CN106746871A - A kind of sustained-release polycarboxylic protects agent of collapsing - Google Patents
A kind of sustained-release polycarboxylic protects agent of collapsing Download PDFInfo
- Publication number
- CN106746871A CN106746871A CN201510808233.9A CN201510808233A CN106746871A CN 106746871 A CN106746871 A CN 106746871A CN 201510808233 A CN201510808233 A CN 201510808233A CN 106746871 A CN106746871 A CN 106746871A
- Authority
- CN
- China
- Prior art keywords
- collapsing
- sustained
- water
- concrete
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Agent of collapsing is protected the invention provides a kind of sustained-release polycarboxylic, is related to technical field of concrete additives, the weight proportion of its component is：Prenyl polyoxyethylene ether 7%, maleic anhydride 5.5%, acryloyl ammonium 16%, ammonium persulfate 18%, NaOH 3.7%, sodium gluconate 12%, balance of water.The sustained-release polycarboxylic protects agent of collapsing and overcomes the excessive too fast shortcoming of existing polycarboxylate water-reducer loss of slump with polycarboxylate water-reducer compound use, guarantor's effect of collapsing is obvious, simultaneously, it can keep the mobility of fresh concrete, be that the use of concrete creates favourable condition, in addition, the sustained-release polycarboxylic protects collapse agent and polycarboxylate water-reducer compound use, due to the raising of water-reducing rate, the intensity of concrete increased, and also overcome the low shortcoming of early age strength of concrete.
Description
Technical field
The present invention relates to technical field of concrete additives, more particularly to a kind of sustained-release polycarboxylic protects agent of collapsing.
Background technology
Guarantor's agent of collapsing is the additive that can keep slump not immediate loss, and guarantor's agent of collapsing mainly rises and delays hydrated cementitious to condense, and reaches the effect for keeping slump.
Most common problem is too fast loss of slump in cement adaptability.The method for being used for reducing polycarboxylate water-reducer loss of slump at present mainly has 5 kinds：（1）Compound slow setting component；（2）The repeated multiple times addition of water reducer；（3）Additive process after water reducer；（4）Sustained release method；（5）Compounding reactive polymer copolymer.
In too fast this problem for loss of slump, additive worker generally improves the guarantor of water reducer and collapses ability with polycarboxylate water-reducer and retarder compounding.It is particularly problematic particularly when transportation range is more long but above-mentioned way far can not meet requirement of engineering.It is weak that the addition of retarder can not fundamentally solve the problems, such as that existing polycarboxylate water-reducer protects ability of collapsing, excessive incorporation retarder can extend on the contrary the setting time of concrete, reduce concrete quality, influence construction speed is then, exploitation one kind can keep slump not lose in a long time, and not influence the guarantor of maturing later stage performance to collapse agent just into the study hotspot of concrete admixture.
The content of the invention
The technical problem to be solved in the present invention is to provide one kind can keep slump not lose in a long time, and not influence the guarantor of maturing later stage performance to collapse agent.
In order to solve the above-mentioned technical problem, the present invention is adopted the following technical scheme that：A kind of sustained-release polycarboxylic protects agent of collapsing, and the weight proportion of its component is：Prenyl polyoxyethylene ether 7%, maleic anhydride 5.5%, acryloyl ammonium 16%, ammonium persulfate 18%, NaOH 3.7%, sodium gluconate 12%, balance of water.
In the present invention, prepare above-mentioned sustained-release polycarboxylic and protect the method for agent of collapsing and comprise the following steps：
The first step, each component is ready to according to above-mentioned weight proportion, and is contained in cell therefor, a part of water taken from the container of dress water and is added in reactor and the water in reactor is heated to 52-55 DEG C, then while stirring, while toward adding prenyl polyoxyethylene ether in reactor；
Second step, after prenyl polyoxyethylene ether is completely dissolved, then toward maleic anhydride, acryloyl ammonium, ammonium persulfate is sequentially added in reactor, is then heated to 72-74 DEG C by solution, continuously stirs 3.5 hours；
3rd step, sequentially adds NaOH, sodium gluconate, then continuously stirs 1 hour, finally adds and can obtain foregoing sustained-release polycarboxylic into remaining water and protect agent of collapsing；
Above steps is to carry out at ambient pressure.
The present invention obtain beneficial effect be：The sustained-release polycarboxylic that the present invention is provided protects agent of collapsing and overcomes the excessive too fast shortcoming of existing polycarboxylate water-reducer loss of slump with polycarboxylate water-reducer compound use, guarantor's effect of collapsing is obvious, simultaneously, it can keep the mobility of fresh concrete, be that the use of concrete creates favourable condition, in addition, the sustained-release polycarboxylic protects collapse agent and polycarboxylate water-reducer compound use, due to the raising of water-reducing rate, the intensity of concrete increased, and also overcome the low shortcoming of early age strength of concrete.
Specific embodiment
Used as one embodiment of the present invention, a kind of sustained-release polycarboxylic protects agent of collapsing, and the weight proportion of its component is：Prenyl polyoxyethylene ether 7%, maleic anhydride 5.5%, acryloyl ammonium 16%, ammonium persulfate 18%, NaOH 3.7%, sodium gluconate 12%, balance of water.
