CN107236438A - 一种农机用复合防火涂料及其制备方法 - Google Patents
一种农机用复合防火涂料及其制备方法 Download PDFInfo
- Publication number
- CN107236438A CN107236438A CN201710462715.2A CN201710462715A CN107236438A CN 107236438 A CN107236438 A CN 107236438A CN 201710462715 A CN201710462715 A CN 201710462715A CN 107236438 A CN107236438 A CN 107236438A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- agricultural machinery
- fire retardant
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种农机用复合防火涂料及其制备方法，包括以下重量份的原料：聚氨酯树脂68～92份，环氧树脂12～24份，双马来酰亚胺树脂34～46份，云母粉12～24份，陶瓷粉24～36份，PETS 10～16份，二甲基硅油10～16份，流变助剂2～6份，光稳定剂0.3～0.8份，季戊四醇磷酸酯三聚氰胺盐10～25份，乳化剂1.6～3.8份，缓蚀剂0.15～0.25份，溶剂110～150份；其制备方法包括：树脂的溶解，助剂的混入以及季戊四醇磷酸酯三聚氰胺盐、云母粉和陶瓷粉的分散。本发明提出的防火涂料，不但具有高阻燃性能，同时耐磨、耐高温和抗老化性能优异，且制备过程简单、易操作，可进行大规模生产。
Description
技术领域
本发明涉及农业机械设备技术领域，尤其涉及一种农机用复合防火涂料及其制备方法。
背景技术
农机是农业生产中使用的各种机器的统称。如大小型拖拉机、平整土地机械、耕地犁具、耕耘机、插秧机、播种机、脱粒机、抽水机、联合收割机、卷帘机、保温毡等设备，应用十分广泛，对农产品的耕种、加工和生产起着重要作用。
为了防止农机的基本机构框架的生锈常会在农机表面涂覆一层涂料，然而现有的农机用涂料暴露在自然环境下易发生老化现象，导致涂层从农机本体上开裂、脱落，使涂料对农机本体的防锈作用减弱，而且由于农机在使用时需要与其他物质频繁接触，使农机表面的涂料易被挂擦掉，再遇霉雨天气，被挂擦掉的地方就会伸入水汽，加速农机本体生锈的速度。
发明内容
本发明的目的是为了解决现有技术中存在的缺点，而提出的一种农机用复合防火涂料及其制备方法。
一种农机用复合防火涂料，包括以下重量份的原料：聚氨酯树脂68～92份，环氧树脂12～24份，双马来酰亚胺树脂34～46份，云母粉12～24份，陶瓷粉24～36份，PETS 10～16份，二甲基硅油10～16份，流变助剂2～6份，光稳定剂0.3～0.8份，季戊四醇磷酸酯三聚氰胺盐10～25份，乳化剂1.6～3.8份，缓蚀剂0.15～0.25份，溶剂110～150份。
优选的，所述的一种农机用复合防火涂料，包括以下重量份的原料：聚氨酯树脂72～ 88份，环氧树脂14～20份，双马来酰亚胺树脂38～40份，云母粉14～20份，陶瓷粉26～34份，PETS 12～15份，二甲基硅油12～15份，流变助剂3～5份，光稳定剂0.3～0.8份，季戊四醇磷酸酯三聚氰胺盐10～20份，乳化剂2～3.4份，缓蚀剂0.15～0.25份，溶剂120～ 140份。
