CN106700674A - Road marking paint and preparation method thereof - Google Patents
Road marking paint and preparation method thereof Download PDFInfo
- Publication number
- CN106700674A CN106700674A CN201611188024.XA CN201611188024A CN106700674A CN 106700674 A CN106700674 A CN 106700674A CN 201611188024 A CN201611188024 A CN 201611188024A CN 106700674 A CN106700674 A CN 106700674A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- ethyl acetate
- glass
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a road marking paint and a preparation method thereof. The road marking paint is prepared from the following components in parts by mass: 60 to 100 parts of deionized water, 1 to 2 parts of defoaming agent, 2 to 3 parts of wetting agent, 15 to 17 parts of titanium dioxide, 11 to 13 parts of quartz powder, 1 to 2 parts of flatting agent, 2 to 3 parts of thickening agent, 1 to 3 parts of oxidizing agent, 6 to 8 parts of dioctyl phthalate, 10 to 14 parts of ethyl acetate, 13 to 15 parts of glass bead, 10 to 20 parts of glass fabric, and 2 to 3 parts of dispersing agent. The road marking paint provided by the invention has an environmental protection characteristic, overcomes the defects of environment pollution at normal temperature, short service life, complex hot-melt construction, low efficiency and poor recoatability when being constructed, has a good night retroreflecting effect, and has the characteristic of drying quickness. The road marking paint provided by the invention is mainly characterized in that the used materials have no hazardous substance, raw materials are more environmental-friendly, the drying speed is fast, the convenience in construction is realized, and the service life is long.
Description
Technical field
The present invention relates to road marking line field, in particular to a kind of road mark paint and preparation method thereof.
Background technology
" wanting richness, first repair the roads " is a jingle of current common people, and it indicates China during striving for a relatively comfortable life,
Development traffic is the guide that gets rich therefore, from 1998, China put into every year highway construction fund be up to 200,000,000,000 yuan with
On, complete 315,000,000,000 yuan of transportation fixed asset investment within 2002.Acquired achievement was also extremely encouraging, by 2002
Bottom, mileage in highway open to traffic reaches 175.8 ten thousand kilometers, occupies the 4th, world highway total kilometrage and reaches 2.52 ten thousand kilometers, position
Second place of the world is occupied, more than Canada and Germany, the U.S. is only second to, when the Tenth Five-year plan in 2005 is completed, highway ratio " 95 "
Newly-increased more than 200,000 kilometers of period, highway is newly-increased more than 10,000 kilometers, during Eleventh Five-Year Plan thereafter and " 12 ", entirely
State's road total length is also also driving series of road auxiliary products with the growth of high speed sustainable development, link length always
Demand it is soaring, wherein the most closely related is exactly road mark paint.
The content of the invention
The invention provides a kind of road mark paint and preparation method thereof, the present invention has environmental protection characteristic, and its construction overcomes
Normal temperature type pollution environment, service life is short, and heat molten type construction is complicated, efficiency is low, recoatability is poor deficiency, and reflecting at night
It is good, and possess the quick feature of drying, the main characteristic of the invention lies in that it is more environmentally friendly using material unharmful substance raw material, dry
Speed is fast, convenient, long service life of constructing.
To achieve the above object, the present invention provides following technical scheme：
A kind of road mark paint and preparation method thereof, is made up of following mass fraction formula components：Deionized water 60-100
Part, defoamer 1-2 parts, wetting agent 2-3 parts, titanium dioxide 15-17 parts, silica flour 11-13 parts, levelling agent 1-2 parts, thickener 2-3
Part, oxidant 1-3 parts, dioctyl ester 6-8 parts, ethyl acetate 10-14 parts, bead 13-15 parts, glass-fiber-fabric 10-20 parts, dispersant
2-3 parts.
Further：It is made up of following mass fraction formula components：60 parts of deionized water, 1 part of defoamer, 2 parts of wetting agent, titanium
15 parts of white powder, 11 parts of silica flour, 1 part of levelling agent, 2 parts of thickener, 1 part of oxidant, 6 parts of dioctyl ester, 10 parts of ethyl acetate, glass
13 parts of pearl, 10 parts of glass-fiber-fabric, 2 parts of dispersant.
Further：It is made up of following mass fraction formula components：80 parts of deionized water, 1.5 parts of defoamer, wetting agent 2.5
Part, 16 parts of titanium dioxide, 12 parts of silica flour, 1.5 parts of levelling agent, 2.5 parts of thickener, 2 parts of oxidant, 7 parts of dioctyl ester, ethyl acetate
12 parts, 14 parts of bead, 15 parts of glass-fiber-fabric, 2.5 parts of dispersant.
Further：It is made up of following mass fraction formula components：100 parts of deionized water, 2 parts of defoamer, 3 parts of wetting agent,
17 parts of titanium dioxide, 13 parts of silica flour, 2 parts of levelling agent, 3 parts of thickener, 3 parts of oxidant, 8 parts of dioctyl ester, 14 parts of ethyl acetate, glass
15 parts of glass pearl, 20 parts of glass-fiber-fabric, 3 parts of dispersant.
Further：Preparation method comprises the following steps：
Step one, dispersant is added in a reservoir, low whipping speed is once to add froth breaking under conditions of 350~450rpm
Agent, wetting agent, levelling agent, thickener, oxidant, 8~12min of stirring it is to be mixed it is uniform after, packaged spare after filtering；
Step 2, by deionized water, the titanium dioxide that disappears, silica flour, dioctyl ester, ethyl acetate, bead, glass-fiber-fabric etc. fully
Mix, packaged spare after stirring；
Step 3, when in use will step one gained with step 2 gained mix can water-based road guide line paint.
