CN107382066A - A kind of special ceramet glaze of ceramics - Google Patents
A kind of special ceramet glaze of ceramics Download PDFInfo
- Publication number
- CN107382066A CN107382066A CN201710734376.9A CN201710734376A CN107382066A CN 107382066 A CN107382066 A CN 107382066A CN 201710734376 A CN201710734376 A CN 201710734376A CN 107382066 A CN107382066 A CN 107382066A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- special
- ceramics
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of special ceramet glaze of ceramics, it is characterised in that：It is made up of the raw material components of following number：10 15 parts of orthoclase, 38 parts of cupric oxide, 28 parts of zinc oxide, calcium hydroxide are 5 10 parts, magnesia is 23 parts, lead oxide is 38 parts, 12 parts of vanadic anhydride, 5 10 parts of phosphorus pentoxide, 0.1 1 parts of cobalt oxide, 28 parts of sodium sulphate, 12 parts of nickel oxide, 45 parts of manganese dioxide, 26 parts of piperonyl butoxide, 38 parts of di-iron trioxide；A kind of special ceramet glaze of ceramics of the invention, using cupric oxide, zinc oxide and di-iron trioxide as coloring oxide, golden light flashes under light irradiation, more aobvious magnificent rich and honour quality, the hard axis face smoothness that makes one to look over so as to check is good, and enamel is good, and especially high brightness is high, the advantages that aesthetics is good, the highlighted ceramet glaze of people's high request standard can be met.
Description
Technical field
The present invention relates to a kind of technical field of ceramet glaze, the special ceramet glaze of specially a kind of ceramics.
Background technology
At present, in porcelain industry, the moulding of porcelain billet is the basis of quality product, and the allotment of glaze makes porcelain more gorgeous
It is colorful；The porcelain billet of same moulding, often because of the difference of glaze paint, and different influences, that metal are produced to the vision of consumer
Gloss, the glaze paint that color can reflect can make porcelain obtain do not open life decoration effect, this be also current porcelain industry it is a kind of when
Still.
The content of the invention
It is an object of the invention to provide a kind of special ceramet glaze of ceramics, to solve to propose in above-mentioned background technology
The problem of.
The purpose of the present invention is achieved by following technical proposals：A kind of special ceramet glaze of ceramics, it is special
Sign is：It is made up of the raw material components of following number：Orthoclase 10-15 parts, cupric oxide 3-8 parts, zinc oxide 2-8 parts, hydroxide
Calcium is 5-10 parts, magnesia is 2-3 parts, lead oxide is 3-8 parts, vanadic anhydride 1-2 parts, phosphorus pentoxide 5-10 parts, is aoxidized
Cobalt 0.1-1 parts, sodium sulphate 2-8 parts, nickel oxide 1-2 parts, manganese dioxide 4-5 parts, piperonyl butoxide 2-6 parts, di-iron trioxide 3-8
Part.
Further, the number of each raw material components is 10 parts of orthoclase, 3 parts of cupric oxide, 2 parts of zinc oxide, calcium hydroxide 5
Part, magnesia be 2 parts, lead oxide is 3 parts, 1 part of vanadic anhydride, 5 parts of phosphorus pentoxide, 0.1 part of cobalt oxide, 2 parts of sodium sulphate,
1 part of nickel oxide, 4 parts of manganese dioxide, 2 parts of piperonyl butoxide, 3 parts of di-iron trioxide.
Either, the number of each raw material components is 15 parts of orthoclase, 8 parts of cupric oxide, 8 parts of zinc oxide, calcium hydroxide 10
Part, magnesia be 3 parts, lead oxide is 8 parts, 2 parts of vanadic anhydride, 10 parts of phosphorus pentoxide, 1 part of cobalt oxide, 8 parts of sodium sulphate,
2 parts of nickel oxide, 5 parts of manganese dioxide, 6 parts of piperonyl butoxide, 8 parts of di-iron trioxide.
