CN106868662B - A kind of imitative cotton terylen false twist yarn and manufacturing method and braided fabric - Google Patents
A kind of imitative cotton terylen false twist yarn and manufacturing method and braided fabric Download PDFInfo
- Publication number
- CN106868662B CN106868662B CN201710009519.XA CN201710009519A CN106868662B CN 106868662 B CN106868662 B CN 106868662B CN 201710009519 A CN201710009519 A CN 201710009519A CN 106868662 B CN106868662 B CN 106868662B
- Authority
- CN
- China
- Prior art keywords
- roller
- terylen
- tension
- ratio
- false twist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of imitative cotton terylen false twist yarn and manufacturing method and braided fabric, the surface hairiness length of silk is 300/1000m or more in the hairiness number of 2mm or more.Manufacturing method includes by terylen preoriented yarn by entering the 2nd roller after the 1st roller to hot-rolling, is heated to the 1st hot tank, then successively obtains product through importing scroll tube, the 3rd roller, the 4th roller；Extension ratio between 1st roller and the 2nd roller are as follows: 1.0-1.5%；Extension ratio between 2nd roller and the 3rd roller are as follows: the ratio 1.5-4.0 of 1.0-1.5%, untwister tension and twisting tension presses sky 2.0-5.0kg/cm2, the 1st heater temperature: 220-250 DEG C.Processed filament product of the invention is capable of processing the braided fabric for providing cotton fiber characteristic.
Description
Technical field
The present invention relates to textile fabric field, specifically a kind of imitative cotton terylen false twist yarn and manufacturing method and braiding
Object.
Background technique
Cotton fiber is the natural fiber of tradition spinning, and the advantages of cotton fiber is, fluffy, sense of touch is submissive, soft, table
Face soft glossy；Though there is filoplume but without tingling sensation, generally keep warm fair, when low perspiration can radiate, without electrostatic under general environment.By
In the shortage of resources of natural fiber, using there is regional difference, southern dosage is bigger, and the production of existing polyester fiber
Can be superfluous, in conjunction with this two o'clock, the yield of polyester in synthetic fibers can be upgraded and this 2 point knot of the shortage of resources of natural fiber
It is combined.Cotton fiber is substituted using polyester fiber.The prior art mainly adopts the modes of Compound Machining to form imitative cotton
Effect.
Summary of the invention
The purpose of the present invention is to provide a kind of fluffy, the soft and hygroscopicity with cotton fiber, anti-pilling.It is reachable
To the imitative cotton terylen long filament and its manufacturing method of substitution cotton fiber and manufactured braided fabric.
The present invention is achieved through the following technical solutions:
A kind of imitative cotton terylen false twist yarn, including a kind of common terylen POY, section be circular cross-section or profiled-cross-section,
Above-mentioned terylen POY is allowed to machining deformation using specified conditions by false twisting machine and generates the imitative cotton terylen of a certain number of filoplumes
False twist yarn, the filoplume number of the terylen false twist yarn are as follows: measurement 300/1000m or more of filoplume number, and measure filoplume length
2.0mm or more, and the filament number range 0.3-2.8dtex of the terylen false twist yarn.
A kind of imitative cotton terylen false twist yarn and manufacturing method, it is characterized in that: a kind of ordinary polyester POY is passed through first sieve
Enter the second roller after drawing hot-rolling to heat, heated to the first hot tank, then successively through importing scroll tube, third roller, the 4th sieve
It draws, obtains product；Extension ratio between the 1st roller and the 2nd roller of the terylen preoriented yarn are as follows: 1.0-1.5%；2nd sieve
Draw the extension ratio between the 3rd roller are as follows: the ratio 2.0-4.0 of 1.0-1.5%, untwister tension and twisting tension presses sky 2.0-
5.0kg/cm2, the 1st heater temperature: 220-250 DEG C, optimal effectiveness range is the ratio 2.2- of untwister tension and twisting tension
3.3, pressure is empty: 3.0-4.5kg/cm2, the 1st heater temperature: 225-245 DEG C.
Processed filament of the invention has filoplume different in size on the surface of silk, extremely close with the surface of cotton, has both the soft of cotton
Soft bulkiness, glossiness, water imbibition, wet guilding, rapid-drying properties, and processing cost is low, and yield is big, is suitable for most of in the market
Elasticizer.
