CN107236283A - A kind of anti-aging cable sheath material and preparation method thereof - Google Patents
A kind of anti-aging cable sheath material and preparation method thereof Download PDFInfo
- Publication number
- CN107236283A CN107236283A CN201710609839.9A CN201710609839A CN107236283A CN 107236283 A CN107236283 A CN 107236283A CN 201710609839 A CN201710609839 A CN 201710609839A CN 107236283 A CN107236283 A CN 107236283A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable sheath
- sheath material
- aging cable
- polyurethane resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to electric power field of material technology there is provided a kind of anti-aging cable sheath material and preparation method thereof, described CABLE MATERIALS includes the raw material of following parts by weight：52 64 parts of modified polyurethane resin, 13 22 parts of haloflex, 7 22 parts of dibutyl maleate, 12 19 parts of organic nano imvite, 25 parts of phthalocyanine blue, 25 parts of chlorinated paraffin, 14 parts of age resister, 0.6 2.8 parts of coupling agent, 1.3 3.4 parts of ultra-violet absorber, 1.6 2.9 parts of plasticizer.The cable sheath material of the present invention, the characteristics of possessing ageing-resistant, due to having used modified polyurethane resin as primary raw material, it is aided with organic nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, ultra-violet absorber, so that prepared cable sheath material has excellent ageing-resistant performance.
Description
Technical field
The invention belongs to electric power field of material technology, in particular it relates to a kind of anti-aging cable sheath material and its system
Preparation Method.
Background technology
Cable cover(ing) is the indispensable intermediate structure part of cable, plays a part of protecting cable, it is ensured that cable it is logical
Electric safety, allows the medium such as copper wire and water, air to completely cut off, it is to avoid leaky occur.With expanding economy, it is necessary to use cable
Place become variation, have more strict and various requirement to the performance indications of cable jacket material, such as insulate
The index such as property, tensile strength, temperature in use, fire resistance has strict requirements.There is anti-flammability traditional sheath material more
Difference, poor chemical stability, high temperature is yielding, poor mechanical property, short service life the problems such as, particularly in high temperature, rainy, ultraviolet
The strong area of line, ozone, easily occurs to early the aging phenomena such as deformation, cracking, and aging further speeds up cable cover(ing)
The mechanical degradations such as insulating properties, tensile strength, have a strong impact on the performance of cable, and many inconvenience are brought to actual use,
Therefore, it is badly in need of changing original sheath material formula, improved materials performance, with the various demand in appropriate cable market.
Accordingly, it would be desirable to research and develop a kind of anti-aging CABLE MATERIALS sheath material.
The content of the invention
For defect of the prior art, it is an object of the invention to provide a kind of anti-aging cable sheath material and preparation
Method.
A kind of anti-aging cable sheath material provided according to an aspect of the present invention, described anti-aging cable cover(ing)
Material includes the raw material of following parts by weight：52-64 parts of modified polyurethane resin, 13-22 parts of haloflex, maleic acid
7-22 parts of dibutyl ester, 12-19 parts of organic nano imvite, 2-5 parts of phthalocyanine blue, 2-5 parts of chlorinated paraffin, 1-4 parts of age resister, idol
Join 0.6-2.8 parts of agent, 1.3-3.4 parts of ultra-violet absorber, 1.6-2.9 parts of plasticizer；Wherein, the modified polyurethane resin
Method of modifying is specific as follows：
(1), the acetone soln and mass concentration by the sulfonic anionic polyurethane of side chain band, mass concentration for 11%
It is added to for 9% hydrochloric acid solution in reactor, the volume of the anionic polyurethane, acetone soln and hydrochloric acid solution consumption
Than for 2:65:0.4, heated, when temperature is increased to 65-70 DEG C, deionized water is slowly added into mixed solution
Row hydrolysis, the consumption of the deionized water accounts for the mass percent of the anionic polyurethane consumption for 6-7%, hydrolysis
The time of reaction is 1-1.5h, obtains a hydrolyzate；
(2), tetra-n-butyl titanate is dissolved in the acetone soln, tetra-n-butyl titanate lysate is obtained；
(3) the tetra-n-butyl titanate lysate in (2), heating temperature, are slowly dropped to toward a hydrolyzate in (1)
Spend for 65-80 DEG C, then proceed to be added dropwise deionized water and carry out secondary hydrolysis, the consumption of the deionized water account for it is described once
The mass percent of hydrolyzate consumption is 8-12%, and the time of hydrolysis is 1-1.9h, obtains secondary hydrolyzate；
(4) the secondary hydrolyzate in (3), is subjected to vacuum distillation, the pressure of the vacuum distillation is 0.04-0.05MPa,
Temperature is 80-120 DEG C, obtained distillate as modified polyurethane resin.
