CN105714559A - Non-iron finishing method for piece-dyed pure cotton fabric - Google Patents

Non-iron finishing method for piece-dyed pure cotton fabric Download PDF

Info

Publication number
CN105714559A
CN105714559A CN201610203180.2A CN201610203180A CN105714559A CN 105714559 A CN105714559 A CN 105714559A CN 201610203180 A CN201610203180 A CN 201610203180A CN 105714559 A CN105714559 A CN 105714559A
Authority
CN
China
Prior art keywords
fabric
concentration
bake
formaldehyde
ironing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610203180.2A
Other languages
Chinese (zh)
Inventor
张战旗
王艾德
李美玉
李娜
祝辉
耿飞
王以臣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lufeng Weaving and Dyeing Co Ltd
Original Assignee
Lufeng Weaving and Dyeing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lufeng Weaving and Dyeing Co Ltd filed Critical Lufeng Weaving and Dyeing Co Ltd
Priority to CN201610203180.2A priority Critical patent/CN105714559A/en
Publication of CN105714559A publication Critical patent/CN105714559A/en
Pending legal-status Critical Current

Abstract

The invention provides a non-iron finishing method for piece-dyed pure cotton fabric. The non-iron finishing method is characterized by comprising technological processes in sequence as follows: cloth turning, singeing, desizing and scouring, bleaching, mercerizing, liquid ammonia finishing, non-ironing, baking, washing, tentering, pre-shrinking as well as checking and packaging, wherein an intelligent non-iron technology is adopted for the fabric, resin and fibers are subjected to a crosslinking reaction sufficiently, formaldehyde and strength loss caused by resin residues are avoided, strength repair is avoided in a dyeing and finishing process, the content of formaldehyde of a cloth cover can be reduced, and the increase of formaldehyde can be prevented; with the adoption of non-iron finishing, the appearance of the fabric washed 5 times with an AATCC 124 method can reach level 3.2 or higher, and the content of formaldehyde is 60 PPM or lower through testing with a JIS L1041:2011/8.1.4B method. The processed fabric is soft and comfortable to wear, is environment-friendly and has an excellent non-iron effect.

