CN106965292B - A kind of imitative Wu Kangshi - Google Patents
A kind of imitative Wu Kangshi Download PDFInfo
- Publication number
- CN106965292B CN106965292B CN201710347106.2A CN201710347106A CN106965292B CN 106965292 B CN106965292 B CN 106965292B CN 201710347106 A CN201710347106 A CN 201710347106A CN 106965292 B CN106965292 B CN 106965292B
- Authority
- CN
- China
- Prior art keywords
- imitative
- sand
- water
- kangshi
- kang shi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of imitative Wu Kangshi, the imitative force Kang Shi includes the sand material concrete layer similar to military Kang Shi colors positioned at upper strata and the sandstone concrete layer similar to military Kang Shi colors positioned at lower floor, the upper surface of the sand material concrete layer is provided with rugged natural pearl not exactly round in shape reason, the depth of natural pearl not exactly round in shape reason is not more than 5mm, the upper surface of the imitative force Kang Shi is polished by sander, and the imitative force Kang Shi upper surfaces after polishing are jetted through water and stone protectant modelled after an antique successively.One kind of the present invention imitates that military Kang Shi production is cheap, derives from a wealth of sources, and can meet the requirement of building stone.
Description
Technical field
The present invention relates to a kind of imitative Wu Kangshi, belong to artificial stone technical field.
Background technology
Wu Kangshi also known as flower stone, mainly originate in the hilly and mountainous land in Huzhou City of Zhejiang Province Deqing County Wu Kang towns eastern suburb.The stone face
Color depth is reddish brown, and there are many tiny honeycomb holes on surface, and shape is like rotten wood, simple and unsophisticated beautiful, thousand appearances, ten thousand state.Wu Kangshi is primarily used for Jiangnan
Building and gardens, including garden rockery stone, two kinds of paring stone, Northern Song Dynasty has had great reputation.Military Kang Shi construction timbers are a kinds
Molten bonding tufa stone in the effusive rock of volcano, its quality hardness is moderate, is adapted with ancient mining technology, productivity level.
Nature majority is in lavender, and minority is in yellowish-brown, but surface is just oxidized to the purple of beauty once erosion by wind and rain, in ancient times
Purple signifies auspicious sign, therefore people's custom claims this kind of stone " military health purple stone ".This kind of stone pattern is cleared clear, can fell into
Large-scale various construction materials, while can also chisel and carve out the art pattern of complexity.Somewhat water imbibition, the rock mass of moistening often have rattan for it
Climing to climb up by holding on to, moss derives, and gives simple and unsophisticated U.S..Wu Kangshi is a kind of sandstone, even if processing is very smooth, surface still has puckery
Property, stepping in the rain thereon will not be smooth, is the outstanding stone material of ancient bridge.
Wu Kangshi is exploited by long-term, and current force Kang Shi resources are fewer and fewer, and are prevented or restricted from exploiting by country,
Therefore it provides a kind of imitative Wu Kangshi that is cheap, deriving from a wealth of sources has become urgent need.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of imitative Wu Kangshi, can produce imitative Wu Kang that is cheap, deriving from a wealth of sources
Stone, meets the requirement of building stone.
In order to solve the above technical problems, the present invention a kind of imitative Wu Kangshi, the imitative force Kang Shi include be located at upper strata with
The similar sand material concrete layer of military Kang Shi colors and the sandstone concrete layer similar to military Kang Shi colors positioned at lower floor, the sand
The upper surface of material concrete layer is provided with rugged natural pearl not exactly round in shape reason, and the depth of natural pearl not exactly round in shape reason is not more than 5mm, the imitative Wu Kang
The upper surface of stone is polished by sander, and the imitative force Kang Shi upper surfaces after polishing are jetted through water and stone protector modelled after an antique successively
Agent.
As the improvement of the present invention, the size of the imitative force Kang Shi is：Long by 110 × wide by 47 × high 7cm.
As the improvement of the present invention, the height of the sand material concrete layer is 1-30mm, and sand material concrete presses mass fraction
Including 2 parts dry husky, the water-reducing agent mixing of the water and cement amount 5% of cement more than 1 part of 32.5 grade, cement amount 28-35% and
Into it is dark brown to do sand color, and dry grains of sand footpath is 0.1-1.5mm.