Detailed description of the invention
Present invention will be further explained below with reference to the attached drawings and examples.
Fig. 1 is the sketch map of special polyester false twist processing wire manufacturing method of the present invention.
Fig. 2 is terylene false twist yarn of the invention with 50S cotton yarn side description schematic diagram.
In Fig. 1: 1, not extending silk；2, first roller；3, hot-rolling；4, the second roller；5, the first hot tank；6, scroll tube (6-
1. false twist tension, 6- 2. untwister tension)；7, third roller；8, middle net；9, the 4th roller；10, coldplate (1.1m)
In Fig. 2, above one be 50S cotton, below one be cotton-simulated terylene processed filament of the present invention.
Specific embodiment
Polyester false twist yarn of the present invention has basic, fixed form, by extending twice and high untwister tension
Characteristic and constitute.In the processing shown in figure one, the 1st roller, the stretching of the 2nd roller and the stretching of the 2nd roller, the 3rd roller make
False twist yarn produces the effect of thickness unevenness, is set by the low speed of navel, is allowed to the great expansion of untwister tension, with twisting
The ratio that tension is formed increases.To which the monofilament of thickness unevenness in false twist yarn is broken, the hair close to cotton fiber is generated
Plumage quantity.The filoplume determining instrument that we use are as follows: MODEL MFC-120 (F), obtained filoplume number is to be determined by
What condition was realized: filoplume silk detects length setting: 2mm, speed: 200m/min, minute: 5min.In the side description of silk
The situation of filoplume is suitable (see Fig. 2) with cotton.The feel of braided fabric is very soft.
Embodiment 1:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 225 DEG C of heater temperature, untwister tension with plus
The ratio 2.2 of tension is twisted, middle net is 3.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 580/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 2:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 225 DEG C of heater temperature, untwister tension with plus
The ratio 2.2 of tension is twisted, middle net is 4.5kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 720/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 3:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 225 DEG C of heater temperature, untwister tension with plus
The ratio 3.3 of tension is twisted, middle net is 3.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 930/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 4:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 225 DEG C of heater temperature, untwister tension with plus
The ratio 3.3 of tension is twisted, middle net is 4.5kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 1080/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 5:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 245 DEG C of heater temperature, untwister tension with plus
The ratio 2.2 of tension is twisted, middle net is 3.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 1000/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 6:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 245 DEG C of heater temperature, untwister tension with plus
The ratio 2.2 of tension is twisted, middle net is 4.5kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 1170/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 7:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 245 DEG C of heater temperature, untwister tension with plus
The ratio 3.3 of tension is twisted, middle net is 3.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 1300/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 8:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 245 DEG C of heater temperature, untwister tension with plus
The ratio 3.3 of tension is twisted, middle net is 4.5kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 1490/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 9:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 220 DEG C of heater temperature, untwister tension with plus
The ratio 1.5 of tension is twisted, middle net is 2.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 330/1000m, braided fabric pliability, bulkiness connect
It is bordering on cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 10:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 250 DEG C of heater temperature, untwister tension with plus
The ratio 4.0 of tension is twisted, middle net is 5.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 1550/1000m, braided fabric pliability, bulkiness are excellent
Yu Mian.It is slightly poor to grasp industry.Specific value is shown in Table 1.
Embodiment 11:
83 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.225, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.240, the first 235 DEG C of heater temperature, untwister tension with plus
The ratio 2.5 of tension is twisted, middle net is 3.5kg/cm using pressure2, obtain fiber number be 50 dtexs, 0.35 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 980/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Embodiment 12:
550 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.190, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.270, the first 235 DEG C of heater temperature, untwister tension with plus
The ratio 2.5 of tension is twisted, middle net is 3.5kg/cm using pressure2, obtain fiber number be 400 dtexs, 2.78 dtex of filament number/
Root, the measurement quantity of filoplume length 2mm or more are the special processing false silk of 1011/1000m, and braided fabric pliability is fluffy
Property is completely close to cotton.It is good to grasp industry.Specific value is shown in Table 1.
Comparative example 1:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 210 DEG C of heater temperature, untwister tension with plus
The ratio 1.5 of tension is twisted, middle net is 2.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 102/1000m, braided fabric pliability, bulkiness are poor
Yu Mian.It is slightly good to grasp industry.Specific value is shown in Table 2.
