CN106752546A - 一种水性酒瓶涂料及其制备方法 - Google Patents
一种水性酒瓶涂料及其制备方法 Download PDFInfo
- Publication number
- CN106752546A CN106752546A CN201710063520.0A CN201710063520A CN106752546A CN 106752546 A CN106752546 A CN 106752546A CN 201710063520 A CN201710063520 A CN 201710063520A CN 106752546 A CN106752546 A CN 106752546A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- agent
- coalescents
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种水性酒瓶涂料及其制备方法，涉及涂料生产加工技术领域。由如下重量份的原料制成：水性环氧改性丙烯酸树脂30‑50份、环氧硬脂酸辛酯5‑15份、分散剂1‑10份、消泡剂1‑10份、颜料1‑5份、氨中和剂1‑5份、固化剂1‑10份、偶联剂1‑20份、钛白粉1‑10份、改性高岭土1‑10份、杀菌防霉剂1‑10份、滑石粉1‑10份、水性蜡1‑5份、重质碳酸钙1‑10份、成膜助剂1‑5份、增稠剂1‑5份、流平剂1‑5份、银杏叶提取物1‑5份、去离子水5‑25份。在确保耐水性、附着力的前提下，通过合理设计组分及配比含量，可显著降低涂料内的挥发性有机化合物的含量，从而显著改善了环境。
Description
技术领域
本发明涉及一种水性酒瓶涂料及其制备方法，涉及涂料生产加工技术领域。
背景技术
酒瓶涂料通过多年的快速发展，已经迅速成为涂料行业的新宠，但是，目前的这类涂料主要存在耐水性及附着力差、对环境影响大污染高等缺陷。
发明内容
为了克服现有技术中所存在的上述技术问题，本发明的目的在于提供一种水性酒瓶涂料及其制备方法。
为实现上述目的，本发明采用了以下技术方案：
一种水性酒瓶涂料，由如下重量份的原料制成：
水性环氧改性丙烯酸树脂30-50份、
环氧硬脂酸辛酯5-15份、
分散剂1-10份、
消泡剂1-10份、
颜料1-5份、
氨中和剂1-5份、
固化剂1-10份、
偶联剂1-20份、
钛白粉1-10份、
改性高岭土1-10份、
杀菌防霉剂1-10份、
滑石粉1-10份、
水性蜡1-5份、
重质碳酸钙1-10份、
成膜助剂1-5份、
增稠剂1-5份、
流平剂1-5份、
银杏叶提取物1-5份、
去离子水5-25份。
优选的，本发明的一种水性酒瓶涂料，由如下重量份的原料制成：
水性环氧改性丙烯酸树脂35-45份、
环氧硬脂酸辛酯7-12份、
分散剂4-6份、
消泡剂4-6份、
颜料2-4份、
氨中和剂2-4份、
固化剂4-6份、
偶联剂5-15份、
钛白粉4-6份、
改性高岭土4-6份、
杀菌防霉剂4-6份、
滑石粉4-6份、
水性蜡2-4份、
重质碳酸钙4-6份、
成膜助剂2-4份、
增稠剂2-4份、
流平剂2-4份、
银杏叶提取物2-4份、
去离子水10-15份。
进一步优选的，本发明的一种水性酒瓶涂料，由如下重量份的原料制成：
水性环氧改性丙烯酸树脂40份、
环氧硬脂酸辛酯10份、
分散剂5份、
消泡剂4.5份、
颜料3份、
氨中和剂3.5份、
固化剂5.5份、
偶联剂11份、
钛白粉5份、
改性高岭土5份、
杀菌防霉剂4.5份
滑石粉5.5份、
水性蜡2.5份、
重质碳酸钙5.5份、
成膜助剂3份、
增稠剂2.5份、
流平剂3.5份、
银杏叶提取物2.5份、
去离子水13份。
本发明的水性酒瓶涂料的制备方法，步骤如下：
1)、常温条件下，向搅拌设备中依次加入水性环氧改性丙烯酸树脂、环氧硬脂酸辛酯、分散剂、消泡剂、颜料、氨中和剂和固化剂，搅拌混合半小时；
2)、接着加入偶联剂、钛白粉、改性高岭土、杀菌防霉剂、滑石粉、水性蜡，搅拌混合半小时；
3)、最后加入重质碳酸钙、成膜助剂、增稠剂、流平剂、银杏叶提取物、去离子水，搅拌混合1小时。
本发明的有益效果主要表现在：
在确保耐水性、附着力的前提下，通过合理设计组分及配比含量，可显著降低涂料内的挥发性有机化合物的含量，从而显著改善了环境。
具体实施方式
实施例1