As the improvement of the present invention, the height of the sand material concrete layer is 2-5mm, and sand material concrete presses mass fraction bag
The water-reducing agent for including 2 parts of dry sand, 1 part of 52.5 rating cement, the water of cement amount 30% and cement amount 5% mixes, dry grains of sand footpath
For 0.5-1.0mm.
As the improvement of the present invention, the sander is wheel sander, and emery wheel fineness is No. 50-100.
As the present invention improvement, the water modelled after an antique by mass fraction include 3 parts of water, 2 parts of rape oils, 1 part of liquid detergent and
0.01-0.1 parts of black pigments mix.
As the improvement of the present invention, the black pigment is iron oxide, needs to place infiltration 2 days after being jetted through water modelled after an antique.
As the improvement of the present invention, the rugged natural pearl not exactly round in shape reason that the sand material concrete layer upper surface is set passes through elder generation
Shaping powder is sprayed into mold bottom to be formed, then spraying into sand material concrete layer on mold bottom and shaping powder is consolidated
It is fixed, then expire whole mould, demoulding maintenance hardening with the sandstone filling concrete similar to military Kang Shi colors, then use alloyed steel sand
The shaping powder of sand material concrete layer upper surface is removed and produces a kind of weathering face for being uneven not of uniform size by shot-blasting machine,
The height of shaping powder be not more than 5mm, shaping powder by mass fraction includes 10 parts of common stones dry powder and 3-5 parts of water mix and
Into the particle diameter of common stones dry powder is 60-120 mesh.
As the improvement of the present invention, the shaping powder includes 10 parts of common stones dry powder by mass fraction and 4 parts of water mix
Conjunction forms, and the particle diameter of common stones dry powder is 80-100 mesh, and the shaping powder and sand material concrete pass through artificial stone plate's raw material
Mixing sprays into after being stirred with mixer.
As the improvement of the present invention, the demoulding carries out after concrete tentatively hardens, and the maintenance firm time is 7-
10 days.
A kind of imitative Wu Kangshi of the present invention, the imitative force Kang Shi include the sand material similar to military Kang Shi colors positioned at upper strata
Concrete layer and the sandstone concrete layer similar to military Kang Shi colors positioned at lower floor, the upper surface of the sand material concrete layer are set
Rugged natural pearl not exactly round in shape reason is equipped with, the depth of natural pearl not exactly round in shape reason is not more than 5mm, and sander is passed through in the upper surface of the imitative force Kang Shi
Polish, the imitative force Kang Shi upper surfaces after polishing are jetted through water and stone protectant modelled after an antique, a kind of imitative Wu Kang of the invention successively
Stone production is cheap, derives from a wealth of sources, and can meet the requirement of building stone.
Brief description of the drawings
The present invention will be further described in detail below with reference to the accompanying drawings and specific embodiments.
Fig. 1 is artificial stone plate's raw material mixing mixer structure diagram in a kind of imitative force Kang Shi production technologies of the present invention.
Fig. 2 is the discharging gate part of artificial stone plate's raw material mixing mixer in a kind of imitative force Kang Shi production technologies of the present invention
Structure diagram.
Embodiment
A kind of imitative Wu Kangshi, the imitative force Kang Shi include the sand material concrete layer similar to military Kang Shi colors positioned at upper strata
With the sandstone concrete layer similar to military Kang Shi colors positioned at lower floor, the upper surface of the sand material concrete layer is provided with height
A kind of uneven natural pearl not exactly round in shape reason (pearl not exactly round in shape reason refers to weathering face for being uneven not of uniform size, similarly hereinafter), the depth of natural pearl not exactly round in shape reason
No more than 5mm, the upper surface of the imitative force Kang Shi is polished by sander, and the imitative force Kang Shi upper surfaces after polishing are sprayed successively
Cross water and stone protectant modelled after an antique.
As the improvement of the present invention, the size of the imitative force Kang Shi is：Long by 110 × wide by 47 × high 7cm.
As the improvement of the present invention, the height of the sand material concrete layer is 1-30mm, and sand material concrete presses mass fraction
Including 2 parts dry husky, the water-reducing agent mixing of the water and cement amount 5% of cement more than 1 part of 32.5 grade, cement amount 28-35% and
Into it is dark brown to do sand color, and dry grains of sand footpath is 0.1-1.5mm.Cement can use 32.5 grades, 42.5 grades and 52.5 etc.
