CN106433300A - Mobile phone cover plate glass black ink formula - Google Patents
Mobile phone cover plate glass black ink formula Download PDFInfo
- Publication number
- CN106433300A CN106433300A CN201610789029.1A CN201610789029A CN106433300A CN 106433300 A CN106433300 A CN 106433300A CN 201610789029 A CN201610789029 A CN 201610789029A CN 106433300 A CN106433300 A CN 106433300A
- Authority
- CN
- China
- Prior art keywords
- black ink
- hand
- ink formulations
- set lid
- lid glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a mobile phone cover plate glass black ink formula; with the total weight of the ink as a benchmark, the mobile phone cover plate glass black ink formula mainly includes the following components by the mass percentage: 20-55% of water-soluble resin, 3-15% of a solvent, 10-30% of waterborne amino resin, 1-2% of a dispersant, 0.5-2% of a defoaming agent, 0.5-2% of a leveling agent, 15-30% of carbon black, 5-10% of a packing, 5-10% of an additive, and 1-20% of a curing agent. The black ink prepared by the formula has the advantages of good adhesion power, uniform color, and good covering ability and chemical resistance.
Description
Technical field
The present invention relates to a kind of ink formulations are and in particular to a kind of hand-set lid glass black ink formulations.
Background technology
Abundant perfect, the smart mobile phone of black or flat board etc. with the electronic product color such as smart mobile phone, flat board, style
Become the new lover of user, become the object that most women pursue.But it is applied to the black of these products in the market
Color ink is opacifying property poor, and traditional method to meet preferable covering power using increasing print pass, and existing process typically prints 3
Secondary, or even can be only achieved more satisfactory covering power 4 times, so lead to complicated construction technique, ink film thickness management and control is difficult, defective products
Rate is higher.
In view of above-mentioned defect, the design people, actively research and innovation in addition is black to founding a kind of hand-set lid glass
Color ink formula is so as to more the value in industry.
Content of the invention
For solving above-mentioned technical problem, it is an object of the invention to provide a kind of hand-set lid glass black ink formulations.
Technical scheme is as follows：
A kind of hand-set lid glass black ink formulations, on the basis of the gross weight of described ink, it is mainly by following matter
The group of amount percentage composition is grouped into：
Water-soluble resin：20-55%；
Solvent：3-15%；
Water-compatible amino resin：10-30%；
Dispersant：1-2%；
Defoamer：0.5-2%；
Levelling agent：0.5-2%；
White carbon black：15%-30%；
Filler：5-10；
Additive：5%-10%；
Firming agent：1%-20%.
Further, described water-soluble resin is water soluble acrylic resin.
Further, described solvent is one of esters solvent or ketones solvent or two kinds.
Further, described filler is one or more of Calcium Carbonate, calcium silicates, aluminium silicate, aluminium carbonate.
Further, described dispersant is polyvinyl alcohol.
Further, described is Polyether Modified Polysiloxanes Defoaming Agent for defoamer.
Further, described levelling agent is the acrylate of fluorine richness.
Further, described additive is Ketohexamethylene.
Further, described firming agent is methyl tetrahydro phthalic anhydride.
By such scheme, the present invention at least has advantages below：
The black ink that inventive formulation makes has good adhesive force, and color even, has good covering energy
Power and endurance；Respectively being grouped of the black ink for cover-plate glass of the present invention point directly can be buied by commercial sources,
Material is easy to get, and preparation is simple, and safety and environmental protection.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention,
And can be practiced according to the content of description, below with presently preferred embodiments of the present invention and coordinate detailed description as after.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is described in further detail.Following examples are used for
The present invention is described, but is not limited to the scope of the present invention.
Embodiment 1
A kind of hand-set lid glass black ink formulations, on the basis of the gross weight of described ink, it is mainly by following matter
The group of amount percentage composition is grouped into：
Water soluble acrylic resin：20%；
Ketones solvent：15%；
Water-compatible amino resin：30%；
Polyvinyl alcohol：2%；
Organic silicon modified by polyether：2%；
The acrylate of fluorine richness：2%；
White carbon black：15%；
Calcium Carbonate, calcium silicates：6%；
Ketohexamethylene：7%；
Methyl tetrahydro phthalic anhydride：1%.