优选的，所述的一种农机用复合防火涂料，包括以下重量份的原料：聚氨酯树脂78份，环氧树脂17份，双马来酰亚胺树脂39份，云母粉17份，陶瓷粉30份，PETS 14份，二甲基硅油14份，流变助剂4份，光稳定剂0.5份，季戊四醇磷酸酯三聚氰胺盐15份，乳化剂2.8份，缓蚀剂0.2份，溶剂130份。
优选的，所述聚氨酯树脂、环氧树脂和双马来酰亚胺树脂的重量份比为2.5～7：1：1.5～3。
优选的，所述光稳定剂为2-(2’-羟基-5’-甲基苯基)苯并三氮唑、二氧化锌和二氧化钛的混合物，且2-(2’-羟基-5’-甲基苯基)苯并三氮唑、二氧化锌和二氧化钛的重量份比为1：0.5～1：0.5～1。
优选的，所述缓蚀剂为炔醇类缓蚀剂，所述炔醇类缓蚀剂为2-甲基-3-炔-2-丁醇、甲基戊炔醇和二甲基己炔醇中的任意一种或几种混合。
优选的，所述溶剂为甲苯、苯和乙醇的混合物，所述甲苯、苯和乙醇的重量份比为2～ 4：1～6：3～8。
本发明还提出了一种农机用复合防火涂料的制备方法，包括以下步骤：
S1：将相应重量份的聚氨酯树脂、环氧树脂和双马来酰亚胺树脂置于切片机中切片，再转移至反应瓶中，于60～80℃，边搅拌边加入相应重量份的溶剂，直至聚氨酯树脂、环氧树脂和双马来酰亚胺树脂溶解完全，即得树脂混合液；
S2：保持S1步骤中的温度，并向树脂混合液中加入相应重量份的PETS、二甲基硅油和流变助剂，搅拌20～40min后保温10～30min，再将温度降至40～60℃，然后加入相应重量份的光稳定剂、乳化剂和缓蚀剂，继续搅拌10～30min，得混合物A；
S3：向混合物A中依次分散季戊四醇磷酸酯三聚氰胺盐、云母粉和陶瓷粉，再超声脱气即得农机用复合防火涂料。
本发明提出的防火涂料，不但具有较高的阻燃性能，同时耐磨、耐高温和抗老化性能优异；涂料以廉价易得的聚氨酯树脂、环氧树脂和双马来酰亚胺树脂为主料，三者的合理配比可以克服使用单一树脂时的不足，使制备的涂料的耐温、耐磨性能好，且与基体的结合力强，在原料中填充陶瓷粉末和云母粉，可以增强涂料的耐磨和耐温性能，且涂料在使用时均匀分散的陶瓷粉可以吸收阳光中的紫外线，一方面降低阳光中紫外线对涂料的老化性能的影响，另一方面还可以起到抑菌、杀菌的功效，再配合由2-(2’-羟基-5’-甲基苯基) 苯并三氮唑、二氧化锌和二氧化钛组成的复合型光稳定剂，可以显著提高涂料的稳定性，避免其在使用过程中的出现开裂、脱落的现象；而且炔醇类缓蚀剂的加入可以在涂料使用时在基体表面形成一层防腐蚀膜，对基体起到保护作用，尤其是对金属类的基体，保护效果尤为突出，本发明还提出了一种简单的制备农机用复合防火涂料的方法，制备过程简单、易操作，并可进行大规模生产。
本发明的附加方面和优点将在下面的描述中部分给出，部分将从下面的描述中变得明显，或通过本发明的实践了解到。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
本发明提出的一种农机用复合防火涂料，包括以下重量份的原料：聚氨酯树脂78份，环氧树脂17份，双马来酰亚胺树脂39份，云母粉17份，陶瓷粉30份，PETS 14份，二甲基硅油14份，流变助剂4份，2-(2’-羟基-5’-甲基苯基)苯并三氮唑0.2份，二氧化锌0.2份，二氧化钛0.1份，季戊四醇磷酸酯三聚氰胺盐15份，乳化剂2.8份，二甲基己炔醇0.2份，溶剂130份。
其制备方法，包括以下步骤：
S1：将相应重量份的聚氨酯树脂、环氧树脂和双马来酰亚胺树脂置于切片机中切片，再转移至反应瓶中，于70℃，边搅拌边加入相应重量份的溶剂，直至聚氨酯树脂、环氧树脂和双马来酰亚胺树脂溶解完全，即得树脂混合液；
