CN105146989A - Method for producing comfortable jute fiber jacquard summer blanket - Google Patents
Method for producing comfortable jute fiber jacquard summer blanket Download PDFInfo
- Publication number
- CN105146989A CN105146989A CN201510622978.6A CN201510622978A CN105146989A CN 105146989 A CN105146989 A CN 105146989A CN 201510622978 A CN201510622978 A CN 201510622978A CN 105146989 A CN105146989 A CN 105146989A
- Authority
- CN
- China
- Prior art keywords
- flaxen fiber
- yarn
- blanket
- dyeing
- jacquard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for producing a comfortable jute fiber jacquard summer blanket. The method sequentially comprises the steps of yarn dyeing, jacquard weaving, washing preshrinking, tension-free drying and tailoring and covered edge sewing. Yarns contain comfortable jute fibers. According to the method, the comfortable jute fibers applied to the summer blanket endow a common bamboo fiber summer blanket with a jute texture, and the summer blanket is stiff and smooth without wrinkles in use and has the skin-friendly effect and the skin-caring effect like real silk due to rich amino acid.
Description
Technical field
The present invention relates to a kind of blanket class household textiles, be specifically related to a kind of flaxen fiber jacquard blanket that relaxes.
Background technology
Bamboo fiber jacquard summer cool blanket is a most salable product series products in the middle of overall summer cool blanket on market, and maximum advantage is that cost performance is high.Compare the blanket class of the fine hair classes such as flannel, bamboo fiber jacquard blanket surface is cool sliding without fine hair, and style is close to fabric, and the soft cool cunning of skin contact, is applicable to hot summer.Domestic applications number are the patent of invention application that discloses a kind of bamboo pulp fiber yarn and be in textile fabric of 2009100548725, it is take fineness as the bamboo pulp fiber of 0.8dtex is raw material, by blowing, comb and parallel cotton fibers prior to spinning, drafting, rove and spun yarn, be spun into the bamboo pulp fiber yarn of 60S and 40S, bamboo pulp fiber content in described bamboo pulp fiber yarn, with the percentages of weight, its ratio is X, 5≤X≤15.By bamboo pulp fiber yarn by warping, sizing, weaving, full process and dyeing process, process textile fabric of getting married, this family's textile fabric can be used for preparing cool blanket or three-piece.In addition bamboo fibre raw material in addition antibacterial, moisture absorption to breathe freely, easily wash the advantage of rapid-curing cutback.But this summer, cool blanket was too soft, there is the phenomenon that sticky sticky body easily wrinkles in use procedure, washing intensity is low, yielding.It is single that the cool blanket of summer in the market also also exists material, and product lacks the problem of characteristic.
Flaxen fiber has good moisture absorption and falls apart wet with ventilative function, heat transfer heat conduction is fast, nice and cool well-pressed, perspire not next to the skin, quality light, powerful large, be originally the alternative materials that a kind of jacquard weave summer cool blanket is good, but also there is the shortcoming of Boardy Feeling.
In a word, jacquard weave summer of the prior art cool blanket material is single, and product lacks characteristic.
Summary of the invention
The shortcoming of prior art in view of the above, the object of the present invention is to provide a kind of flaxen fiber jacquard weave summer cool blanket that relaxes, to overcome in prior art the flaxen fiber jacquard weave summer cool blanket that relaxes.
In order to reach foregoing invention object and other objects, the present invention is achieved by the following technical solutions:
Produce a method for easypro flaxen fiber jacquard weave summer cool blanket, in turn include the following steps: bound edge is made in yarn dyeing, jacquard weaving, washing preshrunk, no-station pole canopy oven dry and cutting; Containing the flaxen fiber that relaxes in described yarn.
Preferably, in the gross weight of described yarn for benchmark, the weight percentage of described easypro flaxen fiber is 30 ~ 100wt%.
