CN107460616B - A kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament - Google Patents
A kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament Download PDFInfo
- Publication number
- CN107460616B CN107460616B CN201710733593.6A CN201710733593A CN107460616B CN 107460616 B CN107460616 B CN 107460616B CN 201710733593 A CN201710733593 A CN 201710733593A CN 107460616 B CN107460616 B CN 107460616B
- Authority
- CN
- China
- Prior art keywords
- fabric
- monofilament
- section
- show
- cross
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament, it is related to a kind of knitting fabric, including following steps, step A: cotton or polyester cotton blended yarns and polyester monofilament are chosen by the single side circle big jacquard woven of latitude into fabric embryo cloth, the fabric embryo cloth includes spun yarn face, if weaving has main line monofilament alternatively up and down on spun yarn face；Step B: fabric fabric is subjected to pre-setting；Step C: opposite material base cloth is dyed；Step D: opposite material base cloth is post-processed；Step E: opposite material base cloth carries out multiple sizing, obtains a kind of show-through transparent jacquard weave three-dimensional shell fabric of cross section monofilament after the completion of multiple sizing.Compared with prior art, this three-dimensional shell fabric fabric it is frivolous, it is soft, have and spend grey effect, patterns of fabric novel design is transparent, with indistinct aesthetic feeling, while the performance indexess such as bursting, shrink are outstanding, also have moisture-absorbing and fast-drying function, and service performance is high.
Description
Technical field
The present invention relates to a kind of knitting fabric, in particular to a kind of jacquard fabric.
Background technique
There are circle, triangle, five-pointed star etc. in the special-shaped monofilament section seen on the market at present, and patent CN202323155U is public
A kind of five jiaos of special-shaped monofilaments of big bright-polyester synthetic fibre are opened, it is characterised in that monofilament is that core is arranged in pentagonal monofilament in cross section
Body, the cross section of core are that unconnected five triangles, each triangle are respectively in an angle of monofilament each other, core
Cross-sectional area account for the 1/3 ~ 1/10 of monofilament cross-sectional area.For another example application No. is patent CN104342778A to disclose one kind
Luminous polyester fiber monofilament and preparation method thereof is made of luminous PBT particle and big bright PET chips, wherein the PBT particle that shines exists
Mass fraction in luminous polyester fiber monofilament is 5%~15%, and there are the circular arc and triangle of evagination in fibre section, can fiber by
Original shape is kept when power, its totality portion is kept to deform.Yarn due to being used in knitting and weaving cannot be excessively thick, and in order to embody
The monofilament of the flower pattern of transparent stereo in contrast can be thinner, and the strength of silk is lower, so if transparent part flower pattern is whole
Accounting in a cloth cover is relatively more a wide range of or accounting than it is heavier when may will be greatly reduced the bursting strength of fabric, thus
Influence wearability.And because monofilament is the yarn formed by single fiber, it is partially hard often to there is feel in the fabric of design
And the defects of poor color fastness, while being also possible to along with easy aging, not sun-proof the problem of washing.
Summary of the invention
The present invention aiming at the shortcomings in the prior art, provides a kind of show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament
Preparation method, this three-dimensional shell fabric fabric is frivolous, it is soft, have and spend grey effect, patterns of fabric novel design, if transparent, have
If hidden existing aesthetic feeling, while the performance indexess such as bursting, shrink are outstanding, also have moisture-absorbing and fast-drying function, service performance is high.
In order to solve the above-mentioned technical problem, the preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of a kind of odd-shaped cross section monofilament,
It is characterized in that including following steps, step A: chooses cotton or polyester cotton blended yarns and polyester monofilament and pass through single side circle latitude
For big jacquard woven at fabric embryo cloth, the fabric embryo cloth includes spun yarn face, and weaving has alternatively up and down on spun yarn face
If main line monofilament；Step B: fabric fabric is subjected to pre-setting；Step C: opposite material base cloth is dyed；Step D: opposite material base
Cloth is post-processed；Step E: opposite material base cloth carries out multiple sizing, and it is show-through to obtain a kind of cross section monofilament after the completion of multiple sizing
Transparent jacquard weave three-dimensional shell fabric.
In above-mentioned technical proposal, it is preferred that in step B pre-setting, at 150 DEG C ~ 200 DEG C, speed exists pre-setting temperature
15m/min~25 m/ min。
In above-mentioned technical proposal, it is preferred that in step C dyeing, between 50 DEG C ~ 70 DEG C, dyestuff is temperature when dyeing
Reactive dye.
In above-mentioned technical proposal, it is preferred that in step D post-processing, treatment temperature is between 40 DEG C ~ 80 DEG C, post-processing
Agent is water-absorbing fast-drying auxiliary agent, and additional amount is 1.5%-3% (owf).
In above-mentioned technical proposal, it is preferred that when step E is formed again, fabric fabric is subjected to multiple sizing by forming machine,
Wherein pick-up rate in 70% ~ 90%, platen pressure in 2Kpa ~ 5KPa, oven temperature in 100 DEG C ~ 130 DEG C, speed in 15 m/ min
~35 m/ min。
In above-mentioned technical proposal, it is preferred that in step, the polyester monofilament is cross section polyester monofilament.
