CN106592223A - 一种衬衫的防水防油防污型免烫整理液及其整理方法 - Google Patents

一种衬衫的防水防油防污型免烫整理液及其整理方法 Download PDF

Info

Publication number
CN106592223A
CN106592223A CN201611190549.7A CN201611190549A CN106592223A CN 106592223 A CN106592223 A CN 106592223A CN 201611190549 A CN201611190549 A CN 201611190549A CN 106592223 A CN106592223 A CN 106592223A
Authority
CN
China
Prior art keywords
shirt
proofing
water
drying
pressing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611190549.7A
Other languages
English (en)
Inventor
曹群
王素琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fuyang Leopard Head Clothing Technology Co Ltd
Original Assignee
Fuyang Leopard Head Clothing Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fuyang Leopard Head Clothing Technology Co Ltd filed Critical Fuyang Leopard Head Clothing Technology Co Ltd
Priority to CN201611190549.7A priority Critical patent/CN106592223A/zh
Publication of CN106592223A publication Critical patent/CN106592223A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种衬衫的防水防油防污型免烫整理液及整理方法，由下列原料制备制成：丁烷四酸、柠檬酸胺、三乙醇胺、苹果酸、次磷酸钠、硼酸、二苯乙烯二璜酸衍生物、聚乙烯蜡、氯化镁、双氨基有机硅乳液、壳聚糖、N，N‑二甲基甲酰胺、二氧化钛、聚丙二醇200、丙基三乙氧基硅烷、四乙氧基硅烷、多聚磷酸钠、硅溶胶、浓盐酸、烷基醇酰胺聚氧乙烯醚、马来酸酐适量、无水乙醇适量、去离子水适量；本发明提供的整理液及衬衫成衣整理方法，生产出了具有防皱、防油、防水、防污的功能性衬衫，超能防护，性能持久，重复洗涤，不易色变和黄变，手感轻柔舒适，穿着清新自然，透气舒适，绿色环保，健康无刺激。

Description

一种衬衫的防水防油防污型免烫整理液及其整理方法
技术领域
本发明涉及成衣功能性整理技术领域，尤其涉及一种衬衫的防水防油防污型免烫整理液及其整理方法。
背景技术
棉质成衣以其穿着舒适、天然环保等特点深受人们的喜爱，但由于在穿着和洗涤过程中存在容易起皱、不易打理的性能缺陷，给人们的生活带来了诸多不便。因此穿着舒适、平挺有形、无需熨烫、方便打理的抗皱成衣应用前景十分广阔。而目前使用最广泛的N-羟甲基类的抗皱整理剂，会出现甲醛、pH值超标以及残留物质引起皮肤刺痒的问题，造成广大消费者对抗皱成衣安全性能的心理恐慌，同时由于传统抗皱处理对原有面料性能的改变，导致丧失了棉质成衣原有的吸水、导湿的舒适性能，因此生产出满足市场大众需求的成衣具有十分重要的意义。