Easypro flaxen fiber take viscose glue as carrier, and by crosslinked, the technological means such as blended, forms stable combination by fibroin and flaxen fiber element with viscose glue pulp.In fiber formation process, by delaying forming technique, the distribution at fiber surface of effective control silk protein and flaxen fiber element, the skin of fiber is allowed to be uniformly distributed fibroin (being cross-linked), fiber internal layer is that flaxen fiber element forms blended combination with viscose glue, and like this, the feel of fiber and gloss just possess the feature of real silk, and the mechanical property of entirety has the feature of certain bast-fibre, realize the common embodiment of feature on fiber of two kinds of compositions.Easypro flaxen fiber take viscose glue as a kind of tencel of base material, there is the problems such as shrinkage is large, needs in process of production to adopt special technique to solve this problem.
More preferably, one or more for being selected from 1.5D × 38mm, 3D × 64mm, 3D × 55mm, 3D × (76 ~ 114mm) of the specification of the easypro flaxen fiber used in the present invention.
The meaning of 1.5D × 38mm described above is fibre fineness was 1.5 dawn, and fibre length is 38mm.
Preferably, also containing one or both in bamboo fibre or flaxen fiber in described yarn, in the gross weight of described yarn for benchmark, the weight percentage of described bamboo fibre is no more than 50wt%, and the weight percentage of described flaxen fiber is no more than 30wt%.
More preferably, when in described yarn also containing one or both in bamboo fibre or flaxen fiber time, in the gross weight of described yarn for benchmark, the weight percentage of described easypro flaxen fiber is not less than 30wt%.
Preferably, the number of described yarn is 19 ~ 40S.
Preferably, described no-station pole canopy is dried when referring to and adopt roller drying machine to dry and is adopted selvage guide to carry the fabric of the jacquard weave summer cool blanket that described jacquard weaving step is formed, and feeds together in drying cylinder.
Preferably, the hot strength of described selvage guide is greater than the hot strength of described jacquard weave summer cool blanket.
Adopt selvage guide to carry jacquard weave summer cool blanket in the present invention to feed together in drying cylinder, selvage guide aid dispersion tension force in the operation that drying cylinder is dried, decreases the pressure that jacquard weave summer cool blanket carries.Described selvage guide can select the selvage guide of any conventional material in prior art.
More preferably, described selvage guide is selected from woven cloths or non-weaving cloth.Preferably, the material of described selvage guide is chemical fibre material.
Any technique that yarn dyeing technology in the present invention can adopt the yarn containing flaxen fiber in prior art to carry out dyeing dyes.
Preferably, in the present invention, the technique of yarn dyeing is single bath process, be specially: first dye yarn at least 30min in the dyeing bath of 35 ~ 45 DEG C, then according to the speed of 1 DEG C/min, dyeing bath is warming up to 55 ~ 65 DEG C of at least 30min that dye, then according to the speed of 1 DEG C/min, dyeing bath is cooled to room temperature.
Preferably, in technique scheme, in dyeing, the formula of body lotion is as follows:
In the technical scheme of above-mentioned body lotion, preferably, described dyestuff is reactive dye.
Adopt above-mentioned body lotion to carry out in the technical scheme dyeed, preferably, described bath raio is 1:15 ~ 20.
In technique scheme, preferably, described glauber salt and soda ash add in body lotion gradually.
More preferably, the glauber salt of 2/3 is had to add before intensification at the most.
More preferably, heat up at the end of dyeing, have the soda ash of 6/10 to be added in body lotion at the most.
In dyeing of the present invention, soda ash is added in batches, prevent uneven dyeing.
No-station pole canopy dry technique and each technique in parameter be: drying tube temperature 80 ~ 120 DEG C, cloth speed 10 ~ 25 meters/min.
In the present invention, the mode of bound edge can be adopt polyester color fourth cloth diagonal angle bound edge, also can be from crimping.
The invention also discloses a kind of flaxen fiber jacquard weave summer cool blanket that relaxes, prepared by method described above.
Preferably, the grammes per square metre of cool blanket of described summer is 250gsm ~ 400gsm.
Preferably, plain weave is become through jacquard weaving in described easypro flaxen fiber jacquard weave summer cool blanket.
In the present invention, jacquard weaving and washing preshrunk and cutting are made bound edge conventional process means in prior art all can be adopted to carry out.
Adopt this yarn containing the flaxen fiber that relaxes of method disclosed in the present invention can weave the jacquard blanket fabric with various flower pattern with jacquard weaving equipment.