In above-mentioned technical proposal, it is preferred that in step, spun yarn face have 2 road three-legged structures, the 1st, 2 Lu Douwei at
Circle, lopping weaving structure and be the blended scribbled of polyester-cotton blend；Monofilament has 2 road three-legged structures, the 1st, 2 tunnels in spun yarn face front
All it is lopping, lopping weaving structure and is cross section polyester monofilament；Monofilament has 2 road three-legged structures at the spun yarn face back side,
1st tunnel is tuck, flotation line weaving structure, and the 2nd tunnel is flotation line, tuck weaving structure, and is cross section polyester monofilament.
In above-mentioned technical proposal, it is preferred that the cross section polyester monofilament is interrupted on the spun yarn face to be knitted
It makes, and cross section polyester monofilament is weaved alternatively up and down on the spun yarn face.
If the method for the present invention weaves next fabric with moisture-absorbing and fast-drying function and style is novel, flower pattern is different, it is hidden to have
If existing effect.This fabric selects the monofilament with cross section, solves the problems, such as that monofilament is unable to line transfer on jacquard machine, leads to
The rational proportion using cross section monofilament and preferred yarn, and the reasonable Jacquard of design are crossed, enables fabric is perfect to present
Various flower pattern out；And solve the problems, such as that the bursting of monofilament jacquard fabric is bad.This three-dimensional shell fabric by 90-95% cotton or polyester-cotton blend
Scribbled, wherein for yarn count thickness range between 20S ~ 50S, 5-10% has the cross section terylene list of water-absorbing fast-drying function
Silk, wherein yarn count thickness range obtains, fabric between 20D ~ 50D by designing relatively uniform transparent jacquard weaving
If upper there are several road spun yarns and main line monofilament alternately to weave, every piece of every road of spun yarn needle is all lopping, and monofilament is in spun yarn
Front is also lopping, is then overleaf flotation line and tuck, can thus generate indistinct feeling.The monofilament of this cross section
It is to replace traditional round spinneret section by the way that the shape of spinning nozzle is transformed, so that direct spinneret spins the length of star section
Silk, the groove of this fiber surface form capillary phenomenon and make moisture through wicking, diffusion, transmission effect, and because thus fibre
Dimension is small with the contact area of skin, and skin can be made to keep dry and comfortable feeling, fabric is made to reach the function of water-absorbing fast-drying.Due to single side
Circle the big jacquard of latitude for harder monofilament can not line transfer, so monofilament is all connected on several roads in machine, even if having
When a little places do not need to embody monofilament, monofilament is hidden in the reverse side of body yarn in a particular manner, both solves list in this way
Silk can not line transfer the problem of, also meet and do not show the effect of monofilament in fabric surface.Due to the dye uptake and color fastness of monofilament
It all compares poor, thus only fabric is handled with Dyeing of Cotton Fabric with Reactive Dyes, for temperature at 60 DEG C or so, such fabric is only the portion of cotton
Divide and painting, and monofilament is not painted, and transparent, indistinct feeling is more given.Since this fabric is mainly used for summer clothing,
It is required that there is water-absorbing fast-drying function, although cross section monofilament has the function of water-absorbing fast-drying, the ratio accounted for is fewer, so
The yarn of selection generally contains the more slightly higher yarn of the amount of washing, and water-absorbing fast-drying auxiliary agent is added in last handling process, and assistant concentration is
1.5-3% or so, temperature is 40-80 DEG C or so, so that it is guaranteed that fabric has the function of strong water-absorbing fast-drying.
Compared with prior art, this three-dimensional shell fabric fabric it is frivolous, it is soft, have and spend grey effect, patterns of fabric novel design,
It is transparent, with indistinct aesthetic feeling, while the performance indexess such as bursting, shrink are outstanding, also have moisture-absorbing and fast-drying function, make
With performance height.
Detailed description of the invention
Fig. 1 is spun yarn face of the present invention cam chart.
Fig. 2 is monofilament of the present invention in spun yarn face front cam chart.
Fig. 3 is monofilament of the present invention in spun yarn face back side cam chart.
Fig. 4 is 1 effect photo figure of the embodiment of the present invention.
Specific embodiment
Present invention is further described in detail with specific embodiment with reference to the accompanying drawing.
