[go: up one dir, main page]

CN106583727A - 一种金属基颗粒增强构件的增材制造方法 - Google Patents

一种金属基颗粒增强构件的增材制造方法 Download PDF

Info

Publication number
CN106583727A
CN106583727A CN201611149951.0A CN201611149951A CN106583727A CN 106583727 A CN106583727 A CN 106583727A CN 201611149951 A CN201611149951 A CN 201611149951A CN 106583727 A CN106583727 A CN 106583727A
Authority
CN
China
Prior art keywords
metal
melt
nozzle
based particle
ceramic particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611149951.0A
Other languages
English (en)
Other versions
CN106583727B (zh
Inventor
李正阳
彭爽
蒋华臻
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Aerospace Science And Technology Research Institute
Original Assignee
Institute of Mechanics of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Institute of Mechanics of CAS filed Critical Institute of Mechanics of CAS
Priority to CN201611149951.0A priority Critical patent/CN106583727B/zh
Publication of CN106583727A publication Critical patent/CN106583727A/zh
Application granted granted Critical
Publication of CN106583727B publication Critical patent/CN106583727B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种金属基颗粒增强构件的增材制造方法,包括在底部带有喷嘴的坩埚中熔化金属、然后加入陶瓷颗粒、设置一个可作三维运动的水平基板、设置水平基板控制程序、通过施加一定压力使含有陶瓷颗粒的金属熔体从喷嘴中流出、熔体逐层凝固、堆积成形等步骤。本发明通过在金属熔体中添加不与其发生化学反应的陶瓷颗粒,通过陶瓷颗粒的尺寸和体积分数来控制熔体的粘度,达到控制流动与成形的目的,解决了过去层间结合不好、不利于成形等问题,提出了一种金属基颗粒增强构件的制备新方法。

Description

一种金属基颗粒增强构件的增材制造方法
技术领域
本发明属于金属增材制造技术领域,特别涉及一种金属基颗粒增强构件的增材制造方法。
背景技术
发明专利《金属构件移动微压铸成型方法》(申请号:CN201310139419)公开了一种无模成形方法,其特征在于:将精炼的金属熔体从坩埚底部出口(喷嘴)连续挤出,喷嘴下方约几百微米是一个可作x-y-z三维运动的水平基板,熔体在喷嘴与基板构成的狭小空间内边凝固边随基板剪切运动,在三维成形制造软件支持下,熔体逐层凝固堆积成形,无需模具。该方法的关键在于:在喷嘴与基板(或已凝固的前一堆积层)之间是一个狭小的半开放、半封闭空间,其中熔体的温度必须严格控制在固液两相区,使一部分熔体发生凝固,其余的熔体则被基板的运动和来自坩埚内部的压力裹挟着向前运动,使刚刚凝固的枝晶被这种运动打碎,晶粒得到细化,从而使构件的性能得到改善。该方法存在的主要问题是:对于许多常用合金来说,±1℃的差别足以使熔体的固相分数发生变化,以致粘度发生变化,温度低,粘度高,有利于成形,但不利于层间结合;温度高,粘度低,有利于层间结合,但不利于成形。因此,需要采取一定的方法,使粘度的变化不依赖于温度,将成形与层间(界面)结合的控制条件分开,为实现金属熔体直接成形(增材制造)创造便利条件。
发明内容
本发明的目的是:提供一种金属基颗粒增强构件的增材制造方法,在金属熔体中添加不与其发生化学反应的陶瓷颗粒,通过颗粒的尺寸和体积分数来控制熔体的粘度,达到控制流动与成形的目的,实现金属基颗粒增强构件的增材制造。
本发明的技术方案是:一种金属基颗粒增强构件的增材制造方法,包括以下步骤:
A.在底部带有喷嘴的坩埚中熔化金属,且温度保持在液相线以上,将不与该金属发生化学反应的陶瓷颗粒加入其中,通过搅拌使陶瓷颗粒均匀分布在金属熔体中,陶瓷颗粒的熔点高于金属熔体的温度,金属熔体的粘度由陶瓷颗粒的粒径、摩尔质量与金属熔体的摩尔质量的比例关系来控制;
B.在喷嘴下方设置一个可作三维运动的水平基板及其控制设备,喷嘴距离水平基板的距离为喷嘴内径的1~8倍;
C.在水平基板控制设备中设置预定的程序,用于控制水平基板三维运动的方向和速度;
D.施加一定的压力使含有陶瓷颗粒的金属熔体从喷嘴中流出,同时控制设备使水平基板以预定的方向和速度运动;
E.含有陶瓷颗粒的金属熔体在喷嘴与水平基板之间边凝固边随基板运动,熔体逐层凝固,堆积成形,得到金属基颗粒增强构件。
更进一步地,所述步骤A中的金属熔体为合金熔体。
更进一步地,所述步骤A中坩埚加热的方式为电阻加热或感应加热。
更进一步地,所述步骤A中使陶瓷颗粒均匀分布在金属熔体中的方法为机械搅拌或电磁搅拌。
更进一步地,所述步骤A中金属熔化与凝固过程中均受到惰性气体保护。
更进一步地,所述步骤C中,控制设备可控制喷嘴开关和坩埚内压力,从而控制金属熔体的流量。
本发明通过在金属熔体中添加不与其发生化学反应的陶瓷颗粒,通过改变陶瓷颗粒的尺寸和体积分数来控制熔体的粘度,达到控制流动与成形的目的,解决了过去层间结合不好、不利于成形等问题,实现了金属基颗粒增强构件的增材制造。
附图说明
图1为本发明流程图;
图2为本发明实际应用示意图。
1--坩埚,2--喷嘴,3--新凝固层,4—陶瓷颗粒,5—搅拌叶片,6--前一凝固层,7—水平基板
具体实施方式
实施例1:参见图1、图2,一种金属基颗粒增强构件的增材制造方法,包括以下步骤:
A.在底部带有喷嘴的坩埚中熔化金属铝,加热方式为电阻加热;且温度保持在660℃以上,将不与金属铝发生化学反应的粒径为10μm的TiC陶瓷颗粒加入其中,陶瓷颗粒与铝的质量比为1:4,通过机械搅拌使陶瓷颗粒均匀分布在金属铝熔体中,金属熔化受到惰性气体保护;
B.在喷嘴下方设置一个可作三维运动的水平基板及其控制设备,喷嘴的内径为2mm,喷嘴距离水平基板的距离为10mm;
C.在水平基板控制设备中设置预定的程序,用于控制水平基板三维运动的方向和速度;水平基板控制设备可控制喷嘴开关和坩埚内压力,陶瓷颗粒的尺寸和体积分数可控制熔体的粘度,从而控制金属铝熔体的流量;
D.施加一定压力使含有陶瓷颗粒的金属铝熔体从喷嘴中流出,同时水平基板控制设备控制水平基板以预定的方向和速度运动;
E.含有陶瓷颗粒的金属铝熔体在喷嘴与水平基板之间边凝固边随基板运动,熔体逐层凝固,堆积成形,得到铝基颗粒增强构件,凝固过程受到惰性气体保护。