通过专利检索，专利号为201010300167.1的对比专利，其公开了一种全棉衬衫的免烫处理方法，步骤依次是树脂吸收→预烘→压烫→焙烘→冷却；树脂吸收步骤是将主要组分改性二羟基甲基二羟基乙烯脲或者改性烷基二羟基乙烯脲的工作液施加到衬衫上，生产出具有抗皱免烫的全棉衬衫，虽然树脂经过改性处理，但是由于改性过程的可逆性，在生产、储运以及穿着使用过程中容易间接产生甲醛，通过最后的冷却环节并不能完全将工作液中残留物质清除干净，存在甲醛、pH值含量不稳定、穿着有刺激性的安全及环保隐患。
专利号为201410639422.3的对比专利2，其公开了一种衬衫的无甲醛抗菌免烫整理液及整理方法，其采用成衣预洗-烘干-整理液处理-定湿烘干-压烫-焙烘-静态平衡-成衣复洗-烘干的工艺流程对衬衫进行处理，此发明中前后两次烘干生产环节，采用的均是40-60℃的低温烘干温度，同时静态平衡生产环节所需时间为“6-12h”，用时长，生产效率低，不利于工业化、流水化、批量化、规模化生产，经济及社会效益低；在成衣预洗和成衣复洗两次水洗环节中，存在水资源消耗大以及环保排放的问题，不利于节能减排。同时多次洗涤容易在衬衫洗涤数量较多时出现衣服相互缠绕、打结而导致衣服严重褶皱、外观较差的问题，影响抗皱级别及产品品质，而数量较少时设备利用率低，规模效益差。针对现有技术存在的问题和缺陷，本发明提供一种环保免烫整理液及其成衣整理方法，使得生产出来的成衣在保持原有抗皱性能的基础上，达到免烫、防水、防油、防污的性能，并且安全、健康、环保，容易实现工业化、流水化、批量化和规模化，达到巨大的经济效益和社会效益。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种衬衫的防水防油防污型免烫整理液及其整理方法。
本发明是通过以下技术方案实现的：
一种衬衫的防水防油防污型免烫整理液，由下列重量份的原料制备制成：丁烷四酸24-26、柠檬酸胺16-18、三乙醇胺2.5-2.7、苹果酸0.9-1.2、次磷酸钠0.8-1、硼酸0.27-0.3、二苯乙烯二璜酸衍生物2-2.5、聚乙烯蜡1.3-1.6、氯化镁0.4-0.5、双氨基有机硅乳液2-3、壳聚糖4.5-5、N，N-二甲基甲酰胺68-80、二氧化钛1.2-1.4、聚丙二醇200 0.25-0.4、丙基三乙氧基硅烷0.6-0.8、四乙氧基硅烷0.3-0.5、多聚磷酸钠0.3-0.4、硅溶胶3.2-3.5、浓盐酸1.2-1.4、烷基醇酰胺聚氧乙烯醚0.35-0.5、马来酸酐适量、无水乙醇适量、去离子水适量。
所述一种衬衫的防水防油防污型免烫整理液，由下列具体步骤制备制成：
（1）将二氧化钛颗粒加到15-18倍量的无水乙醇中，磁力搅拌30min后加入丙基三乙氧基硅烷和四乙氧基硅烷，30min后向体系中以5秒一滴的速率滴加浓盐酸，搅拌48h，然后加入多聚磷酸钠高速剪切搅拌10-20min，搅拌结束后加入硅溶胶继续搅拌1-1.5h得到改性硅溶胶备用；
（2）将壳聚糖和马来酸酐按照质量比1：1.8的比例混合加到N，N-二甲基甲酰胺中，在水浴温度100-120℃下搅拌反应7-9h，反应结束后用去离子水洗涤呈中性后烘干备用；然后将备用的固体物和去离子水混合置于带有搅拌装置的容器中，搅拌至完全溶解后加入步骤（1）制备的产物和烷基醇酰胺聚氧乙烯醚，搅拌均匀后调节体系pH值至7-8备用；
（3）将剩余的其余原料加到去离子水中，按照总原料与去离子水质量比为1：1.5混合搅拌均匀，再加入步骤（2）制备的产物混合搅拌均匀即得整理液。
