CN106272780A - A kind of method preventing cabinet-wood infested - Google Patents
A kind of method preventing cabinet-wood infested Download PDFInfo
- Publication number
- CN106272780A CN106272780A CN201610672635.5A CN201610672635A CN106272780A CN 106272780 A CN106272780 A CN 106272780A CN 201610672635 A CN201610672635 A CN 201610672635A CN 106272780 A CN106272780 A CN 106272780A
- Authority
- CN
- China
- Prior art keywords
- wood
- cabinet
- infested
- parts
- lauxite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to wood surface technical field of modification, it is specifically related to a kind of method preventing cabinet-wood infested, cabinet-wood sand for surface paper is polished, put in hermetic container, heating hermetic container, making the temperature within hermetic container is 100 200 DEG C, simultaneously, add boride aqueous solution vacuum pressure impregnating, being immersed in cyanurotriamide modified low-molecular-weight Lauxite 1 2h the most again, taking-up is dried, then at external coating aqueous epoxide resin paint, brushing thickness is 0.04 0.06mm, is placing 10 15 days under last room temperature.Using the inventive method to process timber, improve dimensional stability, generation of being heated after preventing time length is dry and cracked, physical and mechanical property is improved, in the life-span that prolonging wood uses, environment friendly and pollution-free, the furniture using this timber to prepare uses for a long time is not damaged by worms.
Description
Technical field
The present invention relates to wood surface technical field of modification, be specifically related to a kind of method preventing cabinet-wood infested.
Background technology
In order to protect the primary characteristic of timber, the decoration function improving woodwork and service life, certain table need to be used
Face treatment technology improves its aesthetic, mechanical property, wearability, durability, improves timber processing characteristics and gives timber
Surface combustion heat insulation, resistance to, mothproof, insulate, the New function such as conduction, thus improve the use value of timber, widen the application neck of timber
Territory.
Summary of the invention
It is an object of the invention to provide a kind of method preventing cabinet-wood infested, it is simple that the method possesses production technology,
The furniture of preparation can effectively prevent from being damaged by worms.
The present invention is with the following technical scheme above-mentioned technical problem of solution:
A kind of method preventing cabinet-wood infested, polishes cabinet-wood sand for surface paper, puts in hermetic container, heat close
Close container, make the temperature within hermetic container be 100-200 DEG C, meanwhile, add boride aqueous solution vacuum pressure impregnating, then
Being immersed in cyanurotriamide modified low-molecular-weight Lauxite 1-2h again, taking-up is dried, then is coated with at external coating aqueous epoxy resins
Material, brushing thickness is 0.04-0.06mm, is placing 10-15 days under last room temperature.
Preferably, sand paper model is 800-1000#.
Preferably, the molecular weight of described cyanurotriamide modified low-molecular-weight Lauxite is 5000-9000.
Preferably, the preparation method of described cyanurotriamide modified low-molecular-weight Lauxite, by weight meter: in reaction
Still is sequentially added into 80 parts of formalins, adjusts pH to 8-9, add 90 parts of tripolycyanamide, be warming up to 100-105 DEG C, stir 30-
55min, adds 40 parts of carbamide, continues stirring 10-15min, cools to 75 DEG C, and aqueous hydrochloric acid solution regulation pH is the most neutral in addition,
Being eventually adding 10 parts of ammonium chloride, stir 10min, cooling to room temperature discharging can obtain cyanurotriamide modified low-molecular-weight urea aldehyde tree
Fat.
The method have the benefit that timber is processed by use the inventive method, improve dimensional stability, prevent the time
Generation of being heated after long is dry and cracked, and physical and mechanical property is improved, the life-span that prolonging wood uses, environment friendly and pollution-free, uses this
Furniture prepared by kind timber uses for a long time is not damaged by worms.
Detailed description of the invention
Embodiment 1
A kind of method preventing cabinet-wood infested, is the sand papering of 800# by cabinet-wood surface model, puts into airtight
In container, heating hermetic container, making the temperature within hermetic container is 100 DEG C, meanwhile, adds Boron tribromide aqueous solution vacuum and adds
Pressure is impregnated, and is sequentially added into 80 parts of formalins the most in a kettle., adjusts pH to 8-9, adds 90 parts of tripolycyanamide, be warming up to
100 DEG C, stir 30min, add 40 parts of carbamide, continue stirring 10min, cool to 75 DEG C, add aqueous hydrochloric acid solution regulation pH
To neutral, it is eventually adding 10 parts of ammonium chloride, stirs 10min, cool to room temperature and discharging can prepare cyanurotriamide modified low molecule
Amount Lauxite, then it is immersed in cyanurotriamide modified low-molecular-weight Lauxite 1h, taking-up is dried, then at external coating aqueous ring
Epoxy resins coating, brushing thickness is 0.04mm, is placing 10 days under last room temperature.