The cement of level.
As the improvement of the present invention, the height of the sand material concrete layer is 2-5mm, and sand material concrete presses mass fraction bag
The water-reducing agent for including 2 parts of dry sand, 1 part of 52.5 rating cement, the water of cement amount 30% and cement amount 5% mixes, dry grains of sand footpath
For 0.5-1.0mm.
As the improvement of the present invention, the sander is wheel sander, and emery wheel fineness is No. 50-100.
As the present invention improvement, the water modelled after an antique by mass fraction include 3 parts of water, 2 parts of rape oils, 1 part of liquid detergent and
0.01-0.1 parts of black pigments mix.
As the improvement of the present invention, the black pigment is iron oxide, needs to place infiltration 2 days after being jetted through water modelled after an antique.
As the improvement of the present invention, the rugged natural pearl not exactly round in shape reason that the sand material concrete layer upper surface is set passes through elder generation
Shaping powder is sprayed into mold bottom to be formed, then spraying into sand material concrete layer on mold bottom and shaping powder is consolidated
It is fixed, then expire whole mould, demoulding maintenance hardening with the sandstone filling concrete similar to military Kang Shi colors, then use alloyed steel sand
The shaping powder of sand material concrete layer upper surface is removed and produces a kind of weathering face for being uneven not of uniform size by shot-blasting machine,
The height of shaping powder be not more than 5mm, shaping powder by mass fraction includes 10 parts of common stones dry powder and 3-5 parts of water mix and
Into the particle diameter of common stones dry powder is 60-120 mesh.
As the improvement of the present invention, the shaping powder includes 10 parts of common stones dry powder by mass fraction and 4 parts of water mix
Conjunction forms, and the particle diameter of common stones dry powder is 80-100 mesh, and the shaping powder and sand material concrete pass through artificial stone plate's raw material
Mixing sprays into after being stirred with mixer.
As the improvement of the present invention, the demoulding carries out after concrete tentatively hardens, and the maintenance firm time is 7-
10 days.
A kind of imitative Wu Kangshi of the present invention, is produced by following processing step：
(1) Mold Making；
(2) in mold bottom penetrating, for molding powder, to form rugged natural pearl not exactly round in shape reason, (pearl not exactly round in shape reason refers to one kind
The weathering face for being uneven not of uniform size)；
(3) the sand material concrete similar to force Kang Shi colors is sprayed on mold bottom and shaping powder, it is therefore an objective to fixed
The preceding naturally uneven molding pearl not exactly round in shape reason once sprayed；
(4) whole mould is expired with the sandstone filling concrete similar to military Kang Shi colors；
(5) by the concrete demoulding after preliminary hardening, carrying out maintenance makes its fully hardened obtain imitative force Kang Shi semi-finished product；
(6) the imitative force Kang Shi semi-finished product after maintenance are subjected to surface polishing, alloyed steel sand by shot-blasting machine with alloyed steel sand
Thrown away by shot-blasting machine centrifugal force, imitative force Kang Shi surface of semi-finished impacted, by the shaping powder that step (2) sprays into from partly into
Product surface removes, and thus produces a kind of weathering face for being uneven not of uniform size；
(7) the imitative force Kang Shi semi-finished product after polishing are polished with sander, polish a kind of bag trampled out naturally
Slurry is felt；
(8) the imitative force Kang Shi semi-finished product after polishing are sprayed into water modelled after an antique, places infiltration；
(9) the imitative force Kang Shi semi-finished product for being jetted through water modelled after an antique are sprayed into stone protectant and imitative force Kang Shi finished products is made, with increase
Product Gu rhythm and enhancing concrete.
