CN107630149A - A kind of rigid pure gold watchcase and its compounding method - Google Patents
A kind of rigid pure gold watchcase and its compounding method Download PDFInfo
- Publication number
- CN107630149A CN107630149A CN201710759553.9A CN201710759553A CN107630149A CN 107630149 A CN107630149 A CN 107630149A CN 201710759553 A CN201710759553 A CN 201710759553A CN 107630149 A CN107630149 A CN 107630149A
- Authority
- CN
- China
- Prior art keywords
- gold
- watchcase
- base material
- auxiliary
- pure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to material, and in particular to a kind of rigid pure gold watchcase and its compounding method.The mass ratio of gold element base material and auxiliary base material is 1000：0.27 0.32, the element percent mass proportioning that described auxiliary repaired mouth is included is：6.4% ± 1% ferro element,0.95% ± 0.1% cobalt element,2.397% ± 0.2% nickel element,1.639% ± 0.2% copper,3.6% ± 0.5% Zn-ef ficiency,0.246 ± 0.05% ruthenium element,0.303% ± 0.05% rhodium element,34.827% ± 5% palladium element,34.086% ± 5% silver element,1.361% ± 0.2% osmium element,0.25% ± 0.05% iridium,4.542% ± 0.5% platinum element,9.399% ± 1% gold element,Each component mass percent sum reaches 100%,Rigid pure gold watchcase can have required hardness and intensity in the present invention,There is sustained gloss again,Common thousand pure golds and karat gold are enough made up in jewellery industry and the deficiency of watchmaking so as to wait,It is a preferable new material.
Description
Technical field
The present invention relates to material, and in particular to a kind of rigid pure gold watchcase and its compounding method.
Background technology
Current thousand pure gold is only used for jewellery product, because its essence is too soft, cannot be used as the raw material of clock and watch, and clock
The raw material of the precious metal of table can only be completed with 18K or 9K etc., and this material is because the content of gold is too low, the long meeting of storage
Discoloration is used with regard to inconvenience as collection, and due to being that the karat gold bank that can not directly take away exchanges.
And can not meet the needs of people are on thousand solid gold jewelry products and watchmaking, prevent thousand pure golds from solving
The deficiency of common thousand pure golds and karat gold, does not reach required hardness and intensity, can not persistently keep constant gloss again, can not
It is the technical problem for being currently needed for solving as preferable, practical and collection good merchantable brand.
The content of the invention
It is above-mentioned to solve it is an object of the present invention to provide a kind of formula and its compounding method of rigid pure gold watchcase
Technical problem.
Technical problem solved by the invention can be realized using following technical scheme：
A kind of rigid pure gold watchcase, including gold element base material and auxiliary repaired mouth, it is characterised in that：Described gold element base material and
The mass ratio for aiding in base material is 1000：0.27-0.32.
Preferably, the element percent mass proportioning that described auxiliary repaired mouth is included is：6.4% ± 1% ferro element,
0.95% ± 0.1% cobalt element, 2.397% ± 0.2% nickel element, 1.639% ± 0.2% copper, 3.6% ± 0.5% zinc
Element, 0.246 ± 0.05%% ruthenium element, 0.303% ± 0.05% rhodium element, 34.827% ± 5% palladium element, 34.086%
± 5% silver element, 1.361% ± 0.2% osmium element, 0.25% ± 0.05% iridium, 4.542% ± 0.5% platinum element,
9.399% ± 1% gold element, each component mass percent sum reach 100%.
The present invention also provides the compounding method of above-mentioned rigid pure gold watchcase, comprises the following steps：
A, the gold bullion configured or goldc grains are put into quartzy bowl, the temperature of gold is warming up to thousand with the flame gun of acetylene oxygen
The fusing point of pure gold, when Jinsui River is warming up to surface and turned white, repaired mouth is added, is stirred with quartz pushrod, and poured out after insulation, be in
It is block.
B, watchcase embryo is made to required thickness and machining by punch process in gold bullion, then watchcase embryo is rushed
Watchcase is made in hole, die mould.
C, by the watchcase after die mould, finished product watchcase is obtained after carrying out smart car, polishing and cleaning.
Preferably, in the step A, its soaking time is 2-3 minutes.
Preferably, the hardness of watchcase is more than 70 Vickers, containing fineness of gold more than 99.95%.
Compared with prior art, the beneficial effects of the present invention are：The pure gold of stiffened thousand can be good at making up common thousand foot
Gold and deficiency of the karat gold in jewellery industry and watchmaking, you can reach required hardness and intensity, have again sustained
Gloss, it is a preferable new material.