As another aspect of the present invention, prepare above-mentioned sustained-release polycarboxylic and protect the method for agent of collapsing and comprise the following steps：
The first step, each component is ready to according to above-mentioned weight proportion, and is contained in cell therefor, a part of water taken from the container of dress water and is added in reactor and the water in reactor is heated to 52-55 DEG C, then while stirring, while toward adding prenyl polyoxyethylene ether in reactor；
Second step, after prenyl polyoxyethylene ether is completely dissolved, then toward maleic anhydride, acryloyl ammonium, ammonium persulfate is sequentially added in reactor, is then heated to 72-74 DEG C by solution, continuously stirs 3.5 hours；
3rd step, sequentially adds NaOH, sodium gluconate, then continuously stirs 1 hour, finally adds and can obtain foregoing sustained-release polycarboxylic into remaining water and protect agent of collapsing；
Above steps is to carry out at ambient pressure.
Sustained-release polycarboxylic being prepared according to said ratio and preparation method and protecting agent of collapsing, hereafter, agent of collapsing is protected with the sustained-release polycarboxylic for obtaining carries out paste flowing degree test, and paste flowing degree test is with reference to GB/T8077-2000《Concrete admixture homogeneity test method》In flowing degree of net paste of cement method of testing carry out, finally measure and filled guarantor and collapse after agent, flowing degree of net paste of cement is lost 5% or so with the extension of time, illustrate that guarantor's agent of collapsing is highly beneficial to reduction fluidity loss.
Then the sustained-release polycarboxylic that will be obtained protects agent of collapsing and the test of water-reducing rate, loss of slump, concrete crushing strength is carried out by following concrete mix, and test result is as described below.
Concrete each component weight proportion：The weight portion of cement 32, the weight portion of river sand 73, the weight portion of handstone 33 of 0.3-0.8 centimetres of diameter, the weight portion of middle stone 44 of 1-1.5 centimetres of diameter, the weight portion of big stone 33 of 1.8-2.4 centimetres of diameter.
In water-reducing rate, loss of slump, the test of concrete crushing strength, the adding proportion of polycarboxylate water-reducer is 0.7%（Weight ratio）, the adding proportion that sustained-release polycarboxylic protects agent of collapsing is 0.1%（Weight ratio）.
Water-reducing rate test result is：In the case of the polycarboxylate water-reducer of simple addition 0.7%, water-reducing rate is 26.5%, and in the case where the sustained-release polycarboxylic of simple addition 0.1% protects agent of collapsing, water-reducing rate is 13%, after compound addition polycarboxylate water-reducer and sustained-release polycarboxylic protect agent of collapsing, water-reducing rate is 35%.Can be seen that guarantor agent of collapsing by above-mentioned test result has certain water-reducing effect, after it is compound with polycarboxylate water-reducer, with cooperative effect, the water-reduction of water reducer is substantially increased, the raising of this water-reducing rate will be significant to saving cement and raising concrete strength.
Loss of slump test result is：In the case of the polycarboxylate water-reducer of simple addition 0.7%, initial slump degree is 235 millimeters, it is 215 millimeters after 60 minutes, it is 190 millimeters after 90 minutes, after compound addition polycarboxylate water-reducer and sustained-release polycarboxylic protect agent of collapsing, initial slump degree is 250 millimeters, is 240 millimeters after 60 minutes, is 230 millimeters after 90 minutes.It can thus be seen that be not added with the sustained-release polycarboxylic protect collapse agent when, slump loss it is larger, just have lost within 60 minutes 20 millimeters, after 90 minutes be even more loss reach 45 millimeters；After addition sustained-release polycarboxylic protects agent of collapsing, slump loss is smaller, and 20 millimeters are only have lost after 90 minutes, it was demonstrated that the sustained-release polycarboxylic protects agent of collapsing and overcomes the excessive too fast shortcoming of existing polycarboxylate water-reducer loss of slump, protects effect of collapsing obvious.
Concrete crushing strength experiment is with reference to GB8076-2008《Concrete admixture》, experiment concrete match ratio ratio of mud W/C=0.29,20 DEG C of experimental temperature.Concrete crushing strength test result is：In the case of the polycarboxylate water-reducer of simple addition 0.7%, concrete 3d intensity is 35.3 MPas, 43.6 MPas of 7d intensity, 59.7 MPas of 28d intensity, after compound addition sustained-release polycarboxylic protects agent of collapsing, concrete 3d intensity is 38.5 MPas, 46.4 MPas of 7d intensity, 62.3 MPas of 28d intensity.It is possible thereby to determine, the sustained-release polycarboxylic is protected agent of collapsing and is used with polycarboxylic acids water reducing agent compositional, and because water-reducing rate is improved, the intensity of concrete increased, while overcoming the low shortcoming of early age strength of concrete.
Above-described embodiment is the present invention preferably implementation, and in addition, the present invention can be realized with other manner, and any obvious replacement is within protection scope of the present invention on the premise of the technical program design is not departed from.
Finally, it should be emphasized that, in order to allow those of ordinary skill in the art more easily to understand improvements of the present invention relative to prior art, some descriptions of the invention have been simplified, and for the sake of clarity, present specification is omitted some other elements, and those of ordinary skill in the art should be aware that these elements for omitting also may make up present disclosure.
Claims (1)
1. a kind of sustained-release polycarboxylic protects agent of collapsing, and the weight proportion of its component is：Prenyl polyoxyethylene ether 7%, maleic anhydride 5.5%, acryloyl ammonium 16%, ammonium persulfate 18%, NaOH 3.7%, sodium gluconate 12%, balance of water.