Embodiment 2
A kind of hand-set lid glass black ink formulations, on the basis of the gross weight of described ink, it is mainly by following matter
The group of amount percentage composition is grouped into：
Water soluble acrylic resin：55%；
Esters solvent：5%；
Water-compatible amino resin：10%；
Polyvinyl alcohol：2%；
Organic silicon modified by polyether：1%；
The acrylate of fluorine richness：1%；
White carbon black：15%；
Calcium Carbonate, calcium silicates 5%；
Ketohexamethylene：5%；
Methyl tetrahydro phthalic anhydride：1%.
Embodiment 3
A kind of hand-set lid glass black ink formulations, on the basis of the gross weight of described ink, it is mainly by following matter
The group of amount percentage composition is grouped into：
Water soluble acrylic resin：35%；
Esters solvent：15%；
Water-compatible amino resin：15%；
Polyvinyl alcohol：2%；
Organic silicon modified by polyether：1%；
The acrylate of fluorine richness：1%；
White carbon black：20%；
Aluminium silicate, aluminium carbonate：5%；
Ketohexamethylene：5%；
Methyl tetrahydro phthalic anhydride：1%.
The preparation method of the black ink of the present invention comprises the steps：
(1) add solvent under normal temperature and pressure, rotating speed is 300-500r/min, adds water-soluble acrylic tree while stirring
Fat, adjustment rotating speed is 3000-4000r/min, after stirring 120-180min, is filtrated to get water soluble acrylic resin's solution；
(2) under the rotating speed of 600-900r/min, in water soluble acrylic resin's solution of (1) gained, sequentially add ketone
Class solvent, water-compatible amino resin, polyvinyl alcohol, white carbon black, part Polyether Modified Polysiloxanes Defoaming Agent, lithium aluminium silicate, Ketohexamethylene, stirs
Mix uniformly；Then it is ground to less than 5 μm on three-roller, then add remaining Polyether Modified Polysiloxanes Defoaming Agent, methyl tetrahydrochysene
Phthalic anhydride and the acrylate of fluorine richness, then stir, get product.
The black ink that inventive formulation makes has good adhesive force, and color even, has good covering energy
Power and endurance；Respectively being grouped of the black ink for cover-plate glass of the present invention point directly can be buied by commercial sources,
Material is easy to get, and preparation is simple, and safety and environmental protection.
The above is only the preferred embodiment of the present invention, is not limited to the present invention it is noted that for this skill
For the those of ordinary skill in art field, on the premise of without departing from the technology of the present invention principle, can also make some improve and
Modification, these improve and modification also should be regarded as protection scope of the present invention.
Claims (9)
1. a kind of hand-set lid glass black ink formulations it is characterised in that：On the basis of the gross weight of described ink, including with
The component of lower weight/mass percentage composition：
Water-soluble resin：20-55%；
Solvent：3-15%；
Water-compatible amino resin：10-30%；
Dispersant：1-2%；
Defoamer：0.5-2%；
Levelling agent：0.5-2%；
White carbon black：15-30%；
Filler：5-10%；
Additive：5-10%；
Firming agent：1-20%.
2. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described water-soluble resin is water
Soluble acrylic resin.
3. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described solvent is esters solvent
Or one of ketones solvent or two kinds.
4. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described filler be Calcium Carbonate,
One or more of calcium silicates, aluminium silicate, aluminium carbonate.
5. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described dispersant is polyethylene
Alcohol.
6. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described is polyethers for defoamer
Modified organic silicon defoamer.
7. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described levelling agent is fluorine richness
Acrylate.
8. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described additive is hexamethylene
Ketone.
9. according to claim 1 hand-set lid glass black ink formulations it is characterised in that：Described firming agent is methyl four
Hydrogen phthalic anhydride.