CN105273482A - Putty powder for internal walls - Google Patents
Putty powder for internal walls Download PDFInfo
- Publication number
- CN105273482A CN105273482A CN201510695927.6A CN201510695927A CN105273482A CN 105273482 A CN105273482 A CN 105273482A CN 201510695927 A CN201510695927 A CN 201510695927A CN 105273482 A CN105273482 A CN 105273482A
- Authority
- CN
- China
- Prior art keywords
- parts
- putty powder
- weight
- wall putty
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides putty powder for internal walls. The putty powder comprises raw materials in parts by weight as follows: 30-40 parts of white cement, 25-38 parts of diatomite, 15-21 parts of heavy calcium, 10-17 parts of a binding agent and 3-5 parts of an additive. The putty powder has the benefits as follows: the putty powder has high universality and good water resistance, can prevent cracking and is convenient to use during construction, safe and environment-friendly.
Description
Technical field
The present invention relates generally to putty powder field, is specifically related to a kind of inner wall putty powder.
Background technology
Putty powder is building materials conventional in building trade, and the current putty powder feature of environmental protection is not good, easily ftractures, and smell is comparatively large, causes certain injury to the health of workmen.After brushing putty, need to prevent the long period from just can move in, bring very large inconvenience to construction and life staying idle at home.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of inner wall putty powder, highly versatile, water-tolerant, prevents be full of cracks, easy construction, safety and environmental protection.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of inner wall putty powder, with parts by weight, is made up of following raw material: white cement 30 ~ 40 parts, 25 ~ 38 parts, diatomite, coarse whiting 15 ~ 21 parts, caking agent 10 ~ 17 parts and additive 3 ~ 5 parts.
The invention has the beneficial effects as follows: highly versatile, water-tolerant, prevent be full of cracks, easy construction, safety and environmental protection.
On the basis of technique scheme, the present invention can also do following improvement.
Further, with parts by weight, be made up of following raw material: white cement 36 parts, 33 parts, diatomite, coarse whiting 19 parts, caking agent 14 parts and additive 4 parts.
Further, described caking agent is the mixture of cross-linking starch, benzene emulsion and urethane.
The beneficial effect of above-mentioned further scheme is adopted to be: bond properties is good.
Further, in described caking agent, with parts by weight, cross-linking starch is 3.5 ~ 5.5 parts, benzene emulsion 4.5 ~ 6.5 parts, urethane 2 ~ 5 parts.
Further, in described caking agent, with parts by weight, cross-linking starch is 5 parts, benzene emulsion 6 parts, urethane 3 parts.
The beneficial effect of above-mentioned further scheme is adopted to be: bond properties is good, and not easily bubble.
Further, described additive is the mixture of mould inhibitor, dispersion agent and defoamer.
Further, in described additive, with parts by weight, mould inhibitor 0.5 ~ 1.5 part, dispersion agent 1.8 ~ 2.5 parts, defoamer 0.2 ~ 1 part.
Further, in described additive, with parts by weight, mould inhibitor 1.2 parts, dispersion agent 2 parts, defoamer 0.8 part.
Embodiment
Be described principle of the present invention and feature below in conjunction with embodiment, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment 1:
A kind of inner wall putty powder, with parts by weight, is made up of following raw material: white cement 30 parts, 25 parts, diatomite, coarse whiting 15 parts, caking agent 10 parts and additive 3 parts.
Described caking agent is the mixture of cross-linking starch, benzene emulsion and urethane, and with parts by weight, cross-linking starch is 3.5 parts, benzene emulsion 4.5 parts, urethane 2 parts.
Described additive is the mixture of mould inhibitor, dispersion agent and defoamer, with parts by weight, and mould inhibitor 1 part, dispersion agent 1.8 parts, defoamer 0.2 part.
Embodiment 2:
A kind of inner wall putty powder, with parts by weight, is made up of following raw material: white cement 40 parts, 38 parts, diatomite, coarse whiting 21 parts, caking agent 17 parts and additive 5 parts.
Described caking agent is the mixture of cross-linking starch, benzene emulsion and urethane, and with parts by weight, cross-linking starch is 5.5 parts, benzene emulsion 6.5 parts, urethane 5 parts.
Described additive is the mixture of mould inhibitor, dispersion agent and defoamer, with parts by weight, and mould inhibitor 1.5 parts, dispersion agent 2.5 parts, defoamer 1 part.
Embodiment 3:
A kind of inner wall putty powder, with parts by weight, is made up of following raw material: white cement 36 parts, 33 parts, diatomite, coarse whiting 19 parts, caking agent 14 parts and additive 4 parts.
Described caking agent is the mixture of cross-linking starch, benzene emulsion and urethane, and with parts by weight, cross-linking starch is 5 parts, benzene emulsion 6 parts, urethane 3 parts.
Described additive is the mixture of mould inhibitor, dispersion agent and defoamer, with parts by weight, and mould inhibitor 1.2 parts, dispersion agent 2 parts, defoamer 0.8 part.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (8)
1. an inner wall putty powder, is characterized in that, with parts by weight, is made up of following raw material: white cement 30 ~ 40 parts, 25 ~ 38 parts, diatomite, coarse whiting 15 ~ 21 parts, caking agent 10 ~ 17 parts and additive 3 ~ 5 parts.
2. a kind of inner wall putty powder according to claim 1, is characterized in that, with parts by weight, is made up of following raw material: white cement 36 parts, 33 parts, diatomite, coarse whiting 19 parts, caking agent 14 parts and additive 4 parts.
3. a kind of inner wall putty powder according to claim 1 and 2, is characterized in that, described caking agent is the mixture of cross-linking starch, benzene emulsion and urethane.
4. a kind of inner wall putty powder according to claim 3, is characterized in that, in described caking agent, with parts by weight, cross-linking starch is 3.5 ~ 5.5 parts, benzene emulsion 4.5 ~ 6.5 parts, urethane 2 ~ 5 parts.
5. a kind of inner wall putty powder according to claim 4, is characterized in that, in described caking agent, with parts by weight, cross-linking starch is 5 parts, benzene emulsion 6 parts, urethane 3 parts.
6. a kind of inner wall putty powder according to claim 1 and 2, is characterized in that, described additive is the mixture of mould inhibitor, dispersion agent and defoamer.
7. a kind of inner wall putty powder according to claim 5, is characterized in that, in described additive, with parts by weight, and mould inhibitor 0.5 ~ 1.5 part, dispersion agent 1.8 ~ 2.5 parts, defoamer 0.2 ~ 1 part.
8. a kind of inner wall putty powder according to claim 6, is characterized in that, in described additive, with parts by weight, and mould inhibitor 1.2 parts, dispersion agent 2 parts, defoamer 0.8 part.