CN105441753A - 一种铝合金轨道及其制备方法 - Google Patents
一种铝合金轨道及其制备方法 Download PDFInfo
- Publication number
- CN105441753A CN105441753A CN201510841276.7A CN201510841276A CN105441753A CN 105441753 A CN105441753 A CN 105441753A CN 201510841276 A CN201510841276 A CN 201510841276A CN 105441753 A CN105441753 A CN 105441753A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- alloy rail
- rail
- surplus
- grouped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种铝合金轨道，由以下重量百分比的成分组成：Cu？1.2-1.8；Mg1.6-2.6；Mn0.1-0.4；Zn3-5；余量为Al。本发明铝合金轨道中主要是Al-？Mg和Al-？Mn合金，其耐蚀性好、易于加工成形和焊接，经挤压、淬火、拉伸、人工时效后可得到机械性能高，防锈、防腐蚀性强的导轨型材，完全满足了航空、航天、汽车、机械制造、船舶及化学工业等领域的使用要求。
Description
技术领域
本发明涉及一种铝合金领域，特别是一种铝合金轨道。
背景技术
目前，铝合金已经是工业中应用最广泛的金属结构材料，其在航空、航天、汽车、机械制造、船舶及化学工业中已大量应用。但是现有成分配比的铝合金材料，其机械性能差，防锈、防腐蚀性弱，所以在轨道上急需一种优质的铝合金材料。
发明内容
本发明要解决的技术问题是针对现有技术的不足，提出一种机械性能高，防锈、防腐蚀性强的铝合金轨道及其制备方法。
本发明要解决的技术问题是通过以下技术方案实现的。本发明是一种铝合金轨道，其特点是，由以下重量百分比的成分组成：Cu1.2-1.8；Mg1.6-2.6；Mn0.1-0.4；Zn3-5；余量为Al。
本发明一种铝合金轨道技术方案中，进一步优选的技术方案特征是：
1、由以下重量百分比的成分组成：Cu1.4-1.6；Mg2-2.4；Mn0.1-0.3；Zn3-4；余量为Al；
2、由以下重量百分比的成分组成：Cu1.5；Mg2.2；Mn00.2；Zn3.5；余量为Al；
本发明要解决的技术问题是通过以下技术方案实现的。本发明是一种铝合金轨道的制备方法，其特点是，铝合金经过挤压、淬火、拉伸、人工时效得到抗拉强度为500-700MPa、拉伸率为10%-14%、布氏硬度为120-160的导轨型材。
本发明一种铝合金轨道的制备方法技术方案中，进一步优选的技术方案特征是：
1、所述导轨型材的抗拉强度为600MPa、拉伸率为12%、布氏硬度为140；
2、所述导轨型材为由顶板、腹板和底板组成的工字梁，所述底板呈上大下小的锥形底板。
与现有技术相比，本发明铝合金轨道中主要是Al-Mg和Al-Mn合金，其耐蚀性好、易于加工成形和焊接，经挤压、淬火、拉伸、人工时效后可得到机械性能高，防锈、防腐蚀性强的导轨型材，完全满足了航空、航天、汽车、机械制造、船舶及化学工业等领域的使用要求。
具体实施方式
进一步描述本发明的具体技术方案，以便于本领域的技术人员进一步地理解本发明，而不构成其权力的限制。
实施例1，一种铝合金轨道，由以下重量百分比的成分组成：Cu1.2-1.8；Mg1.6-2.6；Mn0.1-0.4；Zn3-5；余量为Al。
实施例2，实施例1所述的铝合金轨道中：由以下重量百分比的成分组成：Cu1.4-1.6；Mg2-2.4；Mn0.1-0.3；Zn3-4；余量为Al。
实施例3，实施例1或2所述的铝合金轨道中：由以下重量百分比的成分组成：Cu1.5；Mg2.2；Mn00.2；Zn3.5；余量为Al。
实施例4，实施例1或2或3所述的铝合金轨道中：由以下重量百分比的成分组成：Cu1.4；Mg2；Mn0.1；Zn3；余量为Al。
实施例5，实施例1-4任一项所述的铝合金轨道中：由以下重量百分比的成分组成：Cu1.6；Mg2.4；Mn0.3；Zn4；余量为Al。
实施例6，一种铝合金轨道的制备方法中：铝合金经过挤压、淬火、拉伸、人工时效得到抗拉强度为500-700MPa、拉伸率为10%-14%、布氏硬度为120-160的导轨型材。
实施例7，实施例6所述的铝合金轨道的制备方法中：所述导轨型材的抗拉强度为600MPa、拉伸率为12%、布氏硬度为140。
实施例8，实施例6或7所述的铝合金轨道的制备方法中：所述导轨型材为由顶板、腹板和底板组成的工字梁，所述底板呈上大下小的锥形底板。
Claims (6)
1.一种铝合金轨道，其特征在于，由以下重量百分比的成分组成：Cu1.2-1.8；Mg1.6-2.6；Mn0.1-0.4；Zn3-5；余量为Al。
2.根据权利要求1所述的铝合金轨道，其特征在于，由以下重量百分比的成分组成：Cu1.4-1.6；Mg2-2.4；Mn0.1-0.3；Zn3-4；余量为Al。
3.根据权利要求1所述的铝合金轨道，其特征在于，由以下重量百分比的成分组成：Cu1.5；Mg2.2；Mn00.2；Zn3.5；余量为Al。
4.如权利要求1-3任一项所述铝合金轨道的制备方法，其特征在于：铝合金经过挤压、淬火、拉伸、人工时效得到抗拉强度为500-700MPa、拉伸率为10%-14%、布氏硬度为120-160的导轨型材。
5.根据权利要求4所述铝合金轨道的制备方法，其特征在于：所述导轨型材的抗拉强度为600MPa、拉伸率为12%、布氏硬度为140。
6.根据权利要求4所述铝合金轨道的制备方法，其特征在于：所述导轨型材为由顶板、腹板和底板组成的工字梁，所述底板呈上大下小的锥形底板。