CN106381717A - Multifunctional outdoor foaming coating material and preparation method - Google Patents
Multifunctional outdoor foaming coating material and preparation method Download PDFInfo
- Publication number
- CN106381717A CN106381717A CN201610757200.0A CN201610757200A CN106381717A CN 106381717 A CN106381717 A CN 106381717A CN 201610757200 A CN201610757200 A CN 201610757200A CN 106381717 A CN106381717 A CN 106381717A
- Authority
- CN
- China
- Prior art keywords
- foaming
- coating material
- parts
- base fabric
- foaming layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a multifunctional outdoor foaming coating material and a preparation method and belongs to the field of chemical engineering in macromolecule. The multifunctional outdoor foaming coating material comprises a base cloth weaved from a high-strength polyester filament. The base cloth is externally coated to form an adhesive layer and is internally coated to form a foaming layer. The adhesive layer is made from PVC resin, and the foaming layer is molded by taking PVC paste resin special for foaming as a main raw material with a plasticizer, a foaming agent, a fire retardant, a viscosity reducer, a filler and other auxiliary materials added through foaming. The preparation method of the multifunctional outdoor foaming coating material comprises the following steps: 1) preparation of an adhesive layer coating liquid; 2) preparation of a foaming layer coating liquid; 3) coating of an adhesive layer; 4) foaming molding; and 5) cooling. The prepared coating material is large in thickness and good in softness, has multiple functions of good flame retardance, corrosion resistance, shock isolation, and high tensile strength, and can be applied to the fields of transportation of chemical materials, building of outdoor awning houses and protection of caravan glass.
Description
Technical field
The invention belongs to macromolecule chemical industry technical field, it is related to a kind of Multifunction outdoor intumescent coating material and preparation side
Method.
Background technology
Conventional coating material thickness is usually no more than 0.2cm, very slim, though the performance such as waterproof is good, due to too thin
It is only used for laying or show and colour, now because industrial chemicals transport or outdoor fluffy room is built, caravan glass protection needs thickness simultaneously
And there is the demand such as multi-functional, conventional coating material cannot meet requirement.As Chinese patent CN104494257A discloses one
Plant paulin room heat-insulation foam material and preparation method thereof；And as Chinese patent CN104494264A discloses a kind of paulin room with resistance to
Cold heat-insulation foam material and preparation method thereof, existing paulin room expanded material is in insulation, heat-insulated, its anti-noise, cold-proof, anti-ultraviolet
The aspects such as radiation can not effectively balance, and complex manufacturing, and the product environmental requirement being formed is not up to standard, and feel is poor, sternly
Have impact on its development and application, this is those skilled in the art's problem demanding prompt solution again.
Content of the invention
The purpose of the present invention is to there are the problems referred to above for existing technology it is proposed that a kind of Multifunction outdoor intumescent coating
Material, thickness is more than conventional coating material, and flexibility is good, industrial chemicals transport can be applied to, outdoor fluffy room build with
And the field such as caravan glass protection.
The purpose of the present invention can be realized by following technical proposal：
Multifunction outdoor intumescent coating material, including base fabric, base fabric is formed by high tenacity polyester filament weaving, the outer surface of base fabric
Coating forms glue-line, and the inner surface coating of base fabric forms foaming layer, and glue-line adopts polyvinyl chloride resin, and foaming layer is with the special PVC paste that foams
Resin is main material, adds plasticizer, foaming agent, fire retardant, thinner, filler and other adjuvant foamings.
Base fabric is formed using high tenacity polyester filament weaving, and intensity is high, and tear-resistant performance is good, and when using, base fabric is towards the external world
Side be glue-line, there is excellent water resistance, sleet in external environment can be resisted and invade.Foaming layer is in base fabric
Inner side, substantially increases the thickness of this coating material so that the intensity of this coating material is improved.In addition foaming layer makes
Obtain this coating material to be soft and there is elasticity, protective glass is served with good antihunt action, open air is built with fluffy room and rises
To preferably anti-sound insulation, reinforcing etc. effect.Add fire retardant in foaming layer masking liquid, make this coating material have fire resistance,
Security performance is high, can be applied to open air.
In above-mentioned Multifunction outdoor intumescent coating material, foaming layer masking liquid includes the component of following weight portion：60～
100 parts of foaming special PVC paste resins；80～120 parts of plasticizers；1～10 part of stabilizer；10～20 parts of foaming agent；30～90 parts
Fire retardant；40～80 parts of filleies；10～40 parts of PB-1000；5～20 parts of XP-140；5～20 parts of PSM-31；5～20 parts of PR-
415.
