CN107012688A - A kind of luminescence lace fabric and preparation method thereof - Google Patents
A kind of luminescence lace fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107012688A CN107012688A CN201710304779.XA CN201710304779A CN107012688A CN 107012688 A CN107012688 A CN 107012688A CN 201710304779 A CN201710304779 A CN 201710304779A CN 107012688 A CN107012688 A CN 107012688A
- Authority
- CN
- China
- Prior art keywords
- parts
- yarn
- luminescence
- lace fabric
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of luminescence lace fabric and preparation method thereof, belongs to fabric technology and preparation field.A kind of luminescence lace fabric is prepared from by following component fiber with parts by weight：10 12 parts of 58 parts of polyurethane fibre, 15 18 parts of Fypro, 10 15 parts of luminescent fibre, 35 parts of polypropylene fibre and vinylon；A kind of preparation method of luminescence lace fabric, including recombing, network and twist with the fingers, weave and post-processing shape four steps.The present invention has good occlusion performance, does not contain any chemical addition agent, the addition of fluoride improves luminescent fibre core molten quality and reduces the phonon energy of luminescent fibre core matrix.And the present invention is free of fluorescer, harmless to the body, preparation technology is simple, to making the life better and low-carbon environment-friendly plays an important roll, it is easy to accomplish.
Description
Technical field
The present invention relates to lace fabric and preparation method thereof, belong to fabric technology and preparation field, and in particular to Yi Zhongfa
Light lace fabric and preparation method thereof.
Background technology
With the development of science and technology textile industry has obtained development of seeking dreams, people are to the technique of lace fabric and wanting for purposes
Asking also becomes more and more higher.The lace fabric that can be lighted receives people's highest attention, is widely used in the danger such as traffic, mining
Dangerous industry, is that the safety of the mankind escorts, wide market.However, like product complex process in the market, and
Containing fluorescer, harmful to body, luminescent properties are unstable.
The content of the invention
In order to solve the above problems, the present invention discloses a kind of luminescence lace fabric and preparation method thereof, and energy-conserving and environment-protective are free of
There is fluorescer, technique is simple.
The object of the present invention is achieved like this：
A kind of luminescence lace fabric, the luminescence lace fabric includes 5-8 parts of polyurethane fibre, gathered by weight
10-12 parts of 15-18 parts of nylon, 10-15 parts of luminescent fibre, 3-5 parts of polypropylene fibre and vinylon；Institute
The obverse and reverse of luminescence lace fabric is stated containing synthesis softening agent, the synthesis softening agent includes amino silicone micro emulsion and poly- second
Alkene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO215-20 parts, Al2O318-
30 parts, LiF8-10 parts, CaF25-15 parts, SmF30.5-1 parts, DyF30.05-0.1 parts, CeO20.05-0.2 parts and Tb4O70.1-0.5
Part.
The SiO2As the network topology adult of fiber core, and Al2O3In Al3+Oxygen around ion can be mended
Repay the electric charge of rare earth ion so that rare earth ion can be evenly dispersed in Al2O3In matrix, so as to hinder rare earth ion
Reunite, improve the solubility of rare earth ion.And the addition of metal fluoride is then to have introduced Fluorine source, make fiber core rich in fluorine from
Son, improves fiber core molten quality and reduces the phonon energy of fiber core matrix.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature；The step (1) middle glass melting temperature 1550-1600 degree, soaking time 2 hours.
The twist twisted described in step 2 is that 400-500 twists with the fingers/10 centimetres.
The present invention compared with prior art, has the advantages that：According to proportioning disclosed by the invention and experiment step
Rapid a kind of luminescence lace fabric of gained and preparation method thereof, with good occlusion performance, does not contain any chemical addition agent, fluorine
The addition of compound improves luminescent fibre core molten quality and reduces the phonon energy of luminescent fibre core matrix.And this
Invention is free of fluorescer, harmless to the body, and preparation technology is simple, and clothing logos or job that requires special skills clothes can be made in its finished product,
Product of the present invention and its manufacture craft are to making the life better and low-carbon environment-friendly plays an important roll, suitable for promoting.
