CN105969184A - 一种低腐蚀性的汽车防锈蜡 - Google Patents
一种低腐蚀性的汽车防锈蜡 Download PDFInfo
- Publication number
- CN105969184A CN105969184A CN201610354824.8A CN201610354824A CN105969184A CN 105969184 A CN105969184 A CN 105969184A CN 201610354824 A CN201610354824 A CN 201610354824A CN 105969184 A CN105969184 A CN 105969184A
- Authority
- CN
- China
- Prior art keywords
- parts
- attapulgite
- low
- cooled
- corrosiveness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种低腐蚀性的汽车防锈蜡，由以下原料制成:石蜡油25份、石油磺酸钠15份、改性凹凸棒土1.5份、聚乙烯蜡11份、纳米氯化银0.05份、纳米石墨0.45份、聚乙烯醇9份、三硬脂酸甘油酯2.6份、甲基纤维素1.5份、二氧化钛0.25份、聚丙二醇二缩水甘油醚0.5份、羟基硅油5份、十二烷基磺酸钠1.2份、乙酰丙酮铁0.6份、松节油30份。本发明提供的防锈蜡制备方法简单，无腐蚀性，安全性高。
Description
技术领域
本发明属于涂料领域，具体涉及一种低腐蚀性的汽车防锈蜡。
背景技术
汽车防锈蜡是在汽车出口在海上运输过程中，由于海上空气潮湿，加大对汽车表面的腐蚀力度。在出口前喷上一层防锈蜡，风干后，有一层蜡模留在表面上，可以有效的防止生锈。现有很多防锈蜡具有防锈功能，但是往往都有腐蚀性，长时间使用容易造成腐蚀。
发明内容
本发明的目的是提供一种低腐蚀性的汽车防锈蜡，具有良好的防锈性能，而且具有很好的耐候性。
本发明通过以下技术方案实现：
一种低腐蚀性的汽车防锈蜡，按重量计，由以下原料制成:石蜡油25份、石油磺酸钠15份、改性凹凸棒土1.5份、聚乙烯蜡11份、纳米氯化银0.05份、纳米石墨0.45份、聚乙烯醇9份、三硬脂酸甘油酯2.6份、甲基纤维素1.5份、二氧化钛0.25份、聚丙二醇二缩水甘油醚0.5份、羟基硅油5份、十二烷基磺酸钠1.2份、乙酰丙酮铁0.6份、松节油30份。
所述改性凹凸棒土使用以下方法制备：将凹凸棒土在1520℃下无氧煅烧12min，降温至1000℃使使用凹凸棒土重量8倍的质量分数58%的硫酸溶液浸泡处理，至冷却至常温，过滤出凹凸棒土，水洗至中性，再在1620℃下无氧煅烧5min，自然冷却至常温，粉碎，得到改性凹凸棒土。
一种低腐蚀性的汽车防锈蜡，使用以下方法制备：
（1）、将石蜡油、石油磺酸钠、聚乙烯蜡、甲基纤维素在125℃下搅拌，然后加入羟基硅油、十二烷基磺酸钠升温至142℃继续反应5min；
（2）、将凹凸棒土在1500℃下无氧煅烧12min，降温至1000℃使使用凹凸棒土重量10倍的质量分数58%的硫酸溶液浸泡处理，至冷却至常温，过滤出凹凸棒土，水洗至中性，再在1620℃下无氧煅烧5min，自然冷却至常温，粉碎，得到改性凹凸棒土；
（3）、向松节油中加入聚丙二醇二缩水甘油醚、聚乙烯醇、三硬脂酸甘油酯、改性凹凸棒土、纳米石墨、乙酰丙酮铁，加热至105℃，保温20min，然后加入步骤（1）得到的混合物，升温至110℃，在85转/min的转速下搅拌处理15min；
(4)、将步骤（3）处理好的原料降温至60℃，以75转/min的转速继续搅拌，加入二氧化钛、纳米氧化银，保温处理1h，降温，得到低腐蚀性的汽车防锈蜡。