The beneficial effect of technique scheme of the present invention is: easypro flaxen fiber is applied to the style that summer cool blanket can give common bamboo fibre summer cool blanket picotement matter, and the used time is well-pressed does not wrinkle, and is rich in amino acid, effect with pro-skin skin care the same as real silk.
The flaxen fiber jacquard blanket that relaxes disclosed in the present invention overcomes many disadvantages of the prior art and creative.
Accompanying drawing explanation
Fig. 1 for no-station pole canopy described in the present invention dry process flow diagram:
The easypro flaxen fiber jacquard blanket structural representation that Fig. 2 is plain weave structure described in the present invention.
Fig. 3 is the schematic diagram of dyeing in the embodiment of the present invention 1.
Wherein, in Fig. 1 ~ 3, Reference numeral is as follows:
1 is drying cylinder;
2 is selvage guide;
3 is the numb jacquard blanket fabric that relaxes;
4 is yarn.
Detailed description of the invention
Below by way of specific instantiation, embodiments of the present invention are described, those skilled in the art the content disclosed by this description can understand other advantages of the present invention and effect easily.The present invention can also be implemented or be applied by detailed description of the invention different in addition, and the every details in this description also can based on different viewpoints and application, carries out various modification or change not deviating under spirit of the present invention.
Produce the method for the flaxen fiber jacquard weave summer cool blanket that relaxes disclosed in the embodiment of the present invention, in turn include the following steps: bound edge is made in yarn dyeing, jacquard weaving, washing preshrunk, no-station pole canopy oven dry and cutting; Containing the flaxen fiber that relaxes in described yarn; Containing the flaxen fiber that relaxes in described yarn.Described no-station pole canopy is dried when referring to and adopt roller drying machine to dry and is adopted selvage guide to carry the fabric of the jacquard weave summer cool blanket that described jacquard weaving step is formed, and feeds together in drying cylinder.The hot strength of described selvage guide is greater than the hot strength of described jacquard weave summer cool blanket.Adopt selvage guide to carry jacquard weave summer cool blanket in the present invention to feed together in drying cylinder, selvage guide aid dispersion tension force in the operation that drying cylinder is dried, decreases the pressure that jacquard weave summer cool blanket carries.Described selvage guide can select the selvage guide of any conventional material in prior art.Preferably, described selvage guide is selected from woven cloths or non-weaving cloth.
Easypro flaxen fiber take viscose glue as carrier, and by crosslinked, the technological means such as blended, forms stable combination by fibroin and flaxen fiber element with viscose glue pulp.In fiber formation process, by delaying forming technique, the distribution at fiber surface of effective control silk protein and flaxen fiber element, the skin of fiber is allowed to be uniformly distributed fibroin (being cross-linked), fiber internal layer is that flaxen fiber element forms blended combination with viscose glue, and like this, the feel of fiber and gloss just possess the feature of real silk, and the mechanical property of entirety has the feature of certain bast-fibre, realize the common embodiment of feature on fiber of two kinds of compositions.Easypro flaxen fiber take viscose glue as a kind of tencel of base material, there is the problems such as shrinkage is large, needs in process of production to adopt special technique to solve this problem.
Embodiment 1
In the present embodiment, in the gross weight of described yarn for benchmark, the weight percentage of described easypro flaxen fiber is 30wt%.The number of described yarn is 19S.
The specification of the easypro flaxen fiber used in the present invention is for being selected from 1.5D × 38mm.The meaning of described 1.5D × 38mm is fibre fineness was 1.5 dawn, and fibre length is 38mm.
Any technique that yarn dyeing technology in the present invention can adopt the yarn containing flaxen fiber in prior art to carry out dyeing dyes.
Particularly, in the present invention, the technique of yarn dyeing is single bath process, be specially: first dye yarn 30min in the dyeing bath of 40 DEG C, then according to the speed of 1 DEG C/min, dyeing bath be warming up to 60 DEG C of dyeing 45min, then according to the speed of 1 DEG C/min, dyeing bath be cooled to room temperature.
Particularly, in technique scheme, in dyeing, the formula of body lotion is as follows:
Particularly, described dyestuff is reactive dye.Described bath raio is 1:20.