Description

Textile piece dyeing fabric noniron finish method
Technical field
The present invention provides a kind of textile piece dyeing fabric noniron finish method, belongs to technical field of textile printing.
Background technology
Cotton conventional take fiber as a kind of, have that moisture absorption is ventilative, antistatic, an advantage such as comfortable and easy to wear, very popular；But there is also poor flexibility, crease easily, wear the shortcomings such as not well-pressed.Therefore, noniron finish is to improve bafta wearability, improves the important arranging process of added value.
But along with the raising of the non-ironing rank of fabric, the tearing brute force of fabric reduces, cloth cover formaldehyde content raises, and after fabric placement, formaldehyde raises.Therefore, in order to prevent tearing brute force damage wearability from reducing, reducing cloth cover formaldehyde content and improve the non-ironing rank of fabric, the intelligent noniron finish of bafta has great importance.
Summary of the invention
The present invention provides one can overcome in drawbacks described above, fabric fiber strength in process of production little, the dyeing and finishing course of processing of damage and can wash as whiteness reaches Customer Standard, using water wisely, is absent from the problems such as formaldehyde and gives the higher easy-care properties of fabric, dimensional stability and the low formaldehyde environmental protection textile piece dyeing fabric noniron finish method to health fanout free region.Its technical scheme is:
A kind of textile piece dyeing fabric noniron finish method, it is characterized in that: according to non-ironing front fabric strength and client's flatness quality standard, choose optimum resin and catalyst amount, ensure bake add man-hour resin with fiber there is cross-linking reaction completely, avoid cull to cause formaldehyde and strength damage, its technological process is followed successively by weaving, turns over cloth, singes, desizing kiering, bleaching, mercerising, liquid ammonia finishing, non-ironing, bake, wash, tentering, preshrunk and test dress.
Non-ironing operation: carry out on stenter; the component of non-ironing auxiliary agent and weight proportion are resin EFR-3::100～130g/l, acidic catalyst 531:40～52g/l, fiber protection agent SF-P20～30g/l; softening agent SMH-10:20～30 acid 1～2g/l; all the other are water; drying room temperature controls at 90～120 DEG C; cropping humidity is between 5～5.5%, and tentering overfeeding 2%, expanding is the upper limit 2～3cm of Fabric width；
Bake operation: process at guide roll type baker, drying room temperature: 140～150 degree, bake the time 3 minutes, bake powerful control 7～7.5N
Washing step: 70 DEG C～90 DEG C cleanings on rinsing machine, acid adjustment groove pH value 3.5, cloth cover pH value controls 6.5～7.5
Tentering operation: fabric keeps relaxed state to dry, softening agent SMI-52 consumption 20g/l～30g/l, penetrant m RZ consumption 1～2g/l
The present invention compared with prior art, has an advantage in that:
1, the formulation of the selection of low formaldehyde resin and catalyst and optimised process formula: by selecting low formaldehyde resin EFR-3 and catalyst 531, according to according to non-ironing front fabric strength and client's flatness quality standard, optimum resin catalyst proportion technical recipe is determined by little sample testing, ensure that resin reacts with fiber completely, cloth cover noresidue resin.
2, best baking is formulated: bakes brute force by high temperature 140～150 degree and reaches customer requirement standard, easy-care properties reaches Customer Standard more than 3.2 grades, bake formaldehyde and control below 60PPM, fabric flat appearance degree can be effectively improved and content of formaldehyde prevents strength damage big, conventional non-ironing face fabric easy-care properties at about 3.0 grades, more than content of formaldehyde 75PPM and bake fibre damage under the bad hot conditions of control and be seriously unfavorable for dress.
3, the non-ironing face fabric adopting present invention processing can reduce brute force in arrangement process and reprocess, reduce washing and save the energy, and fabric whiteness, easy-care properties, formaldehyde are superior to conventional non-ironing face fabric in the market, soft with this fabric, breathability, good hygroscopicity, wrinkle resistance is more superior, and fabric 5 water-cleaning appearances under AATCC124 method can reach more than 3.2 grades, content of formaldehyde JISL1041:2011/8.1.4B method test below 60PPM, belongs to high-grade wash-and-wear of shirt fabric.
Detailed description of the invention
Embodiment 1: fabric specification is: the plain fabric of CM50*CM80/2T*160*70*60/61, and technological process is followed successively by:
Turn over cloth: singe, move back boil, bleach, mercerising, liquefied ammonia, non-ironing, bake, wash, tentering, preshrunk and test dress
Turning over cloth operation: positive and negative is consistent, margin to seam place is straight, firm；
Singe operation: singe clean；
Desizing kiering operation: desizing is clean, and desizing rate reaches more than 98%, and after kiering, capillary effect reaches 5cm/5min, to ensure non-ironing effect and feel；
Bleaching process: the CIE resin under d 65 illuminant of the fabric whiteness after bleaching reaches 87；
Mercerizing process: mercerising is abundant, and cloth cover pH value is 7～9.
Liquid ammonia finishing operation: adopting conventional liquid ammonia finishing, the fabric pH value after liquid ammonia finishing is 6.
Non-ironing operation: carry out on stenter; in non-ironing auxiliary agent the concentration of resin EFR-3 be 130g/l, acidic catalyst 531 concentration be 52g/l, fiber protection agent SF-P concentration be 30g/l; the concentration of softening agent SMH-10 is 30g/l; organic acid concentration is 2g/l; all the other are water, and drying room temperature controls at 120 DEG C, and cropping humidity is between 5～5.5%; tentering overfeeding 2%, expanding is the upper limit 2～3cm of Fabric width；
Bake operation: process at guide roll type baker, drying room temperature: 150 degree, bake the time 3 minutes, bake powerful control 7～7.5N；
Washing step: 70 DEG C of cleanings on rinsing machine, acid adjustment groove pH value 3.5, cloth cover pH value controls 7.0；
Tentering operation: fabric keeps relaxed state to dry, softening agent SMI-52 concentration 30g/l, penetrant m RZ concentration 2g/l；
Preshrunk: for meeting the shrink requirement of fabric, carrying out on preshrinking machine, washing shrinkage controls-2.5%；
Manufacture test data are as follows:
Embodiment 2: fabric specification is: the plain fabric of CPT36*CPT36*112*80 plain weave, and technological process is followed successively by:
Turn over cloth: singe, move back boil, bleach, mercerising, liquefied ammonia, non-ironing, bake, wash, tentering, preshrunk and test dress
Turning over cloth operation: positive and negative is consistent, margin to seam place is straight, firm；
Singe operation: singe clean；
Desizing kiering operation: desizing is clean, and desizing rate reaches more than 98%, and after kiering, capillary effect reaches 5cm/5min, to ensure non-ironing effect and feel；
Bleaching process: the CIE resin under d 65 illuminant of the fabric whiteness after bleaching reaches 87；
Mercerizing process: mercerising is abundant, and cloth cover pH value is 7～9.
Liquid ammonia finishing operation: adopting conventional liquid ammonia finishing, the fabric pH value after liquid ammonia finishing is 6.
Non-ironing operation: carry out on stenter; in non-ironing auxiliary agent the concentration of resin EFR-3 be 160g/l, acidic catalyst 531 concentration be 64g/l, fiber protection agent SF-P concentration be 30g/l; the concentration of softening agent SMH-10 is 30g/l; organic acid concentration is 2g/l; all the other are water, and drying room temperature controls at 120 DEG C, and cropping humidity is between 5～5.5%; tentering overfeeding 2%, expanding is the upper limit 2～3cm of Fabric width；
Bake operation: process at guide roll type baker, drying room temperature: 150 degree, bake the time 3 minutes, bake powerful control 7～7.5N；
Washing step: 70 DEG C of cleanings on rinsing machine, acid adjustment groove pH value 3.5, cloth cover pH value controls 7.0；
Tentering operation: fabric keeps relaxed state to dry, softening agent SMI-52 concentration 30g/l, penetrant m RZ concentration 2g/l；
Preshrunk: for meeting the shrink requirement of fabric, carrying out on preshrinking machine, washing shrinkage controls-2.5%；
Manufacture test data are as follows:
Note: the resin EFR-3, the acidic catalyst 531 that use in the present invention, be the product of Hong Kong advanced person Chemical Co., Ltd., fiber protection agent SF-P, softening agent SMH-10 are Lu Rui Chemical Co., Ltd. product.Softening agent SMI-52 Lu Rui Chemical Co., Ltd. product, penetrant m RZ is Ang Gao Chemical Co., Ltd. product.

