CN107189604A - 一种环保型建筑施工装修涂料及其制备方法 - Google Patents
一种环保型建筑施工装修涂料及其制备方法 Download PDFInfo
- Publication number
- CN107189604A CN107189604A CN201710566518.5A CN201710566518A CN107189604A CN 107189604 A CN107189604 A CN 107189604A CN 201710566518 A CN201710566518 A CN 201710566518A CN 107189604 A CN107189604 A CN 107189604A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- building construction
- friendly building
- finishing coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种环保型建筑施工装修涂料，属于涂料技术领域，包括以下重量份的原料：硅丙乳液30‑40份、水玻璃10‑14份、椰油5‑8份、棕榈油10‑12份、气相二氧化硅15‑17份、蛭石粉4‑6份、钛白粉5‑7份、碳酸钙4‑6份、溴化环氧树脂13‑15份、间苯二酚双(二苯基磷酸酯)3‑5份、羧甲基纤维素1‑3份、乙二醇9‑13份、减水剂2‑4份、消泡剂1‑2份、光稳定剂0.5‑1份、成膜助剂1‑2份、水26‑30份；本发明还公开了一种环保型建筑施工装修涂料的制备方法；本发明环保污染小，附着能力强，具有较佳地阻燃能力。
Description
技术领域
本发明涉及涂料技术领域，具体的说，涉及了一种环保型建筑施工装修涂料及其制备方法。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。
中国涂料界比较权威的《涂料工艺》一书是这样定义的：涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。
目前，在建筑施工装修中使用的装饰涂料，无论是水性涂料还是油性涂料，都存在着与水泥基层粘接力较低，耐久性差，容易开裂、起皮脱落；价格较高等不足。尤其是应用在清水混凝土基层的喷涂时上述弊端会更加明显，装修纠纷也时有发生。
在公开号为CN104628328A的专利文件中，公开了一种环保型建筑施工装修涂料及其制备方法，其组成(重量份)：30-40％白水泥，20-35％石英粉，5-10％淀粉粘胶，3-4％硅酸盐，0.2-1.0％消泡剂，2-3.5％颜料，3-5％聚氨酯；将组份按比例搅拌混合均匀，将干粉包装。施工时，将干粉涂料加水，搅拌均匀后喷涂。该发明与水泥基面能牢固粘合，涂层不开裂、不易脱落、防水、防腐、耐碱、耐刷洗、耐火、无毒、无味、装饰性强；但该发明的耐火、耐高温能力仍能进一步提高。
发明内容
本发明的目的在于克服上述现有技术的不足，提供了一种环保型建筑施工装修涂料及其制备方法，制备简单，环保污染小，附着能力强，具有较佳地阻燃能力。
本发明提供的一种环保型建筑施工装修涂料，包括以下重量份的原料：
硅丙乳液30-40份、水玻璃10-14份、椰油5-8份、棕榈油10-12份、气相二氧化硅15-17份、蛭石粉4-6份、钛白粉5-7份、碳酸钙4-6份、溴化环氧树脂13-15份、间苯二酚双(二苯基磷酸酯)3-5份、羧甲基纤维素1-3份、乙二醇9-13份、减水剂2-4份、消泡剂1-2份、光稳定剂0.5-1份、成膜助剂1-2份、水26-30份。
作为优选，蛭石粉和钛白粉的目数为300目，碳酸钙为目数600目的轻质碳酸钙。
作为优选，减水剂为萘磺酸盐甲醛缩合物、三聚氰胺磺酸盐甲醛缩合物、氨基磺酸盐、脂肪族羟基磺酸盐缩合物的一种或二种以上的混合物。
作为优选，消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷的一种或二种以上的混合物。
作为优选，光稳定剂为光屏蔽剂和紫外线吸收剂的混合物，两者之间的重量比为1:2，光屏蔽剂为碳黑、氧化钛、酞菁蓝、酞菁绿的一种或二种以上的混合物。
