CN107199608A - Wicker basket colouring earlier stage processing method - Google Patents
Wicker basket colouring earlier stage processing method Download PDFInfo
- Publication number
- CN107199608A CN107199608A CN201710533001.6A CN201710533001A CN107199608A CN 107199608 A CN107199608 A CN 107199608A CN 201710533001 A CN201710533001 A CN 201710533001A CN 107199608 A CN107199608 A CN 107199608A
- Authority
- CN
- China
- Prior art keywords
- parts
- wicker basket
- wicker
- powder
- basket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Wicker basket colouring earlier stage processing method, is related to wicker plaiting article bamboo basket working process technical field, comprises the following steps：Semi-finished product wicker basket is sent in cabinet type dryer and heated up, water content test is carried out to it, carry out ultraviolet sterilization, wicker basket is put into processing pond after sterilization and soaked, after wicker basket is taken out from processing pond, enters room of painting and is painted, powder basket, which is smoked, in colouring time point burning smoke carries out sootiness, remove stifling groove, ventilation dissipates gas, after wicker basket is naturally cold go after paint and complete.The present invention can accelerate the colouring speed and colouring effect of semi-finished product wicker basket, the overall toughness of wicker basket can be lifted after colouring, the phenomenon for preventing wicker plaiting article from fractureing and ftractureing, lifts the quality of wicker plaiting article basket products, and carrying out polishing japanning maintenance etc. in the later stage to wicker basket all has certain facilitation.
Description
Technical field：
The present invention relates to wicker plaiting article bamboo basket working process technical field, and in particular to a kind of wicker basket colouring early stage processing side
Method.
Background technology：
Wicker plaiting article is one of folks of china traditional handicraft product, and people are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project exported goods and earned foreign currency as selected areas of China gradually.Wicker is soft easily
Curved, thickness is well-balanced, color and luster is graceful, by novel design, can be woven into that various honesties are natural, handsome in appearance, Portable durable
Practical art product.Wicker products is the artifacts of China's widespread among the people, because raw material sources are quite varied, and the whole nation is each
Ground has wicker plaiting article product to abound with, with the increase of the market demand, and the process technology to wicker plaiting article product is also increasingly stricter, there is a lot
Generation of the product often being gone mouldy after listing, the problems such as have peculiar smell, fracture and change colour, these problems be all due to
Process technology in process is not mature enough and the inadequate science of skilled worker's method caused by, occur the wicker plaiting article product of these problems
Use feeling will be reduced using, the decline of wicker plaiting article product quality is directly resulted in.
The content of the invention：
The technical problems to be solved by the invention are that providing a kind of colouring speed that can accelerate wicker basket and colouring imitates
Really, the overall toughness of wicker basket can be lifted after colouring, prevents wicker plaiting article from falling the phenomenon of paint and cracking, lifting wicker plaiting article basket products
Quality, carrying out polishing japanning maintenance etc. in the later stage to wicker basket all has certain facilitation.
