CN106637561A - 一种抗菌防辐射纱线及其生产工艺 - Google Patents
一种抗菌防辐射纱线及其生产工艺 Download PDFInfo
- Publication number
- CN106637561A CN106637561A CN201611106422.2A CN201611106422A CN106637561A CN 106637561 A CN106637561 A CN 106637561A CN 201611106422 A CN201611106422 A CN 201611106422A CN 106637561 A CN106637561 A CN 106637561A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- radiation proof
- yarn
- strand
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种抗菌防辐射纱线及其生产工艺，所述纱线包括：芯层及包覆于芯层外壁的表层，所述芯层由抗菌股线和防辐射股线交捻形成，表层包括由内至外依次设置于芯层表面的抗菌涂层、保温涂层及抗氧化涂层；所述抗菌股线由纳米二氧化钛触媒纤维和竹炭纤维混纺形成；所述防辐射股线由银纤维和PBO纤维混纺形成。所述纱线由抗菌股线和防辐射股线交捻形成，抗菌股线由抗菌股线由纳米二氧化钛触媒纤维和竹炭纤维混纺形成；防辐射股线由银纤维和PBO纤维混纺形成，多种纤维的复合，并配合设置于表层的抗菌涂层、保温涂层及抗氧化涂层，使得所述纱线具有较好的抗菌、防辐射效果，且纱线制备成本低，经济效益好，利于大规模生产。
Description
技术领域
本发明属于纺织品领域，具体地，涉及一种抗菌防辐射纱线及其生产工艺。
背景技术
纱线是用各种纺织纤维加工成一定细度的产品，用于织布、制绳、制线、针织和刺绣等。
纱分为：①短纤维纱，由短纤维（天然短纤维或化纤切段纤维）经纺纱加工而成，分环锭纱、自由端纺纱、自拈纱等。②连续长丝，如天然蚕丝和化纤长丝，分加拈或不加拈、光滑长丝或变形长丝等。③短纤维与连续长丝组合纱，例如涤棉长丝包芯纱等。线由两股或两股以上的单纱并合加拈而成。
纱线的分类很多，这里只介绍一般的分类方法：
A）按纺纱工艺方法分类可分为：精梳纱和普梳纱、半精梳纱
B）按纱线的染整及后加工分类可分为：本白纱、漂白纱、 染色纱、烧光纱、丝光纱等等。
C）按纱线的粗细（纱支）分类，如粗支纱，中支纱，细支纱和高支纱。
其中，混纺（纤）纱，又称混纺或交捻纱线，是由两种或两种以上纤维组成的纱线，如涤/棉混纺纱、毛/涤混纺纱、毛/腈混纺纱、涤/粘/腈混纺纱、真丝/棉纱交捻纱等等。有两种以上短纤维混合纺成的短纤维纱，称为混纺纱；而由两种以上长丝纱组合（如加捻）成的纱，叫混纤纱。
混纺纱线由于综合了多种纤维的特性，使得纱线同时具备多种性能。然而现有混纺纱线虽然将两种特性纤维混合，但无法充分发挥两种纤维的特质，难以实现使得纱线具备多种功效的目的。
对于纱线，目前国内主要存在如下专利文献：
中国专利授权公告号：CN205474199U，公开了一种抗菌美肌防辐射纱线，其包括纱芯、抗氧化层和抗菌美肤层，所述抗氧化层包覆所述纱芯外表面呈环状，所述抗菌美肤层包覆所述抗氧化层外表面，所述纱芯为金属化银纤维，所述抗氧化层为酚酞抗氧化涂层，所述抗菌美肤层包括两根相对的竹炭纤维条、两根相对的珍珠纤维条、两根相对的壳聚糖纤维条和两根相对的牛奶纤维条顺序布置。采用合理的结构设计，优选不同功能的纤维制成纱线，能够起到高效持久防辐射，且有效实现抗菌美肤的效果，确保其舒适性和质感，具有广泛的用途和市场前景。然而该专利所提供的纱线，抗菌美肌效果较好，但未选用具备防辐射功效的纤维，使得防辐射效果不明显。
