CN107163768A - A kind of anti-oxidation wiping agent of wicker plaiting article product - Google Patents
A kind of anti-oxidation wiping agent of wicker plaiting article product Download PDFInfo
- Publication number
- CN107163768A CN107163768A CN201710533506.2A CN201710533506A CN107163768A CN 107163768 A CN107163768 A CN 107163768A CN 201710533506 A CN201710533506 A CN 201710533506A CN 107163768 A CN107163768 A CN 107163768A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxidation
- plaiting article
- wicker plaiting
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of anti-oxidation wiping agent of wicker plaiting article product, is related to wicker plaiting article product routine servicing articles for use field, is prepared from by following component：Rosin, Nano Silver powder, styrene, styrene, lignoceric acid, eucalyptus oil, cold cream, potassium bromate, levelling agent, calixarenes, sodium alginate, water, montmorillonite, ammonium polyacrylate, anhydrous salt, mercury chloride, sodium fluoride, dry powder, anti-oxidation auxiliary agent.The present invention can carry out routine servicing and maintenance to wicker plaiting article product; prevent wicker plaiting article product from occurring aging; the spray has efficient anti-oxidation effect, trickle cut can also be repaired while carrying out anti-oxidation to wicker plaiting article product, effectively protect wicker plaiting article product.
Description
Technical field：
The present invention relates to wicker plaiting article product routine servicing articles for use field, and in particular to a kind of anti-oxidation wiping of wicker plaiting article product
Agent.
Background technology：
Wicker plaiting article is one of folks of china traditional handicraft product, and people are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project exported goods and earned foreign currency as selected areas of China gradually, and wicker is soft easily
Curved, thickness is well-balanced, color and luster is graceful, by novel design, can be woven into that various honesties are natural, handsome in appearance, Portable durable
Practical art product.Wicker products is the artifacts of China's widespread among the people.Because the raw material sources of this technique
It is quite varied.The primary raw material that the north is used to compile basket volume basket has withy, Chinese tamarisk branch, mulberry shoot, the twigs of the chaste tree, false indigo stem etc. a variety of,
Salt-soda soil and marshland are produced.
With the change of quality of the life and custom, increasing wicker plaiting article product is used as ornament and handicraft comes
Sold and used, because wicker plaiting article when handicraft and ornament to the quality requirement of wicker plaiting article as being considerably improved,
Therefore it is accomplished by that periodically wicker plaiting article product is conserved, maintained and cleaned during routine use, to ensure that wicker plaiting article is produced
The gloss of product, color and attractive in appearance etc., prevent the wicker plaiting article aging of product to be damaged, therefore also turn into a kind of new city for the maintenance of wicker plaiting article
Field demand, but commercially few specialties are used for the Related product of the routine servicings of wicker plaiting article product at present, even if having a small amount of
Its price of the universal product is also fairly expensive, and maintenance effect is not obvious, therefore this patent is intended to provide a kind of wicker plaiting article production
The anti-oxidation wiping agent of product, fills up the blank of respective market.
The content of the invention：
The technical problems to be solved by the invention are that routine servicing and maintenance can be carried out to wicker plaiting article product by providing one kind,
Prevent wicker plaiting article product from occurring the anti-oxidation wiping agent of aging, the spray has efficient anti-oxidation effect, entered to wicker plaiting article product
Row can also be repaired while anti-oxidation to trickle cut, effectively protect wicker plaiting article product.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of anti-oxidation wiping agent of wicker plaiting article product, the spray is prepared from by following component：
10-12 parts of rosin, 6-8 parts of Nano Silver powder, 4-6 parts of isopropylbenzene, 8-10 parts of styrene, 0.5-1 parts of lignoceric acid,
