[go: up one dir, main page]

CN107286407A - 一种橡塑绝热保温材料 - Google Patents

一种橡塑绝热保温材料 Download PDF

Info

Publication number
CN107286407A
CN107286407A CN201710626399.8A CN201710626399A CN107286407A CN 107286407 A CN107286407 A CN 107286407A CN 201710626399 A CN201710626399 A CN 201710626399A CN 107286407 A CN107286407 A CN 107286407A
Authority
CN
China
Prior art keywords
rubber
insulation material
plastic insulating
low temperature
temperature resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710626399.8A
Other languages
English (en)
Inventor
吴小松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Deqing Jinwei Building Heat Insulating Material Co Ltd
Original Assignee
Zhejiang Deqing Jinwei Building Heat Insulating Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Deqing Jinwei Building Heat Insulating Material Co Ltd filed Critical Zhejiang Deqing Jinwei Building Heat Insulating Material Co Ltd
Priority to CN201710626399.8A priority Critical patent/CN107286407A/zh
Publication of CN107286407A publication Critical patent/CN107286407A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种橡塑绝热保温材料，包括本体，所述本体的外表面开设有凹槽，所述本体的外表面从内向外依次涂设有防静电涂层和玻璃布涂层，所述本体由NBR、EVA、PVC、无卤阻燃剂、耐低温增塑剂、发泡剂、填充剂、防老剂和氯化石蜡组成，其重量百分比为：NBR13％～30％；EVA8％～25％；PVC2％～5％；无卤阻燃剂20％～40％；耐低温增塑剂10％～20％；发泡剂7％～15％；填充剂3％～20％；防老剂13％～30％；氯化石蜡0.5％～2％。本发明以NBR和EVA为主体材料，配合耐低温增塑剂、发泡剂、填充剂和防老剂等共同构成了本发明的配方体系，同时通过无卤阻燃剂的作用，可有效提高本材料的绝热效果，保障了人们使用的安全性。

