CN104877264A - Wood-plastic board composition - Google Patents
Wood-plastic board composition Download PDFInfo
- Publication number
- CN104877264A CN104877264A CN201510259944.5A CN201510259944A CN104877264A CN 104877264 A CN104877264 A CN 104877264A CN 201510259944 A CN201510259944 A CN 201510259944A CN 104877264 A CN104877264 A CN 104877264A
- Authority
- CN
- China
- Prior art keywords
- wood
- parts
- plastic board
- board composition
- plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a wood-plastic board composition, relating to the technical field of wood-plastic floorboards. The wood-plastic board composition is characterized by comprising the following components in parts by weight: 35-50 parts of PVC (polyvinyl chloride), 45-65 parts of calcium carbonate, 4-6 parts of blowing promotor, 0.3-1 part of plasticizer, 0.5-1 part of lubricant, 0-2 parts of wood meal and 3-5 parts of clinoptilolite. The wood-plastic board has the advantages of high strength, low deformation tendency, favorable plasticity and lower reflectance.
Description
Technical field:
The present invention relates to wood-plastic floor board production technical field, specifically plate composition moulded by a kind of wood.
Background technology:
Wood-plastic floor board is a kind of novel environment-friendly wood-plastic composite material products, aborning, the wooden phenol that produces in high density fiberboard process, adds reprocessed plastic(s) and makes wood plastic composite through granulating equipment, then carry out extrusion group and make wood-plastic floor board.Wood-plastic composite panel is a kind of primarily of material and thermoplastic macromolecule material (plastics) and processing aid etc. based on timber (wood cellulose, plant cellulose), the high-tech environmental protection new decorative material made through die apparatus heating extrusion moulding again after mixing, having performance and the feature of timber and plastics concurrently, is the advanced composite material that can substitute timber and plastics.The intensity of more existing Wood plastic boards material is lower, easy flexural deformation, and the plastotype of template is poor, and has higher reflectance under light illumination, more dazzling.
Summary of the invention:
It is high that technical problem to be solved by this invention is to provide a kind of wood to mould plate intensity, and be not easy distortion, template plastotype is good, and plate composition moulded by the wood that reflectance is lower.
Technical problem to be solved by this invention realizes by the following technical solutions.
Plate composition moulded by a kind of wood, it is characterized in that: comprise following component by weight,
Comprise following component by weight,
By also comprising chabazite 0.2 ~ 0.4 by weight.
At the clinoptilolite at rock dense structure place, be like radial plate aggregate titanium miniplate more, and at pores'growth place, the plate crystal of the intact or intact geometric shape of part of tool can be formed, widely reach 20mm, thick about 5mm, end is about in 120 degree of angles, therefore clinoptilolite has good tabular plastotype ability, and joining in the present invention can the function of plastotype, also can strengthen intensity.
The large I of chabazite feature titanium miniplate short water chestnut cylindricality is from 1mm to a few mm, and diamond structure has good light-dispersing effect, can reduce the reflectance of base plate.
The invention has the beneficial effects as follows: it is high that plate intensity moulded by wood of the present invention, be not easy distortion, template plastotype is good, and reflectance is lower.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
Plate composition moulded by a kind of wood, comprises following component by weight,
Embodiment 2
Plate composition moulded by a kind of wood, comprises following component by weight,
By also comprising chabazite 0.3 by weight.
Embodiment 3
Plate composition moulded by a kind of wood, comprises following component by weight,
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (3)
1. a plate composition moulded by wood, it is characterized in that: comprise following component by weight,
2. plate composition moulded by a kind of wood according to claim 1, it is characterized in that: comprise following component by weight,
3. plate composition moulded by a kind of wood according to claim 1, it is characterized in that: by also comprising chabazite 0.2 ~ 0.4 by weight.