Preferably, the organic nano imvite average wafer thickness is less than 20nm, and smectite content is more than 95%.
Preferably, the still head of the vacuum distillation uses kirschner still head.
Preferably, the plasticizer is the tricaprylate of triethylene glycol two or dihexyl adipate.
Preferably, the ultra-violet absorber is Ultraviolet Absorber UV-P.
Preferably, the age resister includes the raw material of following parts by weight：35-55 parts of aromatic naphtha, alpha-naphthylamine 30-50
5-10 parts of part, 5-10 parts of emulsifying agent and water.
Preferably, the coupling agent is silane coupler.
There is provided a kind of anti-aging cable sheath material preparation method, methods described bag according to another aspect of the present invention
Include following steps：
Step 1: weighing modified polyurethane resin, haloflex, along fourth according to the parts by weight described in claim 1
Enedioic acid dibutyl ester, organic nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticising
Agent；
Step 2: after modified polyurethane resin, haloflex, dibutyl maleate are blended uniformly, addition has
Machine nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticizer, send into high-speed kneading
In machine, 10-25min is mediated under 90-110 DEG C of temperature conditionss, after material cooling is mediated, feeding double screw extruder granulation, i.e.,
.
Compared with prior art, the present invention has following beneficial effect：
1st, a kind of anti-aging cable sheath material that the present invention is provided, the characteristics of possessing ageing-resistant, with stronger warp
Ji value.The cable sheath material of the present invention is aided with organic nano due to having used modified polyurethane resin as primary raw material
Montmorillonite, phthalocyanine blue, chlorinated paraffin, age resister, ultra-violet absorber, so that prepared cable sheath material has
Excellent ageing-resistant performance.
2nd, a kind of anti-aging cable sheath material for providing of the present invention, the sulfonic anionic polyurethane of side chain band and
Tetra-n-butyl titanate can effectively control the degree of cross linking of polyurethane resin by fractional hydrolysis, so as to improve cable sheath material
Elasticity, with organic nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, ultra-violet absorber compound, effectively increase
Resistance to ag(e)ing.
3rd, the organic nano added in a kind of anti-aging cable sheath material that the present invention is provided, cable material formula covers de-
Soil has larger specific surface area, and adsorptivity greatly, enhances the compatibility between each component in material prescription, can significantly improve shield
Intensity, the hardness of cover material so that the mechanical property of sheath material is significantly improved, and reduces ageing rate.
4th, the age resister in a kind of anti-aging cable sheath material that the present invention is provided, cable material formula is former with other
Expect compound use, and then improve the ageing resistace of sheath material, increase the service life.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.
Embodiment 1
A kind of anti-aging cable sheath material that the present embodiment is provided, described anti-aging cable sheath material includes
The raw material of following parts by weight：64 parts of modified polyurethane resin, 13 parts of haloflex, 22 parts of dibutyl maleate, have
12 parts of machine nano imvite, 5 parts of phthalocyanine blue, 2 parts of chlorinated paraffin, 4 parts of age resister, 0.6 part of coupling agent, ultra-violet absorber
3.4 parts, 1.6 parts of plasticizer；Wherein, the method for modifying of the modified polyurethane resin is specific as follows：
(1), the acetone soln and mass concentration by the sulfonic anionic polyurethane of side chain band, mass concentration for 11%
It is added to for 9% hydrochloric acid solution in reactor, the volume of the anionic polyurethane, acetone soln and hydrochloric acid solution consumption
Than for 2:65:0.4, heated, when temperature is increased to 70 DEG C, deionized water is slowly added into mixed solution and enters water-filling
Solution reaction, it is 6% that the consumption of the deionized water, which accounts for the mass percent of the anionic polyurethane consumption, hydrolysis
Time is 1.5h, obtains a hydrolyzate；
(2), tetra-n-butyl titanate is dissolved in the acetone soln, tetra-n-butyl titanate lysate is obtained；
(3) the tetra-n-butyl titanate lysate in (2), heating temperature, are slowly dropped to toward a hydrolyzate in (1)
Spend for 80 DEG C, then proceed to that the secondary hydrolysis of deionized water progress is added dropwise, the consumption of the deionized water accounts for a water
The mass percent for solving liquid consumption is 8%, and the time of hydrolysis is 1.9h, obtains secondary hydrolyzate；
(4) the secondary hydrolyzate in (3), is subjected to vacuum distillation, the pressure of the vacuum distillation is 0.05MPa, temperature
For 80 DEG C, obtained distillate as modified polyurethane resin.