Claims (6)

1.一种金属基颗粒增强构件的增材制造方法,其特征在于,包括以下步骤:
A.在底部带有喷嘴的坩埚中熔化金属,且温度保持在液相线以上,将不与该金属发生化学反应的陶瓷颗粒加入其中,通过搅拌使陶瓷颗粒均匀分布在金属熔体中,陶瓷颗粒的熔点高于金属熔体的温度,金属熔体的粘度由陶瓷颗粒的粒径、摩尔质量与金属熔体的摩尔质量的比例关系来控制;
B.在喷嘴下方设置一个可作三维运动的水平基板及其控制设备,喷嘴距离水平基板的距离为喷嘴内径的1~8倍;
C.在水平基板控制设备中设置预定的程序,用于控制水平基板三维运动的方向和速度;
D.施加一定的压力使含有陶瓷颗粒的金属熔体从喷嘴中流出,同时控制设备使水平基板以预定的方向和速度运动;
E.含有陶瓷颗粒的金属熔体在喷嘴与水平基板之间边凝固边随基板运动,熔体逐层凝固,堆积成形,得到金属基颗粒增强构件。
2.如权利要求1所述的一种金属基颗粒增强构件的增材制造方法,其特征在于:所述步骤A中的金属熔体为合金熔体。
3.如权利要求1所述的一种金属基颗粒增强构件的增材制造方法,其特征在于:所述步骤A中坩埚加热的方式为电阻加热或感应加热。
4.如权利要求1所述的一种金属基颗粒增强构件的增材制造方法,其特征在于:所述步骤A中使陶瓷颗粒均匀分布在金属熔体中的方法为机械搅拌或电磁搅拌。
5.如权利要求1所述的一种金属基颗粒增强构件的增材制造方法,其特征在于:所述步骤A中金属熔化与凝固过程中均受到惰性气体保护。
6.如权利要求1所述的一种金属基颗粒增强构件的增材制造方法,其特征在于:所述步骤C中,水平基板控制设备可控制喷嘴开关和坩埚内压力,从而控制金属熔体的流量。
CN201611149951.0A 2016-12-14 2016-12-14 一种金属基颗粒增强构件的增材制造方法 Active CN106583727B (zh)