CN106145816A - A kind of high water proof fire retardant thermal insulation mortar containing slag powders - Google Patents
A kind of high water proof fire retardant thermal insulation mortar containing slag powders Download PDFInfo
- Publication number
- CN106145816A CN106145816A CN201610493558.7A CN201610493558A CN106145816A CN 106145816 A CN106145816 A CN 106145816A CN 201610493558 A CN201610493558 A CN 201610493558A CN 106145816 A CN106145816 A CN 106145816A
- Authority
- CN
- China
- Prior art keywords
- slag
- thermal insulation
- insulation mortar
- slag powders
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of high water proof fire retardant thermal insulation mortar containing slag powders, including the component of following weight: portland cement 200 300, slag micropowder 50 80, slag coarse aggregate 100 150, boron nitride 35, starch ether 5 10, diatomite 5 10, carborundum 5 10, stearic acid 35, asbestos fibre 5 10, sodium alginate 24, redispersable latex powder 24, water reducer 13；Water is appropriate.Compared with prior art, the invention has the beneficial effects as follows: the present invention contains the thermal insulation mortar of slag powders and asbestos fibre, use slag powders to be raw material, be equipped with asbestos fibre and modifying agent, there is the premium properties such as intensity height, good toughness, insulation, antiseep, fire-proof heat-insulating be good.
Description
Technical field
The present invention relates to building material field, particularly relate to a kind of high water proof fire retardant thermal insulation mortar containing slag powders.
Background technology
Concrete mortar is widely used in the engineerings such as bridge, building, power station, not only needs higher intensity, toughness
And stability requirement, and must have self certain water resistance, at northern area, in addition it is also necessary to possess cold-resistant freeze proof simultaneously
Performance.Especially extremely frigid zones, difference variation is big, concrete easily occur through repeatedly repeatedly freezing, after melting process crackle,
Becoming crisp, infiltration phenomenon, the index such as its intensity, toughness and stability is severely impacted.
Slag powders is the discarded object of metallurgy industry, if by slag powders in addition modification, making mortar, will have very well
Economic benefit, and solve the storage problem of slag powders.
It was verified that asbestos fibre has well fire prevention and heat-proof quality in concrete.
Content of the invention
The present invention provides a kind of high water proof fire retardant thermal insulation mortar containing slag powders, uses slag powders to be raw material, is equipped with stone
Cotton fiber and modifying agent, have intensity height, good toughness, insulation, fireproof premium properties.
In order to achieve the above object, the present invention realizes by the following technical solutions:
A kind of high water proof fire retardant thermal insulation mortar containing slag powders, including the component of following weight: silicate cement
Mud 200-300, slag micropowder 50-80, slag coarse aggregate 100-150, boron nitride 3-5, starch ether 5-10, diatomite 5-10, carbon
SiClx 5-10, stearic acid 3-5, asbestos fibre 5-10, sodium alginate 2-4, redispersable latex powder 2-4, water reducer 1-3；Water is fitted
Amount.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention contains the thermal insulation mortar of slag powders and asbestos fibre, uses slag powders to be raw material, be equipped with asbestos fibre and
Modifying agent, has the premium properties such as intensity height, good toughness, insulation, antiseep, fire-proof heat-insulating be good.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A kind of high water proof fire retardant thermal insulation mortar containing slag powders, including the component of following weight: silicate cement
Mud the 200th, slag micropowder the 60th, slag coarse aggregate the 100th, boron nitride the 3rd, starch ether the 6th, diatomite the 8th, carborundum the 7th, stearic acid the 4th, asbestos are fine
Dimension the 8th, sodium alginate the 4th, redispersable latex powder the 4th, water reducer 2；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm of square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is formulated by weight proportion by following grain size distribution:
Slag coarse aggregate 3 weight portion of granularity >=25mm
Slag coarse aggregate 25 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 25 weight portion of granularity≤16mm
Described raw material ratio by weight is stirred, by the preparation method of described thermal insulation mortar: in addition to cement
Rear addition cement, mixes and makes product.
Embodiment 2
A kind of high water proof fire retardant thermal insulation mortar containing slag powders, including the component of following weight: silicate cement
Mud the 260th, slag micropowder the 70th, slag coarse aggregate the 120th, boron nitride the 5th, starch ether the 10th, diatomite the 5th, carborundum the 5th, stearic acid the 3rd, asbestos
Fiber the 5th, sodium alginate the 2nd, redispersable latex powder the 2nd, water reducer 3；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm of square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is formulated by weight proportion by following grain size distribution:
Slag coarse aggregate 5 weight portion of granularity >=25mm
Slag coarse aggregate 30 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 30 weight portion of granularity≤16mm
The preparation method of described thermal insulation mortar, with embodiment 1.
Embodiment 3
A kind of high water proof fire retardant thermal insulation mortar containing slag powders, including the component of following weight: silicate cement
Mud the 300th, slag micropowder the 80th, slag coarse aggregate the 150th, boron nitride the 4th, starch ether the 8th, diatomite the 10th, carborundum the 10th, stearic acid the 5th, asbestos
Fiber the 10th, sodium alginate the 4th, redispersable latex powder the 4th, water reducer 2；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm of square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is formulated by weight proportion by following grain size distribution:
Slag coarse aggregate 1 weight portion of granularity >=25mm
Slag coarse aggregate 20 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 20 weight portion of granularity≤16mm
The preparation method of described thermal insulation mortar, with embodiment 1.
Embodiment 4
A kind of high water proof fire retardant thermal insulation mortar containing slag powders, including the component of following weight: silicate cement
Mud the 24th, slag micropowder the 60th, slag coarse aggregate the 120th, boron nitride the 4th, starch ether the 6th, diatomite the 6th, carborundum the 6th, stearic acid the 4th, asbestos are fine
Dimension the 7th, sodium alginate the 3rd, redispersable latex powder the 3rd, water reducer 2；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm of square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is formulated by weight proportion by following grain size distribution:
Slag coarse aggregate 1 weight portion of granularity >=25mm
Slag coarse aggregate 20 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 20 weight portion of granularity≤16mm
The preparation method of described thermal insulation mortar, with embodiment 1.
The performance testing index of products obtained therefrom such as following table:
Claims (1)
1. the high water proof fire retardant thermal insulation mortar containing slag powders, it is characterised in that include the component of following weight:
Portland cement 200-300, slag micropowder 50-80, slag coarse aggregate 100-150, boron nitride 3-5, starch ether 5-10, diatomite
5-10, carborundum 5-10, stearic acid 3-5, asbestos fibre 5-10, sodium alginate 2-4, redispersable latex powder 2-4, water reducer 1-
3；Water is appropriate.