Wherein, the organic nano imvite average wafer thickness is less than 20nm, and smectite content is more than 95%.
Wherein, the still head of the vacuum distillation uses kirschner still head.
Wherein, the plasticizer is the tricaprylate of triethylene glycol two or dihexyl adipate.
Wherein, the ultra-violet absorber is Ultraviolet Absorber UV-P.
Wherein, the age resister includes the raw material of following parts by weight：55 parts of aromatic naphtha, 30 parts of alpha-naphthylamine, emulsifying agent
10 parts and 5 parts of water.
Wherein, the coupling agent is silane coupler.
There is provided a kind of anti-aging cable sheath material preparation method, methods described bag according to another aspect of the present invention
Include following steps：
Step 1: weighing modified polyurethane resin, haloflex, along fourth according to the parts by weight described in claim 1
Enedioic acid dibutyl ester, organic nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticising
Agent；
Step 2: after modified polyurethane resin, haloflex, dibutyl maleate are blended uniformly, addition has
Machine nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticizer, send into high-speed kneading
In machine, 10min is mediated under 110 DEG C of temperature conditionss, after material cooling is mediated, feeding double screw extruder granulation is produced.
Embodiment 2
A kind of anti-aging cable sheath material that the present embodiment is provided, described anti-aging cable sheath material includes
The raw material of following parts by weight：It is 52 parts of modified polyurethane resin, 22 parts of haloflex, 7 parts of dibutyl maleate, organic
19 parts of nano imvite, 2 parts of phthalocyanine blue, 5 parts of chlorinated paraffin, 1 part of age resister, 2.8 parts of coupling agent, ultra-violet absorber 1.3
Part, 2.9 parts of plasticizer；Wherein, the method for modifying of the modified polyurethane resin is specific as follows：
(1), the acetone soln and mass concentration by the sulfonic anionic polyurethane of side chain band, mass concentration for 11%
It is added to for 9% hydrochloric acid solution in reactor, the volume of the anionic polyurethane, acetone soln and hydrochloric acid solution consumption
Than for 2:65:0.4, heated, when temperature is increased to 65 DEG C, deionized water is slowly added into mixed solution and enters water-filling
Solution reaction, it is 7% that the consumption of the deionized water, which accounts for the mass percent of the anionic polyurethane consumption, hydrolysis
Time is 1h, obtains a hydrolyzate；
(2), tetra-n-butyl titanate is dissolved in the acetone soln, tetra-n-butyl titanate lysate is obtained；
(3) the tetra-n-butyl titanate lysate in (2), heating temperature, are slowly dropped to toward a hydrolyzate in (1)
Spend for 65 DEG C, then proceed to that the secondary hydrolysis of deionized water progress is added dropwise, the consumption of the deionized water accounts for a water
The mass percent for solving liquid consumption is 12%, and the time of hydrolysis is 1h, obtains secondary hydrolyzate；
(4) the secondary hydrolyzate in (3), is subjected to vacuum distillation, the pressure of the vacuum distillation is 0.04MPa, temperature
For 120 DEG C, obtained distillate as modified polyurethane resin.
Wherein, the organic nano imvite average wafer thickness is less than 20nm, and smectite content is more than 95%.
Wherein, the still head of the vacuum distillation uses kirschner still head.
Wherein, the plasticizer is the tricaprylate of triethylene glycol two or dihexyl adipate.
Wherein, the ultra-violet absorber is Ultraviolet Absorber UV-P.
Wherein, the age resister includes the raw material of following parts by weight：35 parts of aromatic naphtha, 50 parts of alpha-naphthylamine, emulsifying agent 5
10 parts of part and water.
