CN104861856A - Modified wear-resistance paint for casts - Google Patents
Modified wear-resistance paint for casts Download PDFInfo
- Publication number
- CN104861856A CN104861856A CN201510285531.4A CN201510285531A CN104861856A CN 104861856 A CN104861856 A CN 104861856A CN 201510285531 A CN201510285531 A CN 201510285531A CN 104861856 A CN104861856 A CN 104861856A
- Authority
- CN
- China
- Prior art keywords
- parts
- modified
- polyurethane
- component
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses modified wear-resistance paint for casts. The paint is prepared from the following components in parts by weight: 20-27 parts of dual-component polyurethane, 15-22 parts of modified graphene, 6-8 parts of mica powder, 2-3 parts of a silane coupling agent KH-570, 5-7 parts of sodium orthophosphate, 8-19 parts of an alkyd resin, 5-9 parts of aluminum silicate, 25-35 parts of acrylic modified polyurethane, and 15-26 parts of a glycerine epoxy resin. The invention provides the modified wear-resistance paint for the casts, and the outside paint films of the casts, using the paint, not only have high abrasion resistance, but also have high corrosion resistance.
Description
Technical field
The present invention relates to coating, especially, relate to a kind of Modified Abrasion Resistant Coatings for foundry goods.
Background technology
Coating is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.
Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.The classification of the Chemicals of passing through according to the modern times, coating belongs to fine chemical product.Modern coating is progressively becoming the polyfunctional engineering materials of a class, is an important industry in chemical industry.Existing casting exterior film often comes off because of wearing and tearing, causes bad order or impact to use.
Summary of the invention
The object of the invention is to provide a kind of Modified Abrasion Resistant Coatings for foundry goods, often comes off because of wearing and tearing, cause the problem that bad order or impact use to solve the outside film of prior art medium casting.
For achieving the above object, the invention provides a kind of Modified Abrasion Resistant Coatings for foundry goods, wherein, this coating is made up of the component of following weight fraction:
Two component polyurethane 20-27 part;
Modified graphene 15-22 part;
Mica powder 6-8 part;
Silane coupling reagent KH-570 2-3 part;
Sodium orthophosphate 5-7 part;
Synolac 8-19 part;
Pure aluminium silicate 5-9 parts;
Acrylic acid modified polyurethane 25-35 part; And
Glycerol epoxy resin 15-26 part.
Further, the invention provides a kind of Modified Abrasion Resistant Coatings for foundry goods, wherein, this coating is made up of the component of following weight fraction: two component polyurethane 25 parts; Modified graphene 18 parts; Mica powder 6 parts; Silane coupling reagent KH-570 3 parts; Sodium orthophosphate 5 parts; Synolac 15 parts; Pure aluminium silicate 9 parts; Acrylic acid modified polyurethane 35 parts; And glycerol epoxy resin 26 parts.
Further, the invention provides a kind of Modified Abrasion Resistant Coatings for foundry goods, wherein, this coating is made up of the component of following weight fraction: two component polyurethane 20 parts; Modified graphene 18 parts; Mica powder 6 parts; Silane coupling reagent KH-570 2 parts; Sodium orthophosphate 5 parts; Synolac 10 parts; Pure aluminium silicate 8 parts; Acrylic acid modified polyurethane 30 parts; And glycerol epoxy resin 20 parts.
The present invention has following beneficial effect: the invention provides a kind of Modified Abrasion Resistant Coatings for foundry goods, and not only wear resisting property is high to use the casting exterior film of this coating, and corrosion resistance and good.
Embodiment
The Modified Abrasion Resistant Coatings for foundry goods that this preferred embodiment provides, its specific implementation process is as follows:
The invention provides a kind of Modified Abrasion Resistant Coatings for foundry goods, wherein, this coating is made up of the component of following weight fraction:
Two component polyurethane 20-27 part;
Modified graphene 15-22 part;
Mica powder 6-8 part;
Silane coupling reagent KH-570 2-3 part;
Sodium orthophosphate 5-7 part;
Synolac 8-19 part;
Pure aluminium silicate 5-9 parts;
Acrylic acid modified polyurethane 25-35 part; And
Glycerol epoxy resin 15-26 part.
Embodiment 1:
Wherein, this coating is made up of the component of following weight fraction: two component polyurethane 25 parts; Modified graphene 18 parts; Mica powder 6 parts; Silane coupling reagent KH-570 3 parts; Sodium orthophosphate 5 parts; Synolac 15 parts; Pure aluminium silicate 9 parts; Acrylic acid modified polyurethane 35 parts; And glycerol epoxy resin 26 parts.
Embodiment 2:
Wherein, this coating is made up of the component of following weight fraction: two component polyurethane 20 parts; Modified graphene 18 parts; Mica powder 6 parts; Silane coupling reagent KH-570 2 parts; Sodium orthophosphate 5 parts; Synolac 10 parts; Pure aluminium silicate 8 parts; Acrylic acid modified polyurethane 30 parts; And glycerol epoxy resin 20 parts.
As can be seen from the above description, the above embodiments of the present invention achieve following technique effect:
The invention provides a kind of Modified Abrasion Resistant Coatings for foundry goods, not only wear resisting property is high to use the casting exterior film of this coating, and corrosion resistance and good.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention; For a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. for a Modified Abrasion Resistant Coatings for foundry goods, it is characterized in that, this coating is made up of the component of following weight fraction:
Two component polyurethane 20-27 part;
Modified graphene 15-22 part;
Mica powder 6-8 part;
Silane coupling reagent KH-570 2-3 part;
Sodium orthophosphate 5-7 part;
Synolac 8-19 part;
Pure aluminium silicate 5-9 parts;
Acrylic acid modified polyurethane 25-35 part; And
Glycerol epoxy resin 15-26 part.
2. the Modified Abrasion Resistant Coatings for foundry goods according to claim 1, is characterized in that, this coating is made up of the component of following weight fraction: two component polyurethane 25 parts; Modified graphene 18 parts; Mica powder 6 parts; Silane coupling reagent KH-570 3 parts; Sodium orthophosphate 5 parts; Synolac 15 parts; Pure aluminium silicate 9 parts; Acrylic acid modified polyurethane 35 parts; And glycerol epoxy resin 26 parts.
3. the Modified Abrasion Resistant Coatings for foundry goods according to claim 1, is characterized in that, this coating is made up of the component of following weight fraction: two component polyurethane 20 parts; Modified graphene 18 parts; Mica powder 6 parts; Silane coupling reagent KH-570 2 parts; Sodium orthophosphate 5 parts; Synolac 10 parts; Pure aluminium silicate 8 parts; Acrylic acid modified polyurethane 30 parts; And glycerol epoxy resin 20 parts.