发明内容
为解决上述存在的问题，本发明的目的在于提供一种抗菌防辐射纱线及其生产工艺，所述纱线由抗菌股线和防辐射股线交捻形成，抗菌股线由抗菌股线由纳米二氧化钛触媒纤维和竹炭纤维混纺形成；防辐射股线由银纤维和PBO纤维混纺形成，多种纤维的复合，并配合设置于表层的抗菌涂层、保温涂层及抗氧化涂层，使得所述纱线具有较好的抗菌、防辐射效果，且纱线制备成本低，经济效益好，利于大规模生产。
为达到上述目的，本发明的技术方案是：
一种抗菌防辐射纱线，所述纱线包括：芯层及包覆于芯层外壁的表层，所述芯层由抗菌股线和防辐射股线交捻形成，表层包括由内至外依次设置于芯层表面的抗菌涂层、保温涂层及抗氧化涂层；所述抗菌股线由纳米二氧化钛触媒纤维和竹炭纤维混纺形成；所述防辐射股线由银纤维和PBO纤维混纺形成。
进一步，所述抗菌涂层为纳米银颗粒抗菌涂层。
另，所述保温涂层为聚氯乙烯保温涂层。
另有，所述抗氧化涂层为酚酞抗氧化涂层。
再，所述抗菌股线截面积占芯层截面积的60~80%。
再有，所述抗菌股线与防辐射股线的股数比为1~3:1。
且，所述抗菌股线与防辐射股线的质量比为2~3:1。
同时，本发明还提供一种抗菌防辐射纱线的生产工艺，包括如下步骤：
1、制备芯层
包括开清棉、梳棉、并条、粗纱、细纱、络筒及倍捻工序，其中，
1) 开清棉
将组成抗菌股线的纳米二氧化钛触媒纤维和竹炭纤维、将组成防辐射股线的银纤维和PBO纤维，分别通过开清棉机械混合、开松、除杂，加工成抗菌棉卷和防辐射棉卷，棉卷定量分别为400~450g/m；
2) 梳棉
将步骤1)所得抗菌棉卷和防辐射棉卷分别分解成单纤维状态，生条定量为3.5~4g/m，刺辊速度为750~800r/min，锡林速度为250~300r/min，得抗菌生条和防辐射生条，生条定量分别为18~22g/m，重量不均匀率分别为4~5%；
3) 并条
分别将6~8根抗菌棉条和防辐射棉条分别送入并条机，出条速度分别为280~290mm/min，得抗菌熟条和防辐射熟条，重量不均匀率分别为0.5~1%，定量分别为2~3g/m；
4) 粗纱
将步骤3)所得抗菌熟条和防辐射熟条进行牵伸、加捻、卷绕成抗菌粗纱和防辐射粗纱，定量分别为4~5g/10m，总牵伸分别为7~7.5倍，捻度分别为40~45捻/m，锭速分别为750~850r/min；
5) 细纱
加大捻度至300~350捻/m，后区牵伸倍数为1.5~2倍，锭速15000~20000r/min，隔距块3~4mm，得抗菌细纱和防辐射细纱；
6) 络筒
筒子重量为1.5~1.8kg/筒，络筒速度为900~1000m/min，得抗菌股线和防辐射股线；
7) 倍捻
将所得抗菌股线和防辐射股线送入倍捻机，按照防辐射股线与抗菌股线的股数比为1~3:1的比例进行倍捻，股线捻系数450~470，捻度400~450，倍捻速度8000r/min，得所述抗菌防辐射纱线芯层；
2、将所述抗菌涂层涂覆于所得芯层表面，然后浸入聚氯乙烯保温涂料中，浸泡20~30min，烘干，完成所述保温涂层的涂覆，取出浸入酚酞抗氧化涂料中，浸泡30~40min，烘干，完成抗氧化涂层的涂覆，得到所述表层，完成所述抗菌防辐射纱线的生产。
