CN106242458B - 一种室内装饰泥 - Google Patents
一种室内装饰泥 Download PDFInfo
- Publication number
- CN106242458B CN106242458B CN201610521993.6A CN201610521993A CN106242458B CN 106242458 B CN106242458 B CN 106242458B CN 201610521993 A CN201610521993 A CN 201610521993A CN 106242458 B CN106242458 B CN 106242458B
- Authority
- CN
- China
- Prior art keywords
- interior decoration
- mud
- water
- agent
- mud according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种长效泥，其成分及其质量配比为：无机胶凝剂45%～50%，硅藻土35%～40%，功能性添加剂1%～2.0%，保水剂0.5%～2%，施工调节剂1%～2.0%，其余为填充材料。由于长效泥健康环保，不仅有很好装饰性，还具有功能性，是替代壁纸和乳胶漆的新一代室内装饰材料。
Description
技术领域
本发明涉及一种室内装饰材料，尤其是涉及一种新材料长效泥，属于E04B建筑的领域。
背景技术
目前常见的真空隔热保温板防火等级虽然能达到国家标准不燃或难燃，保温效果良好。但是，它们在施工过程中容易被刮伤，出现空鼓、漏气现象，利用率大大降低。
此外现有技术的室内装饰净化材料的净化功能较低，而且性能不是很稳定，净化效率低。
现有长效泥市面上同类产品主要是硅藻泥，产品质量不统一，检测条件不具备，有些商家直接用内墙腻子来代替硅藻泥。因此不能达到很好的净化功能，不利于人们的生活健康。
发明内容
本发明的目的是提供一种具有高效净化功能的室内装饰材料，除了可以净化甲醛和其他有害气体，还可以调节室内的湿度，提高居住的舒适度。消除室内的细菌及异味。
本发明的技术方案是：
一种长效泥，其成分及其质量配比为：无机胶凝剂45%～50%，硅藻土35%～40%，功能性添加剂1%～2.0%，保水剂0.5%～2%，施工调节剂1%～2.0%，其余为填充材料。
作为优选，所述无机胶凝剂包括石膏、灰钙、石灰、白水泥中的至少一种。
作为优选，所述无机胶凝剂包括石膏、灰钙、石灰、白水泥，所述的石膏、灰钙、石灰、白水泥的质量比例为1：（1-1.5）：（2-2.45）：（0.8-1.1）。
作为优选，所述填充材料包括石英砂、氧化铁系颜料、复合颜料、重钙、滑石粉、高岭土中的至少一种。
作为优选，填充材料中包括石英砂、氧化铁系颜料、复合颜料、重钙石四种，其中的质量比例为（10-15）：（2-2.5）：（1-1.45）：（8-12）。
作为优选，所述功能性添加剂是纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂中的至少一种。
作为优选，纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂的质量比例为(2-2.4)：（2-2.45）：（0.8-1.2）。
作为优选，所述保水剂是羟丙基甲基纤维素、羧甲基纤维素、淀粉醚中的至少一种。
作为优选，所述施工调节剂是高效减水剂、水泥光亮剂、干粉消泡剂中的至少一种。
前面所述的长效泥的使用方法，其特征在于，在使用时加入质量比的0.6～0.8的水搅拌均匀后，按造型工艺施工成型。