In above-mentioned Multifunction outdoor intumescent coating material, foaming layer masking liquid also includes 1～10 part of UV absorbent.
In above-mentioned Multifunction outdoor intumescent coating material, UV absorbent is UV-531.
In above-mentioned Multifunction outdoor intumescent coating material, plasticizer is DINP, and stabilizer is potassium zinc, and foaming agent is
AC-5000, filler is the ground calcium carbonate of 800 mesh.
In above-mentioned Multifunction outdoor intumescent coating material, fire retardant include 10～30 parts of antimony oxides, 20～50
Part aluminium hydroxide and 1～10 part of DPK.
In above-mentioned Multifunction outdoor intumescent coating material, the fineness of high tenacity polyester filament is 1000D.
In above-mentioned Multifunction outdoor intumescent coating material, the thickness of foaming layer is 0.3～0.6cm.
In above-mentioned Multifunction outdoor intumescent coating material, base fabric is by the woven anti-wicking screen cloth of high tenacity polyester filament.
Another object of the present invention is to there are the problems referred to above for existing technology it is proposed that a kind of Multifunctional household outgoing
The preparation method of bubble coating material, the coating material thus prepared has several functions, can be widely applied for open air.
Another object of the present invention can be realized by following technical proposal：
The preparation method of Multifunction outdoor intumescent coating material, comprises the steps：
1) prepare glue-line masking liquid：Weigh each raw material by glue-line masking liquid each component weight ratio, then put into stainless steel
In, heated and stirred mixes 25～40 minutes, obtains glue-line solution；
2) prepare foaming layer masking liquid：Weigh each raw material by foaming layer masking liquid each component weight ratio, then put into mixing
In container, stirring mixing 10～30 minutes, obtain foaming layer solution；
3) glue-line coating：Base fabric is pressed using one group of heated steel roll, base fabric is preheated, preheating temperature is 100～150
DEG C, after preheating, base fabric is sent into coating machine, through scraper in the front surface coated glue-line masking liquid of base fabric, send in baking oven after coating and dry
And plasticizing, drying fusion time is 30～50 seconds, and oven temperature is 170～250 DEG C, forms glue-line after plasticizing；
4) foaming：Base fabric is sent into coating machine, coats foaming layer masking liquid through scraper in base reverse of the cloth, dry foaming
2～5 minutes, to its roll-in in foaming process, after drying, form foaming layer；
5) cool down：Roll-in is carried out using one group of chill roll, after cooling, obtains Multifunction outdoor intumescent coating material.
Compared with prior art, the present invention has the advantage that：
Through coating for expanded material after, its intensity is high, and tearing strength is good, further increases its service life, and so that product is had
Have that flexibility is good, high fire-retardance, that corrosion-resistant, shockproof, tensile strength is high etc. is multi-functional, can be widely applied for industrial chemicals transport,
The fields such as outdoor fluffy room is built, caravan glass protection.
Brief description
Fig. 1 is the structural representation of the Multifunction outdoor intumescent coating material of the present invention.
In figure, 1, base fabric；2nd, glue-line；3rd, foaming layer.
Specific embodiment
The following is the specific embodiment of the present invention and combine accompanying drawing, technical scheme is further described,
But the present invention is not limited to these embodiments.
As shown in figure 1, the invention provides a kind of Multifunction outdoor intumescent coating material, including base fabric 1, base fabric 1 is by height
Strong dacron thread weaving forms, and the outer surface coating of base fabric 1 forms glue-line 2, and the inner surface coating of base fabric 1 forms foaming layer 3, glue-line
Using polyvinyl chloride resin, foaming layer 3, with the special PVC paste resin that foams as main material, adds plasticizer, foaming agent, fire retardant, viscosity reduction
Agent, filler and other adjuvant foamings.
