CN106318175A - Paint for outer cover of automobile radiator - Google Patents
Paint for outer cover of automobile radiator Download PDFInfo
- Publication number
- CN106318175A CN106318175A CN201610667685.4A CN201610667685A CN106318175A CN 106318175 A CN106318175 A CN 106318175A CN 201610667685 A CN201610667685 A CN 201610667685A CN 106318175 A CN106318175 A CN 106318175A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- paint
- radiator
- enclosing cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides paint for an outer cover of an automobile radiator, and relates to the technical field of automobile part machining and producing. The paint is characterized by being prepared from, by weight, 5 parts of organic silicon resin, 2 parts of allyl heptanoate, 9 parts of an anti-aging agent, 1 part of triethanolamine, 2 parts of hollow microbeads, 1 part of cobalt naphthenate, 0.5 part of asbestos, 7 parts of waterborne polyurethane, 2 parts of shell powder, 2 parts of calcium silicate powder, 1 part of benzalkonium chloride, 2 parts of iron powder, 1 part of triallylisocyanurate, 2 parts of nano-titanium dioxide, 1 part of a titanate coupling agent TMC-TTS and 3 parts of auxiliaries. The paint is reasonable in method and proportion and convenient to operate.
Description
Technical field:
The present invention relates to auto parts and components processing technical field, be specifically related to the painting that a kind of radiator enclosing cover uses
Material.
Background technology:
To vapour in country of China newest standards " automobile and the term and definition of trailer type " (GB/T 3730.1 2001)
Car is defined below: by power drive, has the vehicle of the non-track carrying of 4 or more than 4 wheels, is mainly used in: carrying
Personnel and (or) goods；Traction carrying personnel and (or) the vehicle of goods；Specific use.
Radiator, also known as radiator, is critical part in automobile cooling system；Function is to distribute heat, and cooling water is at water
Absorbing heat in set, after flowing to radiator, heat disperses, and returns circulation in water jacket, reaches homoiothermic.It it is the group of automobile engine
Become part.
And on radiator, having a lid, this lid contacts with water, steam for a long time, and corrosion the most easily occurs in the time
Situation, if process not in time, easily causes harm, damage.
Summary of the invention:
The technical problem to be solved be to overcome existing technological deficiency provide a kind of method rationally, proportioning closes
The coating that reason, easy to operate a kind of radiator enclosing cover use.
The technical problem to be solved uses following technical scheme to realize:
The coating that a kind of radiator enclosing cover uses, it is characterised in that: it is made up of the material of following weight portion,
Organic siliconresin 5 parts, allyl heptanoate 2 parts, 9 parts of age resistor, triethanolamine 1 part, cenosphere 2 parts, aphthenic acids
Cobalt 1 part, 0.5 part of asbestos, aqueous polyurethane 7 parts, conch meal 2 parts, calcium silicate powder 2 parts, benzalkonium chloride 1 part, iron powder 2 parts, triolefin
Propyl group isocyanuric acid ester 1 part, nano titanium oxide 2 parts, titanate coupling agent TMC-TTS1 part, auxiliary agent 3 parts；
Including following preparation process,
Above-mentioned material is put in milling apparatus by I, conventionally grinds 35 minutes, is subsequently adding material gross weight
The deionized water of 1/20, mix and blend 25 minutes；
II will grind after material be placed in the sealed environment of 5-11 DEG C standing 60 minutes；
Mixture in II is put into high-temperature heating 30 minutes in the smelting furnace of 100 DEG C by III, then takes out after 5 minutes and puts into shake
Swing concussion mixing 10 minutes in equipment, be subsequently adding 1/50 distilled water of material gross weight, continue concussion 10 minutes；
IV will stand after material put in high-speed mixing equipment the rotating speed dispersed with stirring according to 1400-1700 rev/min
60-75 minute, then compound is put in ball mill and carry out spheroidal graphite process in a conventional manner；
Described auxiliary agent is made up of the material of following weight portion,
Cornu rhinocerotis 1 part, Radix Scrophulariae 2 parts, Cortex Moutan 3 parts, Folium Sennae 4 parts, Radix Et Rhizoma Rhei 5 parts, Semen Platycladi 6 parts, Fructus Lycii 5 parts, Rhizoma Cibotii 4
Part, Folium et Ramulus Clerodendri Trichotomi 3 parts, 2 parts of Herba Ephedrae, Mirabilitum crystallina 1 part；
Preparation method: above-mentioned material is placed in sealing container airtight 3 hours, is placed under high light sudden and violent after then taking out
Shine 24 hours.
