CN105200554B - A kind of method that original liquid coloring prepares environmentally friendly polyester fiber - Google Patents
A kind of method that original liquid coloring prepares environmentally friendly polyester fiber Download PDFInfo
- Publication number
- CN105200554B CN105200554B CN201510713645.4A CN201510713645A CN105200554B CN 105200554 B CN105200554 B CN 105200554B CN 201510713645 A CN201510713645 A CN 201510713645A CN 105200554 B CN105200554 B CN 105200554B
- Authority
- CN
- China
- Prior art keywords
- original liquid
- polyester fiber
- liquid coloring
- environmentally friendly
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to technical field of polyester fiber preparation, and in particular to a kind of method that original liquid coloring prepares environmentally friendly polyester fiber.The invention provides a kind of method that original liquid coloring prepares environmentally friendly polyester fiber, comprise the following steps：Environment-friendly dye and solvent, dispersant, wetting agent are deployed into the liquid mill base of original liquid coloring；One or more kinds of liquid mill bases is injected in Fusing polyester pipeline using metering injection pump；Polyester fondant is well mixed with liquid mill base by static mixing device, is transported in spinning manifold and is carried out spinning.The present invention prepares original liquid coloring fiber, without using high pressure, high temperature, constructs the dyeing system environmentally friendly, easy to operate that a kind of high temperature resistant, color fastness are excellent, can be mixed with polyester fondant and realize stable dispersion.
Description
Technical field
The invention belongs to technical field of polyester fiber preparation, and in particular to a kind of original liquid coloring prepares environmentally friendly polyester fiber
Method.
Background technology
Original liquid coloring polyester fiber is exactly the fiber for carrying out spinning after first being coloured to polyester fondant again, with normal dyeing
Method is compared, and original liquid coloring fiber no longer needs road after carrying out to dye, and reduces the production cost of fiber color silk, reduce water and
The consumption of the energy, energy-saving and emission-reduction are with the obvious advantage, meanwhile, the production of original liquid coloring technology coloured fiber color is uniform, color fastness is high,
Original liquid coloring technology meets the requirement of recycling economy development, and national correlation department is advocated to be widelyd popularize in textile industry.
At present, original liquid coloring technology is there is also some defects in actual production process, and such as color adjustment is more difficult, matches somebody with somebody
Color scheme hardly possible is determined, is not suitable for small lot production etc..Therefore, most of original liquid coloring fiber produced at present is all black, state
Interior black silk accounts for more than the 60% of original liquid coloring fiber production, Chinese invention patent application CN102731754A (patent applications
Number be CN201210227606.X, entitled " a kind of polyester black original liquid coloring method "), Chinese invention patent Shen
Please CN104499079A (number of patent application is CN201410709477.7, entitled, and " a kind of original liquid coloring prepares black and gathered
The method of ester fiber "), Chinese invention patent CN103710772A (Patent No. CN201310742922.5, it is entitled
" fiber original liquid coloring superfine carbon black aqueous color paste "), Chinese utility model patent CN204237904U (Patent No.
CN201420735798.X, utility model is entitled " a kind of original liquid coloring prepares the process units of black polyester fiber ") it is all public
Open original liquid coloring method and prepare black polyester fiber.(number of patent application is Chinese invention patent application CN103215656A
CN201310150118.8, entitled " original liquid coloring technique before the solvent carrier of polyester fiber is spun "), Chinese invention patent
(Patent No. CN201310147346.X, entitled " a kind of original liquid coloring prepares coloured polyester fiber to CN103255498A
Method "), Chinese invention patent CN103031755A (Patent No. CN201210584296.7, it is entitled " to be used to wash
Ethylene glycol pigment dispersion of synthetic fibre original liquid coloring and preparation method thereof "), Japan Patent JP2000119913 (A) (Patent No.
JP1998291568, entitled " ア Network リ Le system original liquid coloring Xian Victoria System make makes method with Spinning yarn Yuan Ye System；
Preparation of dope for producing acrylic spun-dyed fiber ") disclose original liquid coloring method
Other color polyester fibers are prepared,《Modern textile technology》(Zhu Song, the present situation of production technology of original liquid coloring polyester fiber and market
Prospect, modern textile technology [J], the 6th phase in 2013,32-35) disclose original liquid coloring polyester fiber present situation of production technology and
Market prospects,《Printing and dyeing assistant》(Zhang Qingshan, Mao Qinghui, Mao Zhiping, the research of organic solvent system synthetic fibers original liquid coloring agent
And application, printing and dyeing assistant [J], volume 26 the 9th phase, 13-16 in 2009) inquire into different hyper-dispersant species, hyper-dispersant use
Measure, shadow of the time to the inorganic pigment color paste system stably dispersing performance using DMAC N,N' dimethyl acetamide as decentralized medium is sanded
Ring.
