CN106917300A - One kind fire prevention folding tent cloth - Google Patents
One kind fire prevention folding tent cloth Download PDFInfo
- Publication number
- CN106917300A CN106917300A CN201510978713.XA CN201510978713A CN106917300A CN 106917300 A CN106917300 A CN 106917300A CN 201510978713 A CN201510978713 A CN 201510978713A CN 106917300 A CN106917300 A CN 106917300A
- Authority
- CN
- China
- Prior art keywords
- coating
- parts
- base fabric
- fire prevention
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to one kind fire prevention folding tent cloth, the material includes base cloth layer, the base cloth layer upper and lower faces all include macromolecule fire prevention folding functional coating, described fire prevention folding functional coating includes soaking paste coating and scrapes slurry coating, this invention ensures that the anti-flammability of tent cloth, reduces fire control dangerous, it is ensured that the property and life security of people, product of the present invention has resistance to folding line ability, scour resistance, rain cover higher simultaneously.
Description
Technical field
The present invention relates to tent field, more particularly to a kind of fire prevention folding tent cloth.
Background technology
Tent is for supportting masking wind and rain, daylight on the ground, while being also used as the shed of interim inhabitation, making account
Tent cloth needed for paulin needs that with sunshade, ventilation, windproof, rain-proof, warming, fireproof functional requirement various environment could be met
Demand, but the general fire protecting performance bottom of traditional tent cloth, hold fire hazardous, cause the potential safety hazard of people and property, together
Easily there is folding line after the tent cloth top layer coating of Shi Chuantong, had a strong impact on the outward appearance of tent cloth, cause to produce, store, make
Inconvenience in.
The content of the invention
It is an object of the invention to：In view of the shortcomings of the prior art, there is provided a kind of with high fire-retardance, preferable folding
The tent cloth of trace performance.
To achieve these goals, present invention employs following technical scheme.
One kind fire prevention folding tent cloth, the material includes base cloth layer, and the base cloth layer upper and lower faces all include macromolecule to be prevented
Fiery folding functional coating, described fire prevention folding functional coating includes soaking paste coating and scrapes slurry coating, and soaking paste coating is by following groups
Divide and constitute by weight：
100 parts of polyvinyl chloride resin；
5 ~ 15 parts of DINP plasticizer；
5 ~ 10 parts of flame-retardant plasticizer；
10 ~ 15 parts of solvent；
15 ~ 20 parts of fire retardant；
5 ~ 10 parts of pigment；
0.5 ~ 1 part of UV absorbers；
0.5 ~ 1 part of mould proof auxiliary agent；
1 ~ 2 part of stabilizer；
3 ~ 5 parts of adhesion promoter；
Blade coating slurry coating is made up of by weight following components：
100 parts of polyvinyl chloride resin；
10 ~ 15 parts of DINP plasticizer；
5 ~ 10 parts of flame-retardant plasticizer；
10 ~ 15 parts of fire retardant；
10 ~ 20 parts of solvent；
3 ~ 5 parts of pigment；
0.2 ~ 0.5 part of UV absorbers；
0.2 ~ 0.5 part of mould proof auxiliary agent；
0.5 ~ 1 part of stabilizer.
Described base cloth layer is that PE weaves base fabric.
The described soaking paste coating polyvinyl chloride resin degree of polymerization is 1600 ~ 2000, scrape the slurry coating polyvinyl chloride resin degree of polymerization be 1200 ~
1500。
Described soaking paste is phosphoric acid ester flame-retardant plasticizer with slurry coating flame-retardant plasticizer is scraped.
Described soaking paste is the one kind or several in dimethylbenzene, butanone, toluene, isopropanol, isobutanol with slurry coating solvents are scraped
Kind.
Described soaking paste is septichen phenyl ester, ortho-nitraniline, 2,4- dihydroxies with slurry coating ultraviolet absorber is scraped
One or more in base benzophenone, UV-531.
With to scrape slurry coating mould proof auxiliary agent be OBPA, stabilizer is calcium zinc stabilizer, and adhesion promoter is for described soaking paste
Acetoacetate class adhesion promoter, fire retardant is antimony oxide.
