CN106396498A - Colorful agate jade-like colorful artificial stone and production method thereof - Google Patents
Colorful agate jade-like colorful artificial stone and production method thereof Download PDFInfo
- Publication number
- CN106396498A CN106396498A CN201610754624.1A CN201610754624A CN106396498A CN 106396498 A CN106396498 A CN 106396498A CN 201610754624 A CN201610754624 A CN 201610754624A CN 106396498 A CN106396498 A CN 106396498A
- Authority
- CN
- China
- Prior art keywords
- artificial stone
- colorful
- tone material
- mass
- colorant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a colorful agate jade-like colorful artificial stone. The colorful artificial stone comprises at least one main pigment and at least three auxiliary pigments with different colors, and the proportion of the main pigment is not less than 30%; and the formula of each of the main pigment and the auxiliary pigments comprises, by weight, 35-40% of unsaturated polyester resin, 50-60% of agate powder with the granularity of 425-600 meshes, 0.5-3% of a promoter with the solid content being higher than 60%, 0-3% of a color paste and 0.05-0.1% of a curing agent. The invention also discloses a production method of the colorful artificial stone. The artificial stone produced in the invention can simulate the colorful effect of colorful agate jade, and has the characteristics of formation of a wrapped body in the artificial stone, clear color boundary, high acuteness and bright color.
Description
Technical field
The invention belongs to artificial stone field is and in particular to a kind of imitate the beautiful colorful artificial stone of seven color Achatess and its preparation side
Method.
Background technology
Seven color Achatess jade are a uniqueness and rare kinds in Achatess, originate in Zhejiang Province Songyang County, in the world with its phase
As Achatess that only New Mexico and Oregon produce.
Seven color Achatess with its that especially limpid quality, especially gorgeous color and especially enrich magnificent pattern,
Deeply it is subject to the concern of jade fan and like.Its mineralogical composition is calcedony, is a kind of cryptocrystalline quartz, its chemical composition is dioxy
SiClx (SiO2), mohs hardness, between 6.5-7, is in glassy lustre after sanding and polishing.
Seven color Achatess are especially abundant due to inclusion enclave, and the ratio that these inclusion enclaves account in Achatess is very big, thus its is hard
Degree is smaller with the common Achatess of density ratio and calcedony.So saying to a certain extent, seven color Achatess are not calcedonies purely,
But the complex jade being collectively formed by calcedony and its wrappage.
Seven color Achatess jade have gorgeous color and especially abundant beautiful pattern, almost have the various of the Nature
Color, red, yellow, blue, green, black, white shades of colour and its change color have, beautiful in colour, extremely eye-catching, beautiful.Seven color Achatess
The shape of inclusion enclave has integrity, maintains own form and color in Achatess colloid, and unlike other Achatess
It is in mutually molten state.Transparent glassy of the colloid of seven color Achatess, the parcel shape of the inside, color are very clear.
Part artificial stone manufacturing enterprise, applies natural Achatess material, imitates out its abundant gorgeous color and distinctive
Inclusion enclave, prepares colorful jade sheet material, and mohs hardness, between 5.5-6, has preferable toughness, thoroughly spends substantially, beautiful sense
Stronger.For example, a kind of jade artificial stone plate that the patent of invention of Publication No. CN102775092A provides and preparation method thereof,
Artificial stone plate's formula consists of：Unsaturated polyester resin 28%～30%, aluminium hydroxide 40%～65%, is ground into 1～5 centimetre
The shell 5%～30% of particle diameter, cobalt naphthenate 0.02%～0.04%, methyl ethyl ketone peroxide 0.03%～0.05%, pigment paste
1%～2%, above-mentioned for mass percent, obtained sheet material is as shown in Figure 1；But, in the colorful artificial stone of existing preparation,
Color boundary is fuzzy, and definition is inadequate, and acutance is relatively low.