Described glauber salt and soda ash add in body lotion gradually.The glauber salt of 2/3 adds before intensification.Heat up at the end of dyeing, have the soda ash of 6/10 to be added in body lotion.In the present embodiment dyeing, soda ash is added in batches, prevent uneven dyeing.Shown in concrete Fig. 3.
No-station pole canopy dry technique and each technique in parameter be: drying tube temperature 80 DEG C, cloth speed 12 meters/min.
The material of the selvage guide that no-station pole canopy adopts in drying is polyster fibre.
In the present invention, the mode of bound edge can be adopt polyester color fourth cloth diagonal angle bound edge.
The grammes per square metre of the summer that in the present embodiment, method described above prepares cool blanket is 250gsm, becomes plain weave in described easypro flaxen fiber jacquard weave summer cool blanket through jacquard weaving.
Embodiment 2
In the present embodiment, in the gross weight of described yarn for benchmark, the weight percentage of described easypro flaxen fiber is 100wt%.
Particularly, the specification of the easypro flaxen fiber used in the present invention is for being selected from 3D × 64mm.
The meaning of 3D × 64mm described above is fibre fineness was 3 dawn, and fibre length is 64mm.
The number of yarn described in the present embodiment is 30S, and also containing bamboo fibre and flaxen fiber in described yarn, in the gross weight of described yarn for benchmark, the weight percentage of described bamboo fibre is 50wt%, and the weight percentage of described flaxen fiber is 20wt%; The weight percentage of described easypro flaxen fiber is 30wt%.
Any technique that yarn dyeing technology in the present invention can adopt the yarn containing flaxen fiber in prior art to carry out dyeing dyes.
Particularly, in the present invention, the technique of yarn dyeing is single bath process, be specially: first dye yarn 45min in the dyeing bath of 35 DEG C, then according to the speed of 1 DEG C/min, dyeing bath be warming up to 65 DEG C of dyeing 30min, then according to the speed of 1 DEG C/min, dyeing bath be cooled to room temperature.
In technique scheme, in dyeing, the formula of body lotion is as follows:
Described dyestuff is reactive dye.Described bath raio is 1:15 ~ 20.Described glauber salt and soda ash add in body lotion gradually.The glauber salt of 2/3 adds before intensification.The soda ash of 6/10 is had to be added in body lotion.In dyeing of the present invention, soda ash is added in batches, prevent uneven dyeing.
No-station pole canopy dry technique and each technique in parameter be: drying tube temperature 120 DEG C, cloth speed 25 meters/min.
The selvage guide that no-station pole canopy adopts in drying is blend polyester cloth.
In the present invention, the mode of bound edge can be adopt polyester color fourth cloth diagonal angle bound edge, also can be from crimping.
The grammes per square metre of the summer cool blanket obtained according to above-mentioned technique in the present embodiment is 400gsm.Plain weave or other structures is become through jacquard weaving in described easypro flaxen fiber jacquard weave summer cool blanket.
Embodiment 3
The specification of the easypro flaxen fiber used in the present invention is 3D × 55mm.
The meaning of 3D × 55mm described above is fibre fineness was 3 dawn, and fibre length is 55mm.
Also containing one or both in bamboo fibre or flaxen fiber in yarn described in the present embodiment, in the gross weight of described yarn for benchmark, the weight percentage of described bamboo fibre is 30wt%, the weight percentage of described flaxen fiber is 10wt%, and the weight percentage of described easypro flaxen fiber is not less than 60wt%.
The number of described yarn is 36S.
Any technique that yarn dyeing technology in the present invention can adopt the yarn containing flaxen fiber in prior art to carry out dyeing dyes.In the present embodiment, the technique of yarn dyeing is single bath process, be specially: first dye yarn 50min in the dyeing bath of 45 DEG C, then according to the speed of 1 DEG C/min, dyeing bath is warming up to 60 DEG C of dyeing 60min, then according to the speed of 1 DEG C/min, dyeing bath is cooled to room temperature.
In technique scheme, in dyeing, the formula of body lotion is as follows:
Described dyestuff is reactive dye.Described bath raio is 1:18., described glauber salt and soda ash add in body lotion gradually.The glauber salt of 2/3 adds before intensification.Heat up at the end of dyeing, have the soda ash of 6/10 to be added in body lotion.In dyeing of the present invention, soda ash is added in batches, prevent uneven dyeing.