0.3-0.5 parts of eucalyptus oil, 3-5 parts of cold cream, 0.6-1 parts of potassium bromate, 0.5-0.8 parts of levelling agent, 4-6 parts of calixarenes, sodium alginate
1-1.5 parts, 40-50 parts of water, 2-3 parts of montmorillonite, 0.5-0.8 parts of ammonium polyacrylate, 3-5 parts of anhydrous salt, mercury chloride 1-3
Part, 0.5-1.5 parts of sodium fluoride, 0.1-0.3 parts of dry powder, anti-oxidation auxiliary agent 20-25 parts；
Wherein anti-oxidation auxiliary agent is made from the following raw materials in parts by weight：1-2 parts of chitosan, 6-8 parts of glutamic acid, itaconic acid 2-
4 parts, 1-2 parts of polyvinyl alcohol, 2-3 parts of propandiol butyl ether, 0.5-1 parts of glycidol, 0.1-0.2 parts of sodium benzoate, water 20-30
Part, 30-40 parts of tung oil；
The preparation method of above-mentioned anti-oxidation auxiliary agent is first to mix tung oil, chitosan, glutamic acid, polyvinyl alcohol and glycidol
1-2h is stirred under conditions of being incorporated in 70-100 DEG C, remaining raw material is then added and 1-2h is stirred under the conditions of 100-105 DEG C, is cooled down
After produce anti-oxidation auxiliary agent；
A kind of anti-oxidation wiping agent of wicker plaiting article product, its preparation method comprises the following steps：
(1) raw material is weighed by weight, and rosin, lignoceric acid, eucalyptus oil, cold cream, levelling agent and potassium bromate are mixed and are incorporated in
80 DEG C are stirred together for 10min and obtain component A；
(2) isopropylbenzene, styrene, calixarenes, Nano Silver powder and water are mixed and is incorporated in 60 DEG C, 1200r/min stirrings
0.5h obtains B component；
(3) anti-oxidation auxiliary agent is added after component A is mixed jointly with B component in 80 DEG C of reactor, 800r/min stirrings 2h
Obtain component C；
(4) finally by sodium alginate, montmorillonite, ammonium polyacrylate, anhydrous salt, mercury chloride, sodium fluoride and dry powder
It is added in component C and mixes, and sends into steam box to cool down after 85-100 DEG C of stifling 0.5-1h；
(5) reagent after cooling is ground to and the anti-of the handicraft that is woven for wicker is produced after fineness≤30 μm, filtering
Aoxidize wiping agent；
In use, the reagent dipped using clean cotton after filtering is wiped to wicker plaiting article product；
The present invention will be changed after tung oil, chitosan, glutamic acid and polyvinyl alcohol blending by glycidol and itaconic acid
Property anti-oxidation auxiliary agent is made, by the raw materials such as rosin, isopropylbenzene and styrene carry out reaction making it have good oxygen-proof property, and
And it is strong with the adhesion of wicker, the film of even compact can be formed on wicker products surface, with sterilizing anti-oxidation effect, attached
Put forth effort strong, water resistance and breathable moisture permeability is good, resist blocking and that, high stability the characteristics of, sanitation and hygiene, environmental protection, practical valency
Value is high；
After the anti-oxidation wiping agent prepared by said components and method is handled wicker, we to wicker with
Lower performance is tested, and draws the data in table 1：
Table 1：
| Project | Oxygen protects the time | Adhesive force | Glossiness | Water resistance | Oxidation cycle | Hardness |
| Data | 5-8 minutes | 1 grade | 90 | 24h is without exception | 2-3 | F |
The anti-oxidation wiping agent of the above-mentioned handicraft woven for wicker is carried out to wicker products can be in 10- after even application
Immediately become drying in 20 minutes, and then maintenance processes are completed, can be in one layer of wicker plaiting article product surface formation in maintenance processes
Protecting film, can prevent the erosion to wicker plaiting article product surface such as steam, and improve the glossiness of product surface, by tung oil
Etc. ought to cause wicker plaiting article product occur aging cycle greatly prolong；
The beneficial effects of the invention are as follows：Routine servicing and maintenance can be carried out to wicker plaiting article product, prevent wicker plaiting article product from occurring
Aging, the spray has efficient anti-oxidation effect, and trickle can also be drawn while carrying out anti-oxidation to wicker plaiting article product
Trace is repaired, and effectively protects wicker plaiting article product.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific example is closed, the present invention is expanded on further.