本发明的有益效果是：
1）提供了一种具有净化室内环境的装饰材料-长效泥，该种长效泥具有更好的粘结力，并且具有更高的抗压强度。
2）通过无机胶凝剂、硅藻土、功能添加剂的吸附、分解来除去室内的有害物质，达到净化空气的功能，再配以二氧化钛等活性材料分解甲醛、防止细菌滋生。改善室内居住环境，提高生活品质，创造绿色生态的健康环境。而且该产品可以通过不同的实施手法，装饰室内装修、增强艺术气氛。
具体实施方式
下面结合实施过程对本发明进行详细描述，本部分的描述仅是示范性，不对本发明的保护范围作任何的限制。
一种长效泥复合真空隔热保温板，包括真空隔热保温板和包覆在其外围的长效泥。
通过上述技术方案，解决了施工过程中真空隔热保温板破损漏气的问题，施工安装方便，其具有优良的保温性、耐水性、耐久性和抗冻性，燃烧等级为不燃或难燃，防火性能优良。而且真空绝热保温板具有消除甲醛、净化空气、调节湿度、释放负氧离子、防火阻燃、墙面自洁、杀菌除臭，有利于人们的身心健康。
一种室内装饰用的长效泥，其成分及其质量配比为：无机胶凝剂45%～50%，硅藻土30%～40%，功能性添加剂0.5%～2%，保水剂0.5%～2%，施工调节剂0.5%～2.0%，其余为填充材料。
进一步优选，无机胶凝剂46%～48%，硅藻土32%～37%，功能性添加剂0.8%～1.6%，保水剂0.6%～1.8%，施工调节剂0.7%～1.8%，其余为填充材料。
进一步优选，无机胶凝剂47%，硅藻土33%～35%，功能性添加剂1%～1.5%，保水剂1%～1.5%，施工调节剂1%～1.5%，其余为填充材料。
进一步优选，硅藻土35%-40%。
进一步优选，填充材料10%-20%。
进一步优选，功能性添加剂1%-2%。
进一步优选，施工调节剂1%-2.0%。
进一步优选，功能性添加剂1%～2%。
当然，真空绝热保温板外面包覆的长效泥就是前面所提到的长效泥。
无机胶凝剂使长效泥牢固的附着在墙体表面。同时，这些无机胶凝材料或遇水固化或遇水、气固化，对室内空气的含湿量有一定的调节功能，还可以抑制细菌的滋生。
现有技术中，无机胶凝剂的含量一般多是在30%左右，因此与墙壁的粘结力不强，而如果增加无机胶凝剂的含量，则会因为其他成分比例下降而导致其他杀菌等功能相应的下降，本发明的长效泥，通过增加无机胶凝剂的含量，使其达到45-50%，极大地提高了泥与墙壁的粘结，同时，通过配合其他的成分，例如硅藻土、填充材料、功能性添加剂、保水剂、施工调节剂的成分及其质量比重，使得整个房间使用长效泥具有消除甲醛、净化空气、调节湿度、释放负氧离子、防火阻燃、墙面自洁、杀菌除臭等功能。此外因为无机胶凝剂的比重的增加，使得其他成分比重相应的下降，也从而节省了整体成本。
作为优选，所述无机胶凝剂包括石膏、灰钙、石灰、白水泥中的至少一种。
进一步作为优选，所述无机胶凝剂包括石膏、灰钙、石灰、白水泥，所述的石膏、灰钙、石灰、白水泥的质量比例为1：（1-1.5）：（2-2.45）：（0.8-1.1）。通过实验发现，上述质量比例情况下，长效泥与墙壁的粘结力达到最好。
作为优选，硅藻土的粒径在10～325目之间。所述硅藻土通过自身的粒径级配达到不同的质感，有效的提高了硅藻土在产品中的含量，也就提高了对甲醛等有害气体的吸收能力，更大程度的改善室内生活环境，并且可有效降低其他填充材料的用量，使产品性能提高。
进一步优选，硅藻土的粒径在120～205目之间。通过优选设置，能够使得在保证长效泥性能的同时，同时使填充材料的用量达到较小，从而大大节约了材料和成本。
作为优选，所述填充材料包括石英砂、氧化铁系颜料、复合颜料、重钙中的至少一种。石英砂可以提高产品的强度，有一定的防擦伤功能；颜料可赋予长效泥不同的色感，适合于多种人群的需要，为室内提供美感。