Embodiment
Flexibility test：
Embodiment 1
A kind of luminescence lace fabric, the luminescence lace fabric includes 5 parts of polyurethane fibre, polyamides by weight
10 parts of 15 parts of amine fiber, 10 parts of luminescent fibre, 3 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO215 parts, Al2O318 parts,
LiF8 parts, CaF25 parts, SmF30.5 part, DyF30.05 part, CeO20.05 part and Tb4O70.1 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Embodiment 2
A kind of luminescence lace fabric, the luminescence lace fabric includes 6 parts of polyurethane fibre, polyamides by weight
10.5 parts of 16 parts of amine fiber, 11 parts of luminescent fibre, 3.5 parts of polypropylene fibre and vinylon；The luminous flower bud
The obverse and reverse of silk face fabric is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO215 parts, Al2O318 parts,
LiF8 parts, CaF25 parts, SmF30.5 part, DyF30.05 part, CeO20.05 part and Tb4O70.1 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1600 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Embodiment 3
A kind of luminescence lace fabric, the luminescence lace fabric includes 7 parts of polyurethane fibre, polyamides by weight
11 parts of 17 parts of amine fiber, 13 parts of luminescent fibre, 4 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO215 parts, Al2O318 parts,
LiF8 parts, CaF25 parts, SmF30.5 part, DyF30.05 part, CeO20.05 part and Tb4O70.1 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Embodiment 4
A kind of luminescence lace fabric, the luminescence lace fabric includes 7.5 parts of polyurethane fibre, gathered by weight
11.5 parts of 17.5 parts of nylon, 14 parts of luminescent fibre, 4.5 parts of polypropylene fibre and vinylon；The hair
The obverse and reverse of light lace fabric is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO215 parts, Al2O318 parts,
LiF8 parts, CaF25 parts, SmF30.5 part, DyF30.05 part, CeO20.05 part and Tb4O70.1 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Embodiment 5
A kind of luminescence lace fabric, the luminescence lace fabric includes 8 parts of polyurethane fibre, polyamides by weight
12 parts of 18 parts of amine fiber, 15 parts of luminescent fibre, 5 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO215 parts, Al2O318 parts,
LiF8 parts, CaF25 parts, SmF30.5 part, DyF30.05 part, CeO20.05 part and Tb4O70.1 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Embodiment 1-5 is luminescence lace fabric flexibility test of the present invention, and test result is as shown in table 1.
From table 1 it follows that there is good elasticity by the embodiment 1-5 luminescence lace fabrics provided, with existing skill
Art is compared, and tensile elasticity improves 8% in embodiment 1, is recovered elasticity and is improved 12%；Tensile elasticity is improved in embodiment 2
15%, recover elasticity and improve 19.8%；Tensile elasticity improves 21.4% in embodiment 3, recovers elasticity and improves 25.9%；
Tensile elasticity improves 22.7% in embodiment 4, recovers elasticity and improves 28.8%；Tensile elasticity is improved in embodiment 5
27%, recover elasticity and improve 28%.
Luminescent properties are tested：
Embodiment 6
A kind of luminescence lace fabric, the luminescence lace fabric includes 5 parts of polyurethane fibre, polyamides by weight
10 parts of 15 parts of amine fiber, 10 parts of luminescent fibre, 3 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO215 parts, Al2O318 parts,
LiF8 parts, CaF25 parts, SmF30.5 part, DyF30.05 part, CeO20.05 part and Tb4O70.1 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Compared with the prior art, it is seen that light area reflectivity reduction by 14%, it is seen that light area light transmittance improves 17%.
Embodiment 7
A kind of luminescence lace fabric, the luminescence lace fabric includes 5 parts of polyurethane fibre, polyamides by weight
10 parts of 15 parts of amine fiber, 10 parts of luminescent fibre, 3 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO216 parts, Al2O321 parts,
LiF8.5 parts, CaF27 parts, SmF30.6 part, DyF30.06 part, CeO20.09 part and Tb4O70.2 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Compared with the prior art, it is seen that light area reflectivity reduction by 17%, it is seen that light area light transmittance improves 21.5%.
Embodiment 8
A kind of luminescence lace fabric, the luminescence lace fabric includes 5 parts of polyurethane fibre, polyamides by weight
10 parts of 15 parts of amine fiber, 10 parts of luminescent fibre, 3 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO218 parts, Al2O324 parts,
LiF9 parts, CaF29 parts, SmF30.8 part, DyF30.08 part, CeO20.13 part and Tb4O70.3 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Compared with the prior art, it is seen that light area reflectivity reduction by 20%, it is seen that light area light transmittance improves 22.6%.
Embodiment 9
A kind of luminescence lace fabric, the luminescence lace fabric includes 5 parts of polyurethane fibre, polyamides by weight
10 parts of 15 parts of amine fiber, 10 parts of luminescent fibre, 3 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO219 parts, Al2O327 parts,
LiF9 parts, CaF212 parts, SmF30.9 part, DyF30.09 part, CeO20.17 part and Tb4O70.4 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Compared with the prior art, it is seen that light area reflectivity reduction by 23.7%, it is seen that light area light transmittance improves 25.4%.
