CN106040969A - 一种酚醛树脂自硬砂的制备方法 - Google Patents

一种酚醛树脂自硬砂的制备方法 Download PDF

Info

Publication number
CN106040969A
CN106040969A CN201610354811.0A CN201610354811A CN106040969A CN 106040969 A CN106040969 A CN 106040969A CN 201610354811 A CN201610354811 A CN 201610354811A CN 106040969 A CN106040969 A CN 106040969A
Authority
CN
China
Prior art keywords
sand
weight
phenolic resin
parts
hardening
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610354811.0A
Other languages
English (en)
Inventor
孙爱琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Tenver Precision Casting Co Ltd
Original Assignee
Hefei Tenver Precision Casting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Tenver Precision Casting Co Ltd filed Critical Hefei Tenver Precision Casting Co Ltd
Priority to CN201610354811.0A priority Critical patent/CN106040969A/zh
Publication of CN106040969A publication Critical patent/CN106040969A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种酚醛树脂自硬砂的制备方法，包括以下步骤：（1）、预处理；(2)、制备二次处理砂；(3)、将二次处理砂与混合溶液按重量比1：3的比例混合搅拌，除去悬浮物，过滤，得到三次处理砂；(4)、将步骤（3）中得到的三次处理砂进行水洗、烘干，得到再生砂，将再生砂与新砂按重量比1：0.2的比例混合，将混合后的砂加入覆膜砂装置，加入砂重量0.5%的粉末状热塑性酚醛树脂胶粘剂，在145℃下搅拌处理1h，然后加入砂重量0.08%的石油磺酸钙，继续搅拌2h，自然冷却，得到酚醛树脂自硬砂。本发明制备主要使用旧砂翻新，成本低，节约资源。