It is noted that base fabric 1 is formed using high tenacity polyester filament weaving, intensity is high, and tear-resistant performance is good, is using
When, base fabric 1 is glue-line 2 towards extraneous side, and glue-line 2 adopts polyvinyl chloride resin, has excellent water resistance, can resist outer
Sleet in boundary's environment invades.Foaming layer 3 is in the inner side of base fabric 1, and masking liquid used by foaming layer 3 can after sufficient stirring
Automatic foaming, defines thick foaming layer, the thickness of foaming layer 3 after the inner surface painting of base fabric 1 is covered with this foaming layer masking liquid
0.3-0.6cm can be reached, therefore substantially increase the thickness of this coating material so that the intensity of this coating material obtains
Lifting.In addition foaming layer 3 makes this coating material be soft and have elasticity, and protective glass is served with shockproof work well
With open air being built with fluffy room and playing preferably anti-sound insulation, reinforcing etc. effect.Add fire retardant in foaming layer masking liquid, make this painting
Layer material has fire resistance, and security performance is high, can be applied to open air.
Specifically, foaming layer masking liquid includes the component of following weight portion：60～100 parts of foaming special PVC paste resins；80～
120 parts of plasticizers；1～10 part of stabilizer；10～20 parts of foaming agent；30～90 parts of fire retardants；40～80 parts of filleies；10～40
Part PB-1000；5～20 parts of XP-140；5～20 parts of PSM-31；5～20 parts of PR-415.
Further, foaming layer masking liquid also includes 1～10 part of UV absorbent, and UV absorbent adopts UV-
531, make this coating material have anti-ultraviolet property.
Preferably, plasticizer is DINP, and stabilizer is potassium zinc, and foaming agent is AC-5000, and filler is the heavy of 800 mesh
Calcium Carbonate.
Specifically, fire retardant includes 10～30 parts of antimony oxides, 20～50 parts of aluminium hydroxide and 1～10 part of DPK.Pass through
The proportioning mixing of three kinds of fire retardants, makes this coating material have excellent fire resistance.
It is noted that base fabric 1 is by the woven anti-wicking screen cloth of 1000D high tenacity polyester filament, tensile strength is high, and has
There is fungicidal properties.
Embodiment one
The preparation method of Multifunction outdoor intumescent coating material, comprises the following steps：
1) prepare glue-line masking liquid：Weigh each raw material by glue-line masking liquid each component weight ratio, then put into stainless steel
In, heated and stirred mixes 25 minutes, obtains glue-line solution；
2) prepare foaming layer masking liquid：Weigh each raw material by foaming layer masking liquid each component weight ratio, then put into mixing
In container, stirring mixing 10 minutes, obtain foaming layer solution；
Foaming layer masking liquid includes the component of following weight portion：
PVC-2215C：60 parts； DINP：80 parts；
Potassium zinc：3 parts； AC-5000：15 parts；
Antimony oxide：10 parts；Aluminium hydroxide：20 parts；
UV-531：1 part；Triple superphosphate (800 mesh)：50 parts
PB-1000：10 parts； DPK:3 parts；
XP-140:8 parts； PSM-31：8 parts；
PR-415：8 parts；
3) glue-line coating：Base fabric 1 is pressed using one group of heated steel roll, base fabric 1 is preheated, preheating temperature is 100 DEG C,
After preheating, base fabric 1 is sent into coating machine, through scraper in the front surface coated glue-line masking liquid of base fabric 1, send in baking oven after coating and dry
And plasticizing, drying fusion time is 30 seconds, and oven temperature is 170～250 DEG C, forms glue-line 2 after plasticizing；
4) foaming：Base fabric 1 is sent into coating machine, coats foaming layer masking liquid through scraper in the reverse side of base fabric 1, dry and send out
Bubble 3 minutes, to its roll-in in foaming process, forms foaming layer 3 after drying；
5) cool down：Roll-in is carried out using one group of chill roll, after cooling, obtains Multifunction outdoor intumescent coating material.
This technique is first front surface coated in base fabric 1, and reverse side is then applied in base fabric 1 reverse side with expanded material and directly sent out
Bubble, is carried out with roll-in in foaming process uniformly simultaneously and balances, by roller pressure, tension force, viscosity, temperature, speed, infrared ray
Deng control and adjustment, make product uniform in foaming, thickness reach ideal effect, and flexibility be good, high fire-retardance, resistance to so that product is had
It is multi-functional that burn into is shockproof, tensile strength is high etc..Wherein foaming layer 3 can reach that M2 level is fire-retardant and REACH environmental protection standard, handss
Sense is moderate, and foam mesh uniform and smooth.
