CN106833203A - A kind of cold painting quick-dry type colorful pavement antiskid paint - Google Patents
A kind of cold painting quick-dry type colorful pavement antiskid paint Download PDFInfo
- Publication number
- CN106833203A CN106833203A CN201710086915.2A CN201710086915A CN106833203A CN 106833203 A CN106833203 A CN 106833203A CN 201710086915 A CN201710086915 A CN 201710086915A CN 106833203 A CN106833203 A CN 106833203A
- Authority
- CN
- China
- Prior art keywords
- agent
- resin
- antiskid
- dry type
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of cold painting quick-dry type colorful pavement antiskid paint, is made up of resin, filler, pigment, antiskid aggregate, curing agent, auxiliary agent etc., wherein：Wherein：Resin is active crylic acid resin；Filler is Paris white；Pigment is iron oxide red or medium chrome yellow；Antiskid aggregate is ceramic particle or calcining bauxite；Curing agent is Benzoyl Peroxide；Auxiliary agent is made up of levelling agent, anti-settling agent, wherein：The anti-settling agent 25%~40% of levelling agent 60%~75%.The beneficial effects of the invention are as follows, with performance is more excellent, environmental protection, good endurance, construction easily remarkable advantage.
Description
Technical field
The present invention relates to a kind of colorful pavement antiskid paint, the anti-skidding energy on road surface is improved in highway pavement laying non-skid coating
Power, is mainly paved at some black spots and bend, up and down ramp and parking lot, freeway toll station etc., to cause
The vigilance of driver, improves traffic safety.
Background technology
Pavement antiskid paint is different from common floor coatings and Colorful Asphalt Pavement, is that one kind is used to be applied in different kinds of roads
Coating used by the antiskid marked line and anti-skid surface of paving.In recent years, pavement antiskid paint has wider application, in turnover north
On ETC non-parking charge dedicated Lanes at the highway toll in capital, upper eye-catching and anti-skidding color anti-skid road surface of all mating formation, it is ensured that
Automotive safety it is orderly by charging aperture.Also all mat formation color anti-skid road surface in some pedestrian overpass, it is effective anti-
Only pedestrian falls down because bridge floor is wet and slippery.2015, Beijing completed 34 " hundred kilometers of road slow-vehicle systems transformation works of road altogether
Journey ", sets up nearly 13000 square metres of the special walkway of bicycle and has mated formation color anti-skid road surface, facilitates civic green and goes out
OK.In recent years, the city such as Guangzhou and Shenzhen had also been mated formation cycle track with antislip colour coating, for the citizen of cycling provide
Beautiful safety traffic line, people are referred to as " green road ".
At present, the whole nation has many places charge station for stopping opening in sight and tunnel's entrance and exit and bend and up and down ramp all to spread
Anti-skid surface has been filled, the generation of traffic accident has been effectively prevented.The high-risk section such as the descending long of highway, colour of having mated formation
After anti-skid surface, more than 50% traffic accidents are reduced.
Hot melt type gage mark coating is to be promoted a kind of gage mark coating for using the later stage sixties in the world, and China is in upper
The middle and later periods nineties in century introduces hot-melt coating, and its durability and night vision are major advantage, are widely used in high and highway
And urban road.But, conventional hot melt type pavement marking paint has the following disadvantages：
(1) scoring equipment is complicated, low construction efficiency and security is poor.The construction of current countries in the world hot-melt coating is most of
Be with hot melt kettle by coating high temperature melting after, then be transferred in hand propelled line-marking vehicle artificial blade coating graticule, labour intensity is big, construction effect
The operation of rate low and high temperature is dangerous big, consumes fuel, pollutes bad border.In addition, also to have supporting construction equipment, such as lorry loading
Hot melt kettle, primer flush coater, marking cleaning machine etc., a full set of scoring equipment species are various, somewhat expensive.
(2) construction technology is complicated, is difficult to grasp.Graticule is scratched after first having to high temperature melting due to hot-melt coating, technology is not
It is skilled then easily cause coating to be denatured.Such as：Cause graticule peeling to come off, poor durability, discoloration, cracking, foaming etc., influence graticule
Service life.
(3) hot-melt coating graticule is preferable in the adhesive force of bituminous paving, poor in the adhesive force of cement pavement.Main cause
Be hot-melt coating be thermoplastic, expand with heat and contract with cold, temperature denaturation it is poor, coating contains substantial amounts of stone powder filler, causes graticule to adhere to
Power difference is, it is necessary to first spray primer to strengthen the adhesive force of graticule and ground, primer is treated 14 minutes in primer solvent volatilization pollution bad border
After drying, hot-melt coating graticule could be scratched.