作为优选，成膜助剂为醇酯十二。
本发明还提供了一种环保型建筑施工装修涂料的制备方法，包括以下步骤：
(1)、按上述重量份称取各种原料；
(2)、将水玻璃、椰油、棕榈油、溴化环氧树脂、间苯二酚双(二苯基磷酸酯)、羧甲基纤维素和水加入搅拌机内搅拌8-10min，静置2-4min后加入硅丙乳液、乙二醇、减水剂、消泡剂、光稳定剂、成膜助剂搅拌20-30min后，加入气相二氧化硅、蛭石粉、钛白粉和碳酸钙，搅拌均匀即可。
其中，
步骤(2)中搅拌机搅拌速度为400-500r/min。
本发明的一种环保型建筑施工装修涂料及其制备方法，制备简单，环保污染小，附着能力强，具有较佳地阻燃能力，具体的有益效果如下：
(1)、硅丙乳液是一种高耐候、高耐水、抗污染的环保型建筑用乳液，水玻璃粘结力强、强度较高，耐酸性、耐热性好；椰油和棕榈油的添加能使涂料的气味清新淡雅，提高涂料的耐候性，同时具有良好的净化空气的作用；
(2)、溴化环氧树脂和间苯二酚双(二苯基磷酸酯)具有较佳地阻燃能力，同时十分环保；羧甲基纤维素有增稠、成膜、黏接、水分保持、胶体保护、乳化及悬浮等作用；添加乙二醇具有防冻的效果；
(3)、减水剂、消泡剂、光稳定剂、成膜助剂能改善涂料的物理性能和加工稳定性，提高涂料的使用寿命；气相二氧化硅能提高耐高温能力，蛭石粉和碳酸钙能提高涂料的耐磨能力和物理强度；
(4)、本发明各种原料对应比例的混合，能有效地保证涂料的物理性能、保温隔热能力和耐高温能力；制备方法能有效地将各原料之间充分混合。
具体实施方式
以下结合具体实施例对发明作进一步详细的描述。
实施例1
本实施例的一种环保型建筑施工装修涂料，包括以下重量份的原料：
硅丙乳液30份、水玻璃10份、椰油5份、棕榈油10份、气相二氧化硅15份、蛭石粉4份、钛白粉5份、碳酸钙4份、溴化环氧树脂13份、间苯二酚双(二苯基磷酸酯)3份、羧甲基纤维素1份、乙二醇9份、减水剂2份、消泡剂1份、光稳定剂0.5份、成膜助剂1份、水26份。
本实施例中，蛭石粉和钛白粉的目数为300目，碳酸钙为目数600目的轻质碳酸钙。
本实施例中，减水剂为萘磺酸盐甲醛缩合物、三聚氰胺磺酸盐甲醛缩合物、氨基磺酸盐、脂肪族羟基磺酸盐缩合物的混合物。
本实施例中，消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷的混合物。
本实施例中，光稳定剂为光屏蔽剂和紫外线吸收剂的混合物，两者之间的重量比为1:2，光屏蔽剂为碳黑、氧化钛、酞菁蓝、酞菁绿的混合物。
本实施例中，成膜助剂为醇酯十二。
本实施例还提供了一种环保型建筑施工装修涂料的制备方法，包括以下步骤：
(1)、按上述重量份称取各种原料；
(2)、将水玻璃、椰油、棕榈油、溴化环氧树脂、间苯二酚双(二苯基磷酸酯)、羧甲基纤维素和水加入搅拌机内搅拌8min，静置2min后加入硅丙乳液、乙二醇、减水剂、消泡剂、光稳定剂、成膜助剂搅拌20min后，加入气相二氧化硅、蛭石粉、钛白粉和碳酸钙，搅拌均匀即可。
其中，
步骤(2)中搅拌机搅拌速度为400r/min。
实施例2
本实施例的一种环保型建筑施工装修涂料，包括以下重量份的原料：
硅丙乳液35份、水玻璃12份、椰油7份、棕榈油11份、气相二氧化硅16份、蛭石粉5份、钛白粉6份、碳酸钙5份、溴化环氧树脂14份、间苯二酚双(二苯基磷酸酯)4份、羧甲基纤维素2份、乙二醇11份、减水剂3份、消泡剂1.5份、光稳定剂0.8份、成膜助剂1.5份、水28份。
本实施例中，蛭石粉和钛白粉的目数为300目，碳酸钙为目数600目的轻质碳酸钙。
本实施例中，减水剂为萘磺酸盐甲醛缩合物、三聚氰胺磺酸盐甲醛缩合物、氨基磺酸盐、脂肪族羟基磺酸盐缩合物的混合物。
本实施例中，消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷的混合物。
本实施例中，光稳定剂为光屏蔽剂和紫外线吸收剂的混合物，两者之间的重量比为1:2，光屏蔽剂为碳黑、氧化钛、酞菁蓝、酞菁绿的混合物。
本实施例中，成膜助剂为醇酯十二。
本实施例还提供了一种环保型建筑施工装修涂料的制备方法，包括以下步骤：
(1)、按上述重量份称取各种原料；
