CN105470476A - Lithium ion battery negative electrode for reducing irreversible capacity loss and preparation method of lithium ion battery negative electrode - Google Patents
Lithium ion battery negative electrode for reducing irreversible capacity loss and preparation method of lithium ion battery negative electrode Download PDFInfo
- Publication number
- CN105470476A CN105470476A CN201510730367.3A CN201510730367A CN105470476A CN 105470476 A CN105470476 A CN 105470476A CN 201510730367 A CN201510730367 A CN 201510730367A CN 105470476 A CN105470476 A CN 105470476A
- Authority
- CN
- China
- Prior art keywords
- ion battery
- lithium ion
- negative electrode
- irreversible capacity
- capacity loss
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a lithium ion battery negative electrode for reducing irreversible capacity loss. The lithium ion battery negative electrode comprises a negative electrode current collector and a negative electrode paste, wherein the negative electrode paste is coated on the surface of the negative electrode current collector and comprises the following constituents based on mass: 25-45% of negative electrode active substance, 0.3-5% of conductive agent, 0.3-5% of binding agent, 0-2% of surfactant, 0.0001-0.01% of lithium salt and 50-70% of water, and the percentage sum of all constituents is 100%. With the lithium ion battery negative electrode disclosed by the invention, the irreversible capacity loss of the battery can be effectively reduced, and the energy density of the battery is improved. The invention also provides a preparation method of the lithium ion battery negative electrode for reducing the irreversible capacity loss. The process step is simple, and the method is high in operability, is easy to implement, and can be completely applied to industrial production of a lithium ion battery at a large scale.
Description
Technical field
The present invention relates to lithium ion battery preparing technical field, especially relate to a kind of lithium ion battery negative reducing irreversible capacity loss and preparation method thereof.
Background technology
Directly positive/negative plate is assembled together by barrier film in the manufacture process of lithium ion battery at present, after fluid injection activation, inevitably produces irreversible capacity loss.
The irreversible capacity loss of lithium ion battery is seen as a kind of build-in attribute of lithium ion battery by existing technical scheme, by forming SEI film, the loss portion capacity of battery, first charge-discharge irreversible capacity is increased, this has badly influenced giving full play to of the energy content of battery.At present, large quantity research shows, the SEI film that negative terminal surface is formed is the main cause of irreversible capacity loss.Dissimilar negative material irreversible loss percentage is slightly different, and in general have the negative material of high specific surface area, irreversible capacity loss is larger.Although at present can by Surface coating, improve the surface topography of negative pole particle own and shape, optimization electrolyte solvent composition and use the means such as film for additive to reduce irreversible capacity loss, but irreversible capacity loss percentage is still higher, as Delanium 10 ~ 15%, soft carbon 10 ~ 20% etc.
Such as, application publication number: CN103682347A, the Chinese patent of Shen Qing Publication day 2014.03.26 discloses a kind of composite lithium ion battery cathode material, and this composite lithium ion battery cathode material is mainly composed of the following components: needle-like coke powder, and percentage by weight is 30%-50%; Natural spherical plumbago powder, percentage by weight is 20%-30%; Isotropism coke powder, percentage by weight is 15%-25%; Pitch coke powder, percentage by weight is 10%-20%.The weak point of this negative pole is: can increase irreversible capacity when first charge-discharge, affects giving full play to of the energy content of battery.
Summary of the invention
The present invention is that the lithium ion battery negative in order to solve prior art can increase irreversible capacity when first charge-discharge, affect the problem given full play to of the energy content of battery, provide a kind of formulation optimization, effectively can reduce the irreversible capacity loss of battery, promote the lithium ion battery negative of the reduction irreversible capacity loss of the energy density of battery.
Present invention also offers a kind of lithium ion battery negative preparation method reducing irreversible capacity loss, processing step is simple, workable, is easy to realize, and scale can apply to the suitability for industrialized production of lithium ion battery completely.
To achieve these goals, the present invention is by the following technical solutions:
A kind of lithium ion battery negative reducing irreversible capacity loss, comprise negative current collector and the cathode size being coated on negative pole currect collecting surface, described cathode size is made up of the component of following mass percentage: 25 ~ 45% negative electrode active materials, 0.3 ~ 5% conductive agent, 0.3 ~ 5% binding agent, 0 ~ 2% surfactant, 0.0001 ~ 0.01% lithium salts, 50 ~ 70% water, above-mentioned each component percentages sum is 100%.The cathode size formula of anticathode of the present invention is optimized, particularly in cathode size, with the addition of lithium salts, these lithium salts are after cathode size carries out coating baking, one or more layers metastable state SEI membrane structure evenly can be formed at negative pole particle surface, after battery charging and discharging activation, metastable state SEI film becomes more stable through reforming, can avoid lithium ion battery in follow-up discharge and recharge activation process loss part lithium ion to form SEI film, thus reach the irreversible capacity loss effectively reducing battery, promote the object of the energy density of battery.
As preferably, described negative electrode active material is one or more in Delanium, native graphite, composite graphite, soft carbon, hard carbon.
