Silica 2%.
Further, described magnesium cement is obtained by the light burnt powder or low temperature calcination dolomite obtained by calcined magnesite stone
Ashes.
The magnesia main component of the present invention is magnesia, using magnisite as raw material, at a temperature of 800~850 DEG C
Calcining forms, and is a kind of air-setting cementing material of fine-powdered, coordinates industrial purer magnesia, using alkaline oxygenated magnesium,
Environmental protection is neutralized, it is nontoxic.And magnesium chloride is by 4 with water:1~3:The magnesium chloride solution of 1 mixing, compatibility are good.Magnesium cement is
It is cementing agent with the light burnt powder obtained by calcined magnesite stone or the ashes (main component MgO) obtained by low temperature calcination dolomite,
With magnesium chloride hexahydrate (MgCL2·6H2) etc. O water-soluble magnesium salt is blender, adds water, the light-burning magnesium powder and six water formed
Magnesium chloride is as primary raw material.The hardenite main component that magnesium cement is formed is 5Mg (OH)2·MgCL2·8H2O and 3Mg
(OH)2·MgCL2·8H2Magnesia-magnesium chloride that O crystalline phases are formed-water ternary compound crystalline phase double salt, in addition, also one
Part Mg (OH)2Gel.It can be hardened quickly at normal temperatures and pressures, and the present invention utilizes its this hardening gelling,
It is worked on the interior wall fireproof decoration plate of the present invention, plays gelatification.Titanium dioxide has excellent covering power, Bao Guangbao
Color and automatically cleaning, ageing-resistant performance are good, meanwhile, titanium dioxide also serves as pigment, has opacity.The interior wall of the present embodiment is prevented
Fiery decorative panel fireproofing and heat resistant, 800 DEG C do not burn, and 1120 DEG C, without flare, reach the non-ignitable rank A1 levels of highest fire prevention, fire endurance reaches
By 3 hours, substantial amounts of heat energy can be absorbed during meeting fire burning, postpones the rise of ambient temperature；It is waterproof and dampproof,
Dry and cold and wet weather, stable performance, do not influenceed by the globule and humid air is condensed, taken out even if being put in water and soaking 40h
Natural air drying afterwards, it will not deform, soften, can be with normal use；Light shock strength is high, the interior wall fireproof decoration plate of the present embodiment
Density is smaller, light to be advantageous to structural seismic, effectively reduces basis and main structure body cost, close structure, stability is good, constant
Shape, bending strength reach 316kgf/cm2(vertical) and 207kgf/cm2(level), impact strength is up to 25MPa；Ring health care
Health, without formaldehyde, benzene and harmful radioactive element, fiery smokeless, nontoxic, free from extraneous odour is met, makes room and handles official business more comfortable.This
Outside, perlite itself has certain elastic component in the present embodiment, and it carries out closed perlite or glass bead after glazing
Do not only have some strength, and have certain pliability again, therefore be not in crack performance and hollowing phenomenon.
Embodiment two：A kind of interior wall fireproof decoration plate, includes according to the raw material of percentage by weight：Magnesium chloride solution 20%,
Thermal insulation mortar 15%, magnesia 26%, rock wool 5%, flyash 6%, magnesium cement 14%, titanium dioxide 4%, magnesia 7%, nanometer
Silica 3%.
Further, described magnesium chloride is magnesium chloride granules and water by 4:1~3:1 fused magnesium chloride solution.
Further, described magnesium cement is obtained by the light burnt powder or low temperature calcination dolomite obtained by calcined magnesite stone
Ashes.
