CN105110744A - Wood-like cement fiberboard - Google Patents
Wood-like cement fiberboard Download PDFInfo
- Publication number
- CN105110744A CN105110744A CN201510479872.5A CN201510479872A CN105110744A CN 105110744 A CN105110744 A CN 105110744A CN 201510479872 A CN201510479872 A CN 201510479872A CN 105110744 A CN105110744 A CN 105110744A
- Authority
- CN
- China
- Prior art keywords
- cement
- parts
- wood
- fibrolite plate
- cement fiberboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a wood-like cement fiberboard. The wood-like cement fiberboard comprises the following in parts by weight: 35-50 parts of cement, 3-6 parts of fly ash, 3-5 parts of gangue, 5-10 parts of slag, 0.5-2 parts of forge, 10-25 parts of plant stalk, 10-20 parts of glass fiber powder, 0-0.1 parts of pigment, and water as the balance. The invention also discloses a preparation method for the wood-like cement fiberboard. The obtained wood-like cement fiberboard disclosed by the invention after interaction of the feedstock has high strength, good smooth finish, fireproofing and waterproofing properties, stable performance, no formaldehyde, no radiation, and no harmful substances to volatile; can be cut and processed optionally; and discharge no waste water, no waste gas, and no waste residue during production through cold preparation; deployment of the pigment can produce different visual effects, and in the same time for having all the advantages of traditional cement fiberboard, the wood-like cement fiberboard especially applies to cooperative use of various high-grade furniture, high-grade floor tiles and high-grade marble, so as to be an ideal alternative for wood of cabinets, conference tables, and desks, and is low in absorption rate, long in service life, and low in price.
Description
Technical field
The present invention relates to a kind of cement fibrolite plate, be specifically related to a kind of imitative wooden cement fibrolite plate.
Background technology
Existing cement fibrolite plate is mainly made by hot pressing by after the material spices such as magnesium cement or magnesia oxychloride cement, viscose glue, fortifying fibre.Its purposes is the goods (enclosure wall), interior finish building materials (floor, wall, ceiling) etc. of extraneous adornment building materials (exterior wall, watt), external application.
Solid wood plate or wooden composite fiber plate are the main raws that existing furniture, cabinet, meeting or office furniture use, the material of solid wood plate is good, but water-absorbent is strong, inflammable, wooden composite fiber plate intensity difference, make moist perishable, also there is inflammable problem, these materials all need trees as raw material, to environmental protection and ecotope build-up of pressure simultaneously.But existing cement fibrolite plate cannot substitute wooden composite fiber plate due to problems such as texture, smooth finish, intensity.
Summary of the invention
In order to solve the deficiencies in the prior art, the object of the present invention is to provide a kind of cheap, intensity be high, the life-span is long, smooth finish is good, fire-proof and water-proof, stable performance, formaldehydeless, radiationless, unharmful substance volatilization imitative wooden cement fibrolite plate.
For achieving the above object, the technology used in the present invention means are: a kind of imitative wooden cement fibrolite plate, be made up of following weight part: cement 35 ~ 50, flyash 3 ~ 6, coal gangue 3 ~ 5, slag 5 ~ 10, grass meal 0.5 ~ 2, straw 10 ~ 25, glass fiber powder 10 ~ 20, pigment 0 ~ 0.1, surplus is water.
Further, the preparation method of described imitative wooden cement fibrolite plate, step is as follows: coal gangue, straw, slag are smashed, then be placed in vacuum mixer mix and blend 10 ~ 30 minutes with cement, flyash, grass meal, glass fiber powder, pigment, water, after stirring terminates, compound is sent into direct pressing in compacting tool set shaping, press forming cement fibrolite plate is passed through track drawing machine travel to the automatic demoulding of appointment de-molding position, entering after demoulding cares the car carries out maintenance, and the complete cutting of maintenance is packed.
Further, described cement is magnesia cement or 425 cement.
Further, described slag is blast-furnace slag.
Further, the vacuum tightness of described vacuum mixer is-0.3 ~-0.1Mpa.
The invention has the beneficial effects as follows: by the interaction of above-mentioned batching, the cement fibrolite plate intensity obtained is high, smooth finish good, fire-proof and water-proof, stable performance, formaldehydeless, radiationless, unharmful substance volatilization, can cutting processing arbitrarily, standby by cold compaction, discharge without waste water,waste gas and industrial residue in production; By the allotment of pigment, different visual effect can be produced, the institute with conventional cement fiberboard is advantageous while, especially be suitable for various top-grade furniture, high-grade floor tile and high-grade marble with the use of, it is the desirable substitute of timber of cabinet, conference table, desk, specific absorption is low, long service life, cheap.
Embodiment
Below in conjunction with embodiment, the invention will be further elaborated.
embodiment 1
A kind of imitative wooden cement fibrolite plate, be made up of following weight part: 425 cement 50, flyash 3, coal gangue 3, slag 5, grass meal 0.5, straw 10, glass fiber powder 10, pigment 0, surplus is water.