Content of the invention
The invention provides beautiful colorful artificial stone of a kind of imitative seven color Achatess and preparation method thereof, this colorful artificial stone color
Sharpness of border, possesses higher acutance, and color is gorgeous.The concrete technical scheme of the present invention is as follows：
A kind of beautiful colorful artificial stone of imitative seven color Achatess, described colorful artificial stone includes at least one mass-tone material and at least
The auxiliary colorant of three kinds of different colours, and the accounting of described mass-tone material should be no less than 30%；
In described mass-tone material and auxiliary colorant, its formula composition includes by weight percentage：
In the present invention, selection granularity is the agate powder of 425～600 mesh, in colorant harmonic process, can reduce agate powder
Sedimentation, can suppress the mobility of colorant simultaneously；More preferably granularity is the agate powder of 500～600 mesh；Preferably employ granularity
For the agate powder of 600 mesh, to obtain the balance between sedimentation and mobility.
In addition, the solid content adopting is higher than 60% accelerator, it is more that solid content height represents effective curing agent component, is beneficial to
Lifting fixed line speed, can stop the over-mixed of different colours colorant so that the artificial stone sharpness of border that ultimately forms；Preferably
Using solid content 75～80% accelerator.
As preferred, in described mass-tone material, the viscosity of unsaturated polyester resin is 1350～1550mPa s, described auxiliary
In colorant, the viscosity of unsaturated polyester resin is 1800～2200mPa s.
The viscosity of resin also can affect the mass-tone material and auxiliary colorant mobility in mixed process, in the present invention, mass-tone material
The viscosity of resin is less than the viscosity of resin in auxiliary colorant, on the one hand can reduce mobility and the mixed characteristic of auxiliary colorant, the opposing party
Face, the mass-tone material with stronger mobility can form parcel to auxiliary colorant in mixed process, thus being formed similar to seven color agates
The inclusion enclave of Nao.
As preferred, in described mass-tone material, its formula composition includes by weight percentage：
In described auxiliary colorant, its formula composition includes by weight percentage：
In the present invention, without mill base in mass-tone material, keep the color of unsaturated polyester resin itself, add in auxiliary colorant
Mill base forms the auxiliary colorant of monochrome, and the color for making artificial stone is more gorgeous, generally will prepare the auxiliary colorant of four kinds of colors.
The invention also discloses a kind of preparation method of above-mentioned colorful artificial stone, comprise the steps：
1) it is respectively configured mass-tone material and the auxiliary colorant of at least three kinds of different colours；
2) simultaneously by described mass-tone material and auxiliary colorant injection static mixer, the velocity ratio of injection be equal to mass-tone material and
The weight ratio of various auxiliary colorants；
3) compound that static mixer flows out is poured in the mould that temperature is 40-50 DEG C；
4) in naturalness standing solidification 12～24 hours, die sinking obtains the stone after molding；
5) surface pattern according to stone, is cut along the position parallel with lines tangent line, and should avoid in cutting
Bulk monochrome mottle, obtains colorful artificial stone.
The present invention is mixed to mass-tone material and auxiliary colorant using static mixer, and relied on is the mobility of colorant,
Make colorant still have more clearly border upon mixing, further, control the velocity ratio of each colorant injection to be equal to weight
Colorant distribution is more uniform for ratio.
In addition, when cutting to the stone after being formed, should be according to the cylinder pattern of block faces or lines, Yi Jihuo
According to the extension direction of lines, bulk monochrome mottle or a certain monochromatic boundary curve should be avoided in cutting, should protect as far as possible
Hold line of cut with lines or pattern oblique so that the stone material distribution of color after cutting is uniform.
As preferred, in single molding, prepare the weight of mass-tone material and auxiliary colorant and 2 tons should be no less than, if single
Amount very little, the aesthetic property after cutting is not good enough.
As preferred, after preparing described mass-tone material and auxiliary colorant, described mass-tone material and auxiliary colorant are put
In temperature be -2～2 DEG C environment in, and keep 10～60 minutes, more preferably 10～30 minutes, to reduce colorant
Mobility, hybrid retaining layer EDS maps, thus forming the lines of sharpness of border, color is gorgeous, good visual effect.
Color as preferred, described mass-tone material is yellow, and the color of described auxiliary colorant is redness, kermesinus, indigo plant
Color, green or white.
As preferred, in described mass-tone material, its formula composition includes by weight percentage：
In described auxiliary colorant, its formula composition includes by weight percentage：
It is preferably FL-885 resin, FL-885N resin or FL- as preferred, described unsaturated polyester resin
885IN resin.