Claims (1)

1. a textile piece dyeing fabric noniron finish method, it is characterised in that technological process is followed successively by and turns over cloth, singes, desizing kiering, bleaching, mercerising, liquid ammonia finishing, non-ironing, bake, wash, tentering, preshrunk and test dress；Wherein:
Non-ironing operation: carry out on stenter; in non-ironing auxiliary agent the concentration of resin EFR-3 be 100～130g/l, acidic catalyst 531 concentration be 40～52g/l, fiber protection agent SF-P concentration be 20～30g/l; the concentration of softening agent SMH-10 is 20～30g/l; the concentration of organic acid NA is 1～2g/l; all the other are water, and drying room temperature controls at 90～120 DEG C, and cropping humidity is between 5～5.5%; tentering overfeeding 2%, expanding is the upper limit 2～3cm of Fabric width；
Bake operation: process at guide roll type baker, drying room temperature: 140～150 degree, bake the time 3 minutes, bake powerful control 7～7.5N；
Washing step: 70 DEG C～90 DEG C cleanings on rinsing machine, acid adjustment groove pH value 3.5, cloth cover pH value controls 6.5～7.5；
Tentering operation: fabric keeps relaxed state to dry, softening agent SMI-52 concentration: 20g/l～30g/l, penetrant m RZ concentration: 1～2g/l.
CN201610203180.2A 2016-04-01 2016-04-01 Non-iron finishing method for piece-dyed pure cotton fabric Pending CN105714559A (en)