所述一种衬衫成衣的免烫整理方法，由以下具体步骤制备制成：
（1）面料优选：优选条干均匀，长短一致的长绒棉，采用紧密纺纱工艺织造，并运用液氨+丝光技术对织得的面料进行后整理，获得色泽亮丽、手感舒适，强力值高的高品质面料；
（2）立体裁剪：采用符合人体功能学的立体裁剪技术，将面料裁剪成独立衣片；
（3）嵌条缝制：运用嵌条缝制技术，将热熔性胶条或衬布缝制在缝线处，再经过压烫工艺对其进行高温压烫，获得缝线平挺的半成品；
（4）整理液处理：采用逐段作业的方式在反应室完成整理液吸收，前段采用悬挂放置的方式将衬衫用衣架悬挂在自动传输的流转带上，通过气雾的方式使工作液附着到成衣上，同时通过循环系统将飘落的整理液收集进行循环利用；后段为深度吸收室，使成衣面料纤维带液率控制在50-90%；
（5）预烘调湿：采用红外立体烘干技术，将悬挂放置的衬衫进行预烘调湿，预烘温度80-105℃，预烘时间80-110s，整体湿度控制在20-45%；
（6）压烫塑形：采用立体高温压烫机，对衬衫不同身片进行独立压烫，压烫温度为140-160℃，压烫压力为3-13kg/cm2，压烫时间12-30s；
（7）焙烘定型：焙烘温度为165-185℃、焙烘时间为30-120s；
（8）动态冷却：采用立体悬挂、自动传输的动态方式，在温度为17-20℃，湿度为60-65%的恒温恒湿密封冷却房中，冷却10-30min；
（9）手感调节：采用雾化喷施的技术对冷却后的衬衫进行手感调节，带液率控制在55-80%；
（10）烘燥冷却：将进行手感调节后的衬衫进行翻滚式烘箱烘燥，烘干温度设定在90-105℃，烘干冷却时间为15-30min。
本发明的优点是：壳聚糖作为自然界唯一带正电荷的天然生物高分子多糖，由于天然无毒可降解、良好的生物相容性、抗菌性作为优良的染色促染剂、防缩整理剂、抗菌剂等被广泛用于纺织加工业，壳聚糖的表面含有大量的羟基和氨基基团，生物活性高，有利于提高整理剂的防缩抗皱效果，由于壳聚糖的不溶水性，本发明采用二甲基甲酰胺作为反应介质，对壳聚糖进行N-马来酰化改性，提高水溶性，利用丙基三乙氧基硅烷对二氧化钛颗粒进行改性，降低表面能，还利用四乙氧基硅烷通过酸碱催化作用使与硅溶胶的硅羟基进一步缩合成键，提高硅溶胶的机械性能、化学稳定性和自清洁、防油防水等性能，再利用改性的壳聚糖溶胶和改性的硅溶胶复合形成杂化溶胶，和多元羧酸复配物等在复合催化剂的作用下，制成的整理液能够与纤维素的羟基反应，将纤维素分子连接起来，形成酯交联的三维网络，赋予织物抗皱性、免烫性、防污自清洁性，提高了织物的手感、增强了织物的强力，和耐洗性。
此外本发明提供的衬衫成衣整理方法避免了传统烘箱烘干方式中不同衣片间出现的寒潮不均匀问题，减少传统烘干烘燥所带来的衣服缠绕、堆积产生的褶皱而引起衬衫外观较差的问题，能够对衬衫中获得巨大能量的纤维分子进行急速冷却，使其获得的抗皱性能得到迅速固化，达到优异的免烫级别，在避免传统水洗方式产生的资源浪费和环保排放问题的同时，处理后的衬衫手感非常的柔软，穿着舒适自然，经检测经过本专利生产的成衣，在水洗前吸水性小于等于8s，水洗50次后吸水性在25s以内，同时其甲醛含量达到未检出的水平，pH值、异味及可分解致癌芳香胺染料等基本安全性能指标达到国家标准要求，做到环保、安全、无残留，并且外观平整度、褶裥外观、接缝外观高出国家标准的0.5-1级。同时实现工业化、流水化、批量化、规模化的生产，达到较好的经济及社会效益。
本发明提供的整理液及衬衫成衣整理方法，生产出了具有防皱、防油、防水、防污的功能性衬衫，超能防护，性能持久，重复洗涤，不易色变和黄变，手感轻柔舒适，穿着清新自然，透气舒适，绿色环保，健康无刺激。
