CN105924160A - Preparation method for dental zirconia ceramic restoration - Google Patents
Preparation method for dental zirconia ceramic restoration Download PDFInfo
- Publication number
- CN105924160A CN105924160A CN201610275456.8A CN201610275456A CN105924160A CN 105924160 A CN105924160 A CN 105924160A CN 201610275456 A CN201610275456 A CN 201610275456A CN 105924160 A CN105924160 A CN 105924160A
- Authority
- CN
- China
- Prior art keywords
- dental zirconia
- oxide
- zirconia ceramics
- dental
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for a dental zirconia ceramic restoration. The preparation method for the dental zirconia ceramic restoration comprises the following steps: weighing, grinding, stirring and drying. The dental zirconia ceramic restoration obtained in the invention has high hardness; since a dispersing agent and honeysuckle flower extract are used as the components of the restoration, the problems of frangibility, low glossiness, poor color contrast performance, low transparency and poor antibacterial performance of an all-ceramic material are overcome; used raw materials are widely available and beneficial for human health; and since a coloring agent is used as a component of the dental zirconia ceramic restoration, individual needs of modern society are met and wide market prospects are obtained. The preparation method for the dental zirconia ceramic restoration is simple to operate, convenient in preparation, low in cost and suitable for industrial large-scale production.
Description
Technical field
The invention belongs to dental materials field, be specifically related to the preparation method of a kind of dental zirconia ceramics dummy.
Background technology
Flos Lonicerae is dry flower or the first flower opened of band of caprifoliaceae plant Radix Ophiopogonis.In bar-shaped, upper coarse and lower fine, slightly curved song,
Long 2～3cm, upper diameter 3mm, lower diameter 1.5mm, surface yellow-white or green white, close by pubescence.Flos Lonicerae is extracted
Thing, extracts from honeysuckle flower, and Main Ingredients and Appearance is chlorogenic acid.Can be as medicine, health product, the raw material of cosmetics.Modern
Medical research proves, Flos Lonicerae is for streptococcus, staphylococcus, Bacillus typhi, dysentery bacterium, large intestine and bacillus pyocyaneus, pneumonia
Diplococcus, bordetella pertussis, meningococcus etc., have stronger antibacterial power, and treatment influenza and inflammation are all had one
Constant current modulation is imitated.
Dispersant (Dispersant) is a kind of to have lipophile and two kinds of opposite nature of hydrophilic in intramolecular simultaneously
Interfacial agent.Can homogeneous dispersion those be poorly soluble in liquid inorganic, the solid of organic pigment and liquid particles, the most also
Sedimentation and the cohesion of granule can be prevented, form the amphipathic reagent needed for stable suspension.Dispersant can promote gloss, prevent
Floating, minimizing flocculation, increase color developing, increase color saturation, increase transparency.
The development of Oral Repair is inseparable with the development of oral cavity material and technique, dentures repai material mainly have pottery,
Resin and metal material.And the ceramic material own intensity deficiency of traditional glass ceramics base and alumina base and fragility are relatively big,
Easily rupturable, limit its use in the reparation in oral cavity.
Along with developing rapidly of current recovery technique of oral cavity, All-ceramic material is by feat of self good biocompatibility, resistance to
A series of speciality such as corrosivity, dielectricity, heat stability and excellent aesthetic effect, become currently used widest oral cavity
Repair materials.The All-ceramic material generally making artificial tooth mainly has aluminium oxide and zirconium oxide, and aluminium oxide has good anti-wear performance,
But fragility is relatively big, easily rupturable, zirconium oxide makes it produce stable four directions due to the effect of mixing of other oxides by contrast
Crystalline phase, therefore, zirconia ceramics has high tenacity, high-flexural strength and high-wearing feature.Therefore, zirconia ceramics is to be currently used for
The All-ceramic material that in the full magnetic material of Oral Repair, mechanical performance is best, suitably as dental prosthesis.But pure zirconia is made pottery
The ceramic product that porcelain sinters out is white, and single this color is difficult to meet the most personalized social need, and mesh
Front dental zirconium oxide prosthesis needs to improve on hardness, anti-inflammation and glossiness, color developing etc., is badly in need of exploitation new
Material.