一种水性酒瓶涂料，由如下重量份的原料制成：
水性环氧改性丙烯酸树脂40份、
环氧硬脂酸辛酯10份、
分散剂5份、
消泡剂4.5份、
颜料3份、
氨中和剂3.5份、
固化剂5.5份、
偶联剂11份、
钛白粉5份、
改性高岭土5份、
杀菌防霉剂4.5份
滑石粉5.5份、
水性蜡2.5份、
重质碳酸钙5.5份、
成膜助剂3份、
增稠剂2.5份、
流平剂3.5份、
银杏叶提取物2.5份(将银杏叶加其3倍重量的水，进行煎煮，过滤后将滤液浓缩成流浸膏，然后干燥获得粉末状的提取物)、
去离子水13份。
水性酒瓶涂料的制备方法，步骤如下：
1)、常温条件下，向搅拌设备中依次加入水性环氧改性丙烯酸树脂、环氧硬脂酸辛酯、分散剂、消泡剂、颜料、氨中和剂和固化剂，搅拌混合半小时。
2)、接着加入偶联剂、钛白粉、改性高岭土、杀菌防霉剂、滑石粉、水性蜡，搅拌混合半小时。
3)、最后加入重质碳酸钙、成膜助剂、增稠剂、流平剂、银杏叶提取物、去离子水，搅拌混合1小时。
实施例2
水性环氧改性丙烯酸树脂30份、
环氧硬脂酸辛酯15份、
分散剂1份、
消泡剂1份、
颜料5份、
氨中和剂1份、
固化剂10份、
偶联剂1份、
钛白粉10份、
改性高岭土10份、
杀菌防霉剂10份、
滑石粉1份、
水性蜡1份、
重质碳酸钙1份、
成膜助剂5份、
增稠剂5份、
流平剂1份、
银杏叶提取物1份、
去离子水25份。
制备方法同实施例1。
实施例3
水性环氧改性丙烯酸树脂50份、
环氧硬脂酸辛酯5份、
分散剂10份、
消泡剂1份、
颜料5份、
氨中和剂1份、
固化剂10份、
偶联剂20份、
钛白粉1份、
改性高岭土1份、
杀菌防霉剂1份、
滑石粉1份、
水性蜡5份、
重质碳酸钙10份、
成膜助剂1份、
增稠剂5份、
流平剂1份、
银杏叶提取物5份、
去离子水5份。
制备方法同实施例1。
以下将结合实施例，对本发明进行较为详细的说明。但是，实施例内容仅是对本发明所作的举例和说明，所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，只要不偏离发明的构思或者超越本权利要求书所定义的范围，均应属于本发明的保护范围。
Claims (4)
1.一种水性酒瓶涂料，其特征在于：由如下重量份的原料制成：
水性环氧改性丙烯酸树脂 30-50份、
环氧硬脂酸辛酯 5-15份、
分散剂 1-10份、
消泡剂 1-10份、
颜料 1-5份、
氨中和剂 1-5份、
固化剂 1-10份、
偶联剂 1-20份、
钛白粉 1-10份、
改性高岭土 1-10份、
杀菌防霉剂 1-10份、
滑石粉 1-10份、
水性蜡 1-5份、
重质碳酸钙 1-10份、
成膜助剂 1-5份、
增稠剂 1-5份、
流平剂 1-5份、
银杏叶提取物 1-5份、
去离子水 5-25份。
2.如权利要求1所述的一种水性酒瓶涂料，其特征在于，由如下重量份的原料制成：
水性环氧改性丙烯酸树脂 35-45份、
环氧硬脂酸辛酯 7-12份、
分散剂 4-6份、
消泡剂 4-6份、
颜料 2-4份、
氨中和剂 2-4份、
固化剂 4-6份、
偶联剂 5-15份、
钛白粉 4-6份、
改性高岭土 4-6份、
杀菌防霉剂 4-6份、
滑石粉 4-6份、
水性蜡 2-4份、
重质碳酸钙 4-6份、
成膜助剂 2-4份、
增稠剂 2-4份、
流平剂 2-4份、
银杏叶提取物 2-4份、
去离子水 10-15份。
3.如权利要求1或2所述的一种水性酒瓶涂料，其特征在于，由如下重量份的原料制成：
水性环氧改性丙烯酸树脂 40份、
环氧硬脂酸辛酯 10份、
分散剂 5份、
消泡剂 4.5份、
颜料 3份、
氨中和剂 3.5份、
固化剂 5.5份、
偶联剂 11份、
钛白粉 5份、
改性高岭土 5份、
杀菌防霉剂 4.5份
滑石粉 5.5份、
水性蜡 2.5份、
重质碳酸钙 5.5份、
成膜助剂 3份、
增稠剂 2.5份、
流平剂 3.5份、
银杏叶提取物 2.5份、
去离子水 13份。
4.一种制备如权利要求1或2或3所述水性酒瓶涂料的方法，其特征在于，步骤如下：
1)、常温条件下，向搅拌设备中依次加入水性环氧改性丙烯酸树脂、环氧硬脂酸辛酯、分散剂、消泡剂、颜料、氨中和剂和固化剂，搅拌混合半小时；
2)、接着加入偶联剂、钛白粉、改性高岭土、杀菌防霉剂、滑石粉、水性蜡，搅拌混合半小时；
3)、最后加入重质碳酸钙、成膜助剂、增稠剂、流平剂、银杏叶提取物、去离子水，搅拌混合1小时。