Artificial stone prepared by the present invention can simulate the beautiful multi colour effect of seven color Achatess, and internally carries out inclusion enclave, color
Color sharpness of border, possesses higher acutance, and color is gorgeous.
Brief description
Fig. 1 is the design sketch of existing artificial jade's sheet material；
Fig. 2 is the design sketch of the artificial stone in embodiment 2；
Fig. 3 is the design sketch of the artificial stone in embodiment 2.
Specific embodiment
With reference to specific embodiment, the present invention is described further.
Embodiment 1
(1) configuration mass-tone material and auxiliary colorant：
The unsaturated FL-885N resin (purchased from Jiangsu FuLing Chemical Industry Co., Ltd) of 380kg, granularity is added in blender
For the agate powder 600kg of 500～600 mesh, the cyclohexanone peroxide of 1kg and the cobalt naphthenate of 19kg, led after uniform stirring
Colorant.
Add the unsaturated FL-885N resin of 175kg in blender, granularity is the agate powder 300kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the red mill base of 15kg, obtain red auxiliary color after uniform stirring
Material；
Add the unsaturated FL-885N resin of 175kg in blender, granularity is the agate powder 300kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the blue mill base of 15kg, obtain blue auxiliary color after uniform stirring
Material；
Add the unsaturated FL-885N resin of 175kg in blender, granularity is the agate powder 300kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the white colorant of 15kg, obtain white auxiliary color after uniform stirring
Material.
After preparing mass-tone material and auxiliary colorant, colorant is placed in the environment that temperature is -2～2 DEG C, keeps 10 points
Clock.
(2) simultaneously by mass-tone material and auxiliary colorant injection static mixer, the velocity ratio of injection is equal to mass-tone material and various
The weight ratio of auxiliary colorant；
(3) compound that static mixer flows out is poured in the mould that temperature is 40-50 DEG C；
(4) in naturalness standing solidification 12～24 hours, die sinking obtains the stone after molding；
(5) surface pattern according to stone, is cut along the position parallel with lines tangent line, and should avoid in cutting
Bulk monochrome mottle, obtains colorful artificial stone.
Embodiment 2
(1) configuration mass-tone material and auxiliary colorant：
The unsaturated FL-885N resin (purchased from Jiangsu FuLing Chemical Industry Co., Ltd) of 400kg, granularity is added in blender
For the agate powder 570kg of 500～600 mesh, the cyclohexanone peroxide of 1kg and the cobalt naphthenate of 29kg, led after uniform stirring
Colorant.
Add the unsaturated FL-885N resin of 200kg in blender, granularity is the agate powder 275kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the red mill base of 15kg, obtain red auxiliary color after uniform stirring
Material；
Add the unsaturated FL-885N resin of 200kg in blender, granularity is the agate powder 275kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the blue mill base of 15kg, obtain blue auxiliary color after uniform stirring
Material；
Add the unsaturated FL-885N resin of 200kg in blender, granularity is the agate powder 275kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the white colorant of 15kg, obtain white auxiliary color after uniform stirring
Material.
After preparing mass-tone material and auxiliary colorant, colorant is placed in the environment that temperature is -2～2 DEG C, keeps 60 points
Clock.
(2) simultaneously by mass-tone material and auxiliary colorant injection static mixer, the velocity ratio of injection is equal to mass-tone material and various
The weight ratio of auxiliary colorant；
(3) compound that static mixer flows out is poured in the mould that temperature is 40-50 DEG C；
(4) in naturalness standing solidification 12～24 hours, die sinking obtains the stone after molding；
(5) surface pattern according to stone, is cut along the position parallel with lines tangent line, and should avoid in cutting
Bulk monochrome mottle, obtains colorful artificial stone, wherein pattern as shown in Fig. 2 image color lump is evenly distributed, sharpness of border.
Embodiment 3
(1) configuration mass-tone material and auxiliary colorant：
The unsaturated FL-885N resin (purchased from Jiangsu FuLing Chemical Industry Co., Ltd) of 400kg, granularity is added in blender
For the agate powder 570kg of 100 mesh, the cyclohexanone peroxide of 1kg and the cobalt naphthenate of 29kg, after uniform stirring, obtain mass-tone material.
