CN106048855A - Production method of coconut carbon blended fabric - Google Patents
Production method of coconut carbon blended fabric Download PDFInfo
- Publication number
- CN106048855A CN106048855A CN201610641818.0A CN201610641818A CN106048855A CN 106048855 A CN106048855 A CN 106048855A CN 201610641818 A CN201610641818 A CN 201610641818A CN 106048855 A CN106048855 A CN 106048855A
- Authority
- CN
- China
- Prior art keywords
- yarn
- production method
- sizing
- fabric
- coconut
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of a coconut carbon blended fabric. The method comprises the steps that 1, a compact siro spinning technology is adopted for blending 60wt% of Australian cotton and 40wt5 of coconut carbon fiber into a functional yarn; 2, yarn sizing is carried out, wherein high-performance PR-SU is used as a main sizing agent, and solid acrylic nitrile and wax sheets are used as auxiliaries for preparing a sizing agent for carrying out sizing on the functional yarn; 3, the yarn subjected to sizing is used as a raw material for preparing the fabric. According to the production method of the coconut carbon blended fabric, the hairiness value of the resultant yearn is obviously lowered, yarn levelness is significantly improved, the produced yarn is large in specific surface area, bright and clean, and the fabric has the properties of removing odor, resisting ultraviolet light, emitting anions, keeping warmth and the like.
Description
Technical field
The present invention relates to the production method of coconut palm carbon blend fabric.
Background technology
Along with improving constantly of living standard, people have higher pursuit, clothing to class and the requirement of dress ornament
Fabric is not only embodied in appearance, and what is more important presses close to the real daily life of consumer, adapts to consumer demand, various
Change.
Summary of the invention
It is an object of the invention to provide the production method of a kind of coconut palm carbon blend fabric, make resultant yarn filoplume value substantially reduce,
Bar is dry to be significantly improved, and the yarn specific surface area of production is big, bright and clean, and fabric has taste removal, anti-ultraviolet and transmitting anion, warming
Etc. performance.
For achieving the above object, the technical scheme is that the production method designing a kind of coconut palm carbon blend fabric, including
Following steps:
1) using tight SEILE textile technology, 60wt% Australia is cotton, 40wt% coconut carbon fibre blending becomes functional yarn；
2) yarn sizing: be main slurry with high-performance starch PR-SU, prepare slurry with solid propylene and wax disk(-sc) for auxiliary agent, to merit
Starching can be carried out by yarn；
3) fabric is prepared with sizing yarn for raw material.
Preferably, the specification of described coconut carbon fibre is 1.33dtex × 38mm.
Preferably, the rate of sizing in described yarn sizing controls 12%, uses layering preliminary drying to close drying mode again and entrys,
Protection serous coat, reduces coconut carbon fibre damage, and regain controls 5%.
Preferably, air-jet weaving is used to prepare fabric: heald frame height 140mm, 32 ° of angular apertures, the back rest/and through frame-2, upper machine
Tension force 260kg.
Advantages of the present invention and having the beneficial effects that: the production method of a kind of coconut palm carbon blend fabric is provided, makes resultant yarn filoplume
Value substantially reduces, and bar is dry to be significantly improved, and the yarn specific surface area of production is big, bright and clean, and fabric has taste removal, anti-ultraviolet and transmitting
Anion, the performance such as warming.
The present invention has a characteristic that
1, spun yarn uses match network compact spinning technology.
2, sizing: select environmental protection, high-performance starch PR-SU that adhesion property is good to decide slurry, simultaneously for preventing warp thread from rising
Hair balling-up, selects solid propylene and high-quality wax disk(-sc) to make auxiliary agent.The rate of sizing controls 12%, uses layering preliminary drying to close drying mode again
Entrying, protect serous coat, reduce coconut carbon fibre damage, regain controls 5%.
3, air-jet weaving: heald frame height 140mm, 32 ° of angular apertures, the back rest/through frame-2, warp tension 260kg.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
The production method of a kind of coconut palm carbon blend fabric, comprises the steps:
1) using tight SEILE textile technology, 60wt% Australia is cotton, 40wt% coconut carbon fibre blending becomes functional yarn；
2) yarn sizing: be main slurry with high-performance starch PR-SU, prepare slurry with solid propylene and wax disk(-sc) for auxiliary agent, to merit
Starching can be carried out by yarn；
3) fabric is prepared with sizing yarn for raw material.
Preferably, the specification of described coconut carbon fibre is 1.33dtex × 38mm.
Preferably, the rate of sizing in described yarn sizing controls 12%, uses layering preliminary drying to close drying mode again and entrys,
Protection serous coat, reduces coconut carbon fibre damage, and regain controls 5%.
Preferably, air-jet weaving is used to prepare fabric: heald frame height 140mm, 32 ° of angular apertures, the back rest/and through frame-2, upper machine
Tension force 260kg.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. the production method of coconut palm carbon blend fabric, it is characterised in that comprise the steps:
1) using tight SEILE textile technology, 60wt% Australia is cotton, 40wt% coconut carbon fibre blending becomes functional yarn；
2) yarn sizing: be main slurry with high-performance starch PR-SU, prepare slurry with solid propylene and wax disk(-sc) for auxiliary agent, to merit
Starching can be carried out by yarn；
3) fabric is prepared with sizing yarn for raw material.
The production method of coconut palm carbon blend fabric the most according to claim 1, it is characterised in that the specification of described coconut carbon fibre
For 1.33dtex × 38mm.
The production method of coconut palm carbon blend fabric the most according to claim 2, it is characterised in that upper in described yarn sizing
Slurry rate controls 12%, uses layering preliminary drying to close drying mode again and entrys, protect serous coat, reduces coconut carbon fibre damage, regain control
System is 5%.
The production method of coconut palm carbon blend fabric the most according to claim 3, it is characterised in that use air-jet weaving preparation to knit
Thing: heald frame height 140mm, 32 ° of angular apertures, the back rest/through frame-2, warp tension 260kg.