Wherein, the coupling agent is silane coupler.
There is provided a kind of anti-aging cable sheath material preparation method, methods described bag according to another aspect of the present invention
Include following steps：
Step 1: weighing modified polyurethane resin, haloflex, along fourth according to the parts by weight described in claim 1
Enedioic acid dibutyl ester, organic nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticising
Agent；
Step 2: after modified polyurethane resin, haloflex, dibutyl maleate are blended uniformly, addition has
Machine nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticizer, send into high-speed kneading
In machine, 25min is mediated under 90 DEG C of temperature conditionss, after material cooling is mediated, feeding double screw extruder granulation is produced.
Embodiment 3
A kind of anti-aging cable sheath material that the present embodiment is provided, described anti-aging cable sheath material includes
The raw material of following parts by weight：57 parts of modified polyurethane resin, 19 parts of haloflex, 11 parts of dibutyl maleate, have
17 parts of machine nano imvite, 3 parts of phthalocyanine blue, 4 parts of chlorinated paraffin, 3 parts of age resister, 1.3 parts of coupling agent, ultra-violet absorber
2.4 parts, 2.3 parts of plasticizer；Wherein, the method for modifying of the modified polyurethane resin is specific as follows：
(1), the acetone soln and mass concentration by the sulfonic anionic polyurethane of side chain band, mass concentration for 11%
It is added to for 9% hydrochloric acid solution in reactor, the volume of the anionic polyurethane, acetone soln and hydrochloric acid solution consumption
Than for 2:65:0.4, heated, when temperature is increased to 68 DEG C, deionized water is slowly added into mixed solution and enters water-filling
Solution reaction, it is 6% that the consumption of the deionized water, which accounts for the mass percent of the anionic polyurethane consumption, hydrolysis
Time is 1.5h, obtains a hydrolyzate；
(2), tetra-n-butyl titanate is dissolved in the acetone soln, tetra-n-butyl titanate lysate is obtained；
(3) the tetra-n-butyl titanate lysate in (2), heating temperature, are slowly dropped to toward a hydrolyzate in (1)
Spend for 70 DEG C, then proceed to that the secondary hydrolysis of deionized water progress is added dropwise, the consumption of the deionized water accounts for a water
The mass percent for solving liquid consumption is 9%, and the time of hydrolysis is 1.5h, obtains secondary hydrolyzate；
(4) the secondary hydrolyzate in (3), is subjected to vacuum distillation, the pressure of the vacuum distillation is 0.05MPa, temperature
For 90 DEG C, obtained distillate as modified polyurethane resin.
Wherein, the organic nano imvite average wafer thickness is less than 20nm, and smectite content is more than 95%.
Wherein, the still head of the vacuum distillation uses kirschner still head.
Wherein, the plasticizer is the tricaprylate of triethylene glycol two or dihexyl adipate.
Wherein, the ultra-violet absorber is Ultraviolet Absorber UV-P.
Wherein, the age resister includes the raw material of following parts by weight：45 parts of aromatic naphtha, 35 parts of alpha-naphthylamine, emulsifying agent 7
7 parts of part and water.
Wherein, the coupling agent is silane coupler.
There is provided a kind of anti-aging cable sheath material preparation method, methods described bag according to another aspect of the present invention
Include following steps：
Step 1: weighing modified polyurethane resin, haloflex, along fourth according to the parts by weight described in claim 1
Enedioic acid dibutyl ester, organic nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticising
Agent；
Step 2: after modified polyurethane resin, haloflex, dibutyl maleate are blended uniformly, addition has
Machine nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticizer, send into high-speed kneading
In machine, 19min is mediated under 95 DEG C of temperature conditionss, after material cooling is mediated, feeding double screw extruder granulation is produced.
Performance test：
According to the raw material and proportioning described in embodiment 1-3, anti-aging cable sheath material is prepared, and passed through with above-mentioned material
Conventional method prepares cable, and the cable of preparation is divided into 1 group, 2 groups, 3 groups, and it is control group to take commercially available common cable.To above-mentioned
Each group cable carries out ultraviolet light and aging experiment, and degradation condition is UVB313 type uviol lamps, and radiation energy is 0.63W/m2/nm；
It is first 60 DEG C of radiation 4h in blackboard temperature that conditions of exposure, which is, and rear stopping radiation condensing 4h at 50 DEG C；Open-assembly time is 1000h.
