CN107675550A - A kind of parchment and preparation method thereof - Google Patents
A kind of parchment and preparation method thereof Download PDFInfo
- Publication number
- CN107675550A CN107675550A CN201710932897.5A CN201710932897A CN107675550A CN 107675550 A CN107675550 A CN 107675550A CN 201710932897 A CN201710932897 A CN 201710932897A CN 107675550 A CN107675550 A CN 107675550A
- Authority
- CN
- China
- Prior art keywords
- parts
- pulp
- parchment
- cotton
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of parchment, include the raw material of following parts by weight：50 80 parts of hardwood pulp, 25 40 parts of Phyllostachys pubescens pulp, 20 50 parts of cotton pulp, 50 100 parts of rag stock, 10 25 parts of abaca fibre, dry 10 20 parts of cotton seed hulls, 5 10 parts of durian shell, 15 parts of vinyltrimethoxy silane, 25 parts of nano titanium oxide, 14 parts of kaolin, 25 parts of cupric oxide, 58 parts of water-base fluorocarbon emulsion, 13 parts of adipic dihydrazide, 13 parts of sodium alginate, 25 parts of xanthans, 28 parts of pure-acrylic emulsion, 28 parts of water soluble chitosan, 15 parts of nanometer silicon carbide, 48 parts of dodecafluoroheptyl methacrylate, 0.1 1 parts of dyestuff, 12 parts of thickener, 25 parts of bleeding agent, 12 parts of color fixing agent.The parchment of the present invention is not easy to fade, two sides aberration size, and the sense of paper soft quality is good, bright-colored；And preparation method is simple, be advantageous to industrialized production；In addition, the parchment third dimension of the present invention is strong, there is the visual effect of very strong sheepskin.
Description
Technical field
The present invention relates to pulp technology for making paper, specifically a kind of parchment and preparation method thereof.
Background technology
Parchment is also known as industrial parchment, is a kind of translucent wrapping paper, is the one kind for making books or providing writing
Material.It is mainly for packaging machine part, instrument, chemical industry medicine etc..The primary raw material of manufacture parchment is chemical wood pulp and broken
Cloth is starched.Raw material is copied into after page to be re-fed into 72% concentrated sulfuric acid bath and handles a few minutes, this procedure is referred to as " parchment " and made
With.Parchment is a kind of paper of high intensity, due to have passed through sulfuric acid treatment, so the intensity of parchment is fine, widely should
Used for the inner packing such as the industrial products such as machine components, instrument, chemicals and food, pharmaceuticals, pasteurization material.It is but existing
Parchment still have the shortcomings that paper easily fades, two sides aberration is big.Therefore, the present invention provides a kind of new parchment
And preparation method thereof.
The content of the invention
It is an object of the invention to provide a kind of parchment and preparation method thereof, to solve what is proposed in above-mentioned background technology
Problem.
To achieve the above object, the present invention provides following technical scheme：
A kind of parchment, include the raw material of following parts by weight：Hardwood pulp 50-80 parts, Phyllostachys pubescens pulp 25-40 parts, cotton pulp 20-50
Part, rag stock 50-100 parts, abaca fibre 10-25 parts, dry cotton seed hulls 10-20 parts, durian shell 5-10 parts, vinyl trimethoxy
Base silane 1-5 parts, nano titanium oxide 2-5 parts, kaolin 1-4 parts, cupric oxide 2-5 parts, water-base fluorocarbon emulsion 5-8 parts, oneself two
Acid dihydrazide 1-3 parts, sodium alginate 1-3 parts, xanthans 2-5 parts, pure-acrylic emulsion 2-8 parts, water soluble chitosan 2-8 parts, nanometer
It is carborundum 1-5 parts, dodecafluoroheptyl methacrylate 4-8 parts, dyestuff 0.1-1 parts, thickener 1-2 parts, bleeding agent 2-5 parts, solid
Toner 1-2 parts.