Embodiment 1, as shown in Figures 1 to 3, a kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament,
Including following steps, step A: the terylene list of the blended CVS40/60 of 30S polyester-cotton blend and 30D/1F (FDY) cross section is chosen
Silk is by the single side circle big jacquard woven of latitude at fabric embryo cloth, and the fabric embryo cloth has spun yarn face, on spun yarn face
If weaving has the polyester monofilament of main line cross section alternatively up and down；The cross section polyester monofilament is in the spun yarn face
Upper interruption weaving, and cross section polyester monofilament is weaved alternatively up and down on the spun yarn face.That is 30S polyester-cotton blend is blended
CVS40/60 is weaved into spun yarn face, and the polyester monofilament of cross section carries out reciprocal cross on spun yarn face and knits, this reciprocal cross
Knit be not gamut weaving, then regular can be weaved on spun yarn face, can also be irregular in short fibre
Yarn is weaved on face.Spun yarn face has 2 road three-legged structures, the 1st, 2 Lu Douwei lopping, lopping weaving structure and washs for 30S
Cotton blend CVS40/60；Monofilament has 2 road three-legged structures, the 1st, 2 Lu Douwei lopping, lopping weaving structure in spun yarn face front
It and is the polyester monofilament of 30D/1F (FDY) cross section；Monofilament has 2 road three-legged structures at the spun yarn face back side, and the 1st tunnel is collection
Circle, flotation line weaving structure, the 2nd tunnel are flotation line, tuck weaving structure, and are the polyester monofilament of 30D/1F (FDY) cross section.?
A certain piece of spun yarn face can be considered as the cloth of 16 file *, 48 row in this implementation column, wherein in the 7th, 8 rows, 15,16
Row, 23,24 rows, 31,32 rows, 39,40 rows, 47,48 rows carry out 12 cross section polyester monofilament weavings, and
Every two difference of 12 cross section polyester monofilaments expand a file to the left and right from top to bottom, thus form the saturating of similar mountain type
Bright band effect, entire cloth can by several this similar mountain types transparent band effect it is regular be composed, such as
Shown in Fig. 4.
Fabric fabric is carried out pre-setting by step B, and in step B pre-setting, pre-setting temperature is at 150 DEG C ~ 200 DEG C, vehicle
Speed is in the m/ of 15m/ min ~ 25 min.Step C, opposite material base cloth are dyed, and in step C dyeing, temperature is 50 when dyeing
DEG C ~ 70 DEG C between, dyestuff is reactive dye.Step D, opposite material base cloth are post-processed, in step D post-processing, processing temperature
For degree between 40 DEG C ~ 80 DEG C, post-treatment agent is water-absorbing fast-drying auxiliary agent, and additional amount is 1.5%-3% (owf).Step E, opposite material base
Cloth carries out multiple sizing, obtains a kind of show-through transparent jacquard weave three-dimensional shell fabric of cross section monofilament after the completion of multiple sizing.It is fixed again in step E
When type, fabric fabric is subjected to multiple sizing by forming machine, wherein pick-up rate 70% ~ 90%, platen pressure 2Kpa ~ 5KPa,
Oven temperature is in 100 DEG C ~ 130 DEG C, speed in 15 m/ of m/ min ~ 35 min.
Claims (5)
1. a kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament, it is characterized in that including following step
Suddenly,
Step A: choosing polyester cotton blended yarns and polyester monofilament by single side and justify the big jacquard woven of latitude into fabric embryo cloth, described
Fabric embryo cloth there is spun yarn face, if weaving has a main line monofilament alternatively up and down on spun yarn face, the polyester monofilament is ten
Word section polyester monofilament, the spun yarn face have a 2 road three-legged structures, the 1st, 2 Lu Douwei lopping, lopping weaving structure and to wash
Cotton blending yarn, monofilament have 2 road three-legged structures in spun yarn face front, the 1st, 2 Lu Douwei lopping, lopping weaving structure and are
Cross section polyester monofilament, monofilament the spun yarn face back side have 2 road three-legged structures, the 1st tunnel be tuck, flotation line weaving structure,
2nd tunnel is flotation line, tuck weaving structure, and is cross section polyester monofilament, and the cross section polyester monofilament is described short
It is interrupted weaving on fine yarn face, and cross section polyester monofilament is weaved alternatively up and down on the spun yarn face；
Step B: fabric fabric is subjected to pre-setting；
Step C: opposite material base cloth is dyed；
Step D: opposite material base cloth is post-processed；
Step E: opposite material base cloth carries out multiple sizing, and it is vertical that a kind of show-through transparent jacquard weave of cross section monofilament is obtained after the completion of multiple sizing
Dignity material.
2. a kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament according to claim 1, special
Sign is, in step B pre-setting, pre-setting temperature is at 150 DEG C ~ 200 DEG C, and speed is in the m/ of 15m/ min ~ 25 min.
3. a kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament according to claim 1, special
Sign is, in step C dyeing, for temperature between 50 DEG C ~ 70 DEG C, dyestuff is reactive dye when dyeing.
4. a kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament according to claim 1, special
Sign is, in step D post-processing, for treatment temperature between 40 DEG C ~ 80 DEG C, post-treatment agent is water-absorbing fast-drying auxiliary agent, and additional amount is
1.5%-3%owf。
5. a kind of preparation method of the show-through transparent jacquard weave three-dimensional shell fabric of odd-shaped cross section monofilament according to claim 1, special
Sign is, when step E is formed again, fabric fabric is carried out multiple sizing by forming machine, wherein pick-up rate is in 70% ~ 90%, pressure roller
Pressure is in 2Kpa ~ 5KPa, oven temperature in 100 DEG C ~ 130 DEG C, speed in 15 m/ of m/ min ~ 35 min.