Test index is as shown in table 1 for the test result of tensile strength, elongation at break and tearing strength.
The test result list of table 1
As can be seen here, the basic performance of the cable can meet or exceed specified value, possess preferable mechanical performance, say
The bright cable material has preferable ageing-resistant performance.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of anti-aging cable sheath material, it is characterised in that：Described anti-aging cable sheath material includes as follows
The raw material of parts by weight：52-64 parts of modified polyurethane resin, 13-22 parts of haloflex, dibutyl maleate 7-22
Part, 12-19 parts of organic nano imvite, 2-5 parts of phthalocyanine blue, 2-5 parts of chlorinated paraffin, 1-4 parts of age resister, coupling agent 0.6-
2.8 parts, 1.3-3.4 parts of ultra-violet absorber, 1.6-2.9 parts of plasticizer；Wherein, the method for modifying of the modified polyurethane resin
It is specific as follows：
（1）, by the sulfonic anionic polyurethane of side chain band, mass concentration be 11% acetone soln and mass concentration be 9%
Hydrochloric acid solution be added in reactor, the volume ratio of the anionic polyurethane, acetone soln and hydrochloric acid solution consumption is
2:65:0.4, heated, when temperature is increased to 65-70 DEG C, deionized water is slowly added into mixed solution and enters water-filling
Solution reaction, the consumption of the deionized water accounts for the mass percent of the anionic polyurethane consumption for 6-7%, hydrolysis
Time be 1-1.5h, obtain a hydrolyzate；
（2）, tetra-n-butyl titanate is dissolved in the acetone soln, obtain tetra-n-butyl titanate lysate；
（3）, toward described（1）In a hydrolyzate be slowly dropped to（2）In tetra-n-butyl titanate lysate, heating-up temperature is
65-80 DEG C, then proceed to be added dropwise deionized water and carry out secondary hydrolysis, the consumption of the deionized water, which is accounted for, described once to be hydrolyzed
The mass percent of liquid consumption is 8-12%, and the time of hydrolysis is 1-1.9h, obtains secondary hydrolyzate；
（4）, will（3）In secondary hydrolyzate carry out vacuum distillation, the pressure of the vacuum distillation is 0.04-0.05MPa, temperature
For 80-120 DEG C, obtained distillate as modified polyurethane resin.
2. a kind of anti-aging cable sheath material according to claim 1, it is characterised in that：The organic nano covers de-
Native average wafer thickness is less than 20nm, and smectite content is more than 95%.
3. a kind of anti-aging cable sheath material according to claim 1, it is characterised in that：The steaming of the vacuum distillation
Head is evaporated using kirschner still head.
4. a kind of anti-aging cable sheath material according to claim 1, it is characterised in that：The plasticizer is three second
The tricaprylate of glycol two or dihexyl adipate.
5. a kind of anti-aging cable sheath material according to claim 1, it is characterised in that：The ultra-violet absorber
For Ultraviolet Absorber UV-P.
6. a kind of anti-aging cable sheath material according to claim 1, it is characterised in that：The age resister includes
The raw material of following parts by weight：5-10 parts of 35-55 parts of aromatic naphtha, 30-50 parts of alpha-naphthylamine, 5-10 parts of emulsifying agent and water.
7. a kind of anti-aging cable sheath material according to claim 1, it is characterised in that：The coupling agent is silane
Coupling agent.
8. a kind of preparation method of anti-aging cable sheath material as described in claim any one of 1-7, it is characterised in that：
The preparation method comprises the following steps：
Step 1: weighing modified polyurethane resin, haloflex, maleic two according to the parts by weight described in claim 1
Dibutyl phthalate, organic nano imvite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticizer；
Step 2: after modified polyurethane resin, haloflex, dibutyl maleate are blended uniformly, adding organic receives
Rice montmorillonite, phthalocyanine blue, chlorinated paraffin, age resister, coupling agent, ultra-violet absorber, plasticizer, send into high-speed kneading machine
In, 10-25min is mediated under 90-110 DEG C of temperature conditionss, after material cooling is mediated, feeding double screw extruder granulation is produced.