The preparation method of described imitative wooden cement fibrolite plate, step is as follows: coal gangue, straw, slag are smashed, then be placed in vacuum mixer mix and blend 10 ~ 30 minutes with cement, flyash, grass meal, glass fiber powder, pigment, water, after stirring terminates, compound is sent into direct pressing in compacting tool set shaping, press forming cement fibrolite plate is passed through track drawing machine travel to the automatic demoulding of appointment de-molding position, entering after demoulding cares the car carries out maintenance, and the complete cutting of maintenance is packed.
The vacuum tightness of described vacuum mixer is-0.1Mpa.
embodiment 2
A kind of imitative wooden cement fibrolite plate, be made up of following weight part: magnesia cement 40, flyash 6, coal gangue 4, blast-furnace slag 10, grass meal 1, straw 20, glass fiber powder 10, pigment 0.05, surplus is water.
The preparation method of described imitative wooden cement fibrolite plate, step is as follows: coal gangue, straw, slag are smashed, then be placed in vacuum mixer mix and blend 10 ~ 30 minutes with cement, flyash, grass meal, glass fiber powder, pigment, water, after stirring terminates, compound is sent into direct pressing in compacting tool set shaping, press forming cement fibrolite plate is passed through track drawing machine travel to the automatic demoulding of appointment de-molding position, entering after demoulding cares the car carries out maintenance, and the complete cutting of maintenance is packed.
The vacuum tightness of described vacuum mixer is-0.3Mpa.
embodiment 3
A kind of imitative wooden cement fibrolite plate, be made up of following weight part: 425 cement 45, flyash 5, coal gangue 5, blast-furnace slag 5, grass meal 2, straw 15, glass fiber powder 15, pigment 0.1, surplus is water.
The preparation method of described imitative wooden cement fibrolite plate, step is as follows: coal gangue, straw, slag are smashed, then be placed in vacuum mixer mix and blend 10 ~ 30 minutes with cement, flyash, grass meal, glass fiber powder, pigment, water, after stirring terminates, compound is sent into direct pressing in compacting tool set shaping, press forming cement fibrolite plate is passed through track drawing machine travel to the automatic demoulding of appointment de-molding position, entering after demoulding cares the car carries out maintenance, and the complete cutting of maintenance is packed.
The vacuum tightness of described vacuum mixer is-0.2Mpa.
embodiment 4
A kind of imitative wooden cement fibrolite plate, be made up of following weight part: magnesia cement 35, flyash 4, coal gangue 4, blast-furnace slag 8, grass meal 1, straw 25, glass fiber powder 15, pigment 0.1, surplus is water.
The preparation method of described imitative wooden cement fibrolite plate, step is as follows: coal gangue, straw, slag are smashed, then be placed in vacuum mixer mix and blend 10 ~ 30 minutes with cement, flyash, grass meal, glass fiber powder, pigment, water, after stirring terminates, compound is sent into direct pressing in compacting tool set shaping, press forming cement fibrolite plate is passed through track drawing machine travel to the automatic demoulding of appointment de-molding position, entering after demoulding cares the car carries out maintenance, and the complete cutting of maintenance is packed.
The vacuum tightness of described vacuum mixer is-0.3Mpa.
By the interaction of above-mentioned batching, the cement fibrolite plate intensity obtained is high, smooth finish good, fire-proof and water-proof, stable performance, the volatilization of formaldehydeless, radiationless, unharmful substance, can cutting processing arbitrarily, standby by cold compaction, discharge without waste water,waste gas and industrial residue in production; By the allotment of pigment, different visual effect can be produced, the institute with conventional cement fiberboard is advantageous while, especially be suitable for various top-grade furniture, high-grade floor tile and high-grade marble with the use of, it is the desirable substitute of timber of cabinet, conference table, desk, specific absorption is low, long service life, cheap.
The explanation of disclosed embodiment of this invention just to technical scheme of the present invention, can not as the restriction to content of the present invention, and the simple change of those skilled in the art on basis of the present invention, still in protection scope of the present invention.
Claims (5)
1. an imitative wooden cement fibrolite plate, it is characterized in that: be made up of following weight part: cement 35 ~ 50, flyash 3 ~ 6, coal gangue 3 ~ 5, slag 5 ~ 10, grass meal 0.5 ~ 2, straw 10 ~ 25, glass fiber powder 10 ~ 20, pigment 0 ~ 0.1, surplus is water.
2. imitative wooden cement fibrolite plate according to claim 1, is characterized in that: described cement is magnesia cement or 425 cement.
3. imitative wooden cement fibrolite plate according to claim 1, is characterized in that: described slag is blast-furnace slag.
4. imitative wooden cement fibrolite plate as claimed in claim 1, its preparation method, be characterised in that, step is as follows: coal gangue, straw, slag are smashed, then be placed in vacuum mixer mix and blend 10 ~ 30 minutes with cement, flyash, grass meal, glass fiber powder, pigment, water, after stirring terminates, compound is sent into direct pressing in compacting tool set shaping, press forming cement fibrolite plate is passed through track drawing machine travel to the automatic demoulding of appointment de-molding position, entering after demoulding cares the car carries out maintenance, and the complete cutting of maintenance is packed.
5. the preparation method of imitative wooden cement fibrolite plate according to claim 4, is characterized in that: the vacuum tightness of described vacuum mixer is-0.3 ~-0.1Mpa.