Original liquid coloring prepares colored fibre can be by way of polymerization process be coloured, such as Chinese invention patent application
(number of patent application is CN201410709477.7 to CN104499079A, and entitled " a kind of original liquid coloring prepares black polyester
The method of fiber "), it is prepared for black fiber；Chinese invention patent CN103031755A (Patent No.
CN201210584296.7, it is entitled " to be used for ethylene glycol pigment dispersion and its preparation side of terylene original liquid coloring
Method ") ethylene glycol pigment dispersion is prepared for, it is molded by the technique such as ester exchange reaction, polymerisation direct fabrics, thus will
Ask dyestuff or pigment, dispersant that there is resistance to elevated temperatures, industrial implementation has larger limitation.Patent of invention Chinese invention
(Patent No. CN201310147346.X, entitled " a kind of original liquid coloring prepares coloured polyester to patent CN103255498A
The method of fiber ") it is improved, it is combined, is solved with polyester fondant direct spinning process using online addition liquid mill base
Big using coloured sewage disposal difficulty caused by the colouring method of high temperature, high pressure or adding carrier, cost is high, and directly discharge can make
Into the problem of serious environmental pollution, while also solving section dry coloring method, dyestuff and feed stock chip co-blended spinning method, color
High energy consumption caused by the discontinuous methods such as master batch and feed stock chip co-blended spinning method, unit consumption is high, the problem such as product batch difference is big, but it is made
Standby dyeing system needs to protect the mixture of polyester support adipic acid and 1,3 butylene glycol through nitrogen, heated up, insulation reaction extremely
Acid value is 10, vacuum distillation 1 hour under 6.67~8.00kPa, and industrializing implementation is relatively complicated.Thus, research and develop a resistance to constant temperature
Degree, stable dispersion, environmental protection, dyeing system easy to operate are the important measures of original liquid coloring polyester fiber production.
Meanwhile, in recent years, ecological textile is all vigorously advocated in countries in the world, and also active development and production are beneficial by research staff
In health, be conducive to the ecological textile of environmental protection, it is nontoxic in itself that ecological textile does not require nothing more than textile, with
Human contact is non-stimulated, while requiring that its production and processing technology such as prints and dyes, arranges process and do not produce poisonous and harmful substance, dyestuff
And printing and dyeing assistant should have the biological degradability that security is become reconciled.It is external to APEO (Anhui base phenol polyethenoxy ether, NPEO and
OPEO limitation requirement) is proposed, and contains NPEO in the terylene spinning finish that most enterprises domestic at present use, after testing
APEO content is 100-250PPM on final products.
Therefore, a kind of high temperature resistant of structure is badly in need of in this area, color fastness is excellent, can mix and be realized stably with polyester fondant
Scattered dyeing system environmentally friendly, easy to operate.
The content of the invention
It is an object of the invention to provide a kind of high temperature resistant, color fastness is excellent, can mix and realizes steady with polyester fondant
Surely the dyeing system environmentally friendly, easy to operate disperseed, i.e., the method that a kind of original liquid coloring prepares environmentally friendly polyester fiber.
The invention provides a kind of method that original liquid coloring prepares environmentally friendly polyester fiber, comprise the following steps：
A, the liquid mill base that environment-friendly dye and solvent, dispersant, wetting agent are deployed into original liquid coloring；
B, using metering injection pump one or more kinds of liquid mill bases is injected in Fusing polyester pipeline；
C, polyester fondant are well mixed with liquid mill base by static mixing device, are transported in spinning manifold and are spun
Silk.
Environment-friendly dye of the present invention, selected from diaminobenzil disulfonic acid class, 4.4- diaminourea hexichol ureas, two
It is more than one or both of amino heterocyclic, environment-friendly type acid dyes, environmental-friendly disperse dye.Described environment-friendly dye is preferred
For direct fast yellow 3BLL, the green IRC of direct sun-proof, direct fast yellow RSC, direct fast red F3B, C.I. acid red 37, C.I.
It is more than one or both of Indian yellow 49, Foron Blue RD-SE 290, Itosperse HW type dyes.
Solvent of the present invention is N,N-dimethylformamide.