Description

一种酚醛树脂自硬砂的制备方法
技术领域
本发明属于铸造领域，具体涉及一种酚醛树脂自硬砂的制备方法。
背景技术
我国是铸造大国，在铸造时，每铸造一吨铸件约产生1.5吨铸造旧砂，我国每年的铸造旧砂产量达到5000万吨以上，很多采用掩埋的方式进行处理，在自硬砂制备时，大多使用新砂制作，成本较高。现在虽然有一些酚醛树脂自硬砂旧砂回收方法，而且其中的酚醛树脂除去率较低，造成在再次利用时，造成硬化效果差或者容易出现缺陷。
发明内容
本发明的目的是提供一种酚醛树脂自硬砂的制备方法，主要使用旧砂回收制造，经过处理可以达到铸造需求。
本发明通过以下技术方案实现：
一种酚醛树脂自硬砂的制备方法，包括以下步骤：
（1）、将100kg旧砂进行破碎，过40目筛，将旧砂放入洗涤池，使用300L质量分数为2%的柠檬酸钾溶液浸泡，浸泡过程中使用超声波进行处理，超声波频率为25-28KHz，震荡10min后，按4m3/h的流量加入质量浓度为6%的氨水，氨水加入量为235L，在25℃下搅拌处理12-15min，过滤，除去滤液，得到预处理砂；
(2)、将步骤（1）处理好的预处理砂使用硅砂擦洗机处理，擦洗处理时，进料浓度为33%，将擦洗处理后的砂烘干，使用磁选机进行磁选处理，磁选时，磁场强度为0.72T，得到二次处理砂；
(3)、将二次处理砂与混合溶液按重量比1：3的比例混合搅拌，除去悬浮物，过滤，得到三次处理砂，混合溶液按重量比由以下原料制成：水100份、硫酸25份、柴油22份、烯丙基磺酸钠2.5份、十二烷基磺酸钠1.2份、硝酸8份；
(4)、将步骤（3）中得到的三次处理砂进行水洗、烘干，得到再生砂，将再生砂与新砂按重量比1：0.2的比例混合，将混合后的砂加入覆膜砂装置，加入砂重量0.5%的粉末状热塑性酚醛树脂胶粘剂，在145℃下搅拌处理1h，然后加入砂重量0.08%的石油磺酸钙，继续搅拌2h，自然冷却，得到酚醛树脂自硬砂。
本发明的有益效果：本发明提供的铸造用酚醛树脂自硬砂的制备方法主要使用酚醛树脂自硬砂旧作为原料，由于旧砂中砂酚醛树脂难以分离去除的特性，采用先使用洗涤液浸泡，然后擦洗、磁选处理，再进行浮选，并精确控制各步骤的温度及处理时间，可以明显提升酚醛树脂及钠离子的去除率，处理后再生砂的LOl＜0.2%，Na2O含量低于0.05%，旧砂回收率达到90%，回收后的再生砂与少量的新砂混合使用进行覆膜处理，砂模稳定性高，可以有效防止出现气孔、砂眼、裂纹等，成品率在98.5%以上，本发明的混合溶液经处理后也可以重复使用，降低了处理成本。
具体实施方式
一种酚醛树脂自硬砂的制备方法，包括以下步骤：
（1）、将100kg旧砂进行破碎，过40目筛，将旧砂放入洗涤池，使用300L质量分数为2%的柠檬酸钾溶液浸泡，浸泡过程中使用超声波进行处理，超声波频率为25-28KHz，震荡10min后，按4m3/h的流量加入质量浓度为6%的氨水，氨水加入量为235L，在25℃下搅拌处理12-15min，过滤，除去滤液，得到预处理砂；
(2)、将步骤（1）处理好的预处理砂使用硅砂擦洗机处理，擦洗处理时，进料浓度为33%，将擦洗处理后的砂烘干，使用磁选机进行磁选处理，磁选时，磁场强度为0.72T，得到二次处理砂；
(3)、将二次处理砂与混合溶液按重量比1：3的比例混合搅拌，除去悬浮物，过滤，得到三次处理砂，混合溶液按重量比由以下原料制成：水100份、硫酸25份、柴油22份、烯丙基磺酸钠2.5份、十二烷基磺酸钠1.2份、硝酸8份；
(4)、将步骤（3）中得到的三次处理砂进行水洗、烘干，得到再生砂，将再生砂与新砂按重量比1：0.2的比例混合， 将混合后的砂加入覆膜砂装置，加入砂重量0.5%的粉末状热塑性酚醛树脂胶粘剂，在145℃下搅拌处理1h，然后加入砂重量0.08%的石油磺酸钙，继续搅拌2h，自然冷却，得到酚醛树脂自硬砂。

Claims (1)

1.一种酚醛树脂自硬砂的制备方法，其特征在于，包括以下步骤：
（1）、将100kg旧砂进行破碎，过40目筛，将旧砂放入洗涤池，使用300L质量分数为2%的柠檬酸钾溶液浸泡，浸泡过程中使用超声波进行处理，超声波频率为25-28KHz，震荡10min后，按4m3/h的流量加入质量浓度为6%的氨水，氨水加入量为235L，在25℃下搅拌处理12-15min，过滤，除去滤液，得到预处理砂；
(2)、将步骤（1）处理好的预处理砂使用硅砂擦洗机处理，擦洗处理时，进料浓度为33%，将擦洗处理后的砂烘干，使用磁选机进行磁选处理，磁选时，磁场强度为0.72T，得到二次处理砂；
(3)、将二次处理砂与混合溶液按重量比1：3的比例混合搅拌，除去悬浮物，过滤，得到三次处理砂，混合溶液按重量比由以下原料制成：水100份、硫酸25份、柴油22份、烯丙基磺酸钠2.5份、十二烷基磺酸钠1.2份、硝酸8份；
(4)、将步骤（3）中得到的三次处理砂进行水洗、烘干，得到再生砂，将再生砂与新砂按重量比1：0.2的比例混合， 将混合后的砂加入覆膜砂装置，加入砂重量0.5%的粉末状热塑性酚醛树脂胶粘剂，在145℃下搅拌处理1h，然后加入砂重量0.08%的石油磺酸钙，继续搅拌2h，自然冷却，得到酚醛树脂自硬砂。
CN201610354811.0A 2016-05-26 2016-05-26 一种酚醛树脂自硬砂的制备方法 Pending CN106040969A (zh)