The technical problems to be solved by the invention are realized using following technical scheme：
Wicker basket colouring earlier stage processing method, comprises the following steps：
Step 1：Semi-finished product wicker basket is sent in cabinet type dryer wicker basket heated up using 60-85 DEG C, risen
The warm time is 10-20min；
Step 2：Wicker basket after will heat up is taken out immediately carries out water content test to it：
When water content is more than 30%, secondary drying is carried out to it, furnace drying method is identical with step 1, until aqueous
Untill amount is between 12-30%；
When water content is reached between 12-30%, wicker basket is taken out and is placed on warm indoor storage 12-20 hours, temperature
The temperature of room is set in 50-70 DEG C；
Step 3：Wicker basket is taken out out of greenhouse, ultraviolet sterilization is carried out；
Step 4：Wicker basket is put into processing pond after sterilization and soaked, the temperature control for the treatment of fluid exists during immersion
40-60 DEG C, wicker basket is taken out after soaking 30min, change soak, 15-20min is then soaked again；
Step 5：After wicker basket is taken out from processing pond, wicker basket, which is stood upside down, is hung its bottom up, then
Evenly distributed be suspended in baking room is dried to it, and baking room temperature is set in 80-90 DEG C, and paint 30min；
Step 6：Stifling groove is laid out below wicker basket after baking room drying 30min, cigarette is put into stifling groove
Smoked powder, and sootiness powder is lighted to wicker basket progress sootiness, then proceed to open baking room, temperature is set as 70-80 DEG C, drying
Baking room is closed after 40-45min, stifling groove, and scattered gas of divulging information is removed；
Step 7：Treating that wicker basket is naturally cold goes post processing to complete, and can directly carry out the processing of next process；
Treatment fluid in the step 4 by：Ethanol, n-butanol, polyacrylamide and the clear water of concentration 60% are prepared from；
Configured during preparation by mass fraction, wherein ethanol 20-30 parts, 8-10 parts of n-butanol, polyacrylamide 3-5
Part, 100-110 parts of clear water；
N-butanol, polyacrylamide are mixed to be put into reactor to be heated up during preparation and do not stop to rock, is heated up
Temperature setting is 40-45 DEG C, is subsequently poured into processing pond and adds ethanol and clear water, does not stop to carry out when adding clear water and ethanol
Stirring, until stirring；
The sootiness powder used in above-mentioned steps 6 by：Folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse, carbon
Powder, adhesion promoter, pine powder and extra large bloom are prepared from；
The sootiness powder each component is calculated according to the mass fraction, is made up of following number：10-15 parts of folium cortex eucommiae, chestnut shell 10-
15 parts, 10-15 parts of pine needle, 3-5 parts of glossy ganoderma powder, 5-10 parts of almond, 10-15 parts of radix glycyrrhizae, 5-8 parts of vinasse, 1-3 parts of carbon dust, help viscous
10-15 parts of agent, 20-30 parts of pine powder and extra large 10-15 parts of bloom；
Described sootiness powder is prepared from by following preparation method：
Folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse are crushed respectively, then by after crushing
Material powder is well mixed, and is then added carbon dust and adhesion promoter and is stir-fried by cylinder type roosting machine, roasting machine when stir-frying
Fire box temperature be arranged on 110-120 DEG C, stir-fry 3-5 minutes, pine powder and extra large bloom added and stirred immediately after taking-up
Being put into sealed container and deposit after mixing uniformly, after can be used after its natural cooling, mixed-powder is directly taken out when using
Light；
The wicker basket handled by the above method, it is proper that when painting in the later stage, color is vivid, moisture is controlled, and wicker is not
100 wicker baskets are tested by easy fracture after colouring, examine testing result as shown in table 1：
Table 1：
| Water content | Color and luster | Warping resistance power | Face crack bar number | Colouring speed |
| 15-23% | It is vivid | 160N | 0-4 bars | 5-8 minutes |
During above-mentioned process is handled wicker basket, using to the accurate water content control of wicker basket, from
And ensure that the degree of drying of wicker basket, it is to avoid the phenomenon that later stage wicker basket is gone mouldy after use occurs, and upper
Color early stage is dehydrated to wicker basket, and wicker plaiting article can be promoted using ethanol and n-butanol collocation polyacrylamide during dehydration
Disengaging for interior moisture, promotes the speed and quality of colouring, and wicker basket is entered using fumigating powder when secondary colouring is carried out
Row is modified so as to improve the toughness that wicker basket is overall, and the phenomenon for preventing wicker plaiting article from fractureing and ftractureing lifts the quality of wicker plaiting article basket products,
Carrying out polishing japanning maintenance etc. in the later stage to wicker basket all has certain facilitation, is shut out using pine powder and extra large bloom collocation
Zhong Ye, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse, carbon dust, adhesion promoter enable flue gas in the willow with temperature
Compile basket surface to carry out resident and absorbed by wicker basket, so as to transform wicker plaiting article inside wicker plaiting article so that the overall property of wicker plaiting article
It can change.