As the further scheme of the present invention：Include the raw material of following parts by weight：65 parts of hardwood pulp, Phyllostachys pubescens pulp 32
Part, 38 parts of cotton pulp, 72 parts of rag stock, 20 parts of abaca fibre, dry 15 parts of cotton seed hulls, 7 parts of durian shell, vinyl trimethoxy silicon
3 parts of alkane, 3 parts of nano titanium oxide, 2 parts of kaolin, 3 parts of cupric oxide, 6 parts of water-base fluorocarbon emulsion, 2 parts of adipic dihydrazide, sea
2 parts of mosanom, 4 parts of xanthans, 5 parts of pure-acrylic emulsion, 3 parts of water soluble chitosan, 2 parts of nanometer silicon carbide, methacrylic acid 12
6 parts of fluorine heptyl ester, 0.5 part of dyestuff, 1.4 parts of thickener, 3 parts of bleeding agent, 1.5 parts of color fixing agent.
As the further scheme of the present invention：The thickener is polyvinyl alcohol, latex and shuttle methylcellulose.
As the further scheme of the present invention：The bleeding agent is methanol, industrial alcohol and isopropanol.
A kind of preparation method of parchment, comprises the following steps：
（1）The production of body paper, comprises the following steps：
A, hardwood pulp, Phyllostachys pubescens pulp, cotton pulp and rag stock are beaten respectively, the beating degree control of mashing slurry is in 30-33SR
Between；
B, abaca fibre, dry cotton seed hulls and durian shell are crushed, sieve 100-200 mesh, obtains mixed-powder；
C, and then by the hardwood pulp completed, Phyllostachys pubescens pulp, cotton pulp, mixed-powder, suitable quantity of water and rag stock is beaten mix, matched somebody with somebody
Slurry, slurry concentration are controlled between 3-4%；
D, by vinyltrimethoxy silane, nano titanium oxide, kaolin, cupric oxide, water-base fluorocarbon emulsion, the acyl of adipic acid two
Hydrazine, sodium alginate, xanthans, water soluble chitosan and nanometer silicon carbide are added and walked in gains, are uniformly mixed；
（2）The production of finished paper, including body paper colouring, coating, press polish and cut, wherein：
A. paint：Pure-acrylic emulsion, thickener, dodecafluoroheptyl methacrylate, bleeding agent and color fixing agent are added in dyestuff, is mixed
Close uniform；
B. it is coated with：Produced from the half tone of 220-250 mesh, the good dyestuff of above-mentioned configuration is uniformly coated on by original using scraper
On paper paper, get product.
As the further scheme of the present invention：Step A, hardwood pulp, Phyllostachys pubescens pulp, cotton pulp and rag stock are beaten respectively
Slurry, the beating degree control of mashing slurry is in 31SR.
As the further scheme of the present invention：Step B, by abaca fibre, cotton seed hulls and durian shell crushing, sieving are dried
160 mesh, obtain mixed-powder.
As the further scheme of the present invention：Step C, and then the hardwood pulp completed, Phyllostachys pubescens pulp, cotton pulp, mixed will be beaten
Powder, suitable quantity of water and rag stock mixing are closed, progress is with slurry, and slurry concentration is controlled 3.2%.
As the further scheme of the present invention：Step b. is coated with：Produced from the half tone of 230 mesh, will using scraper
The good dyestuff of above-mentioned configuration is uniformly coated on body paper paper, is got product.