Add the unsaturated FL-885N resin of 200kg in blender, granularity is the agate powder 275kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the red mill base of 15kg, obtain red auxiliary color after uniform stirring
Material；
Add the unsaturated FL-885N resin of 200kg in blender, granularity is the agate powder 275kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the blue mill base of 15kg, obtain blue auxiliary color after uniform stirring
Material；
Add the unsaturated FL-885N resin of 200kg in blender, granularity is the agate powder 275kg of 500～600 mesh,
The cyclohexanone peroxide of 0.5kg and the cobalt naphthenate of 9.5kg, and the white colorant of 15kg, obtain white auxiliary color after uniform stirring
Material.
(2) simultaneously by mass-tone material and auxiliary colorant injection static mixer, the velocity ratio of injection is equal to mass-tone material and various
The weight ratio of auxiliary colorant；
(3) compound that static mixer flows out is poured in the mould that temperature is 40-50 DEG C；
(4) in naturalness standing solidification 12～24 hours, die sinking obtains the stone after molding；
(5) surface pattern according to stone, is cut along the position parallel with lines tangent line, and should avoid in cutting
Bulk monochrome mottle, obtains colorful artificial stone, wherein pattern as shown in figure 3, in figure color lump boundary module, and mass-tone material expands
Divergence not, more concentrate by distribution.
The foregoing is only the preferable implementation example of the present invention, be not limited to the present invention, all the present invention spirit and
Within principle, any modification, equivalent substitution and improvement made etc., should be included within the scope of the present invention.
Claims (9)
1. a kind of beautiful colorful artificial stone of imitative seven color Achatess is it is characterised in that described colorful artificial stone includes at least one master
The auxiliary colorant of colorant and at least three kinds of different colours, and the accounting of described mass-tone material should be no less than 30%；
In described mass-tone material and auxiliary colorant, its formula composition includes by weight percentage：
2. as claimed in claim 1 colorful artificial stone it is characterised in that in described mass-tone material unsaturated polyester resin viscosity
For 1350～1550mPa s, in described auxiliary colorant, the viscosity of unsaturated polyester resin is 1800～2200mPa s.
3. as claimed in claim 1 colorful artificial stone it is characterised in that in described mass-tone material, its formula composition is by weight
Amount percentages include：
In described auxiliary colorant, its formula composition includes by weight percentage：
4. a kind of preparation method of colorful artificial stone as described in any one as claims 1 to 3 is it is characterised in that include following walking
Suddenly：
1) it is respectively configured mass-tone material and the auxiliary colorant of at least three kinds of different colours；
2) simultaneously by described mass-tone material and auxiliary colorant injection static mixer, the velocity ratio of injection is equal to mass-tone material and various
The weight ratio of auxiliary colorant；
3) compound that static mixer flows out is poured in the mould that temperature is 40-50 DEG C；
4) in naturalness standing solidification 12～24 hours, die sinking obtains the stone after molding；
5) surface pattern according to stone, is cut along the position parallel with lines tangent line, and should avoid bulk in cutting
Monochromatic mottle, obtains colorful artificial stone.
5. the preparation method of colorful artificial stone it is characterised in that in single molding, prepares mass-tone material as claimed in claim 4
With the weight of auxiliary colorant and 2 tons should be no less than.
6. as claimed in claim 4 colorful artificial stone preparation method it is characterised in that prepare described mass-tone material and
After auxiliary colorant, described mass-tone material and auxiliary colorant are placed in the environment that temperature is -2～2 DEG C, and keep 10～60 minutes.
7. as claimed in claim 4 the preparation method of colorful artificial stone it is characterised in that the color of described mass-tone material is Huang
Color, the color of described auxiliary colorant is redness, kermesinus, blueness, green or white.
8. as claimed in claim 4 the preparation method of colorful artificial stone it is characterised in that in described mass-tone material, it is joined
Fang Zucheng includes by weight percentage：
In described auxiliary colorant, its formula composition includes by weight percentage：
9. as claimed in claim 8 the preparation method of colorful artificial stone it is characterised in that described unsaturated polyester resin is
FL-885N resin.