Embodiment 10
A kind of luminescence lace fabric, the luminescence lace fabric includes 5 parts of polyurethane fibre, polyamides by weight
10 parts of 15 parts of amine fiber, 10 parts of luminescent fibre, 3 parts of polypropylene fibre and vinylon；The luminous lace surface
The obverse and reverse of material is containing synthesis softening agent, and the synthesis softening agent includes amino silicone micro emulsion and polyethylene.
The weight part ratio of the amino silicone micro emulsion and polyethylene is 3:2；The luminescent fibre includes fiber core, fibre core
Cladding PET coating outside material；The fiber core includes S by weightiO220 parts, Al2O330 parts,
LiF10 parts, CaF215 parts, SmF31 part, DyF31 part, CeO20.2 part and Tb4O70.5 part.
A kind of preparation method of luminescence lace fabric, comprises the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and
Vinylon 50 be compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn in step one
Line and polyvinyl formal yarn spray through gas transverse, twist doubling, form compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light flower bud
Silk face fabric.
Luminescent fibre preparation process includes described in step one：(1) each mixture of fiber core is fitted into alumina crucible,
It is put into silicon molybdenum rod furnace and is founded, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel
In mould, it is cooled and shaped；(3) the glass after shaping is put into 500 degree of Muffle furnace and annealed, be incubated two hours；(4) will step
Suddenly the glass (3) after annealing insulation is cooled to room temperature.
The step (1) middle 1550 degree of glass melting temperature, soaking time 2 hours.
The twist twisted described in step 2 is 400/10 centimetres of sth. made by twisting.
Compared with the prior art, it is seen that light area reflectivity reduction by 25.8%, it is seen that light area light transmittance improves 28%.
Claims (8)
1. a kind of luminescence lace fabric, it is characterised in that：It is fine that the luminescence lace fabric includes polyurethanes by weight
5-8 parts of dimension, 15-18 parts of Fypro, 10-15 parts of luminescent fibre, 3-5 parts of polypropylene fibre and vinylon
10-12 parts；The obverse and reverse of the luminescence lace fabric is containing synthesis softening agent, and the synthesis softening agent includes amino silicone
Micro emulsion and polyethylene.
2. a kind of luminescence lace fabric according to claim 1, it is characterised in that：The amino silicone micro emulsion and polyethylene
Weight part ratio is 3:2.
3. a kind of luminescence lace fabric according to claim 1, it is characterised in that：The luminescent fibre includes fibre core
Cladding PET coating outside material, fiber core.
4. a kind of luminescence lace fabric according to claim 3, it is characterised in that：The fiber core includes by weight
SiO215-20 parts, Al2O318-30 parts, LiF8-10 parts, CaF25-15 parts, SmF30.5-1 parts, DyF30.05-0.1 parts,
CeO20.05-0.2 parts and Tb4O70.1-0.5 parts.
5. a kind of preparation method of luminescence lace fabric, it is characterised in that：Comprise the following steps：
Step one, recombing：Respectively by polyurethane fibre, Fypro, luminescent fibre, polypropylene fibre and poly- second
Enol formal fiber 50 is compiled into polyurethanes yarn, polyamide yarn, luminous yarn, polypropylene yarn and poly- second
Enol formal yarn, it is soaking, wash yarn, retraction, combing arrange prepared yarn is made；
Step 2, network is simultaneously twisted with the fingers：By polyurethanes yarn in step one, polyamide yarn, luminous yarn, polypropylene yarn and
Polyvinyl formal yarn sprays through gas transverse, twists doubling, forms compound (1) silk thread；
Step 3, weaving：Lace fabric is made through lace machine in compound (1) silk thread in step 2；
Step 4, post-processing sizing：By the lace fabric back scrubbing in step 3, dry, shaping, obtain finished product light lace surface
Material.
6. a kind of preparation method of luminescence lace fabric according to claim 5, it is characterised in that：Lighted described in step one
Fiber preparation process includes：(1) each mixture of fiber core is fitted into alumina crucible, is put into silicon molybdenum rod furnace and is melted
System, is incubated after founding；By step (1) in glass melt pour into preheating after stainless steel mould in, be cooled and shaped；(3) will be into
Glass after type is put into 500 degree of Muffle furnace and annealed, and is incubated two hours；(4) the glass after being incubated of (3) step being annealed is cold
But to room temperature.
7. a kind of preparation method of luminescence lace fabric according to claim 6, it is characterised in that：The step (1) in melt
Temperature 1550-1600 degree processed, soaking time 2 hours.
8. a kind of preparation method of luminescence lace fabric according to claim 5, it is characterised in that：Twisted described in step 2
The twist for 400-500 twist with the fingers/10 centimetres.