Compared with prior art, the beneficial effects of the invention are as follows：
The parchment of the present invention is not easy to fade, two sides aberration size, and the sense of paper soft quality is good, bright-colored；And preparation method letter
It is single, be advantageous to industrialized production；In addition, the parchment third dimension of the present invention is strong, there is the visual effect of very strong sheepskin.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment 1
A kind of parchment, include the raw material of following parts by weight：50 parts of hardwood pulp, 25 parts of Phyllostachys pubescens pulp, 20 parts of cotton pulp, rag stock
50 parts, 10 parts of abaca fibre, dry 10 parts of cotton seed hulls, 5 parts of durian shell, 1 part of vinyltrimethoxy silane, nano titanium oxide
2 parts, 1 part of kaolin, 2 parts of cupric oxide, 5 parts of water-base fluorocarbon emulsion, 1 part of adipic dihydrazide, 1 part of sodium alginate, xanthans 2
Part, 2 parts of pure-acrylic emulsion, 2 parts of water soluble chitosan, 1 part of nanometer silicon carbide, 4 parts of dodecafluoroheptyl methacrylate, dyestuff 0.1
Part, 1 part of thickener, 2 parts of bleeding agent, 1 part of color fixing agent.The thickener is polyvinyl alcohol, latex and shuttle methylcellulose.It is described
Bleeding agent is methanol, industrial alcohol and isopropanol.
A kind of preparation method of parchment, comprises the following steps：
（1）The production of body paper, comprises the following steps：A, hardwood pulp, Phyllostachys pubescens pulp, cotton pulp and rag stock are beaten respectively,
The control of slurry beating degree is beaten between 30SR；B, abaca fibre, dry cotton seed hulls and durian shell are crushed, sieve 100 mesh, obtains
To mixed-powder；C, and then by the hardwood pulp, Phyllostachys pubescens pulp, cotton pulp, mixed-powder, suitable quantity of water and the rag stock that are beaten completion mix
Close, progress is with slurry, and slurry concentration is controlled between 3%；D, by vinyltrimethoxy silane, nano titanium oxide, kaolin,
Cupric oxide, water-base fluorocarbon emulsion, adipic dihydrazide, sodium alginate, xanthans, water soluble chitosan and nanometer silicon carbide add
In upper step gains, it is uniformly mixed；
（2）The production of finished paper, including body paper colouring, coating, press polish and cut, wherein：A. paint：Pure third is added in dyestuff
Emulsion, thickener, dodecafluoroheptyl methacrylate, bleeding agent and color fixing agent, it is well mixed；B. it is coated with：From the net of 220 mesh
Version is produced, and the good dyestuff of above-mentioned configuration is uniformly coated on body paper paper using scraper, got product.
Embodiment 2
A kind of parchment, include the raw material of following parts by weight：80 parts of hardwood pulp, 40 parts of Phyllostachys pubescens pulp, 50 parts of cotton pulp, rag stock
100 parts, 25 parts of abaca fibre, dry 20 parts of cotton seed hulls, 10 parts of durian shell, 5 parts of vinyltrimethoxy silane, nanometer titanium dioxide
5 parts of titanium, 4 parts of kaolin, 5 parts of cupric oxide, 8 parts of water-base fluorocarbon emulsion, 3 parts of adipic dihydrazide, 3 parts of sodium alginate, xanthans 5
Part, 8 parts of pure-acrylic emulsion, 8 parts of water soluble chitosan, 5 parts of nanometer silicon carbide, 8 parts of dodecafluoroheptyl methacrylate, 1 part of dyestuff,
2 parts of thickener, 5 parts of bleeding agent, 2 parts of color fixing agent.The thickener is polyvinyl alcohol, latex and shuttle methylcellulose.It is described to ooze
Saturating agent is methanol, industrial alcohol and isopropanol.
A kind of preparation method of parchment, comprises the following steps：
（1）The production of body paper, comprises the following steps：A, hardwood pulp, Phyllostachys pubescens pulp, cotton pulp and rag stock are beaten respectively,
The control of slurry beating degree is beaten between 33SR；B, abaca fibre, dry cotton seed hulls and durian shell are crushed, sieve 200 mesh, obtains
To mixed-powder；C, and then by the hardwood pulp, Phyllostachys pubescens pulp, cotton pulp, mixed-powder, suitable quantity of water and the rag stock that are beaten completion mix
Close, progress is with slurry, and slurry concentration is controlled between 4%；D, by vinyltrimethoxy silane, nano titanium oxide, kaolin,
Cupric oxide, water-base fluorocarbon emulsion, adipic dihydrazide, sodium alginate, xanthans, water soluble chitosan and nanometer silicon carbide add
In upper step gains, it is uniformly mixed；
（2）The production of finished paper, including body paper colouring, coating, press polish and cut, wherein：A. paint：Pure third is added in dyestuff
Emulsion, thickener, dodecafluoroheptyl methacrylate, bleeding agent and color fixing agent, it is well mixed；B. it is coated with：From the net of 250 mesh
Version is produced, and the good dyestuff of above-mentioned configuration is uniformly coated on body paper paper using scraper, got product.