Described soaking paste coating one side coating amount is 30 ~ 50g/m2, it is 40 ~ 60g/m to scrape slurry coating one side coating amount2。
Described fire retardant granularity is less than 500 mesh.
One kind fire prevention folding tent cloth, its manufacture craft is：
1）Base fabric is rolled up with roll shaft uniform rotation to feeding platform；
2）Dip-coating：Soaking paste coating uniform by slurry tank, is coated on up and down the two of base fabric by base fabric with the speed of 10 ~ 15m/min
Face；
3）The base fabric for having coated dip-coating slurry is dried by vertical drying oven, and temperature is 160 ~ 220 DEG C；
4）Scratch together：By 3）The dried base fabric of step is scraped slurry coating uniform and is coated on the one of base fabric by scraper gap
Face；
5）By 4）Step coat scrape slurry coating base fabric dried by five sections of temperature controls：First paragraph oven temperature is controlled in 150-
170 DEG C, second segment oven temperature is controlled at 160-180 DEG C, and the 3rd section of oven temperature is controlled at 170-185 DEG C, the 4th section of baking oven
, at 170-185 DEG C, the 5th section of oven temperature control is at 170-180 DEG C for temperature control；
6）Pressurizing attaching, combines coating and base fabric tightr；
7）Trimming winds；
8）By 7）The uncoated slurry slurry one of scraping of base fabric after winding faces up, with roll shaft uniform rotation to feeding platform；
9）Second is scratched：Base fabric, by scraper gap, will be scraped slurry coating uniform and coat base fabric with the speed of 10 ~ 15m/min
On；
10）By 9）Step coat scrape slurry coating base fabric dried by five sections of temperature controls：First paragraph oven temperature is controlled in 150-
170 DEG C, second segment oven temperature is controlled at 160-180 DEG C, and the 3rd section of oven temperature is controlled at 170-185 DEG C, the 4th section of baking oven
, at 170-185 DEG C, the 5th section of oven temperature control is at 170-180 DEG C for temperature control；
11）Pressurizing attaching, combines coating and base fabric tightr；
12）Trimming winds；
13) quality inspection, cutting packaging, storage.
The present invention has the advantages that compared with prior art.
1. the present invention uses various flame retarding agents, it is ensured that the anti-flammability of tent cloth, reduces fire control dangerous, it is ensured that people
Property and life security.
2. product tent cloth of the present invention is smaller using grain fineness in coating formula, and the energy of resistance to folding line of product has been effectively ensured
Power, protects the outward appearance of product.
3. product tent cloth of the present invention coordinates coating using coating soaking paste with slurry is scraped, and effectively raises the uniform of tent cloth
Property with it is attractive in appearance.
4. the coating that tent cloth of the present invention is used can be effectively attached in PE braiding base fabrics, with antiscour higher
Ability, rain cover excellent performance.
5. tent cloth coating of the present invention is effectively guaranteed coating and is woven in PE using two kinds of coating methods of dip-coating and blade coating
Base fabric is evenly distributed, it is ensured that the stabilization of properties of product.
Specific embodiment
Below by embodiment, patent of the present invention is described further.
The embodiment of the present invention 1 includes：
One kind fire prevention folding tent cloth, the material includes base cloth layer, and it is resistance to that the base cloth layer upper and lower faces all include macromolecule fire prevention
Folding functional coating, described fire prevention folding functional coating is pressed with slurry coating, soaking paste coating is scraped including soaking paste coating by following components
Parts by weight are constituted：
100 parts of polyvinyl chloride resin；
10 parts of DINP plasticizer；
8 parts of flame-retardant plasticizer；
15 parts of solvent；
18 parts of fire retardant；
5 parts of pigment；
0.8 part of UV absorbers；
0.8 part of mould proof auxiliary agent；
1 part of stabilizer；
4 parts of adhesion promoter；
Blade coating slurry coating is made up of by weight following components：
100 parts of polyvinyl chloride resin；
10 parts of DINP plasticizer；
5 parts of flame-retardant plasticizer；
12 parts of fire retardant
20 parts of solvent；
4 parts of pigment；
0.4 part of UV absorbers；
0.4 part of mould proof auxiliary agent；
0.8 part of stabilizer.