本发明的有益效果在于：
所述纱线由抗菌股线和防辐射股线交捻形成，抗菌股线由抗菌股线由纳米二氧化钛触媒纤维和竹炭纤维混纺形成；防辐射股线由银纤维和PBO纤维混纺形成，多种纤维的复合，并配合设置于表层的抗菌涂层、保温涂层及抗氧化涂层，使得所述纱线具有较好的抗菌、防辐射效果，且纱线制备成本低，经济效益好，利于大规模生产。
附图说明
图1为本发明所提供的一种抗菌防辐射纱线的结构示意图。
具体实施方式
下面通过具体实施例对本发明做进一步的说明，但实施例并不限制本发明的保护范围。
参照图1，本发明所述的一种抗菌防辐射纱线，所述纱线包括：芯层1及包覆于芯层1外壁的表层2，所述芯层1由抗菌股线3和防辐射股线4交捻形成，表层2包括由内至外依次设置于芯层1表面的抗菌涂层5、保温涂层6及抗氧化涂层7；所述抗菌股线3由纳米二氧化钛触媒纤维31和竹炭纤维32混纺形成；所述防辐射股线4由银纤维41和PBO纤维42混纺形成。
进一步，所述抗菌涂层5为纳米银颗粒抗菌涂层。
另，所述保温涂层6为聚氯乙烯保温涂层。
另有，所述抗氧化涂层7为酚酞抗氧化涂层。
再，所述抗菌股线3截面积占芯层截面积的60~80%。
再有，所述抗菌股线3与防辐射股线4的股数比为1~3:1。
且，所述抗菌股线3与防辐射股线4的质量比为2~3:1。
同时，本发明还提供一种抗菌防辐射纱线的生产工艺，包括如下步骤：
1、制备芯层
包括开清棉、梳棉、并条、粗纱、细纱、络筒及倍捻工序，其中，
1) 开清棉
将组成抗菌股线的纳米二氧化钛触媒纤维和竹炭纤维、将组成防辐射股线的银纤维和PBO纤维，分别通过开清棉机械混合、开松、除杂，加工成抗菌棉卷和防辐射棉卷，棉卷定量分别为400~450g/m；
2) 梳棉
将步骤1)所得抗菌棉卷和防辐射棉卷分别分解成单纤维状态，生条定量为3.5~4g/m，刺辊速度为750~800r/min，锡林速度为250~300r/min，得抗菌生条和防辐射生条，生条定量分别为18~22g/m，重量不均匀率分别为4~5%；
3) 并条
分别将6~8根抗菌棉条和防辐射棉条分别送入并条机，出条速度分别为280~290mm/min，得抗菌熟条和防辐射熟条，重量不均匀率分别为0.5~1%，定量分别为2~3g/m；
4) 粗纱
将步骤3)所得抗菌熟条和防辐射熟条进行牵伸、加捻、卷绕成抗菌粗纱和防辐射粗纱，定量分别为4~5g/10m，总牵伸分别为7~7.5倍，捻度分别为40~45捻/m，锭速分别为750~850r/min；
5) 细纱
加大捻度至300~350捻/m，后区牵伸倍数为1.5~2倍，锭速15000~20000r/min，隔距块3~4mm，得抗菌细纱和防辐射细纱；
6) 络筒
筒子重量为1.5~1.8kg/筒，络筒速度为900~1000m/min，得抗菌股线和防辐射股线；
7) 倍捻
将所得抗菌股线和防辐射股线送入倍捻机，按照防辐射股线与抗菌股线的股数比为1~3:1的比例进行倍捻，股线捻系数450~470，捻度400~450，倍捻速度8000r/min，得所述抗菌防辐射纱线芯层；
2、将所述抗菌涂层涂覆于所得芯层表面，然后浸入聚氯乙烯保温涂料中，浸泡20~30min，烘干，完成所述保温涂层的涂覆，取出浸入酚酞抗氧化涂料中，浸泡30~40min，烘干，完成抗氧化涂层的涂覆，得到所述表层，完成所述抗菌防辐射纱线的生产。