Embodiment
In order that those skilled in the art is better understood from technical scheme, below to the technical side of the present invention
Case is further elaborated.
A kind of matter of rigid pure gold watchcase, including gold element base material and auxiliary repaired mouth, gold element base material and auxiliary base material
Amount is than being 1000：0.30.
Ferro element, 0.95% ± 0.1% cobalt that the element percent mass proportioning that described auxiliary repaired mouth is included is 6.4% ± 1%
Element, 2：.397% ± 0.2% nickel element, 1.639% ± 0.2% copper, 3.6% ± 0.5% Zn-ef ficiency, 0.246 ±
0.05%% ruthenium element, 0.303% ± 0.05% rhodium element, 34.827% ± 5% palladium element, 34.086% ± 5% silver element,
1.361% ± 0.2% osmium element, 0.25% ± 0.05% iridium, 4.542% ± 0.5% platinum element, 9.399% ± 1% gold
Element, each component mass percent sum reach 100%.
In specific manufacturing process, comprise the following steps：
A, the gold bullion configured or goldc grains are put into quartzy bowl, the temperature of gold is warming up to thousand with the flame gun of acetylene oxygen
The fusing point of pure gold, when Jinsui River is warming up to surface and turned white, repaired mouth is added, is stirred with quartz pushrod, and poured out after insulation, be in
It is block.
B, watchcase embryo is made to required thickness and machining by punch process in gold bullion, then watchcase embryo is rushed
Watchcase is made in hole, die mould.
C, by the watchcase after die mould, finished product watchcase is obtained after carrying out smart car, polishing and cleaning.
In the step A, its soaking time is 2-3 minutes.
Embodiment two
Compared with Example 1, the mass ratio of gold element base material and auxiliary base material is 1000：0.27, other are identical.
Embodiment three
Compared with Example 1, the mass ratio of gold element base material and auxiliary base material is 1000：0.28, other are identical.
Example IV
Compared with Example 1, the mass ratio of gold element base material and auxiliary base material is 1000：0.29, other are identical.
Embodiment five
Compared with Example 1, the mass ratio of gold element base material and auxiliary base material is 1000：0.31, other are identical.
Embodiment six
Compared with Example 1, the mass ratio of gold element base material and auxiliary base material is 1000：0.32, other are identical.
The hardness of watchcase obtained by above-described embodiment is more than 70 Vickers, containing fineness of gold more than 99.95%.Have again sustained
Gloss, be a preferable new material.
Above for the present invention preferably implementation, it is necessary to illustrate, in the situation without departing substantially from spirit of the invention and its essence
Under, those skilled in the art should belong to the present invention when various corresponding deformations that can be according to made by the present invention and change
Appended scope of the claims.
Claims (5)
1. a kind of rigid pure gold watchcase, including gold element base material and auxiliary repaired mouth, it is characterised in that：Described gold element base material
Mass ratio with auxiliary base material is 1000：0.27-0.32.
2. thousand pure golds watchcase according to claim 1, it is characterised in that：The element quality that described auxiliary repaired mouth is included
Per distribution ratio is：6.4% ± 1% ferro element, 0.95% ± 0.1% cobalt element, 2.397% ± 0.2% nickel element, 1.639% ±
0.2% copper, 3.6% ± 0.5% Zn-ef ficiency, 0.246 ± 0.05%% ruthenium element, 0.303% ± 0.05% rhodium element,
34.827% ± 5% palladium element, 34.086% ± 5% silver element, 1.361% ± 0.2% osmium element, 0.25% ± 0.05% iridium
Element, 4.542% ± 0.5% platinum element, 9.399% ± 1% gold element, each component mass percent sum reach 100%.
3. thousand pure golds watchcase according to claim 1, it is characterised in that：The hardness of the watchcase contains more than 70 Vickers
Fineness of gold is more than 99.95%.
4. a kind of make the method with rigid pure gold watchcase any one of claim 1-3, it is characterised in that including following
Step：
A, the gold bullion configured or goldc grains are put into quartzy bowl, the molten of thousand pure golds is heated to the flame gun of acetylene oxygen
Point, when Jinsui River is warming up to surface and turned white, auxiliary repaired mouth is added, is stirred with quartz pushrod, and poured out after insulation, in block
Shape；
B, by the gold bullion obtained by step A after punch process to required thickness, then watchcase embryo is made by machining, then will
Watchcase embryo is punched out, watchcase is made in die mould；
C, finished product watchcase is obtained after the watchcase obtained by step B being carried out into smart car, polishing and cleaning.
5. preparation method according to claim 4, it is characterised in that in the step A, its soaking time is 2-3 minutes.