S2：保持S1步骤中的温度，并向树脂混合液中加入相应重量份的PETS、二甲基硅油和流变助剂，搅拌30min后保温20min，再将温度降至50℃，然后加入相应重量份的2-(2’-羟基-5’-甲基苯基)苯并三氮唑、二氧化锌、二氧化钛、乳化剂和二甲基己炔醇，继续搅拌20min，得混合物A；
S3：向混合物A中依次分散季戊四醇磷酸酯三聚氰胺盐、云母粉和陶瓷粉，超声脱气即得农机用复合防火涂料。
本发明中，所述溶剂为甲苯、苯和乙醇的混合物，所述甲苯、苯和乙醇的重量份比为3： 2：5。
实施例二
本发明提出的一种农机用复合防火涂料，包括以下重量份的原料：聚氨酯树脂85份，环氧树脂20份，双马来酰亚胺树脂46份，云母粉12份，陶瓷粉36份，PETS 12份，二甲基硅油16份，流变助剂6份，2-(2’-羟基-5’-甲基苯基)苯并三氮唑0.1份，二氧化锌0.1份，二氧化钛0.1份，季戊四醇磷酸酯三聚氰胺盐25份，乳化剂1.6份，甲基戊炔醇0.25份，溶剂150份。
其制备方法，包括以下步骤：
S1：将相应重量份的聚氨酯树脂、环氧树脂和双马来酰亚胺树脂置于切片机中切片，再转移至反应瓶中，于80℃，边搅拌边加入相应重量份的溶剂，直至聚氨酯树脂、环氧树脂和双马来酰亚胺树脂溶解完全，即得树脂混合液；
S2：保持S1步骤中的温度，并向树脂混合液中加入相应重量份的PETS、二甲基硅油和流变助剂，搅拌40min后保温10min，再将温度降至60℃，然后加入相应重量份的2-(2’-羟基-5’-甲基苯基)苯并三氮唑、二氧化锌、二氧化钛、乳化剂和甲基戊炔醇，继续搅拌10～30min，得混合物A；
S3：向混合物A中依次分散季戊四醇磷酸酯三聚氰胺盐、云母粉和陶瓷粉，再超声脱气即得农机用复合防火涂料。
本发明中，所述溶剂为甲苯、苯和乙醇的混合物，所述甲苯、苯和乙醇的重量份比为4： 1：3。
实施例三
本发明提出的一种农机用复合防火涂料，包括以下重量份的原料：聚氨酯树脂72份，环氧树脂16份，双马来酰亚胺树脂38份，云母粉24份，陶瓷粉24份，PETS 16份，二甲基硅油10份，流变助剂4份，2-(2’-羟基-5’-甲基苯基)苯并三氮唑0.2份，二氧化锌0.2份，二氧化钛0.2份，季戊四醇磷酸酯三聚氰胺盐10份，乳化剂2.5份，2-甲基-3-炔-2-丁醇0.15份，二甲基己炔醇0.1份，溶剂120份。
其制备方法，包括以下步骤：
S1：将相应重量份的聚氨酯树脂、环氧树脂和双马来酰亚胺树脂置于切片机中切片，再转移至反应瓶中，于60℃，边搅拌边加入相应重量份的溶剂，直至聚氨酯树脂、环氧树脂和双马来酰亚胺树脂溶解完全，即得树脂混合液；
S2：保持S1步骤中的温度，并向树脂混合液中加入相应重量份的PETS、二甲基硅油和流变助剂，搅拌40min后保温30min，再将温度降至40℃，然后加入相应重量份的2-(2’-羟基-5’-甲基苯基)苯并三氮唑、二氧化锌、二氧化钛、乳化剂、2-甲基-3-炔-2-丁醇和二甲基己炔醇，继续搅拌30min，得混合物A；
S3：向混合物A中依次分散季戊四醇磷酸酯三聚氰胺盐、云母粉和陶瓷粉，再超声脱气即得农机用复合防火涂料。
本发明中，所述溶剂为甲苯、苯和乙醇的混合物，所述甲苯、苯和乙醇的重量份比为2： 4：4。
使用实施例一～三制备的防火涂料涂覆在工件上，进行性能测试，测试结果如下：
其中，老化实验的条件为4000±500lux，100℃照射24h。