本发明的有益效果：本发明提供的低腐蚀性的汽车防锈蜡制备方法简单，对人体及汽车没有腐蚀作用，本发明的防锈蜡以石蜡油及松节油为基体，使用聚乙烯醇、纳米石墨、改性凹凸棒土等配合使用，提升成膜效果及分散效果，提升成膜后的强度及抗冷热冲击性能，而且对车表面不会产生腐蚀性，安全性高，不会因环境变化造成开裂等情况发生，经离心分离无明显的水层，说明本申请中各原料分散均匀，而且成本低，无污染。
具体实施方式
一种低腐蚀性的汽车防锈蜡，按重量计，由以下原料制成:石蜡油25份、石油磺酸钠15份、改性凹凸棒土1.5份、聚乙烯蜡11份、纳米氯化银0.05份、纳米石墨0.45份、聚乙烯醇9份、三硬脂酸甘油酯2.6份、甲基纤维素1.5份、二氧化钛0.25份、聚丙二醇二缩水甘油醚0.5份、羟基硅油5份、十二烷基磺酸钠1.2份、乙酰丙酮铁0.6份、松节油30份。
所述改性凹凸棒土使用以下方法制备：将凹凸棒土在1520℃下无氧煅烧12min，降温至1000℃使使用凹凸棒土重量8倍的质量分数58%的硫酸溶液浸泡处理，至冷却至常温，过滤出凹凸棒土，水洗至中性，再在1620℃下无氧煅烧5min，自然冷却至常温，粉碎，得到改性凹凸棒土。
一种低腐蚀性的汽车防锈蜡，使用以下方法制备：
（1）、将石蜡油、石油磺酸钠、聚乙烯蜡、甲基纤维素在125℃下搅拌，然后加入羟基硅油、十二烷基磺酸钠升温至142℃继续反应5min；
（2）、将凹凸棒土在1500℃下无氧煅烧12min，降温至1000℃使使用凹凸棒土重量10倍的质量分数58%的硫酸溶液浸泡处理，至冷却至常温，过滤出凹凸棒土，水洗至中性，再在1620℃下无氧煅烧5min，自然冷却至常温，粉碎，得到改性凹凸棒土；
（3）、向松节油中加入聚丙二醇二缩水甘油醚、聚乙烯醇、三硬脂酸甘油酯、改性凹凸棒土、纳米石墨、乙酰丙酮铁，加热至105℃，保温20min，然后加入步骤（1）得到的混合物，升温至110℃，在85转/min的转速下搅拌处理15min；
(4)、将步骤（3）处理好的原料降温至60℃，以75转/min的转速继续搅拌，加入二氧化钛、纳米氧化银，保温处理1h，降温，得到低腐蚀性的汽车防锈蜡。
Claims (3)
1.一种低腐蚀性的汽车防锈蜡，其特征在于，按重量计，由以下原料制成:石蜡油25份、石油磺酸钠15份、改性凹凸棒土1.5份、聚乙烯蜡11份、纳米氯化银0.05份、纳米石墨0.45份、聚乙烯醇9份、三硬脂酸甘油酯2.6份、甲基纤维素1.5份、二氧化钛0.25份、聚丙二醇二缩水甘油醚0.5份、羟基硅油5份、十二烷基磺酸钠1.2份、乙酰丙酮铁0.6份、松节油30份。
2.根据权利要求1所述的一种低腐蚀性的汽车防锈蜡，其特征在于，所述改性凹凸棒土使用以下方法制备：将凹凸棒土在1520℃下无氧煅烧12min，降温至1000℃使使用凹凸棒土重量8倍的质量分数58%的硫酸溶液浸泡处理，至冷却至常温，过滤出凹凸棒土，水洗至中性，再在1620℃下无氧煅烧5min，自然冷却至常温，粉碎，得到改性凹凸棒土。
3.根据权利要求1所述的一种低腐蚀性的汽车防锈蜡，其特征在于，使用以下方法制备：
（1）、将石蜡油、石油磺酸钠、聚乙烯蜡、甲基纤维素在125℃下搅拌，然后加入羟基硅油、十二烷基磺酸钠升温至142℃继续反应5min；
（2）、将凹凸棒土在1500℃下无氧煅烧12min，降温至1000℃使使用凹凸棒土重量10倍的质量分数58%的硫酸溶液浸泡处理，至冷却至常温，过滤出凹凸棒土，水洗至中性，再在1620℃下无氧煅烧5min，自然冷却至常温，粉碎，得到改性凹凸棒土；
（3）、向松节油中加入聚丙二醇二缩水甘油醚、聚乙烯醇、三硬脂酸甘油酯、改性凹凸棒土、纳米石墨、乙酰丙酮铁，加热至105℃，保温20min，然后加入步骤（1）得到的混合物，升温至110℃，在85转/min的转速下搅拌处理15min；
(4)、将步骤（3）处理好的原料降温至60℃，以75转/min的转速继续搅拌，加入二氧化钛、纳米氧化银，保温处理1h，降温，得到低腐蚀性的汽车防锈蜡。