本发明所提供的抗菌防辐射纱线，所述纱线由抗菌股线和防辐射股线交捻形成，抗菌股线由抗菌股线由纳米二氧化钛触媒纤维和竹炭纤维混纺形成；防辐射股线由银纤维和PBO纤维混纺形成，多种纤维的复合，并配合设置于表层的抗菌涂层、保温涂层及抗氧化涂层，使得所述纱线具有较好的抗菌、防辐射效果，且纱线制备成本低，经济效益好，利于大规模生产。
需要说明的是，以上实施例仅用以说明本发明的技术方案而非限制。尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的范围，其均应涵盖在本发明的权利要求范围中。
Claims (8)
1.一种抗菌防辐射纱线，其特征在于，所述纱线包括：
芯层及包覆于芯层外壁的表层，所述芯层由抗菌股线和防辐射股线交捻形成，表层包括由内至外依次设置于芯层表面的抗菌涂层、保温涂层及抗氧化涂层；
所述抗菌股线由纳米二氧化钛触媒纤维和竹炭纤维混纺形成；
所述防辐射股线由银纤维和PBO纤维混纺形成。
2.根据权利要求1所述的一种抗菌防辐射纱线，其特征在于，所述抗菌涂层为纳米银颗粒抗菌涂层。
3.根据权利要求1所述的一种抗菌防辐射纱线，其特征在于，所述保温涂层为聚氯乙烯保温涂层。
4.根据权利要求1所述的一种抗菌防辐射纱线，其特征在于，所述抗氧化涂层为酚酞抗氧化涂层。
5.根据权利要求1所述的一种抗菌防辐射纱线，其特征在于，所述抗菌股线截面积占芯层截面积的60~80%。
6.根据权利要求1所述的一种抗菌防辐射纱线，其特征在于，所述抗菌股线与防辐射股线的股数比为1~3:1。
7.根据权利要求6所述的一种抗菌防辐射纱线，其特征在于，所述抗菌股线与防辐射股线的质量比为2~3:1。
8.一种如权利要求1~7中任一项所述的抗菌防辐射纱线的生产工艺，其特征在于，包括如下步骤：
1、制备芯层
包括开清棉、梳棉、并条、粗纱、细纱、络筒及倍捻工序，其中，
开清棉
将组成抗菌股线的纳米二氧化钛触媒纤维和竹炭纤维、将组成防辐射股线的银纤维和PBO纤维，分别通过开清棉机械混合、开松、除杂，加工成抗菌棉卷和防辐射棉卷，棉卷定量分别为400~450g/m；
梳棉
将步骤1)所得抗菌棉卷和防辐射棉卷分别分解成单纤维状态，生条定量为3.5~4g/m，刺辊速度为750~800r/min，锡林速度为250~300r/min，得抗菌生条和防辐射生条，生条定量分别为18~22g/m，重量不均匀率分别为4~5%；
并条
分别将6~8根抗菌棉条和防辐射棉条分别送入并条机，出条速度分别为280~290mm/min，得抗菌熟条和防辐射熟条，重量不均匀率分别为0.5~1%，定量分别为2~3g/m；
粗纱
将步骤3)所得抗菌熟条和防辐射熟条进行牵伸、加捻、卷绕成抗菌粗纱和防辐射粗纱，定量分别为4~5g/10m，总牵伸分别为7~7.5倍，捻度分别为40~45捻/m，锭速分别为750~850r/min；
细纱
加大捻度至300~350捻/m，后区牵伸倍数为1.5~2倍，锭速15000~20000r/min，隔距块3~4mm，得抗菌细纱和防辐射细纱；
络筒
筒子重量为1.5~1.8kg/筒，络筒速度为900~1000m/min，得抗菌股线和防辐射股线；
倍捻
将所得抗菌股线和防辐射股线送入倍捻机，按照防辐射股线与抗菌股线的股数比为1~3:1的比例进行倍捻，股线捻系数450~470，捻度400~450，倍捻速度8000r/min，得所述抗菌防辐射纱线芯层；
2、将所述抗菌涂层涂覆于所得芯层表面，然后浸入聚氯乙烯保温涂料中，浸泡20~30min，烘干，完成所述保温涂层的涂覆，取出浸入酚酞抗氧化涂料中，浸泡30~40min，烘干，完成抗氧化涂层的涂覆，得到所述表层，完成所述抗菌防辐射纱线的生产。