Dispersant of the present invention, for the block polymer containing ethoxy-propoxy, its general molecular formula
EOxPOyEOx, the x for 5~113 integer and including 5 and 113, y is 30~70 integer and including 30 and 70, and preferably x is
5th, 20,80, y is 30,33,56,70.In a preferred embodiment of the invention, dispersant be selected from Pluronic P123,
Pluronic F68, Pluronic F127 etc..
Wetting agent of the present invention, is alkyl naphthalene sulfonic acid sodium salt, and its general molecular formula is RCH10H6SO3Na, R are alkane
Base, preferably C are one kind in 1 to 6 low alkyl group, such as isopropyl, isobutyl group, isopentyl.
By environment-friendly dye and solvent N,N-dimethylformamide, the block polymer containing ethoxy-propoxy it is scattered
Agent, alkyl naphthalene sulfonic acid sodium salt wetting agent constitute dyeing system have resistance to 290 DEG C of high temperature, color fastness it is excellent, can be with polyester
Melt mixes and realizes stable dispersion, is easy to industrializing implementation, the solvent in the technical program such as is substituted for into ethylene glycol, or
Dispersant replaces CH series, AFCONA series, or wetting agent is substituted for K12, K14, infiltration JFC, the tinting strength, tinting power of dyestuff, scattered
Property and dispersion stabilization are poor.
In step A, in described liquid mill base, it is made up of following components by weight percentage：
Environment-friendly dye：20~30, preferably 20,25,30；
Solvent：40~60, preferably 45,55,60；
Dispersant：5~15, preferably 7,8,10,15；
Wetting agent：5~15, preferably 7,8,10,15.
In step A, the preferred preparation method of the liquid mill base is：First dispersant, wetting agent are added in solvent,
Stirring dissolves it, then adds environment-friendly dye, stirs, be fully ground pulp, liquid is obtained after it is uniformly dispersed
Mill base.
In step B, multigroup, the identical or different liquid mill base of every group of placement can be set in described metering injection pump, realizes
By in one or more kinds of liquid mill base injection Fusing polyester pipelines, described polyester fondant, is PET or PBT is heated
Melting, the temperature of the polyester fondant is 277~287 DEG C.
In step C, KENICS types, the HI types of Japan and the Switzerland SULZER of the static mixing device, the preferably U.S.
SMR, SMV, SMX and SMXL type and the JLF tandem reinforcements heat transfer static mixing reactor of Jiangsu GDT that company develops.
After the polyester fondant is uniformly mixed with liquid mill base, it is delivered to spinning manifold through melt pipe and carries out spinning, thing
The incorporation time of material is 5~10 minutes.
Spinning pump is 800~1000g/min for amount in the present invention, and spinning temperature is 280~290 DEG C, spinning speed
For 900~1200m/min, drafting multiple is 2.7~3.8 times.Meanwhile, without using containing Nonyl pheno in production process
The spinning oil of ether (NPEO) composition, is substituted using AEO (AEO).
The beneficial effects of the invention are as follows：
(1) experiments verify that, environment-friendly dye diaminobenzil disulfonic acid class, 4.4- diaminourea hexichol ureas, diamino
Base heterocyclic, environment-friendly type acid dyes, environmental-friendly disperse dye have high temperature resistant and the property mixed of polyester fondant, by environmental protection
Dyestuff and solvent N,N-dimethylformamide, the dispersant of the block polymer containing ethoxy-propoxy, Negel
The dyeing system that salt wetting agent is constituted has that resistance to 290 DEG C of high temperature, color fastness are excellent, can mixed with polyester fondant and realized steady
It is fixed scattered, it is easy to industrializing implementation.
(2) present invention is used in the Fusing polyester pipeline that metering injection pump injects liquid mill base, polyester fondant and liquid
Mill base is well mixed through static mixing device, is transported in spinning manifold and carries out spinning, and metering injection pump can be set multigroup, can put
Put identical or different liquid mill base, it is possible to achieve multi items, the production of many colors on production line.
(3) environment-friendly dye that the present invention is used is short in high-temperature residence time, and fiber color is uniform, color fastness is high, color is full
It is full, more bright-coloured.
(4) present invention prepares original liquid coloring fiber, without using high pressure, the staining method of high temperature, with it is pollution-free, environmentally friendly,
The advantage of energy-conservation.
(5) the environmentally friendly polyester fiber of the original liquid coloring for preparing of the present invention, using in environment-friendly dye, and production process without using
Spinning oil containing NPEO compositions.
