CN104878277A - 一种液压扳手活塞用耐腐蚀球墨铸铁材料及其制备方法 - Google Patents
一种液压扳手活塞用耐腐蚀球墨铸铁材料及其制备方法 Download PDFInfo
- Publication number
- CN104878277A CN104878277A CN201510239110.8A CN201510239110A CN104878277A CN 104878277 A CN104878277 A CN 104878277A CN 201510239110 A CN201510239110 A CN 201510239110A CN 104878277 A CN104878277 A CN 104878277A
- Authority
- CN
- China
- Prior art keywords
- powder
- iron
- piston
- corrosion
- cast iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种液压扳手活塞用耐腐蚀球墨铸铁材料,其含有的化学元素成分及其质量百分比为:Mo0.4-0.66、C2.3-2.8、Mn0.9-1.5、Cr2.3-3.5、Cu0.5-0.9、Si1.2-1.8、Zr0.4-0.7、Ti0.3-0.6、S≤0.01、P0.01-0.02、其余为Fe。本发明活塞添加了Mo、Cu、Si、Zr、Ti,增加了致密性和耐腐蚀性,耐磨性好;本发明生产方法,增加了铸件的抗裂纹性,增加了活塞表面的硬度和抗磨性能,有效地延长了活塞的使用寿命,本发明的球化剂和孕育剂能够使石墨的圆整度更好,有效提高球墨铸铁件的机械性能,抗拉强度高。
Description
技术领域
本发明涉及铸造技术领域,尤其涉及一种液压扳手活塞用耐腐蚀球墨铸铁材料及其制备方法。
背景技术
液压扳手应用到各行各业,液压扳手主要由三部分组成,本体(也叫壳体),油缸和传动部件。油缸活塞是液压扳手的重要组成部件,关系到扳手的工作效率和安全性。
目前活塞还存在着很多问题,还需要提高活塞的硬度、耐磨性、尺寸稳定性、气孔、屈服点、抗疲劳强度、耐腐蚀性。可以通过改进铸件的成分和工艺来改进活塞的性能。
发明内容
本发明的目的在于提供一种液压扳手活塞用耐腐蚀球墨铸铁材料及其制备方法,该活塞材料致密性和耐腐蚀性好,耐磨性好。
本发明的技术方案如下:
一种液压扳手活塞用耐腐蚀球墨铸铁材料,其特征在于:其含有的化学元素成分及其质量百分比为:Mo0.4-0.66、C2.3-2.8、Mn0.9-1.5、Cr2.3-3.5、Cu0.5-0.9、Si1.2-1.8、Zr0.4-0.7、Ti0.3-0.6、S≤0.01、P0.01-0.02、其余为Fe。
所述的液压扳手活塞用耐腐蚀球墨铸铁材料的生产方法,其特征在于:
(1)将原料送入熔炼坩埚,在1550-1650℃下熔炼后检测铁水中各元素的含量并调整各元素含量至符合配方要求;
(2)将相当于铁液重量2.0-2.2%的球化剂倒入浇包中堤坝的一侧,将相当于铁液重量0.3-0.4%的第一孕育剂均匀地覆盖在球化剂上,冲入铁液,进行球化处理和第一次孕育处理,再冲入剩余铁液,相当于铁液重量0.25-0.35%的第二孕育剂随流冲入,完成第二次孕育处理,浇注,得到铸锭;
(3)将铸锭加热至950-1050℃,保温5-6个小时,淬水冷却至100℃以下,再将铸锭加热至600-700℃,保温3-4个小时,再以1-1.5℃/分的速度降温至300-350℃,保温2-3个小时,再自然冷却至室温,进行加工成型;
(4)将整个活塞进行表面氮化处理,氮化处理深度≥0.3mm,即得;
所述球化剂由下列重量份的原料制成:Ba1-1.6、Mg10-12、Ca 1-1.5、Si10-13、稀土 2-3、Fe82-86;制备方法为;将Ba粉、Mg粉、Ca粉、Si粉、稀土混合,加入1/3的铁粉,在氩气氛围中加热至铁粉熔化,搅拌均匀,浇筑,粉碎,过10目筛,得到粉末;将剩余铁粉加入坩埚,将所述粉末用注射法送入铁粉的中央,在氩气氛围中加热至1510-1520℃,在轧辊上轧制成厚度为4-5mm的薄片,再粉碎成粒径小于4mm的颗粒,即得;
所述第一孕育剂由下列重量份的原料制成:La0.1-0.3、Mg3-4、Ca2-4、Mn1-2、Nb0.4-0.7、Si25-30、Fe71-75;制备方法为,将金属粉末混合,在氩气氛围中研磨10-20分钟,即得;
所述第一孕育剂由下列重量份的原料制成:Y0.1-0.3、Mg2-3、Ca3-5、Mn2-4、Sr0.5-0.7、Si29-35、Fe71-75;制备方法为,将金属粉末混合,在氩气氛围中研磨10-20分钟,即得。
本发明的有益效果