作为优选，填充材料中包括石英砂、氧化铁系颜料、复合颜料、重钙石四种，其中的质量比例为（10-15）：（2-2.5）：（1-1.45）：（8-12）。通过上述的比例设置，能够使得长效泥在满足建筑的要求的基础上，具有很好装饰性，是替代壁纸和乳胶漆的新一代室内装饰材料。
作为优选，所述功能性添加剂是纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂中的至少一种。该产品在传统硅藻土的吸附基础上添加了功能性添加剂，可有效的改善长效泥对甲醛等有害物质的吸收、分解能力，提高了产品的长久性。通过添加功能性添加剂，能够分解空气中的甲醛、甲苯、VOC等有害气体，能够起到净化空气的作用。
作为优选，纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂的质量比例为(2-2.4)：（2-2.45）：（0.8-1.2）。本发明通过加大纳米二氧化钛、纳米负离子的比例，相对于现有技术，加大了杀菌离子的杀菌作用，在对其他有害物质吸收的基础上，使得极大地提高了对甲醛、甲苯的吸收。
作为优选，所述保水剂是羟丙基甲基纤维素、羧甲基纤维素、淀粉醚中的至少一种。采用此复配的保水体系，可大大的提高产品的施工性，降低了产品的成本。也节省了原材料的消耗，从能源消耗方面起到了节能的作用。通过保水剂加入，避免泥因为干燥而导致的裂纹。
作为优选，羟丙基甲基纤维素、羧甲基纤维素、淀粉醚的质量比例为（0.3-0.4）：（0.5-0.7）：1。通过优化设置，可以使得泥性能达到最优。
作为优选，所述施工调节剂是高效减水剂、水泥光亮剂、干粉消泡剂中的至少一种。施工调节剂在改善施工性能的同时，又提高了产品固化后的性能，提高了产品的光亮度，不再使此类产品只局限于亚光体系。
将上述原材料精确计量后，投入无重力干粉砂浆混合机中，经机械混合3～5分钟出料包装即可。在使用时只要加入质量比的0.6～0.8的水搅拌均匀后，按造型工艺施工成型。
本发明的长效泥经使用后形成的涂膜，可以提高室内居住环境的生活质量。消除甲醛、净化空气、调节湿度、释放负氧离子、防火阻燃、墙面自洁、杀菌除臭，有利于人们的身心健康。
下面通过具体实施例来进一步说明。
实施例1
一种建筑室内用装饰装修材料，包括质量配比分别如下的成份：无机胶凝剂是石膏：50%，硅藻土：30%，保水剂羟丙基甲基纤维素：0.5%，施工调节剂石膏缓凝剂：0.2%，施工调节剂可再分散乳胶粉：0.3%，功能性添加剂纳米负离子：0.5%，其余是填充剂，是粒径为325目的重钙。
将上述原材料精确计量后，投入无重力干粉砂浆混合机中，经机械混合3～5分钟出料包装即可。在使用时只要加入质量比的0.6的水搅拌均匀后，按造型工艺施工成型。
此配比条件下，涂抹1mm厚的长效泥涂层对甲醛净化性能大于76.1%，净化效果持久性65%，对甲苯净化性能大于37%，净化效果持久性23%，放射性（A类装修材料）内照射指数未检出，外照射指数为0.1，抗霉菌性能2级，吸湿量3h为2.0×10-2Wa(1×10-3kg/m2)，抗压强度为9.2MPa。有效的改善了室内的生活环境。
实施例1的改进，无机胶凝剂是50%，其中所述的石膏、灰钙、石灰、白水泥的质量比例为1：（1-1.5）：（2-2.45）：（0.8-1.1）。
此配比条件下，涂抹1mm厚的长效泥涂层对甲醛净化性能大于80.1%，净化效果持久性74%，对甲苯净化性能大于45%，净化效果持久性30%，放射性（A类装修材料）内照射指数未检出，外照射指数为0.1，抗霉菌性能2级，吸湿量3h为2.2×10-2Wa(1×10-3kg/m2)，抗压强度为9.3MPa。有效的改善了室内的生活环境。