As preferably, described conductive agent is one or more in SP, KS-6, ECP, carbon nano-tube, gas-phase growth of carbon fibre.
As preferably, described binding agent is SBR butadiene-styrene rubber or LA133 aqueous binders.
As preferably, described surfactant is sodium carboxymethylcellulose or polyvinylpyrrolidone.
As preferably, described lithium salts is LiOH, Li
2cO
3, LiF, Li
2c
2o
4, (CH
2oCO
2li)
2, HCOLi, LiCH
2cH
2oCO
2li, CH
3oCO
2one or more in Li.
Reduce a lithium ion battery negative preparation method for irreversible capacity loss, concrete steps are:
(1) lithium salts is dissolved in the water accounting for total Water 10 ~ 20%, obtains lithium salt solution, stand-by.
(2) add conductive agent after surfactant and remaining water being mixed to be uniformly dispersed formation conducting resinl.
(3), add negative electrode active material dispersion in conducting resinl after, add binding agent and lithium salt solution, stir final vacuum deaeration, obtains cathode size.
(4) cathode size is evenly coated on negative pole currect collecting surface, dries, obtain lithium ion battery negative.
Therefore, the present invention has following beneficial effect:
(1) the cathode size formula of anticathode of the present invention is optimized, particularly in cathode size, with the addition of lithium salts, these lithium salts are after cathode size carries out coating baking, one or more layers metastable state SEI membrane structure evenly can be formed at negative pole particle surface, after battery charging and discharging activation, metastable state SEI film becomes more stable through reforming, can avoid lithium ion battery in follow-up discharge and recharge activation process loss part lithium ion to form SEI film, thus reach the irreversible capacity loss effectively reducing battery, promote the object of the energy density of battery;
(2) preparation method of the present invention, processing step is simple, workable, is easy to realize, and scale can apply to the suitability for industrialized production of lithium ion battery completely.
Embodiment
Below by embodiment, the present invention will be further described.
In the present invention, if not refer in particular to, all percentage is unit of weight, and all devices and raw material all can be buied from market or the industry is conventional, and the method in following embodiment, if no special instructions, is this area conventional method.
Embodiment 1
A kind of lithium ion battery negative reducing irreversible capacity loss, comprise negative current collector and the cathode size being coated on negative pole currect collecting surface, cathode size is made up of the component of following mass percentage: 25% negative electrode active material, 1% conductive agent, 2% binding agent, 1.9999% surfactant, 0.0001% lithium salts, 70% water, wherein, negative electrode active material is Delanium; Conductive agent is SP; Binding agent is LA133 aqueous binders; Surfactant is sodium carboxymethylcellulose; Lithium salts is LiOH and Li
2cO
3(mass ratio 1:1);
The lithium ion battery negative of this reduction irreversible capacity loss obtains by the following method:
(1) lithium salts is dissolved in the water accounting for total Water 10%, obtains lithium salt solution, stand-by;
(2) add conductive agent after surfactant and remaining water being mixed to be uniformly dispersed formation conducting resinl;
(3), add negative electrode active material dispersion in conducting resinl after, add binding agent and lithium salt solution, stir final vacuum deaeration, obtains cathode size;
(4) cathode size is evenly coated on negative pole currect collecting surface, dries, obtain lithium ion battery negative.
Embodiment 2
A kind of lithium ion battery negative reducing irreversible capacity loss, comprise negative current collector and the cathode size being coated on negative pole currect collecting surface, cathode size is made up of the component of following mass percentage: 45% negative electrode active material, 0.3% conductive agent, 2.69% binding agent, 2% surfactant, 0.01% lithium salts, 50% water, wherein, negative electrode active material is Delanium and native graphite (mass ratio 1:1); Conductive agent is KS-6 and gas-phase growth of carbon fibre (mass ratio 3:1); Binding agent is SBR butadiene-styrene rubber; Surfactant is sodium carboxymethylcellulose; Lithium salts is LiOH, Li
2cO
3(CH
2oCO
2li)
2(mass ratio 1:1:1);
The lithium ion battery negative of this reduction irreversible capacity loss obtains by the following method:
(1) lithium salts is dissolved in the water accounting for total Water 15%, obtains lithium salt solution, stand-by;
(2) add conductive agent after surfactant and remaining water being mixed to be uniformly dispersed formation conducting resinl;
(3), add negative electrode active material dispersion in conducting resinl after, add binding agent and lithium salt solution, stir final vacuum deaeration, obtains cathode size;
(4) cathode size is evenly coated on negative pole currect collecting surface, dries, obtain lithium ion battery negative.