Comparative example 2:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 255 DEG C of heater temperature, untwister tension with plus
The ratio 1.5 of tension is twisted, middle net is 2.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 1200/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is poor to grasp industry.Specific value is shown in Table 2.
Comparative example 3:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 220 DEG C of heater temperature, untwister tension with plus
The ratio 4.5 of tension is twisted, middle net is 2.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 900/1000m, braided fabric pliability, bulkiness are complete
Entirely close to cotton.It is poor to grasp industry.Specific value is shown in Table 2.
Comparative example 4:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 220 DEG C of heater temperature, untwister tension with plus
The ratio 1.5 of tension is twisted, middle net is 2.0kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 140/1000m, braided fabric pliability, bulkiness are poor
Yu Mian.It is good to grasp industry.Specific value is shown in Table 2.
Comparative example 5:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 220 DEG C of heater temperature, untwister tension with plus
The ratio 1.0 of tension is twisted, middle net is 1.5kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 110/1000m, braided fabric pliability, bulkiness are poor
Yu Mian.It is good to grasp industry.Specific value is shown in Table 2.
Comparative example 6:
128 dtexs are chosen, 144 number of monofilaments sections are the polyester unstretched wire of circular cross-section, pass through spy as shown in Figure 1
Different processing method carries out false twisting, one-off drawing is carried out between the first, the second roller, stretching ratio: 1.162, it is passed through in the second roller
Cross scroll tube and third roller and carry out succeeding stretch, stretching ratio: 1.265, the first 220 DEG C of heater temperature, untwister tension with plus
The ratio 1.5 of tension is twisted, middle net is 5.5kg/cm using pressure2, obtain fiber number be 93 dtexs, 0.65 dtex of filament number/root,
Special processing false silk of the measurement quantity of filoplume length 2mm or more for 270/1000m, braided fabric pliability, bulkiness are poor
Yu Mian.It is good to grasp industry.Specific value is shown in Table 2.
1 embodiment of table
2 comparative example of table:
It can be seen that excellent technical effect of the invention.
Claims (6)
1. a kind of imitative cotton terylen false twist yarn, feature: filoplume length is 300/1000m in the hairiness number of 2mm or more
More than；
Manufacturing method: by terylen preoriented yarn by entering the 2nd roller after the 1st roller to hot-rolling, heating to the 1st hot tank, then according to
It is secondary through import scroll tube, the 3rd roller, the 4th roller, obtain product；Extension ratio between 1st roller and the 2nd roller are as follows: 1.0-
1.5%；Extension ratio between 2nd roller and the 3rd roller are as follows: the ratio 1.5-4.0 of 1.0-1.5%, untwister tension and twisting tension,
Press sky 2.0-5.0kg/cm2, the 1st heater temperature: 220-250 DEG C.
2. a kind of imitative cotton terylen false twist yarn according to claim 1, it is characterized in that: its feature: filoplume length exists
The hairiness number of 2mm or more is 500-1500/1000m.
3. a kind of imitative cotton terylen false twist yarn according to claim 1, it is characterized in that: filament number are as follows: 0.3-
2.8dtex。
4. a kind of manufacturing method of imitative cotton terylen false twist yarn described in claim 1, it is characterized in that: by terylen preoriented yarn
It by entering the 2nd roller after the 1st roller to hot-rolling, is heated to the 1st hot tank, then successively through importing scroll tube, the 3rd roller, the 4th sieve
It draws, obtains product；Extension ratio between 1st roller and the 2nd roller are as follows: 1.0-1.5%；Extension between 2nd roller and the 3rd roller
Multiplying power are as follows: the ratio 1.5-4.0 of 1.0-1.5%, untwister tension and twisting tension presses sky 2.0-5.0kg/cm2, the 1st hot tank temperature
Degree: 220-250 DEG C.
5. the manufacturing method of imitative cotton terylen false twist yarn according to claim 4, it is characterized in that untwister tension and twisting
The ratio 2.2-3.3 of tension, pressure are empty: 3.0-4.5kg/cm2, the 1st heater temperature: 225-245 DEG C.
6. there is the braided fabric of cotton sense made of a kind of imitative cotton terylen false twist yarn described in claim 1, terylen false twist yarn
Content is 100% weight.