CN106116164A - The processing method of metal stricture of vagina microlite ceramic tile - Google Patents
The processing method of metal stricture of vagina microlite ceramic tile Download PDFInfo
- Publication number
- CN106116164A CN106116164A CN201610468175.4A CN201610468175A CN106116164A CN 106116164 A CN106116164 A CN 106116164A CN 201610468175 A CN201610468175 A CN 201610468175A CN 106116164 A CN106116164 A CN 106116164A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- parts
- microlite
- silver metal
- vagina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The processing method that the invention discloses a kind of metal stricture of vagina microlite ceramic tile, including processing a kind of metal stricture of vagina microlite ceramic tile, described metal stricture of vagina microlite ceramic tile includes one layer of microlite ceramic tile plate body, its raw material includes the component of following weight portion: silicon dioxide 60～70 parts, calcium carbonate 16～20 parts, calcium oxide 6～10 parts, zinc oxide 3～4 parts, brium carbonate 2～3 parts, boron oxide 2～3 parts, silver metal silk 0.05 part；The lines of silver metal is had in described microlite tile panel body, its processing method comprises the following steps: carry out the raw material of the microlite ceramic tile plate body outside desilver tinsel pulverizing, dispensing, it is sintered to during maximum temperature natural cooling after 1 hour, liquid level puts into silver metal silk side by side, liquid level surface, then natural cooling is blown with the direction, side of blower fan silver metal silk.The present invention can solve existing microlite ceramic tile does not has metallochrome striped and problem three-dimensional not.
Description
Technical field
The present invention relates to construction material processing technique field, a kind of surface has the microlite porcelain of metallochrome striped
The processing method of brick.
Background technology
The decorative pattern lines of existing ceramic tile surface is typically all and carries out picture mosaic after ceramic tile plate body has sintered again, thus
The effectiveness comparison of picture mosaic is single, and three-dimensional not.Owing to the sintering temperature of ceramic tile, especially microlite is higher, super
Cross 1000 ° of more than C, and metal has melted, form ion, thus can not give birth to existing technology
Output has the striped of metallochrome, and has relief ceramic tile.
Summary of the invention
Problem to be solved by this invention is to provide the processing method of a kind of metal stricture of vagina microlite ceramic tile, existing micro-to solve
Crystal stone tile does not has metallochrome striped and problem three-dimensional not.
In order to solve the problems referred to above, the technical scheme is that the processing method of this metal stricture of vagina microlite ceramic tile includes
A kind of metal stricture of vagina microlite ceramic tile of processing, described metal stricture of vagina microlite ceramic tile includes one layer of microlite ceramic tile plate body, described in include
The component of following weight portion: silicon dioxide 60～70 parts, calcium carbonate 16～20 parts, calcium oxide 6～10 parts, zinc oxide 3～4 parts,
Brium carbonate 2～3 parts, boron oxide 2～3 parts, silver metal silk 0.05 part；The lines of silver metal is had in described microlite tile panel body；
Its processing method comprises the following steps:
Carry out the raw material of the microlite ceramic tile plate body outside desilver tinsel pulverizing, dispensing, afterwards at 1500 ° of C～1550 ° of C
At a temperature of melted 1.8 hours～2.6 hours, natural cooling, after 1 hour, puts into silver metal silk on liquid level side by side, uses blower fan
Liquid level surface is blown in the direction, side of silver metal silk, and silver metal silk is swum by blower fan blowout silver metal when melting
Dynamic lines, after silver metal silk is all melted, blower fan stops, then natural cooling 10 hours～12 hours, forms microlite porcelain
Brick plate body.
In technique scheme, more specifically technical scheme may is that described silver metal filament diameter 0.6 millimeter～
1.5 millimeter.
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that
The metal stricture of vagina microlite ceramic tile of the processing method of this metal stricture of vagina microlite ceramic tile, placed the silver of certain component in its raw material
Metal, and have the lines of silver metal in being maintained at microlite tile panel body, has looked metal lines to increase at ceramic tile surface,
And there is third dimension, to meet the needs in market.This method uses after sintering maximum temperature, cools down 1 hour, makes solution steady
In the case of determining to start crystallization, put into silver metal silk abreast, make silver metal silk to melt but spread the most at once, silver metal silk
When melting while being blown out, by blower fan, the lines that silver metal is travelling；Owing to silver metal silk is opened at a higher temperature
There is the diffusion of smaller portions beginning, and the metal stricture of vagina microlite ceramic tile third dimension so processed is the strongest.