The interior wall fireproof decoration plate fireproofing and heat resistant of the present embodiment, 800 DEG C do not burn, and 1120 DEG C, without flare, reach highest and prevent
The non-ignitable rank A1 levels of fire, fire endurance reach 3 hours, and substantial amounts of heat energy can be absorbed by meeting during fire burns, around delay
The rise of environment temperature；It is waterproof and dampproof, in dry and cold and wet weather, stable performance, not by the shadow for condensing the globule and humid air
Ring, soak natural air drying after 40h takes out even if being put in water, will not deform, soften, can be with normal use；Light shock strength
Height, the interior wall fireproof decoration plate density of the present embodiment is smaller, light to be advantageous to structural seismic, effectively reduces basis and main structure body
Cost, close structure, stability is good, indeformable, and bending strength reaches 312kgf/cm2(vertical) and 204kgf/cm2(level),
Impact strength is up to 24MPa；Environment protection health, without formaldehyde, benzene and harmful radioactive element, chance fire is smokeless, nontoxic, is no different
Taste, make room and handle official business more comfortable.In addition, perlite itself has certain elastic component in the present embodiment, it is carried out
Closed perlite or glass bead do not only have some strength after glazing, and have certain pliability again, therefore are not in cracking
Phenomenon and hollowing phenomenon.
Embodiment three：A kind of interior wall fireproof decoration plate, includes according to the raw material of percentage by weight：Magnesium chloride solution 23%,
Thermal insulation mortar 15%, magnesia 27%, rock wool 5%, flyash 5%, magnesium cement 14%, titanium dioxide 3%, magnesia 5%, nanometer
Silica 3%.
Further, described magnesium chloride is magnesium chloride granules and water by 4:1~3:1 fused magnesium chloride solution.
Further, described magnesium cement is obtained by the light burnt powder or low temperature calcination dolomite obtained by calcined magnesite stone
Ashes.
The interior wall fireproof decoration plate fireproofing and heat resistant of the present embodiment, 800 DEG C do not burn, and 1120 DEG C, without flare, reach highest and prevent
The non-ignitable rank A1 levels of fire, fire endurance reach 3 hours, and substantial amounts of heat energy can be absorbed by meeting during fire burns, around delay
The rise of environment temperature；It is waterproof and dampproof, in dry and cold and wet weather, stable performance, not by the shadow for condensing the globule and humid air
Ring, soak natural air drying after 40h takes out even if being put in water, will not deform, soften, can be with normal use；Light shock strength
Height, the interior wall fireproof decoration plate density of the present embodiment is smaller, light to be advantageous to structural seismic, effectively reduces basis and main structure body
Cost, close structure, stability is good, indeformable, and bending strength reaches 311kgf/cm2(vertical) and 202kgf/cm2(level),
Impact strength is up to 24MPa；Environment protection health, without formaldehyde, benzene and harmful radioactive element, chance fire is smokeless, nontoxic, is no different
Taste, make room and handle official business more comfortable.In addition, perlite itself has certain elastic component in the present embodiment, it is carried out
Closed perlite or glass bead do not only have some strength after glazing, and have certain pliability again, therefore are not in cracking
Phenomenon and hollowing phenomenon.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.
Claims (4)
1. a kind of interior wall fireproof decoration plate, it is characterised in that include according to the raw material of percentage by weight：Magnesium chloride solution 18~
26%, thermal insulation mortar 12~18%, magnesia 21~30%, rock wool 4~8%, flyash 4~8%, magnesium cement 8~15%, titanium
White powder 3~6%, magnesia 5~9%, nano silicon 1~3%.
2. a kind of interior wall fireproof decoration plate according to claim 1, it is characterised in that according to the raw material bag of percentage by weight
Include：Magnesium chloride solution 23%, thermal insulation mortar 15%, magnesia 26%, rock wool 6%, flyash 6%, magnesium cement 10%, titanium dioxide
5%, magnesia 7%, nano silicon 2%.
3. a kind of interior wall fireproof decoration plate according to claim 1 or 2, it is characterised in that described magnesium chloride is chlorination
Magnesium granules press 4 with water:1~3:1 fused magnesium chloride solution.
4. a kind of interior wall fireproof decoration plate according to claim 1 or 2, it is characterised in that described magnesium cement is with forging
Burn the ashes obtained by the light burnt powder or low temperature calcination dolomite obtained by giobertite.