(6) through examine, the original liquid coloring polyester fiber being made, intensity be 4.0~4.8cN/dtex, 5 grades of color fastness to washing,
5 grades of sublimation reliability, APEO is not detected, meets Oeko-Tex Standard 100, standard GB/T/T18885-2009, GB/
T18401-2010, the Oeko-Tex Standard of EU REACH Legislation requirement.
Embodiment
The invention will be further described with reference to embodiments, but the present invention is not limited to following examples, every
Modification, replacement or the realized technical scheme of change that technology basic thought based on the present invention is made belong to the model of the present invention
Enclose.
Embodiment 1：Liquid mill base A preparation
Liquid mill base is made up of following components by weight percentage：
Environment-friendly dye：The diaminobenzil direct sun-proof of disulfonic acid class dyestuff green IRC, 20
Solvent：DMF, 60
Dispersant：Pluronic P123, molecular formula is EO20PO70EO20,10
Wetting agent：Isopropyl naphthalene sulfonate salt, 10
Above environment-friendly dye, solvent, dispersant and wetting agent can be obtained by buying.
The preparation method of liquid mill base is：Dispersant Pluronic P123, wetting agent isopropyl naphthalene sulfonate salt are added
Into solvent, stirring dissolves it, then adds the diaminobenzil disulfonic acid class dyestuff green IRC of direct sun-proof, and stirring is equal
It is even, pulp is fully ground, liquid mill base is obtained after it is uniformly dispersed.
Embodiment 2：Liquid mill base B preparation
Liquid mill base is made up of following components by weight percentage：
Environment-friendly dye：Environment-friendly type acid dyes C.I. acid reds 37,30
Solvent：DMF, 55
Dispersant：Pluronic F68, molecular formula is EO80PO30EO80,8
Wetting agent：Sodium isobutyl naphthalene sulfonate salt, 7
Above environment-friendly dye, solvent, dispersant and wetting agent can be obtained by buying.
The preparation method of liquid mill base is：Dispersant Pluronic F68, wetting agent sodium isobutyl naphthalene sulfonate salt are added
Into solvent, stirring dissolves it, then adds environment-friendly type acid dyes C.I. acid reds 37, stirs, be fully ground into
Pulpous state, obtains liquid mill base after it is uniformly dispersed.
Embodiment 3：Liquid mill base C preparation
Liquid mill base is made up of following components by weight percentage：
Environment-friendly dye：Environmental-friendly disperse dye Foron Blue RD-SE 290,25
Solvent：DMF, 45
Dispersant：Pluronic F127, molecular formula is EO106PO70EO106,15
Wetting agent：Isoamyl anphthalene sulfonate sodium, 15
Above environment-friendly dye, solvent, dispersant and wetting agent can be obtained by buying.
The preparation method of liquid mill base is：Dispersant Pluronic F127, wetting agent isoamyl anphthalene sulfonate sodium are added
Into solvent, stirring dissolves it, then adds environmental-friendly disperse dye Foron Blue RD-SE 290, stirs, fill
Divide grinding pulp, liquid mill base is obtained after it is uniformly dispersed.
Embodiment 4：The preparation of green polyester fiber
Liquid mill base A is injected in PET Fusing polyester pipelines using a Sets of Measurement injection pump, polyester fondant and liquid mill base
It is well mixed by static mixing device, it is transported in spinning manifold and carries out spinning, the temperature of polyester fondant is 277~287 DEG C,
The incorporation time of material is 5~10 minutes.
Spinning technology parameter is as follows：
Spinning pump is 800~1000g/min for amount in the present invention, and spinning temperature is 280~290 DEG C, spinning speed
For 900~1200m/min, drafting multiple is 2.7~3.8 times.
Through examining, the green polyester fiber being made, intensity is 4.2cN/dtex, 5 grades of color fastness to washing, 5 grades of sublimation reliability,
APEO is not detected.
Embodiment 5：The preparation of red polyester fiber
Liquid mill base B is injected in PBT polyester melt pipe using a Sets of Measurement injection pump, polyester fondant and liquid mill base
It is well mixed by static mixing device, it is transported in spinning manifold and carries out spinning, the temperature of polyester fondant is 277~287 DEG C,
The incorporation time of material is 5~10 minutes.
Spinning technology parameter is as follows：
Spinning pump is 800~1000g/min for amount in the present invention, and spinning temperature is 280~290 DEG C, spinning speed
For 900~1200m/min, drafting multiple is 2.7~3.8 times.
Through examining, the red polyester fiber being made, intensity is 4.5cN/dtex, 5 grades of color fastness to washing, 5 grades of sublimation reliability,
APEO is not detected.
