CN104946120A - Water-based wood paint and preparation method thereof - Google Patents
Water-based wood paint and preparation method thereof Download PDFInfo
- Publication number
- CN104946120A CN104946120A CN201510369898.4A CN201510369898A CN104946120A CN 104946120 A CN104946120 A CN 104946120A CN 201510369898 A CN201510369898 A CN 201510369898A CN 104946120 A CN104946120 A CN 104946120A
- Authority
- CN
- China
- Prior art keywords
- water
- woodware paint
- parts
- aqueous woodware
- aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a water-based wood paint and a preparation method thereof. The water-based wood paint is prepared from the following components in parts by weight: a water-based polyurethane acrylate resin, a methylphenyl acid ester-butyl acrylate copolymer, a thickener, a photoinitiator, a defoaming agent, a dispersing agent, a leveling agent, a filler, a cosolvent and water. The water-based wood paint has the characteristics of high hardness, short film-forming time, simple manufacturing technique and environment friendliness.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of aqueous woodware paint and preparation method thereof.
Background technology
While present stage people quality of life improves, also more and more higher to the requirement of environmental protection.People often use wood lacquer when manufacture furniture; can available protecting wood furniture; strengthen work-ing life of wood furniture, but wood lacquer now on the market exists not environmentally, complex process, and difference of hardness, wear no resistance, the shortcoming such as time of drying is long.
Summary of the invention
For solving above-mentioned shortcoming, the invention provides a kind of aqueous woodware paint, being configured by weight by following composition and forming:
Aqueous polyurethane acrylate resin 40-55 part, aminomethyl phenyl acid esters-butyl acrylate copolymer 30-45 part, thickening material 0.3-0.9 part, light trigger 1-2 part, defoamer 0.5 part, dispersion agent 0.2 part, flow agent 0.2 part, stopping composition 15 parts, solubility promoter 11 parts, water 100-120 part.
Described thickening material is alkali-soluble emulsion thickening material.
Described light trigger is that benzophenone and 184 two kinds of light triggers form by 1:1 proportioning.
Described dispersion agent is polymer copolymerization body.
Described stopping composition is talcum powder.
Described defoamer, flow agent and solubility promoter are the conventional defoamer, flow agent and the solubility promoter that use.
The present invention also provides a kind of preparation method of aqueous woodware paint, comprises the following steps:
First aqueous polyurethane acrylate resin 40-55 part and aminomethyl phenyl acid esters-butyl acrylate copolymer 30-45 part are fully mixed, 10 minutes are stirred after adding light trigger 1-2 part again, then thickening material 0.3-0.9 part, defoamer 0.5 part, dispersion agent 0.2 part, flow agent 0.2 part, stopping composition 15 parts stirring 15-20 minute is added successively, then add solubility promoter 11 parts, water 100-120 part, after dispersion, obtain steady aqueous woodware paint.
Described solubility promoter and water management added in 1 minute.
The present invention adopts the collocation of multiple test method, multiple material complexity, finally determines technological method of the present invention, compared with traditional aqueous woodware paint, has the following advantages:
1. the feature that aqueous woodware paint film formation time of the present invention is short, sharpness is high, hardness is high, wear resistance is high.
2. aqueous wooden ware lacquer craftwork of the present invention is simple, can factorial praluction, and materials environmental protection, not there is volatile organic solvent.
Embodiment
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1: a kind of aqueous woodware paint, is configured by weight by following composition and forms:
Aqueous polyurethane acrylate resin 40 parts, aminomethyl phenyl acid esters-butyl acrylate copolymer 30 parts, thickening material 0.3 part, light trigger 1 part, defoamer 0.5 part, dispersion agent 0.2 part, flow agent 0.2 part, stopping composition 15 parts, solubility promoter 11 parts, 100 parts, water.
Prepare above-mentioned wood lacquer, first aqueous polyurethane acrylate resin and aminomethyl phenyl acid esters-butyl acrylate copolymer are fully mixed, add light trigger again and stir 10 minutes, then add thickening material successively, defoamer, dispersion agent, flow agent part, stopping composition part stirs 15 minutes, then in 1 minute, add solubility promoter and water, after dispersion, obtain steady aqueous woodware paint.