Embodiment 1：
A kind of anti-oxidation wiping agent of wicker plaiting article product, the spray is prepared from by following component：
10 parts of rosin, 6 parts of Nano Silver powder, 4 parts of isopropylbenzene, 8 parts of styrene, 0.5 part of lignoceric acid, 0.3 part of eucalyptus oil,
3 parts of cold cream, 0.6 part of potassium bromate, 0.8 part of levelling agent, 6 parts of calixarenes, 1.5 parts of sodium alginate, 50 parts of water, 3 parts of montmorillonite,
0.8 part of ammonium polyacrylate, 3 parts of anhydrous salt, 1 part of mercury chloride, 0.5 part of sodium fluoride, 0.1 part of dry powder, anti-oxidation 20 parts of auxiliary agent；
Wherein anti-oxidation auxiliary agent is made from the following raw materials in parts by weight：2 parts of chitosan, 8 parts of glutamic acid, 4 parts of itaconic acid gathers
2 parts of vinyl alcohol, 3 parts of propandiol butyl ether, 1 part of glycidol, 0.2 part of sodium benzoate, 30 parts of water, 40 parts of tung oil；
The preparation method of above-mentioned anti-oxidation auxiliary agent is first to mix tung oil, chitosan, glutamic acid, polyvinyl alcohol and glycidol
2h is stirred under conditions of being incorporated in 70 DEG C, then add remaining raw material stirred under the conditions of 100 DEG C produced after 2h, cooling it is anti-oxidation
Auxiliary agent；
A kind of anti-oxidation wiping agent of wicker plaiting article product, its preparation method comprises the following steps：
(1) raw material is weighed by weight, and rosin, lignoceric acid, eucalyptus oil, cold cream, levelling agent and potassium bromate are mixed and are incorporated in
80 DEG C are stirred together for 10min and obtain component A；
(2) isopropylbenzene, styrene, calixarenes, Nano Silver powder and water are mixed and is incorporated in 60 DEG C, 1200r/min stirrings
0.5h obtains B component；
(3) anti-oxidation auxiliary agent is added after component A is mixed jointly with B component in 80 DEG C of reactor, 800r/min stirrings 2h
Obtain component C；
(4) finally by sodium alginate, montmorillonite, ammonium polyacrylate, anhydrous salt, mercury chloride, sodium fluoride and dry powder
It is added in component C and mixes, and sends into steam box to cool down after 85 DEG C of stifling 1h；
(5) reagent after cooling is ground to and the anti-of the handicraft that is woven for wicker is produced after fineness≤30 μm, filtering
Aoxidize wiping agent；
In use, the reagent dipped using clean cotton after filtering is wiped to wicker plaiting article product.
Embodiment 2：
A kind of anti-oxidation wiping agent of wicker plaiting article product, the spray is prepared from by following component：
12 parts of rosin, 8 parts of Nano Silver powder, 6 parts of isopropylbenzene, 10 parts of styrene, 1 part of lignoceric acid, 0.5 part of eucalyptus oil,
5 parts of cold cream, 1 part of potassium bromate, 0.8 part of levelling agent, 6 parts of calixarenes, 1.5 parts of sodium alginate, 50 parts of water, 2 parts of montmorillonite gathers
0.5 part of ammonium acrylate, 3 parts of anhydrous salt, 1 part of mercury chloride, 0.5 part of sodium fluoride, 0.1 part of dry powder, anti-oxidation 20 parts of auxiliary agent；
Wherein anti-oxidation auxiliary agent is made from the following raw materials in parts by weight：2 parts of chitosan, 8 parts of glutamic acid, 4 parts of itaconic acid gathers
2 parts of vinyl alcohol, 3 parts of propandiol butyl ether, 1 part of glycidol, 0.2 part of sodium benzoate, 30 parts of water, 40 parts of tung oil；
The preparation method of above-mentioned anti-oxidation auxiliary agent is first to mix tung oil, chitosan, glutamic acid, polyvinyl alcohol and glycidol
1h is stirred under conditions of being incorporated in 100 DEG C, then adds after remaining raw material stirs 1h, cooling under the conditions of 105 DEG C and produces oxygen
Change auxiliary agent；
A kind of anti-oxidation wiping agent of wicker plaiting article product, its preparation method comprises the following steps：
(1) raw material is weighed by weight, and rosin, lignoceric acid, eucalyptus oil, cold cream, levelling agent and potassium bromate are mixed and are incorporated in
80 DEG C are stirred together for 10min and obtain component A；
(2) isopropylbenzene, styrene, calixarenes, Nano Silver powder and water are mixed and is incorporated in 60 DEG C, 1200r/min stirrings
0.5h obtains B component；
(3) anti-oxidation auxiliary agent is added after component A is mixed jointly with B component in 80 DEG C of reactor, 800r/min stirrings 2h
Obtain component C；
(4) finally by sodium alginate, montmorillonite, ammonium polyacrylate, anhydrous salt, mercury chloride, sodium fluoride and dry powder
It is added in component C and mixes, and sends into steam box to cool down after 100 DEG C stifling 0.5；
(5) reagent after cooling is ground to and the anti-of the handicraft that is woven for wicker is produced after fineness≤30 μm, filtering
Aoxidize wiping agent；
In use, the reagent dipped using clean cotton after filtering is wiped to wicker plaiting article product.