(4) reflecting effect is undesirable, reflective short life.Main cause is poor adhesion of the hot-melt coating to reflecting microbead,
The reflecting microbead on graticule surface is come off seriously by wheel friction, and blocked up graticule coating does not wait abrasion, and the reflective function of graticule is
Have decreased to the stage for recoating graticule of having to.The reflective short life of graticule, the friction durability with graticule is asynchronous.Contain in coating
A large amount of stone powder fillers, impurity is more, and titanium white powder content is few, whiteness reduction；Coating turns to be yellow after high temperature is heated and Exposure to Sunlight is aging and sends out
Black cracking, has a strong impact on reflecting effect.
(5) although hot-melt coating is dried quickly, the operational procedure of hot-melt coating is various；Need manually to remove old line, clear
Road surface is swept, real void normal line, high temperature melting coating is drawn, is brushed primer (drying in 14 minutes), a handcart blade coating graticule (hand push
Car can only scratch 4 kilometers of graticules for 1 day) efficiency of construction is very low, and the construction road occupying time is very long.
(6) hot-melt coating graticule aging cracking is serious.Hot-melt coating is thermoplastic, and solid, powdery coating is through high temperature melting
Cool drying turns into graticule after change.The cold and hot change of temperature can cause expanding with heat and contract with cold for graticule, and long-term use cracking comes off, graticule
Rough surface, is easily adhered pitch soil, and antifouling property is poor, and especially the sideline cracking of highway is serious, loses graticule
The eye-catching use requirement of snow-white distinctness.
(7) it is high to road conditions requirement.Hot-melt coating is used for the smooth new road surface effect of pitch preferably, less smooth for road surface
Old road and cement road poor adhesive force, graticule comes off serious less applicable.
(8) integrated cost is high.Hot-melt coating price is low, but because unit consumption is big, consumption fuel, brush primer,
Handcart manually scratches graticule, and low construction efficiency, construction cost is high.
(9) recoating difficulty of construction is big.The thickness of graticule knife-coat application is heated in 2mm, higher than road surface, must when ruling again
Old line, the especially sideline of highway, recoating difficulty of construction very big and high cost must be removed.
New double-component pavement marking paint belongs to energy saving and environment friendly gage mark coating, its main feature：
(1) service life is improved, once there were the record for reaching 10 years in the life-span in foreign countries；
(2) without heating, construction cost is reduced, construction is simple；
(3) without removing old line, construction cost is reduced；
(4) reflecting at night effect is good；
(5) resistance to shovel snow；
(6) efficiency of construction is high, and speed is fast；
(7) hydrophobicity is good, protects roadbed not corroded by ponding；
(8), generally there are quality problems in Hot-Melt Markets dog-eat-dog；
In recent years, with the fast development of highway construction, road pavement gage mark coating proposes requirement higher, it is necessary to study out
Hair more excellent performance, environmental protection, good endurance, easily novel pavement gage mark coating of constructing.
The content of the invention
The purpose of the present invention is precisely in order to overcoming the shortcomings of above-mentioned prior art to exist and providing a kind of new, environmental protection
Type, high-performance color pavement antiskid paint.
The purpose of the present invention is achieved by the following technical solution.
A kind of cold painting quick-dry type colorful pavement antiskid paint, the invention is characterised in that, by resin, filler, pigment, anti-slip bone
Material, curing agent, auxiliary agent etc. are constituted, wherein：
Wherein：
Resin is active crylic acid resin；
Filler is Paris white；
Pigment is iron oxide red or medium chrome yellow；
Antiskid aggregate is ceramic particle or calcining bauxite；
Curing agent is Benzoyl Peroxide；
Auxiliary agent is made up of levelling agent, anti-settling agent, wherein：
Levelling agent 60%~75%
Anti-settling agent 25%~40%.
Levelling agent of the present invention is Siloxane-Oxyalkylene Copolymers.
Levelling agent of the present invention is the titanate esters of tetra isopropyl two.
The proportioning and production technology of coating of the present invention：
1st, the cold proportioning for applying quick-dry type colorful pavement antiskid paint
Colorful pavement antiskid paint is mainly made up of base-material and antiskid aggregate, and base-material is by active crylic acid resin, filler, face
Material, auxiliary agent etc. are main component, and during construction, after adding a certain proportion of curing agent to reconcile, resin and curing agent are crosslinked instead
Should, film forming is chemically crosslinked, antiskid aggregate is mainly ceramic particle or calcining bauxite.