Embodiment 2: a kind of aqueous woodware paint, is configured by weight by following composition and forms:
Aqueous polyurethane acrylate resin 48 parts, aminomethyl phenyl acid esters-butyl acrylate copolymer 38 parts, thickening material 0.6 part, light trigger 1.2 parts, defoamer 0.5 part, dispersion agent 0.2 part, flow agent 0.2 part, stopping composition 15 parts, solubility promoter 11 parts, 110 parts, water.
Prepare above-mentioned wood lacquer, first aqueous polyurethane acrylate resin and aminomethyl phenyl acid esters-butyl acrylate copolymer are fully mixed, add light trigger again and stir 10 minutes, then add thickening material successively, defoamer, dispersion agent, flow agent part, stopping composition part stirs 18 minutes, then in 1 minute, add solubility promoter and water, after dispersion, obtain steady aqueous woodware paint.
Embodiment 3: a kind of aqueous woodware paint, is configured by weight by following composition and forms:
Aqueous polyurethane acrylate resin 55 parts, aminomethyl phenyl acid esters-butyl acrylate copolymer 45 parts, thickening material 0.9 part, light trigger 2 parts, defoamer 0.5 part, dispersion agent 0.2 part, flow agent 0.2 part, stopping composition 15 parts, solubility promoter 11 parts, 120 parts, water.
Prepare above-mentioned wood lacquer, first aqueous polyurethane acrylate resin and aminomethyl phenyl acid esters-butyl acrylate copolymer are fully mixed, add light trigger again and stir 10 minutes, then add thickening material successively, defoamer, dispersion agent, flow agent part, stopping composition part stirs 20 minutes, then in 1 minute, add solubility promoter and water, after dispersion, obtain steady aqueous woodware paint.
The performance test data of embodiment of the present invention 1-3 sees the following form:
As can be seen from the table, each embodiment of aqueous woodware paint of the present invention all meets environmental requirement, has the features such as curing speed is fast, hardness is high, sharpness is high, wear-resisting.
The present invention is not limited only to above-described embodiment, and the improvement that every foundation principle of the invention is done and replacement, all should within protection scope of the present invention.
Claims (7)
1. an aqueous woodware paint, is characterized in that, is configured by weight form by following composition:
Aqueous polyurethane acrylate resin 40-55 part, aminomethyl phenyl acid esters-butyl acrylate copolymer 30-45 part, thickening material 0.3-0.9 part, light trigger 1-2 part, defoamer 0.5 part, dispersion agent 0.2 part, flow agent 0.2 part, stopping composition 15 parts, solubility promoter 11 parts, water 100-120 part.
2. aqueous woodware paint according to claim 1, is characterized in that: described thickening material is alkali-soluble emulsion thickening material.
3. aqueous woodware paint according to claim 1, is characterized in that: described light trigger is that benzophenone and 184 two kinds of light triggers form by 1:1 proportioning.
4. aqueous woodware paint according to claim 1, is characterized in that: described dispersion agent is polymer copolymerization body.
5. aqueous woodware paint according to claim 1, is characterized in that: described stopping composition is talcum powder.
6. a preparation method for the aqueous woodware paint according to any one of claim 1-5, is characterized in that, comprises the following steps:
First aqueous polyurethane acrylate resin 40-55 part and aminomethyl phenyl acid esters-butyl acrylate copolymer 30-45 part are fully mixed, 10 minutes are stirred after adding light trigger 1-2 part again, then thickening material 0.3-0.9 part, defoamer 0.5 part, dispersion agent 0.2 part, flow agent 0.2 part, stopping composition 15 parts stirring 15-20 minute is added successively, then add solubility promoter 11 parts, water 100-120 part, after dispersion, obtain steady aqueous woodware paint.
7. the preparation method of aqueous woodware paint according to claim 6, is characterized in that, described solubility promoter and water management added in 1 minute.