CN105000837A - Vitrified microsphere insulating mortar and preparation method therefor - Google Patents
Vitrified microsphere insulating mortar and preparation method therefor Download PDFInfo
- Publication number
- CN105000837A CN105000837A CN201510401140.4A CN201510401140A CN105000837A CN 105000837 A CN105000837 A CN 105000837A CN 201510401140 A CN201510401140 A CN 201510401140A CN 105000837 A CN105000837 A CN 105000837A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- cement
- preparation
- insulating mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Vitrified microsphere insulating mortar is provided, which is characterized in that: the vitrified microsphere insulating mortar is produced by using the following raw materials in parts by weight: 300-340 parts of cement; 50-55 parts of redispersible powder; 40-45 parts of sea-foam stone powder; 30-35 parts of calcium base bentonite; 20-30 parts of hollow ceramic microsphere; 10-15 parts of hollow glass microsphere; 40-45 parts of silicate aluminum powder; 25-30 parts of titanium dioxide; 35-40 parts of nano fluospar; 30-40 parts of gypsum whisker; 10-12 parts of dried alum; 10-12 parts of sodium sulfate powder; 12-15 parts of polyving akohol; 4-5 parts of tripolycyanamide; 4-6 parts of modified nano carbon powder; and 700-750 parts of water.
Description
Technical field
The invention belongs to building material field, be specifically related to a kind of kervit microbead insulated sand slurry and preparation method thereof.
Background technology
China's exterior-wall heat insulation comprises organic heat insulation system and inorganic heat preservation system and organic and inorganic composite heat-insulating material three class.Wherein, be mainly organic lagging material, produce and operating technique very ripe, but can not prevent fires, contaminate environment, easily aging.Mineral-type thermal insulation mortar material due to its finished product low, intensity is high, insulation, fire prevention, the advantages such as weathering resistance are paid close attention to widely, but still there is the shortcomings such as cost is higher, material source is limited, still have the space of improvement.
Summary of the invention
The object of this invention is to provide a kind of kervit microbead insulated sand slurry and preparation method thereof.
Technical scheme of the present invention is as follows:
A kind of kervit microbead insulated sand slurry, is characterized in that being made up of the raw material of following weight part: cement 300-340, redispersable latex powder 50-55, sepiolite powder 40-45, calcium-base bentonite powder 30-35, ceramic microspheres 20-30, hollow glass microballoon 10-15, aluminium silicate powder 40-45, titanium dioxide 25-30, nanometer fluorite powder 35-40, crystal whisker of gypsum 30-40, alumen 10-12, Weathered Sodium Sulfate 10-12, polyvinyl alcohol 12-15, trimeric cyanamide 4-5, modified Nano carbon dust 4-6, water 700-750; Described modified Nano carbon dust is made up of the raw material of following weight part: nano-sized carbon 10-11, alum 5-6, iron ore ground-slag 1-2, jade powder 4-5, silane resin acceptor kh-550 1-2, Radix Angelicae Sinensis oil 1-2, magnet powder 1-2, silicon carbide 4-5, alcohol ester 12 1-2, tea-polyphenol 1-2, Radix Actinodaphnes Cupularis powder 1-2; Mixed by each material composition, grinding distribution evenly and get final product.
The preparation method of described kervit microbead insulated sand slurry, it is characterized in that other composition later except cement to mix, be heated to 60-70 DEG C, stir 20-30 minute, form slurry, then adds cement mixing and becomes lotion and get final product.
Kervit microbead insulated sand slurry setting time of the present invention is short, fire-retardant, heat-proof quality is good, fire resistance and high insulating effect.
Embodiment
A kind of kervit microbead insulated sand slurry, is made up of the raw material (kilogram) of following weight part: cement 300, redispersable latex powder 50, sepiolite powder 45, calcium-base bentonite powder 30, ceramic microspheres 20, hollow glass microballoon 10, aluminium silicate powder 45, titanium dioxide 25, nanometer fluorite powder 35, crystal whisker of gypsum 30, alumen 10, Weathered Sodium Sulfate 10, polyvinyl alcohol 15, trimeric cyanamide 5, modified Nano carbon dust 4, water 750;
The preparation method of described kervit microbead insulated sand slurry, it is characterized in that other composition later except cement to mix, be heated to 60-70 DEG C, stir 20-30 minute, form slurry, then adds cement mixing and becomes lotion and get final product.
Described modified Nano carbon dust is made up of the raw material of following weight part (kilogram): nano-sized carbon 10, alum 5, iron ore ground-slag 1, jade powder 4, silane resin acceptor kh-550 2, Radix Angelicae Sinensis oil 2, magnet powder 2, silicon carbide 5, alcohol ester 12, tea-polyphenol 2, Radix Actinodaphnes Cupularis powder 1; Mixed by each material composition, grinding distribution evenly and get final product.
Mortar properties of the present invention is: thermal conductivity 0.051W/m.k, and frost resistance meets the requirements (15 times unchanged), and 28d ultimate compression strength: 0.35Mpa, fire-protection rating is A level.
Claims (2)
1. a kervit microbead insulated sand slurry, is characterized in that being made up of the raw material of following weight part: cement 300-340, redispersable latex powder 50-55, sepiolite powder 40-45, calcium-base bentonite powder 30-35, ceramic microspheres 20-30, hollow glass microballoon 10-15, aluminium silicate powder 40-45, titanium dioxide 25-30, nanometer fluorite powder 35-40, crystal whisker of gypsum 30-40, alumen 10-12, Weathered Sodium Sulfate 10-12, polyvinyl alcohol 12-15, trimeric cyanamide 4-5, modified Nano carbon dust 4-6, water 700-750; Described modified Nano carbon dust is made up of the raw material of following weight part: nano-sized carbon 10-11, alum 5-6, iron ore ground-slag 1-2, jade powder 4-5, silane resin acceptor kh-550 1-2, Radix Angelicae Sinensis oil 1-2, magnet powder 1-2, silicon carbide 4-5, alcohol ester 12 1-2, tea-polyphenol 1-2, Radix Actinodaphnes Cupularis powder 1-2; Mixed by each material composition, grinding distribution evenly and get final product.
2. basis is with the preparation method of kervit microbead insulated sand slurry according to claim 1, it is characterized in that to mix except other composition that cement is later, and be heated to 60-70 DEG C, stir 20-30 minute, form slurry, then adds cement mixing and become lotion and get final product.