CN107227063A - A kind of water-proof antibiotic powder of lacquer putty for use on and preparation method thereof - Google Patents
A kind of water-proof antibiotic powder of lacquer putty for use on and preparation method thereof Download PDFInfo
- Publication number
- CN107227063A CN107227063A CN201710498125.5A CN201710498125A CN107227063A CN 107227063 A CN107227063 A CN 107227063A CN 201710498125 A CN201710498125 A CN 201710498125A CN 107227063 A CN107227063 A CN 107227063A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- lacquer putty
- water
- proof antibiotic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-proof antibiotic powder of lacquer putty for use on, include the raw material of following parts by weight：15~25 parts of white cement, 15~25 parts of coarse whiting, 5~10 parts of aluminium-magnesium silicate, 8~12 parts of sodium bentonite, 8~12 parts of kaolin, 1~3 part of nano titanium oxide, 1~3 part of far-infared ceramic powder, 3~5 parts of antiseptic, 4~8 parts of binder；Its preparation method includes mixing fine powders A preparation, the preparation of mixed powder B, then binder is mixed into mixed powder B, produces water-proof antibiotic powder of lacquer putty for use on finished product.Powder of lacquer putty for use on proposed by the present invention, scientific formulation is reasonable, raw materials used safety and environmental protection, preparation method is simple, and all raw material completes mixing in same equipment, avoid dust pollution, production cost is low, waterproof and strong antibacterial, is difficult to go mouldy, and whiteness and texture are good, industrialized production can be carried out, be worthy to be popularized.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of water-proof antibiotic powder of lacquer putty for use on and preparation method thereof.
Background technology
Powder of lacquer putty for use on is a kind of decoration type material of smooth surface of wall, is a kind of product essential before coating is painted.
Painting is imposed on priming paint or directly applied and imposes on object, to remove rugged defect on coated article surface.Using a small amount of paint
Base, auxiliary agent, mass filler and appropriate coloring pigment are formulated, and can fill up part has the working surface of depression, also can be complete
Portion strikes off on surface, is typically after prime coat is parched, to be applied over primer coat surface.It is required that tack is good, do not produce in baking process
Raw crackle.With the continuous improvement of people's living standards, performance requirement more and more higher of the people to ornament materials.In the prior art
Powder of lacquer putty for use on be broadly divided into two kinds of common powder of lacquer putty for use on and water-resistant type powder of lacquer putty for use on, wherein common powder of lacquer putty for use on is only applicable to not require water-fast
Place.And though water-resistant type powder of lacquer putty for use on water-tolerant, itself whiteness and texture are not enough, safety and environmental protection performance is not up to standard, exists
Volatile matter pollution, wet is wet the problems such as go mouldy.Based on above statement, the present invention proposes a kind of water-proof antibiotic powder of lacquer putty for use on and its system
Preparation Method.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of water-proof antibiotic powder of lacquer putty for use on proposed
And preparation method thereof.
A kind of water-proof antibiotic powder of lacquer putty for use on, includes the raw material of following parts by weight：15~25 parts of white cement, 15~25 parts of coarse whiting,
5~10 parts of aluminium-magnesium silicate, 8~12 parts of sodium bentonite, 8~12 parts of kaolin, 1~3 part of nano titanium oxide, far-infrared ceramic
1~3 part of powder, 3~5 parts of antiseptic, 4~8 parts of binder.
It is preferred that, a kind of described water-proof antibiotic powder of lacquer putty for use on includes the raw material of following parts by weight：18~22 parts of white cement,
18~22 parts of coarse whiting, 6~9 parts of aluminium-magnesium silicate, 9~11 parts of sodium bentonite, 9~11 parts of kaolin, nano titanium oxide 1.5~
2.5 parts, 1.5~2.5 parts of far-infared ceramic powder, 3.5~4.5 parts of antiseptic, 5~7 parts of binder.
It is preferred that, a kind of described water-proof antibiotic powder of lacquer putty for use on includes the raw material of following parts by weight：20 parts of white cement, coarse whiting
20 parts, it is 8 parts of aluminium-magnesium silicate, 10 parts of sodium bentonite, 10 parts of kaolin, 2 parts of nano titanium oxide, 2 parts of far-infared ceramic powder, anti-
4 parts of microbial inoculum, 6 parts of binder.