No-station pole canopy dry technique and each technique in parameter be: drying tube temperature 90 DEG C, cloth speed 18 meters/min.
In the present embodiment, the mode of bound edge is from crimping.
The grammes per square metre being prepared summer cool blanket by method described above is 350gsm.Plain weave is become through jacquard weaving in described easypro flaxen fiber jacquard weave summer cool blanket.
Embodiment 4
The specification of the easypro flaxen fiber used in the present invention is for being selected from 3D × 100mm.
The meaning of 3D × 100mm described above is fibre fineness was 3 dawn, and fibre length is 100mm.
In the present embodiment, also containing bamboo fibre and flaxen fiber in described yarn, in the gross weight of described yarn for benchmark, the weight percentage of described bamboo fibre is 20wt%, the weight percentage of described flaxen fiber is 10wt%, and the weight percentage of described easypro flaxen fiber is 70wt%.
The number of described yarn is 25S.
Any technique that yarn dyeing technology in the present invention can adopt the yarn containing flaxen fiber in prior art to carry out dyeing dyes.In the present embodiment, the technique of yarn dyeing is single bath process, be specially: first dye yarn 60min in the dyeing bath of 35 DEG C, then according to the speed of 1 DEG C/min, dyeing bath is warming up to 60 DEG C of dyeing 60min, then according to the speed of 1 DEG C/min, dyeing bath is cooled to room temperature.
Preferably, in technique scheme, in dyeing, the formula of body lotion is as follows:
Described dyestuff is reactive dye.Described bath raio is 1:19.Described glauber salt and soda ash add in body lotion gradually.The glauber salt of 2/3 adds before intensification.Heat up at the end of dyeing, have the soda ash of 6/10 to be added in body lotion.In dyeing of the present invention, soda ash is added in batches, prevent uneven dyeing.
No-station pole canopy dry technique and each technique in parameter be: drying tube temperature 110 DEG C, cloth speed 20 meters/min.
In no-station pole canopy oven dry, selvage guide is polyethylene nonwoven cloth.
In the present invention, the mode of bound edge can be adopt polyester color fourth cloth diagonal angle bound edge.
The grammes per square metre of the summer prepared by method described above cool blanket is 400gsm.Plain weave is become through jacquard weaving in described easypro flaxen fiber jacquard weave summer cool blanket.
Embodiment 5
The specification of the easypro flaxen fiber used in the present invention is 3D × 114mm.The meaning of 3D × 114mm described above is fibre fineness was 3 dawn, and fibre length is 114mm.
Particularly, also containing bamboo fibre in described yarn, in the gross weight of described yarn for benchmark, the weight percentage of described bamboo fibre is 40wt%, and the weight percentage of described easypro flaxen fiber is not less than 60wt%.
The number of described yarn is 19 ~ 40S.
Any technique that yarn dyeing technology in the present invention can adopt the yarn containing flaxen fiber in prior art to carry out dyeing dyes.In the present invention, the technique of yarn dyeing is single bath process, be specially: first dye yarn 40min in the dyeing bath of 35 DEG C, then according to the speed of 1 DEG C/min, dyeing bath is warming up to 65 DEG C of dyeing 50min, then according to the speed of 1 DEG C/min, dyeing bath is cooled to room temperature.
In technique scheme, in dyeing, the formula of body lotion is as follows:
Described dyestuff is reactive dye.Described bath raio is 1:15.Described glauber salt and soda ash add in body lotion gradually.The glauber salt of 2/3 adds before intensification.Heat up at the end of dyeing, have the soda ash of 6/10 to be added in body lotion.In dyeing of the present invention, soda ash is added in batches, prevent uneven dyeing.
No-station pole canopy dry technique and each technique in parameter be: drying tube temperature 100 DEG C, cloth speed 23 meters/min.
The selvage guide adopted in no-station pole canopy baking operation is polypropylene nonwoven.
In the present invention, the mode of bound edge can be adopt polyester color fourth cloth diagonal angle bound edge.
The grammes per square metre being prepared summer cool blanket by method described above is 320gsm.
Embodiment 6
One or more for being selected from 3D × (76 ~ 114mm) of the specification of the easypro flaxen fiber used in the present embodiment.