Described base cloth layer is that PE weaves base fabric.
The described soaking paste coating polyvinyl chloride resin degree of polymerization is 1600, and it is 1500 to scrape the slurry coating polyvinyl chloride resin degree of polymerization.
Described soaking paste is phosphoric acid ester flame-retardant plasticizer with slurry coating flame-retardant plasticizer is scraped.
Described soaking paste is dimethylbenzene with slurry coating solvents are scraped.
Described soaking paste is septichen phenyl ester with slurry coating ultraviolet absorber is scraped.
Described soaking paste is OBPA with the mould proof auxiliary agent of slurry coating is scraped, and Coating Stabilizers are calcium zinc stabilizer, and adhesive force promotes
Agent is acetoacetate class adhesion promoter, and fire retardant is antimony oxide.
Described soaking paste coating one side coating amount is 40g/m2, it is 50g/m to scrape slurry coating one side coating amount2。
Described fire retardant granularity is 600 mesh.
One kind fire prevention folding tent cloth, its manufacture craft is：
1）Base fabric is rolled up with roll shaft uniform rotation to feeding platform；
2）Dip-coating：Base fabric, by slurry tank, soaking paste coating uniform is coated on the upper and lower surface of base fabric with the speed of 10m/min；
3）The base fabric for having coated dip-coating slurry is dried by vertical drying oven, and temperature is 180 DEG C；
4）Scratch together：By 3）The dried base fabric of step is scraped slurry coating uniform and is coated on the one of base fabric by scraper gap
Face；
5）By 4）Step coat scrape slurry coating base fabric dried by five sections of temperature controls：First paragraph oven temperature is controlled 160
DEG C, second segment oven temperature is controlled at 180 DEG C, and at 185 DEG C, the 4th section of oven temperature control exists for the 3rd section of oven temperature control
185 DEG C, the 5th section of oven temperature control is at 180 DEG C；
6）Pressurizing attaching, combines coating and base fabric tightr；
7）Trimming winds；
8）By 7）The uncoated slurry slurry one of scraping of base fabric after winding faces up, with roll shaft uniform rotation to feeding platform；
9）Second is scratched：Base fabric, by scraper gap, will be scraped slurry coating uniform and coated in base fabric with the speed of 10m/min；
10）By 9）Step coat scrape slurry coating base fabric dried by five sections of temperature controls：First paragraph oven temperature is controlled 160
DEG C, second segment oven temperature is controlled at 180 DEG C, and at 185 DEG C, the 4th section of oven temperature control exists for the 3rd section of oven temperature control
185 DEG C, the 5th section of oven temperature control is at 180 DEG C；
11）Pressurizing attaching, combines coating and base fabric tightr；
12）Trimming winds；
13) quality inspection, cutting packaging, storage.
Claims (10)
1. a kind of fire prevention folding tent cloth, the material includes base cloth layer, and the base cloth layer upper and lower faces all include macromolecule fire prevention
Folding functional coating, described fire prevention folding functional coating includes soaking paste coating and scrapes slurry coating, and soaking paste coating is by following components
Constitute by weight：
100 parts of polyvinyl chloride resin；
5 ~ 15 parts of DINP plasticizer；
5 ~ 10 parts of flame-retardant plasticizer；
10 ~ 15 parts of solvent；
15 ~ 20 parts of fire retardant；
5 ~ 10 parts of pigment；
0.5 ~ 1 part of UV absorbers；
0.5 ~ 1 part of mould proof auxiliary agent；
1 ~ 2 part of stabilizer；
3 ~ 5 parts of adhesion promoter；
Blade coating slurry coating is made up of by weight following components：
100 parts of polyvinyl chloride resin；
10 ~ 15 parts of DINP plasticizer；
5 ~ 10 parts of flame-retardant plasticizer；
10 ~ 15 parts of fire retardant；
10 ~ 20 parts of solvent；
3 ~ 5 parts of pigment；
0.2 ~ 0.5 part of UV absorbers；
0.2 ~ 0.5 part of mould proof auxiliary agent；
0.5 ~ 1 part of stabilizer.