It is preferred that, the antiseptic is that mass ratio is 3.5~5:It is anti-that 1~2 silver-zirconium phosphate antimicrobial and zeolite carries silver
The built agent of microbial inoculum.
It is preferred that, the binder is that mass ratio is 4.2~5.8:2~3:1~1.5:1~2 redispersable latex powder,
The mixture of pre-gelatinized starch, sodium carboxymethylcellulose and lignin fibre.
The invention also provides a kind of preparation method of water-proof antibiotic powder of lacquer putty for use on, comprise the following steps：
S1, the white cement of the proportion and coarse whiting added in grinder, after being fully ground, cross 200~300 mesh sieves, must mix
Fine powder A；
S2, the mixing fine powders A in step S1 is added to high-speed mixer, with 1400~2200r/min rotating speed, high-speed stirred
Mix after 15~25min, add the nano titanium oxide of the proportion, continue to stir 15~25min of mixing, add the proportion
Aluminium-magnesium silicate, sodium bentonite, kaolin and far-infared ceramic powder, continue stir mixing 10~20min, obtain mixed powder B；
S3, the antiseptic and binder of the proportion be added in step S2 in the mixed powder B of gained, and keep step S2
In rotating speed it is constant, continue stir mixing 1~2h, be well mixed after, packing produce water-proof antibiotic powder of lacquer putty for use on.
A kind of water-proof antibiotic powder of lacquer putty for use on proposed by the present invention, the white cement and coarse whiting discharged using non-volatility polluter
For primary raw material, after raw material is refined, there is the aluminium-magnesium silicate of water resistance, the Na-bentonite with enhancing whiteness by adding
Soil is auxiliary material with kaolin, the nano titanium oxide with antibacterial functions and far-infared ceramic powder, mixes system successively with binder
Into required water-proof antibiotic powder of lacquer putty for use on, inventive formulation is scientific and reasonable, raw materials used safety and environmental protection, and preparation method is simple, owns
Raw material complete mixing in same equipment, it is to avoid dust pollution, production cost is low, and gained water-proof antibiotic powder of lacquer putty for use on has good
Good water resistance and antibiotic effect, are difficult to go mouldy, and whiteness and texture are good, can carry out industrialized production, be worthy to be popularized.
Embodiment
The present invention is made with reference to specific embodiment further to explain.
Embodiment one
A kind of water-proof antibiotic powder of lacquer putty for use on proposed by the present invention, includes the raw material of following parts by weight：20 parts of white cement, 20 parts of coarse whiting,
8 parts of aluminium-magnesium silicate, 10 parts of sodium bentonite, 8 parts of kaolin, 3 parts of nano titanium oxide, 1 part of far-infared ceramic powder, antiseptic 3
Part, 6 parts of binder.
Its preparation method, comprises the following steps：
S1, the white cement of the proportion and coarse whiting added in grinder, after being fully ground, cross 200~300 mesh sieves, must mix
Fine powder A；
S2, the mixing fine powders A in step S1 is added to high-speed mixer, with 1800r/min rotating speed, high-speed stirred mixing
After 20min, the nano titanium oxide of the proportion is added, continuation, which is stirred, mixes 20min, the aluminium-magnesium silicate of the addition proportion,
Sodium bentonite, kaolin and far-infared ceramic powder, continue to stir mixing 15min, obtain mixed powder B；
S3, the antiseptic and binder of the proportion be added in step S2 in the mixed powder B of gained, and keep step S2
In rotating speed it is constant, continue stir mixing 2h, be well mixed after, packing produce water-proof antibiotic powder of lacquer putty for use on.
In the present invention, the antiseptic is that mass ratio is 4:1.5 silver-zirconium phosphate antimicrobial and zeolite carrying silver antimicrobials
Built agent；Binder is that mass ratio is 4.6:2.4:1.2:1.4 redispersable latex powder, pre-gelatinized starch, carboxymethyl are fine
The mixture of the plain sodium of dimension and lignin fibre.