Embodiment 3
A kind of parchment, include the raw material of following parts by weight：65 parts of hardwood pulp, 32 parts of Phyllostachys pubescens pulp, 38 parts of cotton pulp, rag stock
72 parts, 20 parts of abaca fibre, dry 15 parts of cotton seed hulls, 7 parts of durian shell, 3 parts of vinyltrimethoxy silane, nano titanium oxide
3 parts, 2 parts of kaolin, 3 parts of cupric oxide, 6 parts of water-base fluorocarbon emulsion, 2 parts of adipic dihydrazide, 2 parts of sodium alginate, xanthans 4
Part, 5 parts of pure-acrylic emulsion, 3 parts of water soluble chitosan, 2 parts of nanometer silicon carbide, 6 parts of dodecafluoroheptyl methacrylate, dyestuff 0.5
Part, 1.4 parts of thickener, 3 parts of bleeding agent, 1.5 parts of color fixing agent.The thickener is polyvinyl alcohol, latex and shuttle methylcellulose.
The bleeding agent is methanol, industrial alcohol and isopropanol.
A kind of preparation method of parchment, comprises the following steps：
（1）The production of body paper, comprises the following steps：A, hardwood pulp, Phyllostachys pubescens pulp, cotton pulp and rag stock are beaten respectively,
The control of slurry beating degree is beaten in 31SR.B, abaca fibre, dry cotton seed hulls and durian shell are crushed, sieve 160 mesh, is mixed
Close powder.C, and then by the hardwood pulp completed, Phyllostachys pubescens pulp, cotton pulp, mixed-powder, suitable quantity of water and rag stock is beaten mix, enter
Row is with slurry, and slurry concentration is controlled 3.2%.D, by vinyltrimethoxy silane, nano titanium oxide, kaolin, cupric oxide,
Water-base fluorocarbon emulsion, adipic dihydrazide, sodium alginate, xanthans, water soluble chitosan and nanometer silicon carbide walk institute on adding
Obtain in thing, be uniformly mixed；
（2）The production of finished paper, including body paper colouring, coating, press polish and cut, wherein：A. paint：Pure third is added in dyestuff
Emulsion, thickener, dodecafluoroheptyl methacrylate, bleeding agent and color fixing agent, it is well mixed；B. it is coated with：From the net of 230 mesh
Version is produced, and the good dyestuff of above-mentioned configuration is uniformly coated on body paper paper using scraper, got product.
The parchment of the present invention is not easy to fade, two sides aberration size, and the sense of paper soft quality is good, bright-colored；And preparation side
Method is simple, is advantageous to industrialized production；In addition, the parchment third dimension of the present invention is strong, there is the visual effect of very strong sheepskin.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be on the premise of this patent objective not be departed from one skilled in the relevant art's possessed knowledge
Make a variety of changes.
Claims (9)
1. a kind of parchment, it is characterised in that include the raw material of following parts by weight：Hardwood pulp 50-80 parts, Phyllostachys pubescens pulp 25-
40 parts, cotton pulp 20-50 parts, rag stock 50-100 parts, abaca fibre 10-25 parts, dry cotton seed hulls 10-20 parts, durian shell 5-10
Part, vinyltrimethoxy silane 1-5 parts, nano titanium oxide 2-5 parts, kaolin 1-4 parts, cupric oxide 2-5 parts, water-based fluorocarbon
Emulsion 5-8 parts, adipic dihydrazide 1-3 parts, sodium alginate 1-3 parts, xanthans 2-5 parts, pure-acrylic emulsion 2-8 parts, water soluble shells
Glycan 2-8 parts, nanometer silicon carbide 1-5 parts, dodecafluoroheptyl methacrylate 4-8 parts, dyestuff 0.1-1 parts, thickener 1-2 parts,
Bleeding agent 2-5 parts, color fixing agent 1-2 parts.