(1) resin
Resin is one of pavement antiskid paint key component, as the main film forming substance of graticule coating, plays bonding effect,
During construction, each component of coating can be bonded together, form uniform coating, while penetrating into road surface again, make coating firm
Be bonded on road surface.Cold painting type pavement antiskid paint often uses active crylic acid resin, epoxy resin, polyurethane resin etc., by
In active crylic acid resin good weatherability, environmental protection, construct the excellent combination property such as convenient and as the resin for mainly selecting
Material.
(2) filler
Filler is the packing material of pavement antiskid paint, makes coating plentiful, improves the workability of coating, improves coating
Intensity and wearability, reduce the cost of coating.Using the Paris white more than mesh of fineness 600.
(3) pigment
Pigment is mainly to coat colorization, makes coating eye-catching, causes the vigilance of driver, notes Reduced Speed Now, improves traffic
Security.Main pigment has iron oxide red or medium chrome yellow.
(4) antiskid aggregate
Antiskid aggregate mainly increases the non-skid property of coating, can reach skidproof effect high, is made pottery less than 4mm using particle diameter
The abrasion-resistive hard material such as porcelain particle or calcining bauxite.
(5) curing agent
Curing agent Main Function is to crosslink reaction with resin, is chemically crosslinked film forming.Curing agent uses peroxide hexichol first
Acyl.
(6) levelling agent
Levelling agent is mainly used in improving the pliability of dope viscosity and coating.Conventional levelling agent is polyether-modified poly- silica
Alkane.
(7) anti-settling agent
Anti-settling agent is mainly dispersiveness, the unsinkability for improving coating, and the anti-settling agent for using is the titanate esters of tetra isopropyl two.
2nd, the cold production technology for applying quick-dry type colorful pavement antiskid paint
Cold painting quick-dry type colorful pavement antiskid paint is mixed by raw material such as resin, filler, pigment, auxiliary agents, is applied
In man-hour, after adding a certain proportion of curing agent to reconcile, resin and curing agent crosslink reaction, are chemically crosslinked film forming, meanwhile, then
Face is spread or interior mixed antiskid aggregate, and main production equipments are high speed dispersor.The key of production is to be well mixed various raw material,
Can not be by segregation.The technological process of production is shown in Fig. 1.
The beneficial effects of the invention are as follows, with performance is more excellent, environmental protection, good endurance, construct it is easily notable
Advantage.
Brief description of the drawings
Fig. 1 is the flow sheet of cold painting quick-dry type colorful pavement antiskid paint.
Specific embodiment
According to pavement conditions, environmental condition, the difference of construction method, the formula of cold painting quick-dry type colorful pavement antiskid paint
Proportioning adjustment can as the case may be carried out.
Embodiment one：
The formula has preferable skid resistance, ageing resistace, is primarily adapted for use in black spot and bend, climb and fall
Road and parking lot, freeway toll station etc..
Embodiment two：
The formula has preferable skid resistance, ageing resistace, is primarily adapted for use in black spot and bend, climb and fall
Road and parking lot, freeway toll station etc..
Embodiment three：
The formula has preferable skid resistance, ageing resistace, is primarily adapted for use in black spot and bend, climb and fall
Road and parking lot, freeway toll station etc..
Example IV：
The formula has preferable skid resistance, ageing resistace, is primarily adapted for use in black spot and bend, climb and fall
Road and parking lot, freeway toll station etc..
Embodiment five：
The formula has preferable skid resistance, ageing resistace, is primarily adapted for use in black spot and bend, climb and fall
Road and parking lot, freeway toll station etc..
Embodiment six：
The formula has preferable skid resistance, ageing resistace, is primarily adapted for use in black spot and bend, climb and fall
Road and parking lot, freeway toll station etc..
Claims (3)
1. a kind of cold painting quick-dry type colorful pavement antiskid paint, it is characterised in that by resin, filler, pigment, antiskid aggregate, solid
Agent, auxiliary agent etc. are constituted, wherein：
Wherein：
Resin is active crylic acid resin；
Filler is Paris white；
Pigment is iron oxide red or medium chrome yellow；
Antiskid aggregate is ceramic particle or calcining bauxite；
Curing agent is Benzoyl Peroxide；
Auxiliary agent is made up of levelling agent, anti-settling agent, wherein：
Levelling agent 60%~75%
Anti-settling agent 25%~40%.
2. one kind according to claim 1 is cold applies quick-dry type colorful pavement antiskid paint, it is characterised in that levelling agent is poly-
Ether modified polyorganosiloxane.
3. one kind according to claim 1 is cold applies quick-dry type colorful pavement antiskid paint, it is characterised in that levelling agent is four
The titanate esters of isopropyl two.