实施例2
一种建筑室内用装饰装修材料，包括质量配比分别如下的成份：无机胶凝剂生石膏：45%，硅藻土：35%，保水剂羟丙基甲基纤维素：0.5%，保水剂木质纤维素：0.5%，施工调节剂石膏速凝剂：0.2%，施工调节剂胶粉：1.8%，填充材料石英砂：5%，功能性添加剂纳米二氧化钛：0.5%，其余为填充材料重钙325目。
将上述原材料精确计量后，投入无重力干粉砂浆混合机中，经机械混合3～5分钟出料包装即可。在使用时只要加入质量比的0.6的水搅拌均匀后，按造型工艺施工成型。
此配比条件下，涂抹1mm厚的长效泥涂层对甲醛净化性能大于76.1%，净化效果持久性65%，对甲苯净化性能大于39%，净化效果持久性24%，放射性（A类装修材料）内照射指数未检出，外照射指数为0.2，抗霉菌性能2级，吸湿量3h为1.5×10-2Wa(1×10-3kg/m2)，抗压强度为7.2MPa。有效的改善了室内的生活环境。
作为改进，填充材料是石英砂、氧化铁系颜料、复合颜料、重钙石四种，其中的质量比例为（10-15）：（2-2.5）：（1-1.45）：（8-12）。经过测试，在满足其他条件下，抗压强度为8.2MPa，并且外观颜色新鲜，具有很好的装饰性能。
实施例3
一种建筑室内用装饰装修材料，包括质量配比分别如下的成份：无机胶凝剂灰钙：50%，硅藻土：40%，保水剂羟丙基甲基纤维素：0.5%，保水剂木质纤维素：0.5%，保水剂淀粉醚：0.3%，施工调节剂胶粉：2%，功能性添加剂乙烯脲：1%，其余为填充材料石英砂。
将上述原材料精确计量后，投入无重力干粉砂浆混合机中，经机械混合3～5分钟出料包装即可。在使用时只要加入质量比的0.75的水搅拌均匀后，按造型工艺施工成型。
此配比条件下，涂抹1mm厚的长效泥涂层对甲醛净化性能大于83.2%，净化效果持久性76%，对甲苯净化性能大于41%，净化效果持久性30%，抗霉菌性能1级，吸湿量3h为2.3×10-2Wa(1×10-3kg/m2)，抗压强度为8.8MPa。有效的改善了室内的生活环境。
实施例3的进一步改进，保水剂0.3%，其中羟丙基甲基纤维素、羧甲基纤维素、淀粉醚的质量比例为（0.3-0.4）：（0.5-0.7）：1。通过保水剂的设置，使得产品性能达到质量要求情况下，还能够提高大约12%的保水率。
实施例4
一种建筑室内用装饰装修材料，包括质量配比分别如下的成份：无机胶凝剂灰钙：50%，硅藻土：40%，保水剂羟丙基甲基纤维素：0.8%，保水剂木质纤维素：0.5%，保水剂淀粉醚：0.4%，施工调节剂胶粉：2%，功能性添加剂纳米二氧化钛：0.5%，功能性添加剂纳米负离子：1%，功能性添加剂乙烯脲甲醛捕获剂：0.5%，其余为填充材料石英砂。
将上述原材料精确计量后，投入无重力干粉砂浆混合机中，经机械混合3～5分钟出料包装即可。在使用时只要加入质量比的0.70的水搅拌均匀后，按造型工艺施工成型。
此配比条件下，涂抹1mm厚的长效泥涂层对甲醛净化性能大于88%，净化效果持久性80%，对甲苯净化性能大于45%，净化效果持久性36%，抗霉菌性能1级，吸湿量3h为2.1×10-2Wa(1×10-3kg/m2)，抗压强度为8.8MPa。有效的改善了室内的生活环境。
作为上述实施例的改进，功能性添加剂2.0%，其中纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂的质量比例为(2-2.4)：（2-2.45）：（0.8-1.2）。通过上述设置，涂抹1mm厚的长效泥涂层对甲醛净化性能大于94%，净化效果持久性87%，对甲苯净化性能大于55%，净化效果持久性47%，抗霉菌性能1级。