Description

一种橡塑绝热保温材料
技术领域
本发明涉及保温材料技术领域，具体为一种橡塑绝热保温材料。
背景技术
保温材料一般是指导热系数小于或等于零点二的材料，具有导热系数低、密度小、柔韧性高、防火防水等特性，保温材料发展很快，在工业和建筑中采用良好的保温技术与材料，往往可以起到事半功倍的效果。建筑中每使用一吨矿物棉绝热制品，一年可节约一吨石油，建筑物隔热保温是节约能源、改善居住环境和使用功能的一个重要方面，建筑能耗在人类整个能源消耗中所占比例一般在30％～40％，绝大部分是采暖和空调的能耗，故建筑节能意义重大，而且由于该隔热保温涂料以水为稀释介质，不含挥发性有机溶剂，对人体及环境无危害，其生产成本仅约为国外同类产品的五分之一，而它作为一种新型隔热保温涂料，有着良好的经济效益、节能环保、隔热效果和施工简便等优点而越来越受到人们的关注与青睐，且这种太空绝热反射涂料正经历着一场由工业隔热保温向建筑隔热保温为主的方向转变，由厚层向薄层隔热保温的技术转变，这也是今后隔热保温材料主要的发展方向之一。太空反射绝热涂料通过应用陶瓷球型颗粒中空材料在涂层中形成的真空腔体层，构筑有效的热屏障，不仅自身热阻大、导热系数低，而且热反射率高、减少建筑物对太阳辐射热的吸收、降低被覆表面和内部空间温度，因此它被行家一致公认为最有发展前景的高效节能材料之一。
当今，全球保温隔热材料正朝着高效、节能、薄层、隔热、防水外护一体化方向发展，在发展新型保温隔热材料及符合结构保温节能技术同时，更强调有针对性使用保温绝热材料，按标准规范设计及施工，努力提高保温效率及降低成本，国内外纷纷展开薄层隔热保温涂料的研究，美国已有多家公司生产这种绝热瓷层涂料，这种太空绝热瓷层是根据美国航空和航天宇宙航行局NASA控制航天飞机热传导的工作原理研制而成的，适用于高压喷涂、无污染，具有良好的抗热辐射、薄层隔热、防水防腐蚀等性能，而国内也有多家企业在研发该类材料，如薄层隔热反射涂料、太阳热反射隔热涂料、水性反射隔热涂料、隔热防晒涂料、陶瓷绝热涂料等等，主要是采用耐候性好、耐水性强、耐老化性强、有较强粘结力和弹性的、且能与保温填料、反射填料相溶性好的成膜材料，选择质轻中空、耐高温、热阻大、并具有良好反射性和辐射性的填料、折光系数高、表面光洁度高、热反射率及辐射率高的超细粉料适合作为反射填料，与成膜基料一起构成低辐射传热层，可有效隔断热量的传递，这种薄层隔热反射涂料与多孔材料复合使用可用于建筑物、车船、石化油罐设备、粮库、冷库、集装箱、管道等不同场所涂装。
近年来的火灾事故中，超过死亡数百分之八十的人员致死原因与建筑材料燃烧产生的浓烟和毒气有关，随着越来越多的公共场所、大型建筑物投入使用，建筑物的防火以及燃烧时对人体的影响受到广泛重视，然而，传统的建筑材料中保温材料使用的是PVC体系橡塑发泡保温材料，其配方体系中含有PVC等含卤原料，当火灾发生时，其燃烧放出大量的有毒烟雾和腐蚀性卤酸，造成的人员伤亡远远大于火灾本身，为此，我们提出一种橡塑绝热保温材料。
发明内容
本发明的目的在于提供一种橡塑绝热保温材料，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种橡塑绝热保温材料，包括本体，所述本体的外表面开设有凹槽，所述本体的外表面从内向外依次涂设有防静电涂层和玻璃布涂层，所述本体由NBR、EVA、PVC、无卤阻燃剂、耐低温增塑剂、发泡剂、填充剂、防老剂和氯化石蜡组成，其重量百分比为：NBR13％～30％；EVA8％～25％；PVC2％～5％；无卤阻燃剂20％～40％；耐低温增塑剂10％～20％；发泡剂7％～15％；填充剂3％～20％；防老剂13％～30％；氯化石蜡0.5％～2％。
优选的，所述凹槽为三种形状，且凹槽的深度为0.1～0.3mm。
优选的，所述防静电涂层的厚度为20～50μm。
优选的，所述玻璃布涂层的厚度为100～200μm。
优选的，所述无卤阻燃剂为氢氧化铝，或氢氧化铝和氢氧化镁的混合物。
优选的，所述填充剂为滑石粉、陶土、碳酸钙中的一种或几种的混合物。
优选的，所述耐低温增塑剂为己二酸二辛酯、癸二酸二辛酯中的一种或两种的混合物。
优选的，其制作方法包括以下步骤：
A、将NBR、EVA、PVC、防老化剂和氯化石蜡放入密炼机中混炼；
B、将无卤阻燃剂和发泡剂投入密炼机中，并将至少一半的耐低温增塑剂加入密炼机；
C、在120～130摄氏度温度条件下混炼；
D、将填充剂和剩余部分的耐低温增塑剂加入密炼机中，混炼至温度达150～160摄氏度出料；
E、将密炼机混炼出的混炼胶料倒入开炼机冷却后出片，放置2～3天；
F、取放置后的混炼胶料，投入密炼机中，并加入硫化剂和促进剂，混炼均匀后倒入开炼机；
G、冷却出片，然后通过挤出机定型，放入140～150摄氏度的烘箱中烘干15～20分钟；
H、取出烘箱中半成品，在空气中放置冷却后，再放入160～170摄氏度烘箱下烘干15～20分钟；
I、待完全发泡后取出，冷却定型；
J、将冷却定型后的材料通过打孔机压制出特定形状的凹槽；
K、在开设好凹槽的材料表面涂设防静电涂层和玻璃布涂层。
与现有技术相比，本发明的有益效果如下：
1、本发明以NBR和EVA为主体材料，配合耐低温增塑剂、发泡剂、填充剂和防老剂等共同构成了本发明的配方体系，同时通过无卤阻燃剂的作用，可有效提高本材料的绝热效果，保障了人们使用的安全性。
2、本发明在本体的外表面开设了三种形状的凹槽，可提高本材料的的摩擦力，提高其安装时的稳定性，同时在本体的外表面从内向外依次涂设了防静电涂层和玻璃布涂层，有效提高了本材料的抗静电和耐腐蚀能力，延长了其使用寿命。
附图说明
图1为本发明结构示意图；
图2为本发明涂层结构示意图；
图3为本发明配方表格示意图。
图中：1本体、2凹槽、3防静电涂层、4玻璃布涂层。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
请参阅图1-3，一种橡塑绝热保温材料，包括本体1，本体1的外表面开设有凹槽2，凹槽2为三种形状，且凹槽2的深度为0.1～0.3mm，可提高本材料的的摩擦力，提高其安装时的稳定性，本体1的外表面从内向外依次涂设有防静电涂层3和玻璃布涂层4，有效提高了本材料的抗静电和耐腐蚀能力，延长了其使用寿命，防静电涂层3的厚度为20～50μm，玻璃布涂层4的厚度为100～200μm，本体1由NBR、EVA、PVC、无卤阻燃剂、耐低温增塑剂、发泡剂、填充剂、防老剂和氯化石蜡组成，其重量百分比为：NBR13％～30％；EVA8％～25％；PVC2％～5％；无卤阻燃剂20％～40％；无卤阻燃剂为氢氧化铝，或氢氧化铝和氢氧化镁的混合物，耐低温增塑剂10％～20％；耐低温增塑剂为己二酸二辛酯、癸二酸二辛酯中的一种或两种的混合物，发泡剂7％～15％；填充剂3％～20％；填充剂为滑石粉、陶土、碳酸钙中的一种或几种的混合物，防老剂13％～30％；氯化石蜡0.5％～2％。
其制作方法包括以下步骤：
A、将NBR、EVA、PVC、防老化剂和氯化石蜡放入密炼机中混炼；
B、将无卤阻燃剂和发泡剂投入密炼机中，并将至少一半的耐低温增塑剂加入密炼机；
C、在120～130摄氏度温度条件下混炼；
D、将填充剂和剩余部分的耐低温增塑剂加入密炼机中，混炼至温度达150～160摄氏度出料；
E、将密炼机混炼出的混炼胶料倒入开炼机冷却后出片，放置2～3天；
F、取放置后的混炼胶料，投入密炼机中，并加入硫化剂和促进剂，混炼均匀后倒入开炼机；
G、冷却出片，然后通过挤出机定型，放入140～150摄氏度的烘箱中烘干15～20分钟；
H、取出烘箱中半成品，在空气中放置冷却后，再放入160～170摄氏度烘箱下烘干15～20分钟；
I、待完全发泡后取出，冷却定型；
J、将冷却定型后的材料通过打孔机压制出特定形状的凹槽；
K、在开设好凹槽的材料表面涂设防静电涂层和玻璃布涂层。
使用时，本发明以NBR和EVA为主体材料，配合耐低温增塑剂、发泡剂、填充剂和防老剂等共同构成了本发明的配方体系，同时通过无卤阻燃剂的作用，可有效提高本材料的绝热效果，保障了人们使用的安全性，在本体1的外表面开设了三种形状的凹槽2，可提高本材料的的摩擦力，提高其安装时的稳定性，同时在本体1的外表面从内向外依次涂设了防静电涂层3和玻璃布涂层4，有效提高了本材料的抗静电和耐腐蚀能力，延长了其使用寿命。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。