Summary of the invention
It is an object of the invention to overcome the shortcoming of prior art, it is provided that the system of a kind of dental zirconia ceramics dummy
Preparation Method.
The purpose of the present invention is achieved through the following technical solutions: the preparation side of a kind of dental zirconia ceramics dummy
Method, it comprises the following steps:
S1. weigh: weigh dental zirconia ceramics dummy raw material by formula proportion, standby；Described dental zirconium oxide is made pottery
Porcelain veneer it be made up of the raw material of following weight parts: zirconium oxide: 6～17；Aluminium oxide: 0.5～1.0；Ceramics: 10～25；
Starch: 25～48；Yittrium oxide: 3～12；Dispersant: 0.5～2.5；Water-soluble binder: 1.5～3；Flos Lonicerae extractive solution: 0.3
～2；Coloring agent: 0.5～5；
S2. grind: zirconium oxide, aluminium oxide, ceramics, yittrium oxide, dispersant and coloring agent are put in ball mill and grinds
Mill, the time of described grinding is 1.5～3.5h, obtains grounds travel material mixture；
S3. stirring: will join in crucible in grounds travel material mixture, add starch and water-soluble binder after heating, stir
Adding Flos Lonicerae extractive solution after mixing 30～50min coolings, stir to obtain stirring mixture；
S4. it is dried: above-mentioned stirring mixture is poured in mould, is vacuum dried 2～3h, i.e. prepares dental zirconia ceramics
Dummy.
Further, described dispersant is dehydrated alcohol or stearic acid.
Further, the one during described water-soluble binder is polyvinyl alcohol, xanthan gum or methylcellulose.
Further, the one during described coloring agent is Erbia, cerium oxide, ferrum oxide, Dineodymium trioxide or praseodymium oxide.
Further, the mesh number of described starch is 600～800 mesh.
Further, the mesh number of described ceramics is 700～800 mesh.
Further, described in step S3, the speed of stirring is 420～500rpm, is cooled to 40～50 DEG C after stirring.
The invention have the advantages that to use the dental zirconia ceramics dummy that obtains of the present invention to have higher hard
Degree, adds dispersant and Flos Lonicerae extractive solution in its composition, solve that All-ceramic material is frangible, glossiness is low, color developing is poor, saturating
The problem that lightness is low and antibiotic property is poor, and the material source selected is wide, to health；Dental zirconia ceramics of the present invention
Dummy composition adds coloring agent, meets the social need that modern society is personalized, there is wide market prospect；This
The preparation method of the dental zirconia ceramics dummy that invention provides is simple to operate, prepare convenience, low cost, be applicable to industry
Change large-scale production.
Detailed description of the invention
Below in conjunction with embodiment, the present invention will be further described, and protection scope of the present invention is not limited to following institute
State.
Embodiment 1: the preparation method of a kind of dental zirconia ceramics dummy, it comprises the following steps:
S1. weigh: weigh dental zirconia ceramics dummy raw material by formula proportion, standby；Described dental zirconium oxide is made pottery
Porcelain veneer it be made up of the raw material of following weight parts: zirconium oxide: 6；Aluminium oxide: 0.5；Ceramics: 10；Starch: 25；Oxidation
Yttrium: 3；Dehydrated alcohol: 0.5；Polyvinyl alcohol: 1.5；Flos Lonicerae extractive solution: 0.3；Erbia: 0.5；The mesh number of described starch is
600 mesh；The mesh number of described ceramics is 700 mesh；
S2. grind: zirconium oxide, aluminium oxide, ceramics, yittrium oxide, dehydrated alcohol and Erbia are put in ball mill and grinds
Mill, the time of described grinding is 1.5h, obtains grounds travel material mixture；
S3. stirring: will join in crucible in grounds travel material mixture, add starch and polyvinyl alcohol after heating, with
To 40 DEG C after the speed stirring 30min cooling of 420rpm, adding Flos Lonicerae extractive solution, stir to obtain stirring mixture；
S4. it is dried: above-mentioned stirring mixture is poured in mould, is vacuum dried 2h, i.e. prepares dental zirconia ceramics reparation
Body.
