CN106282725A - A kind of automotive hub material prescription - Google Patents
A kind of automotive hub material prescription Download PDFInfo
- Publication number
- CN106282725A CN106282725A CN201610666493.1A CN201610666493A CN106282725A CN 106282725 A CN106282725 A CN 106282725A CN 201610666493 A CN201610666493 A CN 201610666493A CN 106282725 A CN106282725 A CN 106282725A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnesium
- material prescription
- present
- automotive hub
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of automotive hub material prescription, include according to weight ratio: 30 ~ 36 parts of carbon steel, 20 ~ 30 parts of aluminum, 12 ~ 16 parts of manganese, 5 ~ 10 parts of magnesium, chromium 2 ~ 4 parts, titanium 1 ~ 3 part, 5 ~ 8 parts of magnesium and zinc oxide 12 ~ 18 parts.The advantage of a kind of automotive hub material prescription that the present invention provides is: the formulation ratio that the present invention provides, by the wheel hub that carbon steel, aluminum, manganese, magnesium, chromium, titanium, magnesium and zinc oxide are produced according to proportioning, receiving the shock of external force, or when striking hard objects, it is unlikely to deform, it is simple to the later stage normally uses.
Description
Technical field
The present invention relates to technical field of automobile parts, particularly relate to a kind of automotive hub material prescription.
Background technology
In prior art, automotive hub is restricted due to materials'use, and wheel hub is during using, it is easy to produce
Deformation, when particularly bumping against hard objects, wheel hub directly deforms, and causes the automobile cannot be properly functioning.
Summary of the invention
The present invention according to the deficiencies in the prior art, the present invention provides a kind of a kind of vapour being prevented from wheel hub stress deformation
Wheel hub material prescription.
The present invention is achieved in that a kind of automotive hub material prescription, includes according to weight ratio: carbon steel 30 ~
36 parts, 20 ~ 30 parts of aluminum, 12 ~ 16 parts of manganese, 5 ~ 10 parts of magnesium, chromium 2 ~ 4 parts, titanium 1 ~ 3 part, 5 ~ 8 parts of magnesium and zinc oxide 12 ~ 18 parts.
Further, include according to weight ratio: 30 parts of carbon steel, 20 parts of aluminum, 12 parts of manganese, 5 parts of magnesium, chromium 2 parts, titanium 1
Part, 5 parts of magnesium and zinc oxide 12 parts.
Further, include according to weight ratio: 36 parts of carbon steel, 30 parts of aluminum, 16 parts of manganese, 10 parts of magnesium, chromium 4 parts, titanium 3
Part, 8 parts of magnesium and zinc oxide 18 parts.
Further, include according to weight ratio: 33 parts of carbon steel, 25 parts of aluminum, 14 parts of manganese, 8 parts of magnesium, chromium 3 parts, titanium 2
Part, 7 parts of magnesium and zinc oxide 15 parts.
The advantage of a kind of automotive hub material prescription that the present invention provides is: the formulation ratio that the present invention provides, and passes through
Wheel hub carbon steel, aluminum, manganese, magnesium, chromium, titanium, magnesium and zinc oxide produced according to proportioning, is receiving the shock of external force, or
When person strikes hard objects, it is unlikely to deform, it is simple to the later stage normally uses.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, to the present invention
It is further elaborated.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not used to
Limit the present invention.
Embodiment one:
Described a kind of automotive hub material prescription, includes according to weight ratio: 30 parts of carbon steel, 20 parts of aluminum, 12 parts of manganese, magnesium 5
Part, chromium 2 parts, titanium 1 part, 5 parts of magnesium and zinc oxide 12 parts.
Embodiment two:
Described a kind of automotive hub material prescription, includes according to weight ratio: 36 parts of carbon steel, 30 parts of aluminum, 16 parts of manganese, magnesium 10
Part, chromium 4 parts, titanium 3 parts, 8 parts of magnesium and zinc oxide 18 parts.
Embodiment three:
Described a kind of automotive hub material prescription, includes according to weight ratio: 33 parts of carbon steel, 25 parts of aluminum, 14 parts of manganese, magnesium 8
Part, chromium 3 parts, titanium 2 parts, 7 parts of magnesium and zinc oxide 15 parts.
The advantage of a kind of automotive hub material prescription that the present invention provides is: the formulation ratio that the present invention provides, and passes through
Wheel hub carbon steel, aluminum, manganese, magnesium, chromium, titanium, magnesium and zinc oxide produced according to proportioning, is receiving the shock of external force, or
When person strikes hard objects, it is unlikely to deform, it is simple to the later stage normally uses.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent and the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (4)
1. an automotive hub material prescription, it is characterised in that include according to weight ratio: 30 ~ 36 parts of carbon steel, aluminum 20 ~
30 parts, 12 ~ 16 parts of manganese, 5 ~ 10 parts of magnesium, chromium 2 ~ 4 parts, titanium 1 ~ 3 part, 5 ~ 8 parts of magnesium and zinc oxide 12 ~ 18 parts.
A kind of automotive hub material prescription the most according to claim 1, it is characterised in that include according to weight ratio:
30 parts of carbon steel, 20 parts of aluminum, 12 parts of manganese, 5 parts of magnesium, chromium 2 parts, titanium 1 part, 5 parts of magnesium and zinc oxide 12 parts.
A kind of automotive hub material prescription the most according to claim 1, it is characterised in that include according to weight ratio:
36 parts of carbon steel, 30 parts of aluminum, 16 parts of manganese, 10 parts of magnesium, chromium 4 parts, titanium 3 parts, 8 parts of magnesium and zinc oxide 18 parts.
A kind of automotive hub material prescription the most according to claim 1, it is characterised in that include according to weight ratio:
33 parts of carbon steel, 25 parts of aluminum, 14 parts of manganese, 8 parts of magnesium, chromium 3 parts, titanium 2 parts, 7 parts of magnesium and zinc oxide 15 parts.