Embodiment 3
A kind of lithium ion battery negative reducing irreversible capacity loss, comprise negative current collector and the cathode size being coated on negative pole currect collecting surface, cathode size is made up of the component of following mass percentage: 29.995% negative electrode active material, 0.3 ~ 5% conductive agent, 0.3 ~ 5% binding agent, 0.005% lithium salts, 60% water, wherein, negative electrode active material is Delanium and soft carbon (mass ratio 1:3); Conductive agent is SP, KS-6 and ECP(mass ratio 1:3:1); Binding agent is LA133 aqueous binders; Lithium salts is HCOLi and LiCH
2cH
2oCO
2li(mass ratio 2:3);
The lithium ion battery negative of this reduction irreversible capacity loss obtains by the following method:
(1) lithium salts is dissolved in the water accounting for total Water 20%, obtains lithium salt solution, stand-by;
(2) add conductive agent after surfactant and remaining water being mixed to be uniformly dispersed formation conducting resinl;
(3), add negative electrode active material dispersion in conducting resinl after, add binding agent and lithium salt solution, stir final vacuum deaeration, obtains cathode size;
(4) cathode size is evenly coated on negative pole currect collecting surface, dries, obtain lithium ion battery negative.
Embodiment 4
A kind of lithium ion battery negative reducing irreversible capacity loss, comprise negative current collector and the cathode size being coated on negative pole currect collecting surface, cathode size is made up of the component of following mass percentage: 35% negative electrode active material, 0.3% conductive agent, 0.3% binding agent, 1% surfactant, 0.01% lithium salts, 63.39% water, wherein, negative electrode active material is soft carbon and hard carbon (mass ratio 2:3); Conductive agent is SP, ECP and carbon nano-tube (mass ratio 1:1:1); Binding agent is SBR butadiene-styrene rubber; Surfactant is polyvinylpyrrolidone; Lithium salts is LiF, Li
2c
2o
4, CH
3oCO
2li(mass ratio 1:1:3);
The lithium ion battery negative of this reduction irreversible capacity loss obtains by the following method:
(1) lithium salts is dissolved in the water accounting for total Water 10%, obtains lithium salt solution, stand-by;
(2) add conductive agent after surfactant and remaining water being mixed to be uniformly dispersed formation conducting resinl;
(3), add negative electrode active material dispersion in conducting resinl after, add binding agent and lithium salt solution, stir final vacuum deaeration, obtains cathode size;
(4) cathode size is evenly coated on negative pole currect collecting surface, dries, obtain lithium ion battery negative.
Lithium ion battery negative of the present invention is applied in conventional phosphoric acid lithium iron battery, irreversible capacity loss percentage can be reduced to 3 ~ 5%, compared to Delanium (irreversible capacity loss percentage 10 ~ 15%), the conventional anode such as soft carbon (irreversible capacity loss percentage 10 ~ 20%), effect is very remarkable.
Above-described embodiment is one of the present invention preferably scheme, not does any pro forma restriction to the present invention, also has other variant and remodeling under the prerequisite not exceeding the technical scheme described in claim.
Claims (7)
1. one kind is reduced the lithium ion battery negative of irreversible capacity loss, comprise negative current collector and the cathode size being coated on negative pole currect collecting surface, it is characterized in that, described cathode size is made up of the component of following mass percentage: 25 ~ 45% negative electrode active materials, 0.3 ~ 5% conductive agent, 0.3 ~ 5% binding agent, 0 ~ 2% surfactant, 0.0001 ~ 0.01% lithium salts, 50 ~ 70% water, above-mentioned each component percentages sum is 100%.
2. a kind of lithium ion battery negative reducing irreversible capacity loss according to claim 1, is characterized in that, described negative electrode active material is one or more in Delanium, native graphite, composite graphite, soft carbon, hard carbon.
3. a kind of lithium ion battery negative reducing irreversible capacity loss according to claim 1, is characterized in that, described conductive agent is one or more in SP, KS-6, ECP, carbon nano-tube, gas-phase growth of carbon fibre.
4. a kind of lithium ion battery negative reducing irreversible capacity loss according to claim 1, is characterized in that, described binding agent is SBR butadiene-styrene rubber or LA133 aqueous binders.
5. a kind of lithium ion battery negative reducing irreversible capacity loss according to claim 1, is characterized in that, described surfactant is sodium carboxymethylcellulose or polyvinylpyrrolidone.
6. a kind of lithium ion battery negative reducing irreversible capacity loss according to claim 1, is characterized in that, described lithium salts is LiOH, Li
2cO
3, LiF, Li
2c
2o
4, (CH
2oCO
2li)
2, HCOLi, LiCH
2cH
2oCO
2li, CH
3oCO
2one or more in Li.
7. a lithium ion battery negative preparation method for the reduction irreversible capacity loss as described in any one of claim 1 ~ 6, is characterized in that, concrete steps are:
(1) lithium salts is dissolved in the water accounting for total Water 10 ~ 20%, obtains lithium salt solution, stand-by;
(2) add conductive agent after surfactant and remaining water being mixed to be uniformly dispersed formation conducting resinl;
(3), add negative electrode active material dispersion in conducting resinl after, add binding agent and lithium salt solution, stir final vacuum deaeration, obtains cathode size;
(4) cathode size is evenly coated on negative pole currect collecting surface, dries, obtain lithium ion battery negative.