Embodiment two
A kind of water-proof antibiotic powder of lacquer putty for use on proposed by the present invention, includes the raw material of following parts by weight：25 parts of white cement, 15 parts of coarse whiting,
10 parts of aluminium-magnesium silicate, 10 parts of sodium bentonite, 8 parts of kaolin, 2 parts of nano titanium oxide, 1 part of far-infared ceramic powder, antiseptic 5
Part, 5 parts of binder.
Its preparation method, comprises the following steps：
S1, the white cement of the proportion and coarse whiting added in grinder, after being fully ground, cross 200~300 mesh sieves, must mix
Fine powder A；
S2, the mixing fine powders A in step S1 is added to high-speed mixer, with 1400~2200r/min rotating speed, high-speed stirred
Mix after 15~25min, add the nano titanium oxide of the proportion, continue to stir 15~25min of mixing, add the proportion
Aluminium-magnesium silicate, sodium bentonite, kaolin and far-infared ceramic powder, continue stir mixing 10~20min, obtain mixed powder B；
S3, the antiseptic and binder of the proportion be added in step S2 in the mixed powder B of gained, and keep step S2
In rotating speed it is constant, continue stir mixing 1~2h, be well mixed after, packing produce water-proof antibiotic powder of lacquer putty for use on.
In the present invention, the antiseptic is that mass ratio is 5:2 silver-zirconium phosphate antimicrobial and zeolite carrying silver antimicrobials
Built agent；Binder is that mass ratio is 5:2:1.5:1 redispersable latex powder, pre-gelatinized starch, sodium carboxymethylcellulose and
The mixture of lignin fibre.
Embodiment three
A kind of water-proof antibiotic powder of lacquer putty for use on proposed by the present invention, includes the raw material of following parts by weight：15 parts of white cement, 15 parts of coarse whiting,
10 parts of aluminium-magnesium silicate, 12 parts of sodium bentonite, 8 parts of kaolin, 3 parts of nano titanium oxide, 2 parts of far-infared ceramic powder, antiseptic 4
Part, 6 parts of binder.
Its preparation method, comprises the following steps：
S1, the white cement of the proportion and coarse whiting added in grinder, after being fully ground, cross 200~300 mesh sieves, must mix
Fine powder A；
S2, the mixing fine powders A in step S1 is added to high-speed mixer, with 1400r/min rotating speed, high-speed stirred mixing
After 25min, the nano titanium oxide of the proportion is added, continuation, which is stirred, mixes 25min, the aluminium-magnesium silicate of the addition proportion,
Sodium bentonite, kaolin and far-infared ceramic powder, continue to stir mixing 20min, obtain mixed powder B；
S3, the antiseptic and binder of the proportion be added in step S2 in the mixed powder B of gained, and keep step S2
In rotating speed it is constant, continue stir mixing 2h, be well mixed after, packing produce water-proof antibiotic powder of lacquer putty for use on.
In the present invention, the antiseptic is that mass ratio is 5:1 silver-zirconium phosphate antimicrobial and zeolite carrying silver antimicrobials
Built agent；Binder is that mass ratio is 4.2:3:1.5:1 redispersable latex powder, pre-gelatinized starch, sodium carboxymethylcellulose
With the mixture of lignin fibre.
Example IV
A kind of water-proof antibiotic powder of lacquer putty for use on proposed by the present invention, includes the raw material of following parts by weight：25 parts of white cement, 15 parts of coarse whiting,
10 parts of aluminium-magnesium silicate, 10 parts of sodium bentonite, 12 parts of kaolin, 2 parts of nano titanium oxide, 3 parts of far-infared ceramic powder, antiseptic
4 parts, 4 parts of binder.