具体实施方式
一种衬衫的防水防油防污型免烫整理液，由下列重量份（公斤）的原料制备制成：丁烷四酸24、柠檬酸胺16、三乙醇胺2.5、苹果酸0.9、次磷酸钠0.8、硼酸0.27、二苯乙烯二璜酸衍生物2、聚乙烯蜡1.3、氯化镁0.4、双氨基有机硅乳液2、壳聚糖4.5、N，N二甲基甲酰胺68、二氧化钛1.2、聚丙二醇200 0.25、丙基三乙氧基硅烷0.6、四乙氧基硅烷0.3、多聚磷酸钠0.3、硅溶胶3.2、浓盐酸1.2、烷基醇酰胺聚氧乙烯醚0.35、马来酸酐适量、无水乙醇适量、去离子水适量。
所述一种衬衫的防水防油防污型免烫整理液，由下列具体步骤制备制成：
（1）将二氧化钛颗粒加到15倍量的无水乙醇中，磁力搅拌30min后加入丙基三乙氧基硅烷和四乙氧基硅烷，30min后向体系中以5秒一滴的速率滴加浓盐酸，搅拌48h，然后加入多聚磷酸钠高速剪切搅拌10min，搅拌结束后加入硅溶胶继续搅拌1h得到改性硅溶胶备用；
（2）将壳聚糖和马来酸酐按照质量比1：1.8的比例混合加到N，N二甲基甲酰胺中，在水浴温度100℃下搅拌反应7h，反应结束后用去离子水洗涤呈中性后烘干备用；然后将备用的固体物和去离子水混合置于带有搅拌装置的容器中，搅拌至完全溶解后加入步骤（1）制备的产物和烷基醇酰胺聚氧乙烯醚，搅拌均匀后调节体系pH值至7备用；
（3）将剩余的其余原料加到去离子水中，按照总原料与去离子水质量比为1：1.5混合搅拌均匀，再加入步骤（2）制备的产物混合搅拌均匀即得整理液。
实施案例1：以80支双斜纹衬衫生产为例:
（1）面料优选：选择经过液氨+丝光技术处理过的长绒棉紧密纺80支双斜纹面料；
（2）立体裁剪：采用立体裁剪技术将面料裁剪成独立衣片；
（3）嵌条缝制：采用针距为三公分16针的嵌条包缝技术对衣片进行缝制，得到半成品衬衫；
（4）整理液处理：采用逐段作业的方式在反应室完成整理液吸收，使成衣面料纤维带液率控制在50%；
（5）预烘调湿：采用红外立体烘干技术，将悬挂放置的衬衫进行预烘调湿，预烘温度105℃，预烘时间90s，使衬衫含潮率为45%；
（6）压烫塑形：采用立体高温压烫机，压烫温度为160℃，压烫压力为13kg/cm2，压烫时间30s；
（7）焙烘定型：焙烘温度为185℃、焙烘时间为50s；
（8）动态冷却：采用立体悬挂、自动传输的动态方式，在温度为17℃，湿度为65%的恒温恒湿密封冷却房中，冷却30min；
（9）手感调节：采用雾化喷施的技术对冷却后的衬衫进行手感调节，带液率控制在80%；
（10）烘燥冷却：将进行手感调节后的衬衫进行翻滚式烘箱烘燥，烘干温度设定在105℃，烘干冷却时间为30min。
对实施案例1生产完成的衬衫其免烫性能的检测指标和国家标准GB/T 18863-2002《免烫纺织品》的对比结果以及按照AATCC 79测试水洗前后的吸水性能如表1所示。
实施案例2：以80支双平纹衬衫生产为例：
（1）面料优选：选择经过液氨+丝光技术处理过的长绒棉紧密纺80支双平纹面料；
（2）立体裁剪：采用立体裁剪技术将面料裁剪成独立衣片；
（3）嵌条缝制：采用针距为三公分17针的嵌条包缝技术对衣片进行缝制，得到半成品衬衫；
（4）整理液处理：采用逐段作业的方式在反应室完成整理液吸收，使成衣面料纤维带液率控制在50%；
（5）预烘调湿：采用红外立体烘干技术，将悬挂放置的衬衫进行预烘调湿，预烘温度100℃，预烘时间80s，使衬衫含潮率为42%；
（6）压烫塑形：采用立体高温压烫机，压烫温度为155℃，压烫压力为10kg/cm2，压烫时间26s；
（7）焙烘定型：焙烘温度为180℃、焙烘时间为30s；