Embodiment 2
A kind of method preventing cabinet-wood infested, is the sand papering of 900# by cabinet-wood surface model, puts into airtight
In container, heating hermetic container, making the temperature within hermetic container is 160 DEG C, meanwhile, adds titanium diboride aqueous solution vacuum and adds
Pressure is impregnated, and is sequentially added into 80 parts of formalins the most in a kettle., adjusts pH to 8-9, adds 90 parts of tripolycyanamide, be warming up to
100 DEG C, stir 45min, add 40 parts of carbamide, continue stirring 12min, cool to 75 DEG C, add aqueous hydrochloric acid solution regulation pH
To neutral, it is eventually adding 10 parts of ammonium chloride, stirs 10min, cool to room temperature and discharging can prepare cyanurotriamide modified low molecule
Amount Lauxite, then it is immersed in cyanurotriamide modified low-molecular-weight Lauxite 1.6h, taking-up is dried, then in external coating aqueous
Epoxy coating, brushing thickness is 0.05mm, is placing 11 days under last room temperature.
Embodiment 3
A kind of method preventing cabinet-wood infested, is the sand papering of 1000# by cabinet-wood surface model, puts into airtight
In container, heating hermetic container, making the temperature within hermetic container is 200 DEG C, meanwhile, adds six calcium boride aqueous solution vacuum and adds
Pressure is impregnated, and is sequentially added into 80 parts of formalins the most in a kettle., adjusts pH to 8-9, adds 90 parts of tripolycyanamide, be warming up to
105 DEG C, stir 55min, add 40 parts of carbamide, continue stirring 15min, cool to 75 DEG C, add aqueous hydrochloric acid solution regulation pH
To neutral, it is eventually adding 10 parts of ammonium chloride, stirs 10min, cool to room temperature and discharging can prepare cyanurotriamide modified low molecule
Amount Lauxite, then it is immersed in cyanurotriamide modified low-molecular-weight Lauxite 2h, taking-up is dried, then at external coating aqueous ring
Epoxy resins coating, brushing thickness is 0.06mm, is placing 15 days under last room temperature.
Embodiment described above only represents embodiments of the present invention, and it describes more concrete and detailed, but can not manage
Solve as limitation of the scope of the invention.It should be pointed out that, for the person of ordinary skill of the art, without departing from this
On the premise of bright design, it is also possible to make some deformation and improvement, these broadly fall into scope.
Claims (4)
1. one kind prevents the method that cabinet-wood is infested, it is characterised in that: cabinet-wood sand for surface paper is polished, puts into airtight
In container, heat hermetic container, make the temperature within hermetic container be 100-200 DEG C, meanwhile, add boride aqueous solution vacuum
Pressure impregnating, is immersed in cyanurotriamide modified low-molecular-weight Lauxite 1-2h the most again, and taking-up is dried, then at external coating water
Property epoxy coating, brushing thickness is 0.04-0.06mm, under last room temperature place 10-15 days.
Prevent the method that cabinet-wood is infested the most according to claim 1, it is characterised in that: sand paper model is 800-1000#.
Prevent the method that cabinet-wood is infested the most according to claim 1, it is characterised in that: described cyanurotriamide modified low point
The molecular weight of son amount Lauxite is 5000-9000.
Prevent the method that cabinet-wood is infested the most according to claim 1, it is characterised in that: described cyanurotriamide modified low point
The preparation method of son amount Lauxite, meter by weight: be sequentially added into 80 parts of formalins in a kettle., adjust pH to 8-
9, add 90 parts of tripolycyanamide, be warming up to 100-105 DEG C, stir 30-55min, add 40 parts of carbamide, continue stirring 10-
15min, cools to 75 DEG C, adds aqueous hydrochloric acid solution regulation pH extremely neutrality, is eventually adding 10 parts of ammonium chloride, stirs 10min, cooling
Discharging cyanurotriamide modified low-molecular-weight Lauxite can be obtained to room temperature.