Embodiment 3：
A kind of anti-oxidation wiping agent of wicker plaiting article product, the spray is prepared from by following component：
11 parts of rosin, 7 parts of Nano Silver powder, 5 parts of isopropylbenzene, 9 parts of styrene, 0.8 part of lignoceric acid, 0.4 part of eucalyptus oil,
4 parts of cold cream, 0.8 part of potassium bromate, 0.6 part of levelling agent, 5 parts of calixarenes, 1.2 parts of sodium alginate, 45 parts of water, montmorillonite 2.5
Part, 0.7 part of ammonium polyacrylate, 4 parts of anhydrous salt, 2 parts of mercury chloride, 1 part of sodium fluoride, 0.2 part of dry powder, anti-oxidation 23 parts of auxiliary agent；
Wherein anti-oxidation auxiliary agent is made from the following raw materials in parts by weight：1.5 parts of chitosan, 7 parts of glutamic acid, 3 parts of itaconic acid,
1.5 parts of polyvinyl alcohol, 2.5 parts of propandiol butyl ether, 0.8 part of glycidol, 0.15 part of sodium benzoate, 25 parts of water, 35 parts of tung oil；
The preparation method of above-mentioned anti-oxidation auxiliary agent is first to mix tung oil, chitosan, glutamic acid, polyvinyl alcohol and glycidol
1.5h is stirred under conditions of being incorporated in 85 DEG C, then add remaining raw material stirred under the conditions of 100 DEG C produced after 1.5h, cooling it is anti-
Oxidation promoter；
A kind of anti-oxidation wiping agent of wicker plaiting article product, its preparation method comprises the following steps：
(1) raw material is weighed by weight, and rosin, lignoceric acid, eucalyptus oil, cold cream, levelling agent and potassium bromate are mixed and are incorporated in
80 DEG C are stirred together for 10min and obtain component A；
(2) isopropylbenzene, styrene, calixarenes, Nano Silver powder and water are mixed and is incorporated in 60 DEG C, 1200r/min stirrings
0.5h obtains B component；
(3) anti-oxidation auxiliary agent is added after component A is mixed jointly with B component in 80 DEG C of reactor, 800r/min stirrings 2h
Obtain component C；
(4) finally by sodium alginate, montmorillonite, ammonium polyacrylate, anhydrous salt, mercury chloride, sodium fluoride and dry powder
It is added in component C and mixes, and sends into steam box to cool down after 90 DEG C of stifling 1h；
(5) reagent after cooling is ground to and the anti-of the handicraft that is woven for wicker is produced after fineness≤30 μm, filtering
Aoxidize wiping agent；
In use, the reagent dipped using clean cotton after filtering is wiped to wicker plaiting article product.