（8）动态冷却：采用立体悬挂、自动传输的动态方式，在温度为17℃，湿度为65%的恒温恒湿密封冷却房中，冷却25min；
（9）手感调节：采用雾化喷施的技术对冷却后的衬衫进行手感调节，带液率控制在75%；
（10）烘燥冷却：将进行手感调节后的衬衫进行翻滚式烘箱烘燥，烘干温度设定在100℃，烘干冷却时间为25min。
对实施案例2生产完成的衬衫其免烫性能的检测指标和国家标准GB/T 18863-2002《免烫纺织品》的对比结果以及按照AATCC 79测试水洗前后的吸水性能如表1所示。
实施案例3：以100支双斜纹衬衫生产为例：
（1）面料优选：选择经过液氨+丝光技术处理过的长绒棉紧密纺100支双斜纹面料；
（2）立体裁剪：采用立体裁剪技术将面料裁剪成独立衣片；
（3）嵌条缝制：采用针距为三公分19针的嵌条包缝技术对衣片进行缝制，得到半成品衬衫；
（4）整理液处理：采用逐段作业的方式在反应室完成整理液吸收，使成衣面料纤维带液率控制在50%；
（5）预烘调湿：采用红外立体烘干技术，将悬挂放置的衬衫进行预烘调湿，预烘温度95℃，预烘时间95s，使衬衫含潮率为35%；
（6）压烫塑形：采用立体高温压烫机，压烫温度为150℃，压烫压力为5kg/cm2，压烫时间22s；
（7）焙烘定型：焙烘温度为170℃、焙烘时间为90s；
（8）动态冷却：采用立体悬挂、自动传输的动态方式，在温度为17℃，湿度为65%的恒温恒湿密封冷却房中，冷却15min；
（9）手感调节：采用雾化喷施的技术对冷却后的衬衫进行手感调节，带液率控制在65%；
（10）烘燥冷却：将进行手感调节后的衬衫进行翻滚式烘箱烘燥，烘干温度设定在95℃，烘干冷却时间为20min。
对实施案例3生产完成的衬衫其免烫性能的检测指标和国家标准GB/T 18863-2002《免烫纺织品》的对比结果以及按照AATCC 79测试水洗前后的吸水性能如表1所示。
实施案例4：以120支双斜纹衬衫生产为例：
（1）面料优选：选择经过液氨+丝光技术处理过的长绒棉紧密纺120支双斜纹面料；
（2）立体裁剪：采用立体裁剪技术将面料裁剪成独立衣片；
（3）嵌条缝制：采用针距为三公分21针的嵌条包缝技术对衣片进行缝制，得到半成品衬衫；
（4）整理液处理：采用逐段作业的方式在反应室完成整理液吸收，使成衣面料纤维带液率控制在50%；
（5）预烘调湿：采用红外立体烘干技术，将悬挂放置的衬衫进行预烘调湿，预烘温度80℃，预烘时间110s，使衬衫含潮率为20%；
（6）压烫塑形：采用立体高温压烫机，压烫温度为140℃，压烫压力为3kg/cm2，压烫时间12s；
（7）焙烘定型：焙烘温度为165℃、焙烘时间为120s；
（8）动态冷却：采用立体悬挂、自动传输的动态方式，在温度为17℃，湿度为65%的恒温恒湿密封冷却房中，冷却10min；
（9）手感调节：采用雾化喷施的技术对冷却后的衬衫进行手感调节，带液率控制在55%；
（10）烘燥冷却：将进行手感调节后的衬衫进行翻滚式烘箱烘燥，烘干温度设定在90℃，烘干冷却时间为15min。
对实施案例4生产完成的衬衫其免烫性能的检测指标和国家标准GB/T 18863-2002《免烫纺织品》的对比结果以及按照AATCC 79测试水洗前后的吸水性能如表1所示。
表1 实施案例产品性能测试指标和国家标准对比表
测试项目 国家标准 实施案例1 实施案例2 实施案例3 实施案例4
外观平整度 3.5 4 4 4 4
接缝外观 3 4 4 4 4
褶裥外观 3 4 4 4 4
甲醛含量 ≤75 未检出 未检出 未检出 未检出
水洗前吸水性 - 8 7 6 6
50次水洗后吸水性 - 24 22 18 15