The meaning of 3D described above × (76 ~ 114mm) is fibre fineness was 1.5 dawn, and fibre length is between 76 ~ 114mm.
The number of described yarn is 28S, and also containing flaxen fiber in described yarn, in the gross weight of described yarn for benchmark, the weight percentage of described flaxen fiber is no more than 20wt%.The weight percentage of described easypro flaxen fiber is 80wt%.
Any technique that yarn dyeing technology in the present invention can adopt the yarn containing flaxen fiber in prior art to carry out dyeing dyes.In the present invention, the technique of yarn dyeing is single bath process, be specially: first dye yarn 45min in the dyeing bath of 35 DEG C, then according to the speed of 1 DEG C/min, dyeing bath is warming up to 65 DEG C of dyeing 50min, then according to the speed of 1 DEG C/min, dyeing bath is cooled to room temperature.
In technique scheme, in dyeing, the formula of body lotion is as follows:
Described dyestuff is reactive dye.Described bath raio is 1:16.Described glauber salt and soda ash add in body lotion gradually.
The glauber salt of 2/3 adds before intensification.Heat up at the end of dyeing, have the soda ash of 6/10 to be added in body lotion.In dyeing of the present invention, soda ash is added in batches, prevent uneven dyeing.
No-station pole canopy dry technique and each technique in parameter be: drying tube temperature 90 DEG C, cloth speed 15 meters/min.
The selvage guide material adopted in no-station pole canopy baking operation is blend polyester fiber.
In the present invention, the mode of bound edge can be adopt polyester color fourth cloth diagonal angle bound edge.
The grammes per square metre being prepared summer cool blanket by method described above is 380gsm.
The summer cool blanket obtained in embodiment 1 ~ 6 has the style of picotement matter, and gas permeability is good, and the used time is well-pressed does not wrinkle, and is rich in amino acid, effect with pro-skin skin care the same as real silk.
Above-described embodiment is illustrative principle of the present invention and effect thereof only, but not for limiting the present invention.Any person skilled in the art scholar all without prejudice under spirit of the present invention and category, can modify above-described embodiment or changes.Therefore, such as have in art usually know the knowledgeable do not depart from complete under disclosed spirit and technological thought all equivalence modify or change, must be contained by claim of the present invention.
Claims (10)
1. produce a method for easypro flaxen fiber jacquard weave summer cool blanket, in turn include the following steps: bound edge is made in yarn dyeing, jacquard weaving, washing preshrunk, no-station pole canopy oven dry and cutting; Containing the flaxen fiber that relaxes in described yarn.
2. method as claimed in claim 1, it is characterized in that: in the gross weight of described yarn for benchmark, the weight percentage of described easypro flaxen fiber is 30 ~ 100wt%.
3. method as claimed in claim 1, it is characterized in that: also containing one or both in bamboo fibre or flaxen fiber in described yarn, in the gross weight of described yarn for benchmark, the weight percentage of described bamboo fibre is no more than 50wt%, and the weight percentage of described flaxen fiber is no more than 30wt%.
4. method as claimed in claim 1, is characterized in that: the number of described yarn is 19 ~ 40S.
5. method as claimed in claim 1, is characterized in that: described no-station pole canopy is dried when referring to and adopt roller drying machine to dry and adopted selvage guide to carry the fabric of the jacquard weave summer cool blanket that described jacquard weaving step is formed, and feeds together in drying cylinder.
6. method as claimed in claim 5, is characterized in that: the hot strength of described selvage guide is greater than the hot strength of described jacquard weave summer cool blanket.
7. method as claimed in claim 5, is characterized in that: described selvage guide is chemical fibre material.
8. an easypro flaxen fiber jacquard weave summer cool blanket, is prepared by method described in the arbitrary claim of claim 1 ~ 7.
9. relax flaxen fiber jacquard weave summer cool blanket as claimed in claim 6, it is characterized in that: the grammes per square metre of cool blanket of described summer is 250gsm ~ 400gsm.
10. relax flaxen fiber jacquard weave summer cool blanket as claimed in claim 6, it is characterized in that: become plain weave through jacquard weaving in described easypro flaxen fiber jacquard weave summer cool blanket.