Embodiment two
The preparation method of Multifunction outdoor intumescent coating material, comprises the following steps：
1) prepare glue-line masking liquid：Weigh each raw material by glue-line masking liquid each component weight ratio, then put into stainless steel
In, heated and stirred mixes 30 minutes, obtains glue-line solution；
2) prepare foaming layer masking liquid：Weigh each raw material by foaming layer masking liquid each component weight ratio, then put into mixing
In container, stirring mixing 20 minutes, obtain foaming layer solution；
Foaming layer masking liquid includes the component of following weight portion：
PVC-2215C：80 parts； DINP：100 parts；
Potassium zinc：5 parts； AC-5000：18 parts；
Antimony oxide：15 parts；Aluminium hydroxide：25 parts；
UV-531：2 parts；Triple superphosphate (800 mesh)：60 parts
PB-1000：20 parts； DPK:5 parts；
XP-140:10 parts； PSM-31：10 parts；
PR-415：10 parts；
3) glue-line coating：Base fabric 1 is pressed using one group of heated steel roll, base fabric 1 is preheated, preheating temperature is 120 DEG C,
After preheating, base fabric 1 is sent into coating machine, through scraper in the front surface coated glue-line masking liquid of base fabric 1, send in baking oven after coating and dry
And plasticizing, drying fusion time is 40 seconds, and oven temperature is 170～250 DEG C, forms glue-line 2 after plasticizing；
4) foaming：Base fabric 1 is sent into coating machine, coats foaming layer masking liquid through scraper in the reverse side of base fabric 1, dry and send out
Bubble 4 minutes, to its roll-in in foaming process, forms foaming layer 3 after drying；
5) cool down：Roll-in is carried out using one group of chill roll, after cooling, obtains Multifunction outdoor intumescent coating material.
This technique is first front surface coated in base fabric 1, and reverse side is then applied in base fabric 1 reverse side with expanded material and directly sent out
Bubble, is carried out with roll-in in foaming process uniformly simultaneously and balances, by roller pressure, tension force, viscosity, temperature, speed, infrared ray
Deng control and adjustment, make product uniform in foaming, thickness reach ideal effect, and flexibility be good, high fire-retardance, resistance to so that product is had
It is multi-functional that burn into is shockproof, tensile strength is high etc..Wherein foaming layer 3 can reach that M2 level is fire-retardant and REACH environmental protection standard, handss
Sense is moderate, and foam mesh uniform and smooth.
Embodiment three
The preparation method of Multifunction outdoor intumescent coating material, comprises the following steps：
1) prepare glue-line masking liquid：Weigh each raw material by glue-line masking liquid each component weight ratio, then put into stainless steel
In, heated and stirred mixes 40 minutes, obtains glue-line solution；
2) prepare foaming layer masking liquid：Weigh each raw material by foaming layer masking liquid each component weight ratio, then put into mixing
In container, stirring mixing 30 minutes, obtain foaming layer solution；
Foaming layer masking liquid includes the component of following weight portion：
PVC-2215C：100 parts； DINP：120 parts；
Potassium zinc：8 parts； AC-5000：20 parts；
Antimony oxide：20 parts；Aluminium hydroxide：35 parts；
UV-531：5 parts；Triple superphosphate (800 mesh)：80 parts
PB-1000：30 parts； DPK:7 parts；
XP-140:15 parts； PSM-31：15 parts；
PR-415：15 parts；
3) glue-line coating：Base fabric 1 is pressed using one group of heated steel roll, base fabric 1 is preheated, preheating temperature is 150 DEG C,
After preheating, base fabric 1 is sent into coating machine, through scraper in the front surface coated glue-line masking liquid of base fabric 1, send in baking oven after coating and dry
And plasticizing, drying fusion time is 50 seconds, and oven temperature is 170～250 DEG C, forms glue-line 2 after plasticizing；
4) foaming：Base fabric 1 is sent into coating machine, coats foaming layer masking liquid through scraper in the reverse side of base fabric 1, dry and send out
Bubble 5 minutes, to its roll-in in foaming process, forms foaming layer 3 after drying；
5) cool down：Roll-in is carried out using one group of chill roll, after cooling, obtains Multifunction outdoor intumescent coating material.
This technique is first front surface coated in base fabric 1, and reverse side is then applied in base fabric 1 reverse side with expanded material and directly sent out
Bubble, is carried out with roll-in in foaming process uniformly simultaneously and balances, by roller pressure, tension force, viscosity, temperature, speed, infrared ray
Deng control and adjustment, make product uniform in foaming, thickness reach ideal effect, and flexibility be good, high fire-retardance, resistance to so that product is had
It is multi-functional that burn into is shockproof, tensile strength is high etc..Wherein foaming layer 3 can reach that M2 level is fire-retardant and REACH environmental protection standard, handss
Sense is moderate, and foam mesh uniform and smooth.