2. a kind of fire prevention folding tent cloth according to claim 1, it is characterised in that described base cloth layer is that PE weaves base
Cloth.
3. a kind of fire prevention folding tent cloth according to claim 1, it is characterised in that described soaking paste coating polyvinyl chloride resin gathers
Right is 1600 ~ 2000, and it is 1200 ~ 1500 to scrape the slurry coating polyvinyl chloride resin degree of polymerization.
4. a kind of fire prevention folding tent cloth according to claim 1, it is characterised in that described soaking paste hinders with slurry coating is scraped
Combustion plasticizer is phosphoric acid ester flame-retardant plasticizer.
5. a kind of fire prevention folding tent cloth according to claim 1, it is characterised in that described soaking paste is with to scrape slurry coating molten
Agent is one or more in dimethylbenzene, butanone, toluene, isopropanol, isobutanol.
6. a kind of fire prevention folding tent cloth according to claim 1, it is characterised in that described soaking paste is with to scrape slurry coating purple
Outer absorbent is septichen phenyl ester, ortho-nitraniline, 2,4-DihydroxyBenzophenone, 2- hydroxyl -4- n-octyloxies two
One or more in Benzophenone.
7. a kind of fire prevention folding tent cloth according to claim 1, it is characterised in that described soaking paste is prevented with slurry coating is scraped
Mould auxiliary agent is OBPA；Described soaking paste is calcium zinc stabilizer with slurry Coating Stabilizers are scraped；Described soaking paste coating adhesion promotes
Agent is acetoacetate class adhesion promoter；Described soaking paste is antimony oxide with coating layer fire retardant is scraped.
8. a kind of fire prevention folding tent cloth according to claim 1, it is characterised in that described soaking paste coating one side coating
It is 30 ~ 50g/m to measure2；Described slurry coating one side coating amount of scraping is 40 ~ 60g/m2。
9. a kind of fire prevention folding tent cloth according to claim 1 and 7, it is characterised in that described fire retardant granularity is less than
500 mesh.
10. a kind of fire prevention folding tent cloth, its manufacture craft is：
1）Base fabric is rolled up with roll shaft uniform rotation to feeding platform；
2）Dip-coating：Soaking paste coating uniform by slurry tank, is coated on up and down the two of base fabric by base fabric with the speed of 10 ~ 15m/min
Face；
3）The base fabric for having coated dip-coating slurry is dried by vertical drying oven, and temperature is 160 ~ 220 DEG C；
4）Scratch together：By 3）The dried base fabric of step is scraped slurry coating uniform and is coated on the one of base fabric by scraper gap
Face；
5）By 4）Step coat scrape slurry coating base fabric dried by five sections of temperature controls：First paragraph oven temperature is controlled in 150-
170 DEG C, second segment oven temperature is controlled at 160-180 DEG C, and the 3rd section of oven temperature is controlled at 170-185 DEG C, the 4th section of baking oven
, at 170-185 DEG C, the 5th section of oven temperature control is at 170-180 DEG C for temperature control；
6）Pressurizing attaching, combines coating and base fabric tightr；
7）Trimming winds；
8）By 7）The uncoated slurry slurry one of scraping of base fabric after winding faces up, with roll shaft uniform rotation to feeding platform；
9）Second is scratched：Base fabric, by scraper gap, will be scraped slurry coating uniform and coat base fabric with the speed of 10 ~ 15m/min
On；
10）By 9）Step coat scrape slurry coating base fabric dried by five sections of temperature controls：First paragraph oven temperature is controlled in 150-
170 DEG C, second segment oven temperature is controlled at 160-180 DEG C, and the 3rd section of oven temperature is controlled at 170-185 DEG C, the 4th section of baking oven
, at 170-185 DEG C, the 5th section of oven temperature control is at 170-180 DEG C for temperature control；
11）Pressurizing attaching, combines coating and base fabric tightr；
12）Trimming winds；
13) quality inspection, cutting packaging, storage.