The beneficial effects of the invention are as follows：A kind of special ceramet glaze of ceramics of the invention, use cupric oxide, zinc oxide with
And di-iron trioxide, as coloring oxide, golden light flashes under light irradiation, more aobvious magnificent rich and honour quality, makes one difficulty of looking over so as to check
Forget, the advantages that glaze paint smoothness is good, and enamel is good, and especially high brightness is high, and aesthetics is good, people's high request standard can be met
Highlighted ceramet glaze.
Embodiment
With reference to embodiment further instruction, but following detailed description should not be done and be managed
Solve the limitation to invent body.Those of ordinary skill in the art can apparently make various on the basis of the present invention
Change and change, it should within the scope of invention.
Embodiment 1
A kind of special ceramet glaze of ceramics, is made up of the raw material components of following number：Orthoclase 10-15 parts, oxidation
8 parts of copper, 8 parts of zinc oxide, calcium hydroxide are 10 parts, magnesia is 3 parts, lead oxide is 8 parts, 2 parts of vanadic anhydride, five oxidation two
10 parts of phosphorus, 1 part of cobalt oxide, 8 parts of sodium sulphate, 2 parts of nickel oxide, 5 parts of manganese dioxide, 6 parts of piperonyl butoxide, 8 parts of di-iron trioxide.
Embodiment 2
A kind of special ceramet glaze of ceramics, is made up of the raw material components of following number：Orthoclase 10-15 parts, oxidation
3 parts of copper, 2 parts of zinc oxide, calcium hydroxide are 5 parts, magnesia is 2 parts, lead oxide is 3 parts, 1 part of vanadic anhydride, five oxidation two
5 parts of phosphorus, 0.1 part of cobalt oxide, 2 parts of sodium sulphate, 1 part of nickel oxide, 4 parts of manganese dioxide, 2 parts of piperonyl butoxide, di-iron trioxide 3
Part.
Above description is only the preferred embodiment of the application and the explanation to institute's application technology principle.People in the art
Member should be appreciated that invention scope involved in the application, however it is not limited to the technology that the particular combination of above-mentioned technical characteristic forms
Scheme, while should also cover in the case where not departing from the inventive concept, carried out by above-mentioned technical characteristic or its equivalent feature
The other technical schemes for being combined and being formed.Such as features described above has similar work(with (but not limited to) disclosed herein
The technical scheme that the technical characteristic of energy is replaced mutually and formed.
Claims (3)
- A kind of 1. special ceramet glaze of ceramics, it is characterised in that：It is made up of the raw material components of following number：Orthoclase 10- 15 parts, cupric oxide 3-8 parts, zinc oxide 2-8 parts, calcium hydroxide are 5-10 parts, magnesia is 2-3 parts, lead oxide is 3-8 parts, five V 2 O 1-2 parts, phosphorus pentoxide 5-10 parts, cobalt oxide 0.1-1 parts, sodium sulphate 2-8 parts, nickel oxide 1-2 parts, manganese dioxide 4-5 parts, piperonyl butoxide 2-6 parts, di-iron trioxide 3-8 parts.
- A kind of 2. special ceramet glaze of ceramics according to claim 1, it is characterised in that：The number of each raw material components For 10 parts of orthoclase, 3 parts of cupric oxide, 2 parts of zinc oxide, calcium hydroxide are 5 parts, magnesia is 2 parts, lead oxide is 3 parts, five oxidations Two 1 part of vanadium, 5 parts of phosphorus pentoxide, 0.1 part of cobalt oxide, 2 parts of sodium sulphate, 1 part of nickel oxide, 4 parts of manganese dioxide, piperonyl butoxide 2 Part, 3 parts of di-iron trioxide.
- A kind of 3. special ceramet glaze of ceramics according to claim 1, it is characterised in that：The number of each raw material components For 15 parts of orthoclase, 8 parts of cupric oxide, 8 parts of zinc oxide, calcium hydroxide are 10 parts, magnesia is 3 parts, lead oxide is 8 parts, five oxygen Change 2 parts of two vanadium, 10 parts of phosphorus pentoxide, 1 part of cobalt oxide, 8 parts of sodium sulphate, 2 parts of nickel oxide, 5 parts of manganese dioxide, piperonyl butoxide 6 parts, 8 parts of di-iron trioxide.