The key technical indexes of this Multifunction outdoor intumescent coating material：
1st, fracture strength：(warp/latitude) >=2500N/5cm；
2nd, tearing strength：(warp/latitude) >=300N；
3rd, peel strength：≥90N/5cm；
4th, fire resistance：M2；
5th, grammes per square metre：1000g.
Specific embodiment described herein is only explanation for example to present invention spirit.The affiliated technology of the present invention is led
The technical staff in domain can be made various modifications or supplement or replaced using similar mode to described specific embodiment
Generation, but the spirit without departing from the present invention or surmount scope defined in appended claims.
Although more employing base fabric 1 herein；Glue-line 2；Foaming layer 3 grade term, but be not precluded from using other terms
Probability.It is used for the purpose of more easily describing and explaining the essence of the present invention using these terms；It is construed as appointing
A kind of what additional restriction is all contrary with spirit of the present invention.
Claims (10)
1. it is characterised in that including base fabric, base fabric is formed Multifunction outdoor intumescent coating material by high tenacity polyester filament weaving, base
The outer surface coating of cloth forms glue-line, and the inner surface coating of base fabric forms foaming layer, and glue-line adopts polyvinyl chloride resin, and foaming layer is to send out
Bubble special PVC paste resin is main material, adds plasticizer, foaming agent, fire retardant, thinner, filler and other adjuvants to send out
Soak type.
2. Multifunction outdoor intumescent coating material according to claim 1 it is characterised in that foaming layer masking liquid include following
The component of weight portion：60～100 parts of foaming special PVC paste resins；80～120 parts of plasticizers；1～10 part of stabilizer；10～20
Part foaming agent；30～90 parts of fire retardants；40～80 parts of filleies；10～40 parts of PB-1000；5～20 parts of XP-140；5～20 parts
PSM-31；5～20 parts of PR-415.
3. Multifunction outdoor intumescent coating material according to claim 2 is it is characterised in that foaming layer masking liquid also includes 1
～10 parts of UV absorbent.
4. Multifunction outdoor intumescent coating material according to claim 3 is it is characterised in that UV absorbent is UV-
531.
5. Multifunction outdoor intumescent coating material according to claim 2 is it is characterised in that plasticizer is DINP, stable
Agent is potassium zinc, and foaming agent is AC-5000, and filler is the ground calcium carbonate of 800 mesh.
6. Multifunction outdoor intumescent coating material according to claim 2 is it is characterised in that fire retardant includes 10～30 parts
Antimony oxide, 20～50 parts of aluminium hydroxide and 1～10 part of DPK.
7. Multifunction outdoor intumescent coating material according to claim 1 is it is characterised in that the fineness of high tenacity polyester filament is
1000D.
8. Multifunction outdoor intumescent coating material according to claim 1 is it is characterised in that the thickness of foaming layer is 0.3
～0.6cm.
9. Multifunction outdoor intumescent coating material according to claim 1 is it is characterised in that base fabric is by high tenacity polyester filament
Woven anti-wicking screen cloth.
10. the preparation method of the Multifunction outdoor intumescent coating material as described in claim 1 to 9 any claim, it is special
Levy and be, comprise the steps：
1) prepare glue-line masking liquid：Weigh each raw material by glue-line masking liquid each component weight ratio, then put in stainless steel, plus
Thermal agitation mixes 25～40 minutes, obtains glue-line solution；
2) prepare foaming layer masking liquid：Weigh each raw material by foaming layer masking liquid each component weight ratio, then put into stainless steel
In, stirring mixing 10～30 minutes, obtain foaming layer solution；
3) glue-line coating：Base fabric is pressed using one group of heated steel roll, base fabric is preheated, preheating temperature is 100～150 DEG C,
After preheating, base fabric is sent into coating machine, through scraper base fabric front surface coated glue-line masking liquid, after coating send into baking oven in dry and
Plasticizing, drying fusion time is 30～50 seconds, and oven temperature is 170～250 DEG C, forms glue-line after plasticizing；
4) foaming：Base fabric is sent into coating machine, coats foaming layer masking liquid through scraper in base reverse of the cloth, dry foaming 2～5
Minute, to its roll-in in foaming process, after drying, form foaming layer；
5) cool down：Roll-in is carried out using one group of chill roll, after cooling, obtains Multifunction outdoor intumescent coating material.