The beneficial effects of the invention are as follows：
1st, the present invention has environmental protection characteristic, and its construction overcomes normal temperature type pollution environment, and service life is short, heat molten type construction
The complicated, deficiency that efficiency is low, recoatability is poor；
2nd, reflecting at night is good, and possesses the quick feature of drying, the main characteristic of the invention lies in that using material without having
Evil raw material of substance is more environmentally friendly, and rate of drying is fast, convenient, long service life of constructing.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment one：
A kind of road mark paint is made up of following mass fraction formula components：Deionized water 60-100 parts, defoamer 1-2
Part, wetting agent 2-3 parts, titanium dioxide 15-17 parts, silica flour 11-13 parts, levelling agent 1-2 parts, thickener 2-3 parts, oxidant 1-3
Part, dioctyl ester 6-8 parts, ethyl acetate 10-14 parts, bead 13-15 parts, glass-fiber-fabric 10-20 parts, dispersant 2-3 parts.
Embodiment two：
A kind of road mark paint is made up of following mass fraction formula components：60 parts of deionized water, 1 part of defoamer, wetting
2 parts of agent, 15 parts of titanium dioxide, 11 parts of silica flour, 1 part of levelling agent, 2 parts of thickener, 1 part of oxidant, 6 parts of dioctyl ester, ethyl acetate
10 parts, 13 parts of bead, 10 parts of glass-fiber-fabric, 2 parts of dispersant.
Embodiment three：
A kind of road mark paint is made up of following mass fraction formula components：80 parts of deionized water, 1.5 parts of defoamer, profit
2.5 parts of humectant, 16 parts of titanium dioxide, 12 parts of silica flour, 1.5 parts of levelling agent, 2.5 parts of thickener, 2 parts of oxidant, 7 parts of dioctyl ester,
12 parts of ethyl acetate, 14 parts of bead, 15 parts of glass-fiber-fabric, 2.5 parts of dispersant.
Example IV：
A kind of road mark paint is made up of following mass fraction formula components：100 parts of deionized water, 2 parts of defoamer, wetting
3 parts of agent, 17 parts of titanium dioxide, 13 parts of silica flour, 2 parts of levelling agent, 3 parts of thickener, 3 parts of oxidant, 8 parts of dioctyl ester, ethyl acetate
14 parts, 15 parts of bead, 20 parts of glass-fiber-fabric, 3 parts of dispersant.
Embodiment five：
A kind of preparation method of road mark paint comprises the following steps：
Step one, dispersant is added in a reservoir, low whipping speed is once to add froth breaking under conditions of 350~450rpm
Agent, wetting agent, levelling agent, thickener, oxidant, 8~12min of stirring it is to be mixed it is uniform after, packaged spare after filtering；
Step 2, by deionized water, the titanium dioxide that disappears, silica flour, dioctyl ester, ethyl acetate, bead, glass-fiber-fabric etc. fully
Mix, packaged spare after stirring；
Step 3, when in use will step one gained with step 2 gained mix can water-based road guide line paint.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined
May be appreciated other embodiment.
Claims (5)
1. a kind of road mark paint, it is characterised in that：It is made up of following mass fraction formula components：
Deionized water 60-100 parts, defoamer 1-2 parts, wetting agent 2-3 parts, titanium dioxide 15-17 parts, silica flour 11-13 parts, levelling
Agent 1-2 parts, thickener 2-3 parts, oxidant 1-3 parts, dioctyl ester 6-8 parts, ethyl acetate 10-14 parts, bead 13-15 parts, glass
Fine cloth 10-20 parts, dispersant 2-3 parts.
2. a kind of road mark paint according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
60 parts of deionized water, 1 part of defoamer, 2 parts of wetting agent, 15 parts of titanium dioxide, 11 parts of silica flour, 1 part of levelling agent, thickener 2
Part, 1 part of oxidant, 6 parts of dioctyl ester, 10 parts of ethyl acetate, 13 parts of bead, 10 parts of glass-fiber-fabric, 2 parts of dispersant.
3. a kind of road mark paint according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
80 parts of deionized water, 1.5 parts of defoamer, 2.5 parts of wetting agent, 16 parts of titanium dioxide, 12 parts of silica flour, 1.5 parts of levelling agent, increasing
Thick dose 2.5 parts, 2 parts of oxidant, 7 parts of dioctyl ester, 12 parts of ethyl acetate, 14 parts of bead, 15 parts of glass-fiber-fabric, 2.5 parts of dispersant.
4. a kind of road mark paint according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
100 parts of deionized water, 2 parts of defoamer, 3 parts of wetting agent, 17 parts of titanium dioxide, 13 parts of silica flour, 2 parts of levelling agent, thickener 3
Part, 3 parts of oxidant, 8 parts of dioctyl ester, 14 parts of ethyl acetate, 15 parts of bead, 20 parts of glass-fiber-fabric, 3 parts of dispersant.
5. a kind of a kind of preparation method of road mark paint according to claim 1, it is characterised in that：Including following step
Suddenly：
Step one, add dispersant in a reservoir, low whipping speed be once add under conditions of 350~450rpm defoamer,
Wetting agent, levelling agent, thickener, oxidant, 8~12min of stirring it is to be mixed it is uniform after, packaged spare after filtering；
Step 2, deionized water, the titanium dioxide that disappears, silica flour, dioctyl ester, ethyl acetate, bead, glass-fiber-fabric etc. are sufficiently mixed
Stirring, packages spare after stirring；
Step 3, when in use will step one gained with step 2 gained mix can water-based road guide line paint.