The beneficial effects of the invention are as follows：The colouring speed and colouring effect of semi-finished product wicker basket can be accelerated, after colouring
The overall toughness of wicker basket can be lifted, the phenomenon for preventing wicker plaiting article from fractureing and ftractureing lifts the quality of wicker plaiting article basket products, to wicker plaiting article
Basket, which carries out polishing japanning maintenance etc. in the later stage, all has certain facilitation.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific example is closed, the present invention is expanded on further.
Embodiment 1：
Wicker basket colouring earlier stage processing method, according to following steps：
Step 1：Semi-finished product wicker basket is sent in cabinet type dryer wicker basket heated up using 60 DEG C, during heating
Between be 10min；
Step 2：Wicker basket after will heat up is taken out immediately carries out water content test to it：
When water content is more than 30%, secondary drying is carried out to it, furnace drying method is identical with step 1, until aqueous
Untill amount is between 12%；
When water content is reached between 12-30%, wicker basket is taken out and is placed on warm indoor storage 12 hours, greenhouse
Temperature is set in 50 DEG C；
Step 3：Wicker basket is taken out out of greenhouse, ultraviolet sterilization is carried out；
Step 4：Wicker basket is put into after sterilization treatment fluid is prepared into by ethanol, n-butanol, polyacrylamide and clear water
Processing pond in soaked, during immersion the temperature control for the treatment of fluid at 40 DEG C, immersion 30min after wicker basket is taken out, replacing
Soak, then soaks 15min again；
Step 5：After wicker basket is taken out from processing pond, wicker basket, which is stood upside down, is hung its bottom up, then
Evenly distributed be suspended in baking room is dried to it, and baking room temperature is set in 80 DEG C, dries 30min；
Step 6：Stifling groove is laid out below wicker basket after upper baking room drying 30min, is put into stifling groove
It is prepared from by folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse, carbon dust, adhesion promoter, pine powder and extra large bloom
Sootiness powder, and light sootiness powder sootiness carried out to wicker basket, then proceed to open baking room, temperature is set as 70 DEG C, drying
Baking room is closed after 40min, stifling groove, and scattered gas of divulging information is removed；
Step 7：Treating that wicker basket is naturally cold goes post processing to complete, and can directly carry out the processing of next process；
Configured when wherein prepared by treatment fluid by following mass fraction, wherein 20 parts of ethanol, 8 parts of n-butanol, polypropylene
3 parts of acid amides, 100 parts of clear water；
N-butanol, polyacrylamide are mixed to be put into reactor to be heated up during preparation and do not stop to rock, is heated up
Temperature setting is 40 DEG C, is subsequently poured into processing pond and adds ethanol and clear water, does not stop to be stirred when adding clear water and ethanol
Mix, until stirring；
Sootiness powder each component therein is calculated according to the mass fraction, is made up of following number：10 parts of folium cortex eucommiae, chestnut shell 10
Part, 10 parts of pine needle, 3 parts of glossy ganoderma powder, 5 parts of almond, 10 parts of radix glycyrrhizae, 5 parts of vinasse, 1 part of carbon dust, 10 parts of adhesion promoter, 20 parts of pine powder
With extra large 10 parts of bloom；
Sootiness powder is prepared from by following preparation method：
Folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse are crushed respectively, then by after crushing
Material powder is well mixed, and is then added carbon dust and adhesion promoter and is stir-fried by cylinder type roosting machine, roasting machine when stir-frying
Fire box temperature be arranged on 110 DEG C, stir-fry 3 minutes, pine powder and extra large bloom added and stirred immediately after taking-up
After be put into sealed container deposit, after after its natural cooling i.e. can be used, mixed-powder is directly taken out when using and is lighted i.e.
Can.