2. parchment according to claim 1, it is characterised in that include the raw material of following parts by weight：Hardwood pulp 65
Part, 32 parts of Phyllostachys pubescens pulp, 38 parts of cotton pulp, 72 parts of rag stock, 20 parts of abaca fibre, dry 15 parts of cotton seed hulls, 7 parts of durian shell, ethene
3 parts of base trimethoxy silane, 3 parts of nano titanium oxide, 2 parts of kaolin, 3 parts of cupric oxide, 6 parts of water-base fluorocarbon emulsion, adipic acid
Two 2 parts of hydrazides, 2 parts of sodium alginate, 4 parts of xanthans, 5 parts of pure-acrylic emulsion, 3 parts of water soluble chitosan, 2 parts of nanometer silicon carbide, first
6 parts of base dodecafluorhe-ptylacrylate, 0.5 part of dyestuff, 1.4 parts of thickener, 3 parts of bleeding agent, 1.5 parts of color fixing agent.
3. parchment according to claim 1, it is characterised in that the thickener is polyvinyl alcohol, latex and shuttle methyl
Cellulose.
4. parchment according to claim 1, it is characterised in that the bleeding agent is methanol, industrial alcohol and isopropanol.
5. the preparation method of a kind of parchment as described in claim 1-4 is any, it is characterised in that comprise the following steps：
（1）The production of body paper, comprises the following steps：
A, hardwood pulp, Phyllostachys pubescens pulp, cotton pulp and rag stock are beaten respectively, the beating degree control of mashing slurry is in 30-33SR
Between；
B, abaca fibre, dry cotton seed hulls and durian shell are crushed, sieve 100-200 mesh, obtains mixed-powder；
C, and then by the hardwood pulp completed, Phyllostachys pubescens pulp, cotton pulp, mixed-powder, suitable quantity of water and rag stock is beaten mix, matched somebody with somebody
Slurry, slurry concentration are controlled between 3-4%；
D, by vinyltrimethoxy silane, nano titanium oxide, kaolin, cupric oxide, water-base fluorocarbon emulsion, the acyl of adipic acid two
Hydrazine, sodium alginate, xanthans, water soluble chitosan and nanometer silicon carbide are added and walked in gains, are uniformly mixed；
（2）The production of finished paper, including body paper colouring, coating, press polish and cut, wherein：
A. paint：Pure-acrylic emulsion, thickener, dodecafluoroheptyl methacrylate, bleeding agent and color fixing agent are added in dyestuff, is mixed
Close uniform；
B. it is coated with：Produced from the half tone of 220-250 mesh, the good dyestuff of above-mentioned configuration is uniformly coated on by original using scraper
On paper paper, get product.
6. the preparation method of parchment according to claim 5, it is characterised in that step A, by hardwood pulp, Phyllostachys pubescens pulp,
Cotton pulp and rag stock are beaten respectively, and the beating degree control of mashing slurry is in 31SR.
7. the preparation method of parchment according to claim 5, it is characterised in that step B, by abaca fibre, dry cotton
Seed shell and durian shell crush, and sieve 160 mesh, obtains mixed-powder.
8. the preparation method of parchment according to claim 5, it is characterised in that step C, then will be beaten complete it is wealthy
Leaf wood pulp, Phyllostachys pubescens pulp, cotton pulp, mixed-powder, suitable quantity of water and rag stock mixing, progress is with slurry, and slurry concentration is controlled 3.2%.
9. the preparation method of parchment according to claim 5, it is characterised in that step b. is coated with：From the net of 230 mesh
Version is produced, and the good dyestuff of above-mentioned configuration is uniformly coated on body paper paper using scraper, got product.