本发明活塞添加了Mo、Cu、Si、Zr、Ti,增加了致密性和耐腐蚀性,耐磨性好;本发明生产方法,增加了铸件的抗裂纹性,增加了活塞表面的硬度和抗磨性能,有效地延长了活塞的使用寿命,本发明的球化剂和孕育剂能够使石墨的圆整度更好,有效提高球墨铸铁件的机械性能,抗拉强度高。
具体实施方式
一种液压扳手活塞用耐腐蚀球墨铸铁材料,其含有的化学元素成分及其质量百分比为:Mo0.4-0.66、C2.3-2.8、Mn0.9-1.5、Cr2.3-3.5、Cu0.5-0.9、Si1.2-1.8、Zr0.4-0.7、Ti0.3-0.6、S≤0.01、P0.01-0.02、其余为Fe。
所述的液压扳手活塞用耐腐蚀球墨铸铁材料的生产方法为:
(1)将原料送入熔炼坩埚,在1600℃下熔炼后检测铁水中各元素的含量并调整各元素含量至符合配方要求;
(2)将相当于铁液重量2.1%的球化剂倒入浇包中堤坝的一侧,将相当于铁液重量0.3%的第一孕育剂均匀地覆盖在球化剂上,冲入铁液,进行球化处理和第一次孕育处理,再冲入剩余铁液,相当于铁液重量0.3%的第二孕育剂随流冲入,完成第二次孕育处理,浇注,得到铸锭;
(3)将铸锭加热至1000℃,保温5.5个小时,淬水冷却至90℃,再将铸锭加热至650℃,保温3.5个小时,再以1.3℃/分的速度降温至330℃,保温2.5个小时,再自然冷却至室温,进行加工成型;
(4)将整个活塞进行表面氮化处理,氮化处理深度为0.35mm,即得;
所述球化剂由下列重量份(公斤)的原料制成:Ba1.3、Mg11、Ca 1.3、Si12、稀土 2.5、Fe84;制备方法为;将Ba粉、Mg粉、Ca粉、Si粉、稀土混合,加入1/3的铁粉,在氩气氛围中加热至铁粉熔化,搅拌均匀,浇筑,粉碎,过10目筛,得到粉末;将剩余铁粉加入坩埚,将所述粉末用注射法送入铁粉的中央,在氩气氛围中加热至1515℃,在轧辊上轧制成厚度为4mm的薄片,再粉碎成粒径小于4mm的颗粒,即得;
所述第一孕育剂由下列重量份(公斤)的原料制成:La0.2、Mg3.5、Ca3、Mn1.5、Nb0.5、Si27、Fe73;制备方法为,将金属粉末混合,在氩气氛围中研磨15分钟,即得;
所述第一孕育剂由下列重量份(公斤)的原料制成:Y0.2、Mg2.5、Ca4、Mn3、Sr0.6、Si32、Fe73;制备方法为,将金属粉末混合,在氩气氛围中研磨15分钟,即得。
实验数据:
该实施例的材料经测试,抗拉强度为628MPa,延伸率为12.3%,屈服强度为392MPa,表面硬度为194HBW,韧性为9.8J/㎡。
Claims (2)
1.一种液压扳手活塞用耐腐蚀球墨铸铁材料,其特征在于:其含有的化学元素成分及其质量百分比为:Mo0.4-0.66、C2.3-2.8、Mn0.9-1.5、Cr2.3-3.5、Cu0.5-0.9、Si1.2-1.8、Zr0.4-0.7、Ti0.3-0.6、S≤0.01、P0.01-0.02、其余为Fe。
2.根据权利要求1所述的液压扳手活塞用耐腐蚀球墨铸铁材料的生产方法,其特征在于:
(1)将原料送入熔炼坩埚,在1550-1650℃下熔炼后检测铁水中各元素的含量并调整各元素含量至符合配方要求;
(2)将相当于铁液重量2.0-2.2%的球化剂倒入浇包中堤坝的一侧,将相当于铁液重量0.3-0.4%的第一孕育剂均匀地覆盖在球化剂上,冲入铁液,进行球化处理和第一次孕育处理,再冲入剩余铁液,相当于铁液重量0.25-0.35%的第二孕育剂随流冲入,完成第二次孕育处理,浇注,得到铸锭;
(3)将铸锭加热至950-1050℃,保温5-6个小时,淬水冷却至100℃以下,再将铸锭加热至600-700℃,保温3-4个小时,再以1-1.5℃/分的速度降温至300-350℃,保温2-3个小时,再自然冷却至室温,进行加工成型;
(4)将整个活塞进行表面氮化处理,氮化处理深度≥0.3mm,即得;
所述球化剂由下列重量份的原料制成:Ba1-1.6、Mg10-12、Ca 1-1.5、Si10-13、稀土 2-3、Fe82-86;制备方法为;将Ba粉、Mg粉、Ca粉、Si粉、稀土混合,加入1/3的铁粉,在氩气氛围中加热至铁粉熔化,搅拌均匀,浇筑,粉碎,过10目筛,得到粉末;将剩余铁粉加入坩埚,将所述粉末用注射法送入铁粉的中央,在氩气氛围中加热至1510-1520℃,在轧辊上轧制成厚度为4-5mm的薄片,再粉碎成粒径小于4mm的颗粒,即得;
所述第一孕育剂由下列重量份的原料制成:La0.1-0.3、Mg3-4、Ca2-4、Mn1-2、Nb0.4-0.7、Si25-30、Fe71-75;制备方法为,将金属粉末混合,在氩气氛围中研磨10-20分钟,即得;
所述第一孕育剂由下列重量份的原料制成:Y0.1-0.3、Mg2-3、Ca3-5、Mn2-4、Sr0.5-0.7、Si29-35、Fe71-75;制备方法为,将金属粉末混合,在氩气氛围中研磨10-20分钟,即得。