Embodiment 2：
Wicker basket colouring earlier stage processing method, according to following steps：
Step 1：Semi-finished product wicker basket is sent in cabinet type dryer wicker basket heated up using 85 DEG C, during heating
Between be 10min；
Step 2：Wicker basket after will heat up is taken out immediately carries out water content test to it：
When water content is more than 30%, secondary drying is carried out to it, furnace drying method is identical with step 1, until aqueous
Untill amount is between 12-30%；
When water content is reached between 12-30%, wicker basket is taken out and is placed on warm indoor storage 12-20 hours, temperature
The temperature of room is set in 70 DEG C；
Step 3：Wicker basket is taken out out of greenhouse, ultraviolet sterilization is carried out；
Step 4：Wicker basket is put into after sterilization treatment fluid is prepared into by ethanol, n-butanol, polyacrylamide and clear water
Processing pond in soaked, during immersion the temperature control for the treatment of fluid at 60 DEG C, immersion 30min after wicker basket is taken out, replacing
Soak, then soaks 20min again；
Step 5：After wicker basket is taken out from processing pond, wicker basket, which is stood upside down, is hung its bottom up, then
Evenly distributed be suspended in baking room is dried to it, and baking room temperature is set in 90 DEG C, dries 30min；
Step 6：Stifling groove is laid out below wicker basket after baking room drying 30min, be put into stifling groove by
What folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse, carbon dust, adhesion promoter, pine powder and extra large bloom were prepared from
Sootiness powder, and sootiness powder is lighted to wicker basket progress sootiness, then proceed to open baking room, temperature is set as 70 DEG C, drying
Baking room is closed after 45min, stifling groove, and scattered gas of divulging information is removed；
Step 7：Treating that wicker basket is naturally cold goes post processing to complete, and can directly carry out the processing of next process；
Configured when wherein prepared by treatment fluid by following mass fraction, wherein 30 parts of ethanol, 10 parts of n-butanol, polypropylene
5 parts of acid amides, 110 parts of clear water；
N-butanol, polyacrylamide are mixed to be put into reactor to be heated up during preparation and do not stop to rock, is heated up
Temperature setting is 45 DEG C, is subsequently poured into processing pond and adds ethanol and clear water, does not stop to be stirred when adding clear water and ethanol
Mix, until stirring；
Sootiness powder each component therein is calculated according to the mass fraction, is made up of following number：15 parts of folium cortex eucommiae, chestnut shell 15
Part, 15 parts of pine needle, 5 parts of glossy ganoderma powder, 10 parts of almond, 15 parts of radix glycyrrhizae, 8 parts of vinasse, 3 parts of carbon dust, 15 parts of adhesion promoter, 30 parts of pine powder
With extra large 15 parts of bloom；
Sootiness powder is prepared from by following preparation method：
Folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse are crushed respectively, then by after crushing
Material powder is well mixed, and is then added carbon dust and adhesion promoter and is stir-fried by cylinder type roosting machine, roasting machine when stir-frying
Fire box temperature be arranged between 120 DEG C, stir-fry 5 minutes, pine powder and extra large bloom added and stirred immediately after taking-up
Being put into sealed container and deposit after uniform, after can be used after its natural cooling, mixed-powder point is directly taken out when using
Combustion.