The invention have the benefit that I material cost is the highest, overweight financial burden will not be brought to enterprise；
II material is the most nontoxic, brings body harm will not to Producer, user；
III manufacture method is simple, technique is convenient, and volume production is convenient.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, enter below
One step illustrates the present invention.
The coating that a kind of radiator enclosing cover uses, it is characterised in that: it is made up of the material of following weight portion,
Organic siliconresin 5 parts, allyl heptanoate 2 parts, 9 parts of age resistor, triethanolamine 1 part, cenosphere 2 parts, aphthenic acids
Cobalt 1 part, 0.5 part of asbestos, aqueous polyurethane 7 parts, conch meal 2 parts, calcium silicate powder 2 parts, benzalkonium chloride 1 part, iron powder 2 parts, triolefin
Propyl group isocyanuric acid ester 1 part, nano titanium oxide 2 parts, titanate coupling agent TMC-TTS1 part, auxiliary agent 3 parts；
Including following preparation process,
Above-mentioned material is put in milling apparatus by I, conventionally grinds 35 minutes, is subsequently adding material gross weight
The deionized water of 1/20, mix and blend 25 minutes；
II will grind after material be placed in the sealed environment of 5-11 DEG C standing 60 minutes；
Mixture in II is put into high-temperature heating 30 minutes in the smelting furnace of 100 DEG C by III, then takes out after 5 minutes and puts into shake
Swing concussion mixing 10 minutes in equipment, be subsequently adding 1/50 distilled water of material gross weight, continue concussion 10 minutes；
IV will stand after material put in high-speed mixing equipment the rotating speed dispersed with stirring according to 1400-1700 rev/min
60-75 minute, then compound is put in ball mill and carry out spheroidal graphite process in a conventional manner；
Described auxiliary agent is made up of the material of following weight portion,
Cornu rhinocerotis 1 part, Radix Scrophulariae 2 parts, Cortex Moutan 3 parts, Folium Sennae 4 parts, Radix Et Rhizoma Rhei 5 parts, Semen Platycladi 6 parts, Fructus Lycii 5 parts, Rhizoma Cibotii 4
Part, Folium et Ramulus Clerodendri Trichotomi 3 parts, 2 parts of Herba Ephedrae, Mirabilitum crystallina 1 part；
Preparation method: above-mentioned material is placed in sealing container airtight 3 hours, is placed under high light sudden and violent after then taking out
Shine 24 hours.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (3)
1. the coating that a radiator enclosing cover uses, it is characterised in that: it is made up of the material of following weight portion,
Organic siliconresin 5 parts, allyl heptanoate 2 parts, 9 parts of age resistor, triethanolamine 1 part, cenosphere 2 parts, cobalt naphthenate 1
Part, 0.5 part of asbestos, aqueous polyurethane 7 parts, conch meal 2 parts, calcium silicate powder 2 parts, benzalkonium chloride 1 part, iron powder 2 parts, triallyl
Isocyanuric acid ester 1 part, nano titanium oxide 2 parts, titanate coupling agent TMC-TTS1 part, auxiliary agent 3 parts.
The coating that a kind of radiator enclosing cover the most according to claim 1 uses, it is characterised in that: include following preparation step
Suddenly,
Above-mentioned material is put in milling apparatus by I, conventionally grinds 35 minutes, is subsequently adding material gross weight 1/20
Deionized water, mix and blend 25 minutes；
II will grind after material be placed in the sealed environment of 5-11 DEG C standing 60 minutes；
Mixture in II is put into high-temperature heating 30 minutes in the smelting furnace of 100 DEG C by III, then takes out after 5 minutes and puts into concussion and set
Standby middle concussion mixing 10 minutes, is subsequently adding 1/50 distilled water of material gross weight, continues concussion 10 minutes；
IV will stand after material put in high-speed mixing equipment rotating speed dispersed with stirring 60-75 according to 1400-1700 rev/min
Minute, then compound is put in ball mill and carry out spheroidal graphite process in a conventional manner.
The coating that a kind of radiator enclosing cover the most according to claim 1 uses, it is characterised in that: described auxiliary agent is by following
The material of weight portion is made,
Cornu rhinocerotis 1 part, Radix Scrophulariae 2 parts, Cortex Moutan 3 parts, Folium Sennae 4 parts, Radix Et Rhizoma Rhei 5 parts, Semen Platycladi 6 parts, Fructus Lycii 5 parts, Rhizoma Cibotii 4 parts,
Folium et Ramulus Clerodendri Trichotomi 3 parts, 2 parts of Herba Ephedrae, Mirabilitum crystallina 1 part；
Preparation method: above-mentioned material is placed in sealing container airtight 3 hours, is placed on after then taking out under high light and is exposed to the sun 24
Individual hour.