Embodiment 2: the preparation method of a kind of dental zirconia ceramics dummy, it comprises the following steps:
S1. weigh: weigh dental zirconia ceramics dummy raw material by formula proportion, standby；Described dental zirconium oxide is made pottery
Porcelain veneer it be made up of the raw material of following weight parts: zirconium oxide: 17；Aluminium oxide: 1.0；Ceramics: 25；Starch: 48；Oxidation
Yttrium: 12；Stearic acid: 2.5；Xanthan gum: 3；Flos Lonicerae extractive solution: 2；Cerium oxide: 5；The mesh number of described starch is 800 mesh；Described
The mesh number of ceramics is 800 mesh；
S2. grind: zirconium oxide, aluminium oxide, ceramics, yittrium oxide, stearic acid and cerium oxide are put in ball mill and grinds
Mill, the time of described grinding is 3.5h, obtains grounds travel material mixture；
S3. stirring: will join in crucible in grounds travel material mixture, add starch and xanthan gum after heating, with 500rpm
Speed stirring 50min cooling after to 50 DEG C, add Flos Lonicerae extractive solution, stir to obtain stirring mixture；
S4. it is dried: above-mentioned stirring mixture is poured in mould, is vacuum dried 3h, i.e. prepares dental zirconia ceramics reparation
Body.
The preparation method of 3 one kinds of dental zirconia ceramics dummies of embodiment, it comprises the following steps:
S1. weigh: weigh dental zirconia ceramics dummy raw material by formula proportion, standby；Described dental zirconium oxide is made pottery
Porcelain veneer it be made up of the raw material of following weight parts: zirconium oxide: 13；Aluminium oxide: 0.8；Ceramics: 17；Starch: 36；Oxidation
Yttrium: 7；Dehydrated alcohol: 1.6；Methylcellulose: 2.3；Flos Lonicerae extractive solution: 1.2；Ferrum oxide: 3.5；The mesh number of described starch is
700 mesh；The mesh number of described ceramics is 750 mesh；
S2. grind: zirconium oxide, aluminium oxide, ceramics, yittrium oxide, dehydrated alcohol and ferrum oxide are put in ball mill and grinds
Mill, the time of described grinding is 2.3h, obtains grounds travel material mixture；
S3. stirring: will join in crucible in grounds travel material mixture, add starch and methylcellulose after heating, with
To 45 DEG C after the speed stirring 40min cooling of 460rpm, adding Flos Lonicerae extractive solution, stir to obtain stirring mixture；
S4. it is dried: above-mentioned stirring mixture is poured in mould, is vacuum dried 2.5h, i.e. prepares dental zirconia ceramics and repair
Complex.
Embodiment 4: the preparation method of a kind of dental zirconia ceramics dummy, it comprises the following steps:
S1. weigh: weigh dental zirconia ceramics dummy raw material by formula proportion, standby；Described dental zirconium oxide is made pottery
Porcelain veneer it be made up of the raw material of following weight parts: zirconium oxide: 15；Aluminium oxide: 0.9；Ceramics: 22；Starch: 42；Oxidation
Yttrium: 11；Stearic acid: 2.2；Methylcellulose: 2.6；Flos Lonicerae extractive solution: 1.7；Dineodymium trioxide: 4.2；The mesh number of described starch is
760 mesh；The mesh number of described ceramics is 790 mesh；
S2. grind: zirconium oxide, aluminium oxide, ceramics, yittrium oxide, stearic acid and Dineodymium trioxide are put in ball mill and grinds
Mill, the time of described grinding is 3h, obtains grounds travel material mixture；
S3. stirring: will join in crucible in grounds travel material mixture, add starch and methylcellulose after heating, with
To 47 DEG C after the speed stirring 45min cooling of 440rpm, adding Flos Lonicerae extractive solution, stir to obtain stirring mixture；
S4. it is dried: above-mentioned stirring mixture is poured in mould, is vacuum dried 3h, i.e. prepares dental zirconia ceramics reparation
Body.