Claims (8)

1.一种橡塑绝热保温材料，包括本体(1)，其特征在于：所述本体(1)的外表面开设有凹槽(2)，所述本体(1)的外表面从内向外依次涂设有防静电涂层(3)和玻璃布涂层(4)，所述本体(1)由NBR、EVA、PVC、无卤阻燃剂、耐低温增塑剂、发泡剂、填充剂、防老剂和氯化石蜡组成，其重量百分比为：NBR13％～30％；EVA8％～25％；PVC2％～5％；无卤阻燃剂20％～40％；耐低温增塑剂10％～20％；发泡剂7％～15％；填充剂3％～20％；防老剂13％～30％；氯化石蜡0.5％～2％。
2.根据权利要求1所述的一种橡塑绝热保温材料，其特征在于：所述凹槽(2)为三种形状，且凹槽(2)的深度为0.1～0.3mm。
3.根据权利要求1所述的一种橡塑绝热保温材料，其特征在于：所述防静电涂层(3)的厚度为20～50μm。
4.根据权利要求1所述的一种橡塑绝热保温材料，其特征在于：所述玻璃布涂层(4)的厚度为100～200μm。
5.根据权利要求1所述的一种橡塑绝热保温材料，其特征在于：所述无卤阻燃剂为氢氧化铝，或氢氧化铝和氢氧化镁的混合物。
6.根据权利要求1所述的一种橡塑绝热保温材料，其特征在于：所述填充剂为滑石粉、陶土、碳酸钙中的一种或几种的混合物。
7.根据权利要求1所述的一种橡塑绝热保温材料，其特征在于：所述耐低温增塑剂为己二酸二辛酯、癸二酸二辛酯中的一种或两种的混合物。
8.根据权利要求1所述的一种橡塑绝热保温材料，其特征在于：其制作方法包括以下步骤：
A、将NBR、EVA、PVC、防老化剂和氯化石蜡放入密炼机中混炼；
B、将无卤阻燃剂和发泡剂投入密炼机中，并将至少一半的耐低温增塑剂加入密炼机；
C、在120～130摄氏度温度条件下混炼；
D、将填充剂和剩余部分的耐低温增塑剂加入密炼机中，混炼至温度达150～160摄氏度出料；
E、将密炼机混炼出的混炼胶料倒入开炼机冷却后出片，放置2～3天；
F、取放置后的混炼胶料，投入密炼机中，并加入硫化剂和促进剂，混炼均匀后倒入开炼机；
G、冷却出片，然后通过挤出机定型，放入140～150摄氏度的烘箱中烘干15～20分钟；
H、取出烘箱中半成品，在空气中放置冷却后，再放入160～170摄氏度烘箱下烘干15～20分钟；
I、待完全发泡后取出，冷却定型；
J、将冷却定型后的材料通过打孔机压制出特定形状的凹槽；
K、在开设好凹槽的材料表面涂设防静电涂层和玻璃布涂层。
CN201710626399.8A 2017-07-27 2017-07-27 一种橡塑绝热保温材料 Pending CN107286407A (zh)