Embodiment 3：
Wicker basket colouring earlier stage processing method, according to following steps：
Step 1：Semi-finished product wicker basket is sent in cabinet type dryer wicker basket heated up using 75 DEG C, during heating
Between be 15min；
Step 2：Wicker basket after will heat up is taken out immediately carries out water content test to it：
When water content is more than 30%, secondary drying is carried out to it, furnace drying method is identical with step 1, until aqueous
Untill amount is between 12-30%；
When water content is reached between 12-30%, wicker basket is taken out and is placed on warm indoor storage 12-20 hours, temperature
The temperature of room is set in 60 DEG C；
Step 3：Wicker basket is taken out out of greenhouse, ultraviolet sterilization is carried out；
Step 4：Wicker basket is put into after sterilization treatment fluid is prepared into by ethanol, n-butanol, polyacrylamide and clear water
Processing pond in soaked, during immersion the temperature control for the treatment of fluid at 50 DEG C, immersion 30min after wicker basket is taken out, replacing
Soak, then soaks 18min again；
Step 5：After wicker basket is taken out from processing pond, wicker basket, which is stood upside down, is hung its bottom up, then
Evenly distributed be suspended in baking room is dried to it, and baking room temperature is set in 85 DEG C, dries 30min；
Step 6：Stifling groove is laid out below wicker basket after baking room drying 30min, be put into stifling groove by
What folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse, carbon dust, adhesion promoter, pine powder and extra large bloom were prepared from
Sootiness powder, and sootiness powder is lighted to wicker basket progress sootiness, then proceed to open colouring room, temperature is set as 75 DEG C, colouring
Colouring room is closed after 43min, stifling groove, and scattered gas of divulging information is removed；
Step 7：Treat that the natural cold treatment of wicker basket is completed, can directly carry out the processing of next process；
Configured when wherein prepared by treatment fluid by following mass fraction, wherein 25 parts of ethanol, 9 parts of n-butanol, polypropylene
4 parts of acid amides, 105 parts of clear water；
N-butanol, polyacrylamide are mixed to be put into reactor to be heated up during preparation and do not stop to rock, is heated up
Temperature setting is 43 DEG C, is subsequently poured into processing pond and adds ethanol and clear water, does not stop to be stirred when adding clear water and ethanol
Mix, until stirring；
Sootiness powder each component therein is calculated according to the mass fraction, is made up of following number：13 parts of folium cortex eucommiae, chestnut shell 13
Part, 13 parts of pine needle, 4 parts of glossy ganoderma powder, 8 parts of almond, 13 parts of radix glycyrrhizae, 6 parts of vinasse, 2 parts of carbon dust, 13 parts of adhesion promoter, 25 parts of pine powder
With extra large 13 parts of bloom；
Sootiness powder is prepared from by following preparation method：
Folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse are crushed respectively, then by after crushing
Material powder is well mixed, and is then added carbon dust and adhesion promoter and is stir-fried by cylinder type roosting machine, roasting machine when stir-frying
Fire box temperature be arranged between 115 DEG C, stir-fry 4 minutes, pine powder and extra large bloom added and stirred immediately after taking-up
Being put into sealed container and deposit after uniform, after can be used after its natural cooling, mixed-powder point is directly taken out when using
Combustion.
The wicker basket painted by embodiment 1,2,3, color is vivid, moisture control is proper, and wicker is not easy to break,
The wicker basket handled using different implementations is tested after colouring, examines testing result as shown in table 2：
Table 2：
During above-mentioned process is handled wicker basket, using to the accurate water content control of wicker basket, from
And ensure that the degree of drying of wicker basket, it is to avoid the phenomenon that later stage wicker basket is gone mouldy after use occurs, and upper
Color early stage is dehydrated to wicker basket, and wicker plaiting article can be promoted using ethanol and n-butanol collocation polyacrylamide during dehydration
Disengaging for interior moisture, promotes the speed and quality of colouring, and wicker basket is entered using fumigating powder when secondary colouring is carried out
Row is modified so as to improve the toughness that wicker basket is overall, and the phenomenon for preventing wicker plaiting article from fractureing and ftractureing lifts the quality of wicker plaiting article basket products,
Carrying out polishing japanning maintenance etc. in the later stage to wicker basket all has certain facilitation, is shut out using pine powder and extra large bloom collocation
Zhong Ye, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse, carbon dust, adhesion promoter enable flue gas in the willow with temperature