Claims (3)

1.一种衬衫的防水防油防污型免烫整理液，其特征在于，由下列重量份的原料制备制成：丁烷四酸24-26、柠檬酸胺16-18、三乙醇胺2.5-2.7、苹果酸0.9-1.2、次磷酸钠0.8-1、硼酸0.27-0.3、二苯乙烯二璜酸衍生物2-2.5、聚乙烯蜡1.3-1.6、氯化镁0.4-0.5、双氨基有机硅乳液2-3、壳聚糖4.5-5、N，N-二甲基甲酰胺68-80、二氧化钛1.2-1.4、聚丙二醇200 0.25-0.4、丙基三乙氧基硅烷0.6-0.8、四乙氧基硅烷0.3-0.5、多聚磷酸钠0.3-0.4、硅溶胶3.2-3.5、浓盐酸1.2-1.4、烷基醇酰胺聚氧乙烯醚0.35-0.5、马来酸酐适量、无水乙醇适量、去离子水适量。
2.根据权利要求1所述一种衬衫的防水防油防污型免烫整理液，其特征在于，由下列具体步骤制备制成：
（1）将二氧化钛颗粒加到15-18倍量的无水乙醇中，磁力搅拌30min后加入丙基三乙氧基硅烷和四乙氧基硅烷，30min后向体系中以5秒一滴的速率滴加浓盐酸，搅拌48h，然后加入多聚磷酸钠高速剪切搅拌10-20min，搅拌结束后加入硅溶胶继续搅拌1-1.5h得到改性硅溶胶备用；
（2）将壳聚糖和马来酸酐按照质量比1：1.8的比例混合加到N，N-二甲基甲酰胺中，在水浴温度100-120℃下搅拌反应7-9h，反应结束后用去离子水洗涤呈中性后烘干备用；然后将备用的固体物和去离子水混合置于带有搅拌装置的容器中，搅拌至完全溶解后加入步骤（1）制备的产物和烷基醇酰胺聚氧乙烯醚，搅拌均匀后调节体系pH值至7-8备用；
（3）将剩余的其余原料加到去离子水中，按照总原料与去离子水质量比为1：1.5混合搅拌均匀，再加入步骤（2）制备的产物混合搅拌均匀即得整理液。
3.一种衬衫成衣的免烫整理方法，其特征在于，由以下具体步骤制备制成：
（1）面料优选：优选条干均匀，长短一致的长绒棉，采用紧密纺纱工艺织造，并运用液氨+丝光技术对织得的面料进行后整理，获得色泽亮丽、手感舒适，强力值高的高品质面料；
（2）立体裁剪：采用符合人体功能学的立体裁剪技术，将面料裁剪成独立衣片；
（3）嵌条缝制：运用嵌条缝制技术，将热熔性胶条或衬布缝制在缝线处，再经过压烫工艺对其进行高温压烫，获得缝线平挺的半成品；
（4）整理液处理：采用逐段作业的方式在反应室完成整理液吸收，前段采用悬挂放置的方式将衬衫用衣架悬挂在自动传输的流转带上，通过气雾的方式使工作液附着到成衣上，同时通过循环系统将飘落的整理液收集进行循环利用；后段为深度吸收室，使成衣面料纤维带液率控制在50-90%；
（5）预烘调湿：采用红外立体烘干技术，将悬挂放置的衬衫进行预烘调湿，预烘温度80-105℃，预烘时间80-110s，整体湿度控制在20-45%；
（6）压烫塑形：采用立体高温压烫机，对衬衫不同身片进行独立压烫，压烫温度为140-160℃，压烫压力为3-13kg/cm2，压烫时间12-30s；
（7）焙烘定型：焙烘温度为165-185℃、焙烘时间为30-120s；
（8）动态冷却：采用立体悬挂、自动传输的动态方式，在温度为17-20℃，湿度为60-65%的恒温恒湿密封冷却房中，冷却10-30min；
（9）手感调节：采用雾化喷施的技术对冷却后的衬衫进行手感调节，带液率控制在55-80%；
（10）烘燥冷却：将进行手感调节后的衬衫进行翻滚式烘箱烘燥，烘干温度设定在90-105℃，烘干冷却时间为15-30min。
CN201611190549.7A 2016-12-21 2016-12-21 一种衬衫的防水防油防污型免烫整理液及其整理方法 Pending CN106592223A (zh)