The interior chamber size of mould is in step (1)：Long by 110 × wide by 47 × high 7cm.The bottom plate of mould is bamboo slab rubber, mould
Four sides coaming plate be plank, mould both sides are provided with handle.The mould of other sizes can certainly be used.Mould can also be adopted
Made of other materials.The height of shaping powder is not more than 5mm in step (2), and shaping powder is general including 10 parts by mass fraction
Logical stone dry powder and 3-5 parts of water mix, and the particle diameter of common stones dry powder is 60-120 mesh, and shaping powder passes through artificial stone plate
Raw material mixing sprays after being stirred with mixer.Shaping powder is done by mass fraction including 10 parts of common stones in preferred steps (2)
Powder and 4 parts of water mix, and the particle diameter of common stones dry powder is 80-100 mesh.Sand material concrete is highly 1- in step (3)
30mm, sand material concrete are included cement, the water of cement amount 28-35% more than 2 parts of dry husky, 1 part of 32.5 grades by mass fraction
Mixed with the water-reducing agent of cement amount 5%, it is dark brown to do sand color, and dry grains of sand footpath is 0.1-1.5mm, and sand material concrete leads to
Cross after artificial stone plate's raw material mixing is stirred with mixer and spray.Sand material concrete is highly 2-5mm in preferred steps (3), sand material
Concrete is included the water-reducing agent of 2 parts of dry sand, 1 part of 52.5 rating cement, the water of cement amount 30% and cement amount 5% by mass fraction
Mix, dry grains of sand footpath is 0.5-1.0mm.Concrete conserve the fully hardened time as 7-10 days in step (5).Step
Suddenly sander is wheel sander in (7), and emery wheel fineness is No. 50-100.Water modelled after an antique includes 3 parts by mass fraction in step (8)
Water, 2 parts of rape oils, 1 part of liquid detergent and 0.01-0.1 parts of black pigments mix.Black pigment is iron oxide, and the placement is oozed
The saturating time is 2 days.
As depicted in figs. 1 and 2, the artificial stone plate's raw material mixing mixer used in step (2) and step (3), including
Trolley 1 and motor 2, are fixed with head tree 3 and two secondary columns 4, oblique 5 lower end of support plate is fixed on small on the mounting of trolley 1
On the mounting of car 1, top is fixed on the top of secondary column 4；Strut 6 is fixed with oblique support plate 5, the upper end of strut 6 is fixed with
Platform support 11, the right part of platform support 11 are fixed on head tree 3.Motor 2 is fixed on motor cabinet 8, the lower end hinge of sunpender 7
It is connected on motor cabinet 8, the upper end of sunpender 7 is screwed together through the preset hole in bearing piece 9 with nut 10, and bearing piece 9 is placed in platform
On stent 11, the lower part of motor cabinet 8 is placed on oblique support plate 5.The lower end of elastic support plate 13 is fixed on oblique support plate 5, elasticity
The upper end of support plate 13 and the right side of hopper 12 are fixed together；The first screw rod 14 is fixed with the shaft of motor 2, second is spiral
Bar 16 is fixed together by shaft coupling 15 and the first screw rod 14, and the exit of discharging gate 17 has connected hose 18, the first spiral shell
Swing arm 14 is stretched into hopper 12, and the second screw rod 16 is stretched into discharging gate 17.Discharging gate 17 is by cylinder 171, baffle 172 and cover board
173 compositions, cylinder 171 are connected to each other with hopper 12, and baffle 172 is molded on cylinder 171, and cover board 173 is covered in the outlet of cylinder 171
Place, stretches out in preset hole of 174 sleeve of screw rod on baffle 172 and from the preset hole on cover board 173, fasten nut 175 with
Screw rod 174, which is spirally connected, to be fixed together, and fastens nut 175 and is pressed on cover board 173.The upper end of elastic support plate 13 and the right side of hopper 12
Weld or be fixed by screws in together.Hopper cover 19 is covered with hopper 12, the shaft of motor 2 is passed through from hopper cover 19.It is soft
The exit of pipe 18 is provided with nozzle 176, and the side of nozzle 176 is provided with compressed air feed pipe 177, is fed in compressed air
Compressed air control valve 178 is provided with pipe 177, compressed air can come from air compressor.
Since motor cabinet 8 is hung on sunpender 7, the height of motor 2 can be changed by rotating nuts 10, so as to change
First screw rod 14 stretches into the depth in hopper 12, so that the mixing dynamics of feed change.Since hopper 12 is for hanging shape, material
Bucket 12 can fully vibrate during the work time, and raw material can be sufficiently mixed in vibration processes.Hopper cover 19 can prevent building ring
Dust from flying in border.