Detailed description of the invention
Below the embodiment of the present invention is described in further detail:
Embodiment one:
The processing method of this metal stricture of vagina microlite ceramic tile, including processing a kind of metal stricture of vagina microlite ceramic tile, including one layer of microlite
Ceramic tile plate body, the raw material of microlite ceramic tile plate body includes the component of following weight portion: silicon dioxide 60 parts, calcium carbonate 20 parts, oxygen
Change calcium 6 parts, zinc oxide 4 parts, brium carbonate 2 parts, boron oxide 3 parts, silver metal silk 0.05 part；Silver metal filament diameter 0.6 millimeter, crystallite
The lines of silver metal is had in stone ceramic tile plate body.
Its processing method comprises the following steps:
Carry out the raw material of the microlite ceramic tile plate body outside desilver tinsel pulverizing, dispensing, afterwards at 1500 ° of C～1550 ° of C
At a temperature of melted 1.8 hours, natural cooling, after 1 hour, puts into silver metal silk on liquid level side by side, with blower fan silver metal silk
Liquid level surface is blown in direction, side, the lines that silver metal silk is moved about by blower fan blowout silver metal when melting,
After silver metal silk is all melted, blower fan stops, then natural cooling 10 hours, forms microlite ceramic tile plate body.
This method use sintering maximum temperature after, cool down 1 hour, make solution-stabilized start crystallize in the case of, and
Row ground put into silver metal silk, make silver metal silk to melt but spread the most at once, silver metal silk melt state next
While the lines moved about by blower fan blowout silver metal；Owing to silver metal silk begins with the diffusion of smaller portions at a higher temperature,
The metal stricture of vagina microlite ceramic tile third dimension so processed is the strongest.
Embodiment two:
The processing method of this metal stricture of vagina microlite ceramic tile, including one layer of microlite ceramic tile plate body, described microlite ceramic tile plate body
Raw material includes the component of following weight portion: silicon dioxide 70 parts, calcium carbonate 16 parts, calcium oxide 10 parts, zinc oxide 3 parts, brium carbonate 3
Part, boron oxide 2 parts, silver metal silk 0.05 part, silver metal filament diameter 1.5 millimeters.The stricture of vagina of silver metal is had in microlite tile panel body
Road.
Its processing method comprises the following steps:
Carry out the raw material of the microlite ceramic tile plate body outside desilver tinsel pulverizing, dispensing, afterwards at 1500 ° of C～1550 ° of C
At a temperature of melted 2.6 hours, natural cooling, after 1 hour, puts into silver metal silk on liquid level side by side, with blower fan silver metal silk
Liquid level surface is blown in direction, side, the lines that silver metal silk is moved about by blower fan blowout silver metal when melting,
After silver metal silk is all melted, blower fan stops, then natural cooling 12 hours, forms microlite ceramic tile plate body.
Claims (2)
1. the processing method of a metal stricture of vagina microlite ceramic tile, it is characterised in that: include processing a kind of metal stricture of vagina microlite ceramic tile,
Described metal stricture of vagina microlite ceramic tile includes one layer of microlite ceramic tile plate body, described in include the component of following weight portion: silicon dioxide
60～70 parts, calcium carbonate 16～20 parts, calcium oxide 6～10 parts, zinc oxide 3～4 parts, brium carbonate 2～3 parts, boron oxide 2～3 parts,
Silver metal silk 0.05 part；The lines of silver metal is had in described microlite tile panel body；
Its processing method comprises the following steps:
Carry out the raw material of the microlite ceramic tile plate body outside desilver tinsel pulverizing, dispensing, afterwards at 1500 ° of C～1550 ° of C
At a temperature of melted 1.8 hours～2.6 hours, natural cooling, after 1 hour, puts into silver metal silk on liquid level side by side, uses blower fan
Liquid level surface is blown in the direction, side of silver metal silk, and silver metal silk is swum by blower fan blowout silver metal when melting
Dynamic lines, after silver metal silk is all melted, blower fan stops, then natural cooling 10 hours～12 hours, forms microlite porcelain
Brick plate body.
The processing method of metal stricture of vagina microlite ceramic tile the most according to claim 1, it is characterised in that: described silver metal silk is straight
0.6 millimeter～1.5 millimeters of footpath.