After the completion of preparation, contrast test is carried out to the product in above-mentioned three kinds of embodiments, each item number in table 2 is drawn
According to：
Table 2：
| Project | Oxygen protects the time | Adhesive force | Glossiness | Water resistance | Oxidation cycle | Hardness |
| Embodiment 1 | 16 minutes | 1 grade | 80 | 24h is without exception | 2-3 | F |
| Embodiment 2 | 18 minutes | 1 grade | 86 | 24h is without exception | 2-3 | E |
| Embodiment 3 | 13 minutes | 2 grades | 90 | 24h is without exception | 2-3 | F |
The product in embodiment 1,2,3 is not difficult to find out from upper table, is all had on curing time and water resistance obvious
Effect, and because the superior adhesive force of prominent waterproof effect and wiping agent causes the oxidation cycle of product to greatly increase,
Either glossiness, case hardness etc. are all significantly increased, and have to the overall performance of wicker plaiting article product and are significantly lifted, from
And efficient anti-oxidation effect is realized, trickle cut can also be repaiied while carrying out anti-oxidation to wicker plaiting article product
Mend, effectively protect wicker plaiting article product.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
1. a kind of anti-oxidation wiping agent of wicker plaiting article product, it is characterised in that：The spray is prepared from by following component：
10-12 parts of rosin, 6-8 parts of Nano Silver, 4-6 parts of styrene, 8-10 parts of styrene, 0.5-1 parts of lignoceric acid, eucalyptus oil
0.3-0.5 parts, 3-5 parts of White Mineral Oil, 0.6-1 parts of potassium bromate, 0.5-0.8 parts of levelling agent；4-6 parts of BETA-CD, sodium alginate 1-1.5
Part, 40-50 parts of water, 2-3 parts of montmorillonite, 0.5-0.8 parts of ammonium polyacrylate, 3-5 parts of anhydrous salt, 1-3 parts of mercury chloride, sodium fluoride
0.5-1.5 parts, 0.1-0.3 parts of dry powder, anti-oxidation auxiliary agent 20-25 parts；
Wherein anti-oxidation auxiliary agent is made from the following raw materials in parts by weight：1-2 parts of chitosan, 6-8 parts of glutamic acid, 2-4 parts of itaconic acid,
1-2 parts of polyvinyl alcohol, 2-3 parts of propandiol butyl ether, 0.5-1 parts of glycidol, 0.1-0.2 parts of sodium benzoate, 20-30 parts of water, paulownia
It is oily 30-40 parts.
2. a kind of anti-oxidation wiping agent of wicker plaiting article product, it is characterised in that：The preparation method of the spray, comprises the following steps：
(1) raw material is weighed by weight, and rosin, lignoceric acid, eucalyptus oil, White Mineral Oil, levelling agent and potassium bromate are mixed and are incorporated in 80
DEG C being stirred together for 10min obtains component A；
(2) by styrene, styrene, BETA-CD, Nano Silver and water it is mixed be incorporated in 60 DEG C, 1200r/min stirrings 0.5h obtain B groups
Point；
(3) anti-oxidation auxiliary agent is added after component A is mixed jointly with B component and obtains C in 80 DEG C of reactor, 800r/min stirrings 2h
Component；
(4) sodium alginate, montmorillonite, ammonium polyacrylate, anhydrous salt, mercury chloride, sodium fluoride and dry powder are finally added to C groups
Mixed in point, and send into steam box to cool down after 85-100 DEG C of stifling 0.5-1h；
(5) reagent after cooling is ground to produced after fineness≤30 μm, filtering for wicker weave handicraft it is anti-oxidation
Wiping agent.
3. a kind of anti-oxidation wiping agent of wicker plaiting article product according to claim 1, it is characterised in that：The anti-oxidation auxiliary agent
Preparation method be first to be incorporated in tung oil, chitosan, glutamic acid, polyvinyl alcohol and glycidol are mixed under conditions of 70-100 DEG C
1-2h is stirred, remaining raw material is then added and is stirred under the conditions of 100-105 DEG C anti-oxidation auxiliary agent is produced after 1-2h, cooling.
4. a kind of anti-oxidation wiping agent of wicker plaiting article product according to claim 1, it is characterised in that：The spray is by following group
Divide and be prepared from：12 parts of rosin, 8 parts of Nano Silver, 6 parts of styrene, 10 parts of styrene, 1 part of lignoceric acid, 0.5 part of eucalyptus oil, in vain
5 parts of Dormant oils, 1 part of potassium bromate, 0.8 part of levelling agent, 6 parts of BETA-CD, 1.5 parts of sodium alginate, 50 parts of water, 2 parts of montmorillonite, polypropylene
Sour 0.5 part of ammonium, 3 parts of anhydrous salt, 1 part of mercury chloride, 0.5 part of sodium fluoride, 0.1 part of dry powder, anti-oxidation 20 parts of auxiliary agent；
Wherein anti-oxidation auxiliary agent is made from the following raw materials in parts by weight：2 parts of chitosan, 8 parts of glutamic acid, 4 parts of itaconic acid, polyethylene
2 parts of alcohol, 3 parts of propandiol butyl ether, 1 part of glycidol, 0.2 part of sodium benzoate, 30 parts of water, 40 parts of tung oil.