Its preparation method, comprises the following steps：
S1, the white cement of the proportion and coarse whiting added in grinder, after being fully ground, cross 200~300 mesh sieves, must mix
Fine powder A；
S2, the mixing fine powders A in step S1 is added to high-speed mixer, with 2200r/min rotating speed, high-speed stirred mixing
After 15min, the nano titanium oxide of the proportion is added, continuation, which is stirred, mixes 15min, the aluminium-magnesium silicate of the addition proportion,
Sodium bentonite, kaolin and far-infared ceramic powder, continue to stir mixing 10min, obtain mixed powder B；
S3, the antiseptic and binder of the proportion be added in step S2 in the mixed powder B of gained, and keep step S2
In rotating speed it is constant, continue stir mixing 1h, be well mixed after, packing produce water-proof antibiotic powder of lacquer putty for use on
In the present invention, the antiseptic is that mass ratio is 3.8:1.5 silver-zirconium phosphate antimicrobial and zeolite carrying silver antimicrobials
Built agent；Binder is that mass ratio is 4.6:2.5:1.3:1.8 redispersable latex powder, pre-gelatinized starch, carboxymethyl cellulose
The mixture of plain sodium and lignin fibre.
The performance of the water-proof antibiotic powder of lacquer putty for use on prepared respectively in the test embodiment of the present invention one~tetra-, draws following parameter：
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto, it is any
Those familiar with the art the invention discloses technical scope in, technique according to the invention scheme and its invention
Design is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
1. a kind of water-proof antibiotic powder of lacquer putty for use on, it is characterised in that include the raw material of following parts by weight：15~25 parts of white cement, coarse whiting
15~25 parts, 5~10 parts of aluminium-magnesium silicate, 8~12 parts of sodium bentonite, 8~12 parts of kaolin, 1~3 part of nano titanium oxide,
1~3 part of far-infared ceramic powder, 3~5 parts of antiseptic, 4~8 parts of binder.
2. a kind of water-proof antibiotic powder of lacquer putty for use on according to claim 1, it is characterised in that include the raw material of following parts by weight：
18~22 parts of white cement, 18~22 parts of coarse whiting, 6~9 parts of aluminium-magnesium silicate, 9~11 parts of sodium bentonite, 9~11 parts of kaolin, receive
1.5~2.5 parts of titanium dioxide of rice, 1.5~2.5 parts of far-infared ceramic powder, 3.5~4.5 parts of antiseptic, 5~7 parts of binder.
3. a kind of water-proof antibiotic powder of lacquer putty for use on according to claim 1, it is characterised in that include the raw material of following parts by weight：
It is 20 parts of white cement, 20 parts of coarse whiting, 8 parts of aluminium-magnesium silicate, 10 parts of sodium bentonite, 10 parts of kaolin, 2 parts of nano titanium oxide, remote
2 parts of infrared ceramic powder, 4 parts of antiseptic, 6 parts of binder.
4. a kind of water-proof antibiotic powder of lacquer putty for use on according to claim 1, it is characterised in that the antiseptic is that mass ratio is
3.5~5:1~2 silver-zirconium phosphate antimicrobial and the built agent of zeolite carrying silver antimicrobials.
5. a kind of water-proof antibiotic powder of lacquer putty for use on according to claim 1, it is characterised in that the binder is that mass ratio is
4.2~5.8:2~3:1~1.5:1~2 redispersable latex powder, pre-gelatinized starch, sodium carboxymethylcellulose and lignin is fine
The mixture of dimension.
6. a kind of preparation method of water-proof antibiotic powder of lacquer putty for use on, it is characterised in that comprise the following steps：
S1, the white cement of the proportion and coarse whiting added in grinder, after being fully ground, cross 200~300 mesh sieves, must mix
Fine powder A；
S2, the mixing fine powders A in step S1 is added to high-speed mixer, with 1400~2200r/min rotating speed, high-speed stirred
Mix after 15~25min, add the nano titanium oxide of the proportion, continue to stir 15~25min of mixing, add the proportion
Aluminium-magnesium silicate, sodium bentonite, kaolin and far-infared ceramic powder, continue stir mixing 10~20min, obtain mixed powder B；
S3, the antiseptic and binder of the proportion be added in step S2 in the mixed powder B of gained, and keep step S2
In rotating speed it is constant, continue stir mixing 1~2h, be well mixed after, packing produce water-proof antibiotic powder of lacquer putty for use on.