(2)、将水玻璃、椰油、棕榈油、溴化环氧树脂、间苯二酚双(二苯基磷酸酯)、羧甲基纤维素和水加入搅拌机内搅拌9min，静置3min后加入硅丙乳液、乙二醇、减水剂、消泡剂、光稳定剂、成膜助剂搅拌25min后，加入气相二氧化硅、蛭石粉、钛白粉和碳酸钙，搅拌均匀即可。
其中，
步骤(2)中搅拌机搅拌速度为450r/min。
实施例3
本实施例的一种环保型建筑施工装修涂料，包括以下重量份的原料：
硅丙乳液40份、水玻璃14份、椰油8份、棕榈油12份、气相二氧化硅17份、蛭石粉6份、钛白粉7份、碳酸钙6份、溴化环氧树脂15份、间苯二酚双(二苯基磷酸酯)5份、羧甲基纤维素3份、乙二醇13份、减水剂4份、消泡剂2份、光稳定剂1份、成膜助剂2份、水30份。
本实施例中，蛭石粉和钛白粉的目数为300目，碳酸钙为目数600目的轻质碳酸钙。
本实施例中，减水剂为萘磺酸盐甲醛缩合物、三聚氰胺磺酸盐甲醛缩合物、氨基磺酸盐、脂肪族羟基磺酸盐缩合物的混合物。
本实施例中，消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷的混合物。
本实施例中，光稳定剂为光屏蔽剂和紫外线吸收剂的混合物，两者之间的重量比为1:2，光屏蔽剂为碳黑、氧化钛、酞菁蓝、酞菁绿的混合物。
本实施例中，成膜助剂为醇酯十二。
本实施例还提供了一种环保型建筑施工装修涂料的制备方法，包括以下步骤：
(1)、按上述重量份称取各种原料；
(2)、将水玻璃、椰油、棕榈油、溴化环氧树脂、间苯二酚双(二苯基磷酸酯)、羧甲基纤维素和水加入搅拌机内搅拌10min，静置4min后加入硅丙乳液、乙二醇、减水剂、消泡剂、光稳定剂、成膜助剂搅拌30min后，加入气相二氧化硅、蛭石粉、钛白粉和碳酸钙，搅拌均匀即可。
其中，
步骤(2)中搅拌机搅拌速度为500r/min。
以上所述仅是本发明的优选实施方式，本发明的保护范围并不仅局限于上述实施例，凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理前提下的若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (8)
1.一种环保型建筑施工装修涂料，其特征在于：包括以下重量份的原料：
硅丙乳液30-40份、水玻璃10-14份、椰油5-8份、棕榈油10-12份、气相二氧化硅15-17份、蛭石粉4-6份、钛白粉5-7份、碳酸钙4-6份、溴化环氧树脂13-15份、间苯二酚双(二苯基磷酸酯)3-5份、羧甲基纤维素1-3份、乙二醇9-13份、减水剂2-4份、消泡剂1-2份、光稳定剂0.5-1份、成膜助剂1-2份、水26-30份。
2.根据权利要求1所述的环保型建筑施工装修涂料，其特征在于：蛭石粉和钛白粉的目数为300目，碳酸钙为目数600目的轻质碳酸钙。
3.根据权利要求1所述的环保型建筑施工装修涂料，其特征在于：减水剂为萘磺酸盐甲醛缩合物、三聚氰胺磺酸盐甲醛缩合物、氨基磺酸盐、脂肪族羟基磺酸盐缩合物的一种或二种以上的混合物。
4.根据权利要求1所述的环保型建筑施工装修涂料，其特征在于：消泡剂为乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷的一种或二种以上的混合物。
5.根据权利要求1所述的环保型建筑施工装修涂料，其特征在于：光稳定剂为光屏蔽剂和紫外线吸收剂的混合物，两者之间的重量比为1:2，光屏蔽剂为碳黑、氧化钛、酞菁蓝、酞菁绿的一种或二种以上的混合物。
6.根据权利要求1所述的环保型建筑施工装修涂料，其特征在于：成膜助剂为醇酯十二。
7.根据权利要求1-6任意一项所述的一种环保型建筑施工装修涂料的制备方法，其特征在于：包括以下步骤：
(1)、按上述重量份称取各种原料；
(2)、将水玻璃、椰油、棕榈油、溴化环氧树脂、间苯二酚双(二苯基磷酸酯)、羧甲基纤维素和水加入搅拌机内搅拌8-10min，静置2-4min后加入硅丙乳液、乙二醇、减水剂、消泡剂、光稳定剂、成膜助剂搅拌20-30min后，加入气相二氧化硅、蛭石粉、钛白粉和碳酸钙，搅拌均匀即可。
8.根据权利要求7所述的环保型建筑施工装修涂料的制备方法，其特征在于：步骤(2)中搅拌机搅拌速度为400-500r/min。