Operation principle：When motor 2 works, motor 2 returns generation vibration, this vibration is delivered on oblique support plate 5, triggers bullet
Property support plate 13 vibrate, the hopper 12 being fixed together with elastic support plate 13 can also vibrate, raw material enter material head 12 in after,
Stirred in hopper 12 in vibration by the first screw rod 14, such raw material is sufficiently mixed, and the raw material mixed is again by the
Two screw rods 16 are exported from discharging gate 17 enters hose 18, and the raw material mixed is imported into required position by hose 18
Put, the compressed air that the side of nozzle 176 is passed through can spray raw material.
The penetrating shaping powder and the equipment of sand material concrete used in step (2) and step (3) is not limited only to artificial
Slabstone raw material mixing mixer, other can realize that the equipment of the function can use.
It should be noted that embodiment is only the explanation and illustration to technical solution of the present invention, should not be by it
The restriction to technical solution of the present invention is interpreted as, it is any only to make what is locally changed using the substantive content of the invention of the present invention, should
Fall within the scope of protection of the present invention.
Claims (8)
- A kind of 1. imitative Wu Kangshi, it is characterised in that：The imitative force Kang Shi includes the sand similar to military Kang Shi colors positioned at upper strata Expect concrete layer and the sandstone concrete layer similar to military Kang Shi colors positioned at lower floor, the upper surface of the sand material concrete layer Rugged natural pearl not exactly round in shape reason is provided with, the depth of natural pearl not exactly round in shape reason is not more than 5mm, and the upper surface of the imitative force Kang Shi is by polishing Machine is polished, and the imitative force Kang Shi upper surfaces after polishing are jetted through water and stone protectant modelled after an antique successively；The sand material concrete layer Height be 1-30mm, sand material concrete is included cement, cement amounts more than 2 parts of dry husky, 1 part of 32.5 grades by mass fraction The water of 28-35% and the water-reducing agent of cement amount 5% mix, and it is dark brown to do sand color, and dry grains of sand footpath is 0.1-1.5mm； The rugged natural pearl not exactly round in shape reason that the sand material concrete layer upper surface is set in mold bottom by first spraying into shaping powder shape Into then penetrating sand material concrete layer is fixed on mold bottom and shaping powder, then with similar to military Kang Shi colors Sandstone filling concrete expire whole mould, demoulding maintenance hardening, then with alloyed steel sand shot-blasting machine by sand material concrete layer upper table The shaping powder in face, which removes, produces a kind of weathering face for being uneven not of uniform size, and the height for being molded powder is not more than 5mm, Shaping powder includes 10 parts of common stones dry powder by mass fraction and 3-5 parts of water mix, and the particle diameter of common stones dry powder is 60-120 mesh.
- A kind of 2. imitative Wu Kangshi according to claim 1, it is characterised in that：The size of the imitative force Kang Shi is：Long by 110 × Wide by 47 × high 7cm.
- A kind of 3. imitative Wu Kangshi according to claim 1, it is characterised in that：The height of the sand material concrete layer is 2- 5mm, sand material concrete include 2 parts of dry sand, water and cement amount 5% of 1 part of 52.5 rating cement, cement amount 30% by mass fraction Water-reducing agent mix, dry grains of sand footpath is 0.5-1.0mm.
- A kind of 4. imitative Wu Kangshi according to claim 1, it is characterised in that：The sander is wheel sander, emery wheel Fineness is No. 50-100.
- A kind of 5. imitative Wu Kangshi according to claim 1, it is characterised in that：The water modelled after an antique includes 3 parts by mass fraction Water, 2 parts of rape oils, 1 part of liquid detergent and 0.01-0.1 parts of black pigments mix.
- A kind of 6. imitative Wu Kangshi according to claim 5, it is characterised in that：The black pigment is iron oxide, is jetted through imitating Need to place infiltration 2 days after Gu Shui.
- A kind of 7. imitative Wu Kangshi according to claim 1, it is characterised in that：The shaping powder includes 10 by mass fraction Part common stones dry powder and 4 parts of water mix, and the particle diameter of common stones dry powder is 80-100 mesh, the shaping powder and sand material Concrete sprays into after being stirred by artificial stone plate's raw material mixing with mixer.
- A kind of 8. imitative Wu Kangshi according to claim 1, it is characterised in that：The demoulding is tentatively hardened laggard in concrete OK, the maintenance firm time is 7-10 days.