上述四个实施例，涂抹1mm厚的长效泥涂层的技术效果如下：
进一步作为优选，无机胶凝剂46%～48%，硅藻土32%～37%，功能性添加剂0.8%～1.6%，保水剂0.6%～1.8%，施工调节剂0.7%～1.8%，其余为填充材料。通过选择上述的数值比例，能够使得泥整体综合性能提高5%-7%左右。所谓整体综合性能就是在保证每一参数满足工程需要的时候，上述效果参数相对每一个参数所对应的基准数据的比例，然后将所有的比例相加得到的和。
进一步优选，无机胶凝剂47%，硅藻土33%～35%，功能性添加剂1%～1.5%，保水剂1%～1.5%，施工调节剂1%～1.5%，其余为填充材料。通过选择上述的数值比例，能够使得泥整体综合性能提高7%左右。
在上述四个实施例中，所述无机胶凝剂包括石膏、灰钙、石灰、白水泥，所述的石膏、灰钙、石灰、白水泥的质量比例为1：（1-1.5）：（2-2.45）：（0.8-1.1）。在此种优选设置下，粘结性能能够提高10%左右。
在上述四个实施例中，功能性添加剂选择纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂的质量比例为(2-2.4)：（2-2.45）：（0.8-1.2）。对甲醛、甲苯的吸收提高了8%以上。
在上述四个实施例中，保水剂选取羟丙基甲基纤维素、羧甲基纤维素、淀粉醚，其质量比例为（0.3-0.4）：（0.5-0.7）：1，通过优选，能够提高了保水率11%左右。
在上述四个实施例中，填充材料中包括石英砂、氧化铁系颜料、复合颜料、重钙石四种，其中的质量比例为（10-15）：（2-2.5）：（1-1.45）：（8-12）。通过上述的比例设置，能够使得长效泥提高耐压能力，能够提高13%左右。
虽然本发明已以较佳实施例披露如上，但本发明并非限定于此。任何本领域技术人员，在不脱离本发明的精神和范围内，均可作各种更动与修改，因此本发明的保护范围应当以权利要求所限定的范围为准。
Claims (8)
1.一种室内装饰泥，其成分及其质量配比为：无机胶凝剂45%～50%，硅藻土35%～40%，功能性添加剂1%～2.0%，保水剂0.5%～2%，施工调节剂1%～2.0%，其余为填充材料；所述无机胶凝剂包括石膏、灰钙、石灰、白水泥，所述的石膏、灰钙、石灰、白水泥的质量比例为1：（1-1.5）：（2-2.45）：（0.8-1.1）。
2.根据权利要求1所述的室内装饰泥，其特征在于，所述填充材料包括石英砂、氧化铁系颜料、复合颜料、重钙、滑石粉、高岭土中的至少一种。
3.根据权利要求2所述的室内装饰泥，其特征在于，填充材料中包括石英砂、氧化铁系颜料、复合颜料、重钙四种，其中的质量比例为（10-15）：（2-2.5）：（1-1.45）：（8-12）。
4.根据权利要求1所述的室内装饰泥，其特征在于，所述功能性添加剂是纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂中的至少一种。
5.根据权利要求4所述的室内装饰泥，其特征在于，纳米二氧化钛、纳米负离子、乙烯脲甲醛捕获剂的质量比例为(2-2.4)：（2-2.45）：（0.8-1.2）。
6.根据权利要求1所述的室内装饰泥，其特征在于，所述保水剂是羟丙基甲基纤维素、羧甲基纤维素、淀粉醚中的至少一种。
7.根据权利要求1所述的室内装饰泥，其特征在于，所述施工调节剂是高效减水剂、水泥光亮剂、干粉消泡剂中的至少一种。
8.根据权利要求1-7之一所述的室内装饰泥的使用方法，其特征在于，在使用时加入质量比为0.6～0.8的水搅拌均匀后，按造型工艺施工成型。