Embodiment 5: the preparation method of a kind of dental zirconia ceramics dummy, it comprises the following steps:
S1. weigh: weigh dental zirconia ceramics dummy raw material by formula proportion, standby；Described dental zirconium oxide is made pottery
Porcelain veneer it be made up of the raw material of following weight parts: zirconium oxide: 9；Aluminium oxide: 0.7；Ceramics: 14；Starch: 31；Oxidation
Yttrium: 9；Dehydrated alcohol: 1.8；Polyvinyl alcohol: 2；Flos Lonicerae extractive solution: 0.7；Praseodymium oxide: 1.4；The mesh number of described starch is 620
Mesh；The mesh number of described ceramics is 710 mesh；
S2. grind: zirconium oxide, aluminium oxide, ceramics, yittrium oxide, dehydrated alcohol and praseodymium oxide are put in ball mill and grinds
Mill, the time of described grinding is 2h, obtains grounds travel material mixture；
S3. stirring: will join in crucible in grounds travel material mixture, add starch and polyvinyl alcohol after heating, with
To 42 DEG C after the speed stirring 35min cooling of 490rpm, adding Flos Lonicerae extractive solution, stir to obtain stirring mixture；
S4. it is dried: above-mentioned stirring mixture is poured in mould, is vacuum dried 2h, i.e. prepares dental zirconia ceramics reparation
Body.
Claims (7)
1. the preparation method of a dental zirconia ceramics dummy, it is characterised in that it comprises the following steps:
S1. weigh: weigh dental zirconia ceramics dummy raw material by formula proportion, standby；Described dental zirconium oxide is made pottery
Porcelain veneer is made up of the raw material of following weight parts: zirconium oxide: 6～17；Aluminium oxide: 0.5～1.0；Ceramics: 10～25；Form sediment
Powder: 25～48；Yittrium oxide: 3～12；Dispersant: 0.5～2.5；Water-soluble binder: 1.5～3；Flos Lonicerae extractive solution: 0.3～
2；Coloring agent: 0.5～5；
S2. grind: zirconium oxide, aluminium oxide, ceramics, yittrium oxide, dispersant and coloring agent are put in ball mill and grinds
Mill, the time of described grinding is 1.5～3.5h, obtains grounds travel material mixture；
S3. stirring: will join in crucible in grounds travel material mixture, add starch and water-soluble binder after heating, stir
Adding Flos Lonicerae extractive solution after mixing 30～50min coolings, stir to obtain stirring mixture；
S4. it is dried: above-mentioned stirring mixture is poured in mould, is vacuum dried 2～3h, i.e. prepares dental zirconia ceramics
Dummy.
2. a kind of dental zirconia ceramics dummy as claimed in claim 1, it is characterised in that described dispersant is anhydrous
Ethanol or stearic acid.
3. a kind of dental zirconia ceramics dummy as claimed in claim 1, it is characterised in that described water-soluble binder
For the one in polyvinyl alcohol, xanthan gum or methylcellulose.
4. a kind of dental zirconia ceramics dummy as claimed in claim 1, it is characterised in that described coloring agent is oxidation
One in erbium, cerium oxide, ferrum oxide, Dineodymium trioxide or praseodymium oxide.
5. a kind of dental zirconia ceramics dummy as claimed in claim 1, it is characterised in that the mesh number of described starch is
600～800 mesh.
6. a kind of dental zirconia ceramics dummy as claimed in claim 1, it is characterised in that the mesh number of described ceramics
It is 700～800 mesh.
The preparation method of a kind of dental zirconia ceramics dummy the most as claimed in claim 1, it is characterised in that step S3
Described in stirring speed be 420～500rpm, be cooled to 40～50 DEG C after stirring.