上述结果表明，实施例一～三制备的防火涂料阻燃等级均可到达A级，而市售涂料仅为B1级，表明实施例一～三制备的防火涂料的阻燃防火性能好，且在强紫外线照射和高温的破坏下，使用实施例一～三制备的涂料涂覆的工件均未发生开裂和脱落的现象，而市售涂料在第16h就发生开裂、在第22h就发生脱落的现象，而且到达24h则出现大面积脱落的现象，表明本发明提出的涂料的耐老化性能远优于市售涂料，且耐火时间也比市售涂料高，实施例一～三制备的防火涂料的耐火时间可以达到100min以上。
以上所揭露的仅为本发明一种较佳实施例而已，当然不能以此来限定本发明之权利范围，因此依本发明权利要求所作的等同变化，仍属本发明所涵盖的范围。
Claims (8)
1.一种农机用复合防火涂料，其特征在于，包括以下重量份的原料：聚氨酯树脂68～92份，环氧树脂12～24份，双马来酰亚胺树脂34～46份，云母粉12～24份，陶瓷粉24～36份，PETS 10～16份，二甲基硅油10～16份，流变助剂2～6份，光稳定剂0.3～0.8份，季戊四醇磷酸酯三聚氰胺盐10～25份，乳化剂1.6～3.8份，缓蚀剂0.15～0.25份，溶剂110～150份。
2.根据权利要求1所述的一种农机用复合防火涂料，其特征在于，包括以下重量份的原料：聚氨酯树脂72～88份，环氧树脂14～20份，双马来酰亚胺树脂38～40份，云母粉14～20份，陶瓷粉26～34份，PETS 12～15份，二甲基硅油12～15份，流变助剂3～5份，光稳定剂0.3～0.8份，季戊四醇磷酸酯三聚氰胺盐10～20份，乳化剂2～3.4份，缓蚀剂0.15～0.25份，溶剂120～140份。
3.根据权利要求1所述的一种农机用复合防火涂料，其特征在于，包括以下重量份的原料：聚氨酯树脂78份，环氧树脂17份，双马来酰亚胺树脂39份，云母粉17份，陶瓷粉30份，PETS 14份，二甲基硅油14份，流变助剂4份，光稳定剂0.5份，季戊四醇磷酸酯三聚氰胺盐15份，乳化剂2.8份，缓蚀剂0.2份，溶剂130份。
4.根据权利要求1所述的一种农机用复合防火涂料，其特征在于，所述聚氨酯树脂、环氧树脂和双马来酰亚胺树脂的重量份比为2.5～7：1：1.5～3。
5.根据权利要求1所述的一种农机用复合防火涂料，其特征在于，所述光稳定剂为2-(2’-羟基-5’-甲基苯基)苯并三氮唑、二氧化锌和二氧化钛的混合物，且2-(2’-羟基-5’-甲基苯基)苯并三氮唑、二氧化锌和二氧化钛的重量份比为1：0.5～1：0.5～1。
6.根据权利要求1所述的一种农机用复合防火涂料，其特征在于，所述缓蚀剂为炔醇类缓蚀剂，所述炔醇类缓蚀剂为2-甲基-3-炔-2-丁醇、甲基戊炔醇和二甲基己炔醇中的任意一种或几种混合。
7.根据权利要求1所述的一种农机用复合防火涂料，其特征在于，所述溶剂为甲苯、苯和乙醇的混合物，所述甲苯、苯和乙醇的重量份比为2～4：1～6：3～8。
8.一种农机用复合防火涂料的制备方法，其特征在于，包括以下步骤：
S1：将相应重量份的聚氨酯树脂、环氧树脂和双马来酰亚胺树脂置于切片机中切片，再转移至反应瓶中，于60～80℃，边搅拌边加入相应重量份的溶剂，直至聚氨酯树脂、环氧树脂和双马来酰亚胺树脂溶解完全，即得树脂混合液；
S2：保持S1步骤中的温度，并向树脂混合液中加入相应重量份的PETS、二甲基硅油和流变助剂，搅拌20～40min后保温10～30min，再将温度降至40～60℃，然后加入相应重量份的光稳定剂、乳化剂和缓蚀剂，继续搅拌10～30min，得混合物A；
S3：向混合物A中依次分散季戊四醇磷酸酯三聚氰胺盐、云母粉和陶瓷粉，再超声脱气即得农机用复合防火涂料。