Embodiment 6：The preparation of black polyester fiber
Liquid mill base C is injected in PET Fusing polyester pipelines using a Sets of Measurement injection pump, polyester fondant and liquid mill base
It is well mixed by static mixing device, it is transported in spinning manifold and carries out spinning, the temperature of polyester fondant is 277~287 DEG C,
The incorporation time of material is 5~10 minutes.
Spinning technology parameter is as follows：
Spinning pump is 800~1000g/min for amount in the present invention, and spinning temperature is 280~290 DEG C, spinning speed
For 900~1200m/min, drafting multiple is 2.7~3.8 times.
Through examining, the black polyester fiber being made, intensity is 4.8cN/dtex, 5 grades of color fastness to washing, 5 grades of sublimation reliability,
APEO is not detected.
Embodiment 7：The preparation of blackish green polyester fiber
Liquid mill base A and C are injected separately into PET Fusing polyester pipelines using two Sets of Measurement injection pumps, polyester fondant with
Liquid mill base is well mixed by static mixing device, is transported in spinning manifold and carries out spinning, and the temperature of polyester fondant is 277
~287 DEG C, the incorporation time of material is 5~10 minutes.
Spinning technology parameter is as follows：
Spinning pump is 800~1000g/min for amount in the present invention, and spinning temperature is 280~290 DEG C, spinning speed
For 900~1200m/min, drafting multiple is 2.7~3.8 times.
Through examining, the blackish green polyester fiber being made, intensity is 4.7cN/dtex, 5 grades of color fastness to washing, sublimation reliability 5
Level, APEO is not detected.
The preferred embodiment to the invention is illustrated above, but the invention be not limited to it is described
Embodiment, those skilled in the art can also make a variety of equivalent on the premise of without prejudice to the invention spirit
Modification or replacement, these equivalent modifications or replacement are all contained in the application claim limited range.
Claims (7)
1. a kind of method that original liquid coloring prepares environmentally friendly polyester fiber, it is characterised in that this method comprises the following steps：
A, the liquid mill base that environment-friendly dye and solvent, dispersant, wetting agent are deployed into original liquid coloring；Described solvent is N, N-
Dimethylformamide；Described dispersant, for the block polymer containing ethoxy-propoxy, its general molecular formula
EOxPOyEOx, the x for 5~113 integer and including 5 and 113, y is 30~70 integer and including 30 and 70；Described
Wetting agent, is alkyl naphthalene sulfonic acid sodium salt, and its general molecular formula is RCH10H6SO3Na, R are alkyl；
B, using metering injection pump one or more kinds of liquid mill bases is injected in Fusing polyester pipeline；
C, polyester fondant are well mixed with liquid mill base by static mixing device, are transported in spinning manifold and are carried out spinning.
2. the method that a kind of original liquid coloring according to claim 1 prepares environmentally friendly polyester fiber, it is characterised in that described
Environment-friendly dye, selected from diaminobenzil disulfonic acid class, 4.4- diaminourea hexichol ureas, diamino heterocycle class, environment-friendly type acid
It is more than one or both of property dyestuff, environmental-friendly disperse dye.
3. the method that a kind of original liquid coloring according to claim 2 prepares environmentally friendly polyester fiber, it is characterised in that described
Environment-friendly dye, selected from direct fast yellow 3BLL, the green IRC of direct sun-proof, direct fast yellow RSC, direct fast red F3B, C.I. acid
It is more than one or both of property red 37, C.I. Indian yellows 49, Foron Blue RD-SE290, Itosperse HW type dyes.
4. the method that a kind of original liquid coloring according to claim 1 prepares environmentally friendly polyester fiber, it is characterised in that described
Dispersant is Pluronic P123, Pluronic F68, or Pluronic F127.
5. the method that a kind of original liquid coloring according to claim 1 prepares environmentally friendly polyester fiber, it is characterised in that R is different
Propyl group, isobutyl group, or isopentyl.
6. the method that a kind of original liquid coloring according to claim 1 prepares environmentally friendly polyester fiber, it is characterised in that step A
In, in described liquid mill base, it is made up of following components by weight percentage：
Environment-friendly dye：20~30；
Solvent：40~60；
Dispersant：5~15；
Wetting agent：5~15.
7. the method that a kind of original liquid coloring according to claim 1 prepares environmentally friendly polyester fiber, it is characterised in that step B
In, described polyester fondant is PET or the heated meltings of PBT, and the temperature of the polyester fondant is 277~287 DEG C.