Compile basket surface to carry out resident and absorbed by wicker basket, so as to transform wicker plaiting article inside wicker plaiting article so that the overall property of wicker plaiting article
It can change.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
- The earlier stage processing method 1. wicker basket is painted, it is characterised in that：Comprise the following steps：Step 1：Semi-finished product wicker basket is sent in cabinet type dryer wicker basket heated up using 60-85 DEG C, during heating Between be 10-20min；Step 2：Wicker basket after will heat up is taken out immediately carries out water content test to it：When water content is more than 30%, secondary drying is carried out to it, furnace drying method is identical with step 1, until water content exists Untill between 12-30%；When water content is reached between 12-30%, wicker basket is taken out and is placed on warm indoor storage 12-20 hours, greenhouse Temperature is set in 50-70 DEG C；Step 3：Wicker basket is taken out out of greenhouse, ultraviolet sterilization is carried out；Step 4：Wicker basket is put into processing pond after sterilization and soaked, the temperature control for the treatment of fluid is in 40-60 during immersion DEG C, wicker basket is taken out after immersion 30min, changes soak, 15-20min is then soaked again；Step 5：After wicker basket is taken out from processing pond, wicker basket, which is stood upside down, is hung its bottom up, then uniformly Arrangement is suspended in colouring room and it is dried, and baking room temperature is set in 80-90 DEG C, dries 30min；Step 6：Stifling groove is laid out below wicker basket after baking room drying 30min, sootiness powder is put into stifling groove, And sootiness powder is lighted to wicker basket progress sootiness, then proceed to open baking room, temperature is set as 70-80 DEG C, dries 40- Baking room is closed after 45min, stifling groove, and scattered gas of divulging information is removed；Step 7：Treating that wicker basket is naturally cold goes post processing to complete, and can directly carry out the processing of next process.
- The earlier stage processing method 2. wicker basket according to claim 1 is painted, it is characterised in that：Processing in the step 4 Liquid by：Ethanol, n-butanol, polyacrylamide and the clear water of concentration 60% are prepared from, and are configured during preparation by mass fraction, Wherein ethanol 20-30 parts, 8-10 parts of n-butanol, 3-5 parts of polyacrylamide, 100-110 parts of clear water, by n-butanol, poly- during preparation Acrylamide, which mixes to be put into reactor to be heated up, not to stop to rock, and warming temperature is set to 40-45 DEG C, is subsequently poured into Into processing pond and add ethanol and clear water, do not stop to be stirred when adding clear water and ethanol, until stirring.
- The earlier stage processing method 3. wicker basket according to claim 1 is painted, it is characterised in that：The sootiness powder by：The bark of eucommia Leaf, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse, carbon dust, adhesion promoter, pine powder and extra large bloom are prepared from, sootiness Powder each component is calculated according to the mass fraction, is made up of following number：10-15 parts of folium cortex eucommiae, 10-15 parts of chestnut shell, pine needle 10-15 Part, 3-5 parts of glossy ganoderma powder, 5-10 parts of almond, 10-15 parts of radix glycyrrhizae, 5-8 parts of vinasse, 1-3 parts of carbon dust, 10-15 parts of adhesion promoter, pine 20-30 parts of powder and extra large 10-15 parts of bloom.
- The earlier stage processing method 4. wicker basket according to claim 3 is painted, it is characterised in that：Described sootiness powder by with Lower preparation method is prepared from：Folium cortex eucommiae, chestnut shell, pine needle, glossy ganoderma powder, almond, radix glycyrrhizae, vinasse are crushed respectively, so The material powder after crushing is well mixed afterwards, carbon dust and adhesion promoter is then added and is stir-fried by cylinder type roosting machine, The fire box temperature of roasting machine is arranged on 110-120 DEG C when stir-frying, and stir-fries 3-5 minutes, immediately by pine powder and sea after taking-up Bloom is added and is put into after stirring in sealed container and deposited, direct when using after can be used after its natural cooling Mixed-powder is taken out to light.
- The earlier stage processing method 5. wicker basket according to claim 3 is painted, it is characterised in that：The sootiness powder each component is pressed Mass fraction is calculated, and is made up of following number：13 parts of folium cortex eucommiae, 13 parts of chestnut shell, 13 parts of pine needle, 4 parts of glossy ganoderma powder, 8 parts of almond, 13 parts of radix glycyrrhizae, 6 parts of vinasse, 2 parts of carbon dust, 13 parts of adhesion promoter, 25 parts of pine powder and extra large 13 parts of bloom.